Molybdenum disilicide （MoSi2） sheath and aluminum oxide （Al2O3） core blended powders were fabricated by spray drying. A derived coating material was produced for the application as microwave absorbers using the as...Molybdenum disilicide （MoSi2） sheath and aluminum oxide （Al2O3） core blended powders were fabricated by spray drying. A derived coating material was produced for the application as microwave absorbers using the as prepared powders by atmospheric plasma spray （APS） technology. The effects of MoSi2/Al2O3 mass ratio on the dielectric and physical mechanical properties of the composite coatings were investigated. When the MoSi2 content of the composites increases from 0 to 45%, the flexure strength and fracture toughness improve from 198 to 324 MPa and 3.05 to 4.82 MPa-m1/2 then decline to 310 MPa and 4.67 MPa-m1/2, respectively. The dielectric loss tangent increases with increasing MoSi2 content, and the real part of permittivity decreases conversely over the frequency range of 8.2-12.4 GHz. These effects are due to the agglomeration of early molten MoSi2 particles and the increase of the electrical conductivity with increasing MoSi2 content.展开更多
The pyrolytic carbon （PyC） coatings were fabricated on A1203 fiber fabrics by the method of chemical vapor deposition （CVD）. The microstructures of A1203 fibers with and without PyC coatings were characterized by ...The pyrolytic carbon （PyC） coatings were fabricated on A1203 fiber fabrics by the method of chemical vapor deposition （CVD）. The microstructures of A1203 fibers with and without PyC coatings were characterized by SEM and Raman spectroscopy. The influence of deposition time of PyC on the DC conductivity （ad） of A1203 filaments and complex permittivity of fabrics at X band （8.2-12.4 GHz） were investigated. The values of Crd and complex permittivity increase with increasing deposition time of PyC. The electron relaxation polarization and conductance loss were supposed to be contributed to the increase of ε＇ and ε＂, respectively. In addition, the reflection loss （RL） of fabrics was calculated. The results show that the microwave absorbing properties of Al2O3 fiber fabrics can be improved by PyC coatings. The best RL results are for 60 min-deposition sample, of which the minimum value is about -40.4 dB at about 9.5 GHz and the absorbing frequency band （AFB） is about 4 GHz.展开更多
Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and cer...Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.展开更多
Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employ...Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.展开更多
To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And e...To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And effect of Y2O3 content on gradient bioceramic composite coating was studied. The experimental results indicate that adding rare earth can refine grain. Different rare earth contents affect formation of HA and β-TCP in bioceramic coating. When the content of rare earth ranges from 0.4% to 0.6%, the active extent of rare earth in synthesizing HA and β-TCP is the best, which indicates that “monosodium glutamate” effect of rare earth plays a dominant role. However, when rare earth content is up to 0.8%, the amount of synthesizing HA and β-TCP in coating conversely goes down, which demonstrates that rare earth gradually losts its catalysis in manufacturing HA and β-TCP.展开更多
Cored wires for electric arc spraying of Al/Al 2 O 3 MMC coatings were developed, with Al 2 O 3 powder as the core material and commercial aluminium strip as the retaining sheath. The bond strength, ...Cored wires for electric arc spraying of Al/Al 2 O 3 MMC coatings were developed, with Al 2 O 3 powder as the core material and commercial aluminium strip as the retaining sheath. The bond strength, Al 2 O 3 content, microstructure, micro-hardness and wear resistance of coatings produced by arc spraying of the cored wires were experimentally investigated and were compared with those of pure aluminum coating.展开更多
The commonly-employed material for thermal barrier coatings(TBCs)is 7 wt.%Y2O3 ZrO2(7YSZ),generally deposited by electron beam-physical vapor deposition(EB-PVD).Due to the increasing demand for higher operating temper...The commonly-employed material for thermal barrier coatings(TBCs)is 7 wt.%Y2O3 ZrO2(7YSZ),generally deposited by electron beam-physical vapor deposition(EB-PVD).Due to the increasing demand for higher operating temperature in aero-derivative gas turbines,a lot of effort has been made to prevent the premature failure of columnar 7YSZ TBCs,which is induced by the microstructure degradation,sintering and spallation after the deposition of infiltrated siliceous mineral(consisting of calcium magnesium aluminum silicate(CaO MgO Al2O3 SiO2,i.e.,CMAS)).A new method called Al-modification for columnar 7YSZ TBCs against CMAS corrosion was present.The Al film was magnetron-sputtered on the surface of the columnar 7YSZ TBCs,followed by performing vacuum heat treatment of the Al-deposited TBCs.During the heat treatment,the molten Al reacted with ZrO2 to formα-Al2O3 overlay that effectively hindered CMAS infiltration.Moreover,the Al film could evaporate and re-nucleate,leading to the generation of Al2O3 nanowires,which further restrained the moving of molten CMAS.展开更多
Two types of plasma sprayed coatings (NiCrAlY and NiCrAlY-A12O3) were remelted by a 5 kW cw CO2 laser. With increasing laser power and decreasing traverse speed in the ranges of 200-700 W and 5-30 mm/s respectively, t...Two types of plasma sprayed coatings (NiCrAlY and NiCrAlY-A12O3) were remelted by a 5 kW cw CO2 laser. With increasing laser power and decreasing traverse speed in the ranges of 200-700 W and 5-30 mm/s respectively, the melted track grew in width and depth. In the optimum range of laser parameters, a homogeneous remelted layer without voids, cavities, unmelted particles and microcracks was formed. On the surface of remelted layers, Al203 and YAIO3 were detected. As a result of isothermal oxidation tests, weight gains of laser remelted coatings were obviously lower than that only plasma sprayed, especially laser remelted NiCrAlY-Al2O3 coatings. The effects of laser remelting and incorporation of A12O3 second phase in N1CrAlY matrix on high temperature oxidation resistance were discussed.展开更多
ZrO2, Al2O3, ZrO2/Al2O3 and Al2O3/ZrO2 coatings were fabricated on low carbon steel using atmospheric plasma spraying technique. The microstructure and phase composition of the as-sprayed coatings were examined by sca...ZrO2, Al2O3, ZrO2/Al2O3 and Al2O3/ZrO2 coatings were fabricated on low carbon steel using atmospheric plasma spraying technique. The microstructure and phase composition of the as-sprayed coatings were examined by scanning electron microscopy （SEM） and X-ray diffraction （XRD）, respectively. The polarization test, salt spray test and immersion test were used to investigate the corrosion behavior of the coatings in 3.5% NaCl solution. The results suggested that the bilayered Al2O3/ZrO2 coating exhibits superior corrosion resistance when compared with the other coatings. This is ascribed to the presence of very few interconnected pores and stable phases in the coating.展开更多
Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser. Al2O3 coatings were sprayed by air pl...Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser. Al2O3 coatings were sprayed by air plasma spray（APS） on the 45^# steel substrate, and then were irradiated by CO2 CW laser from 795 W/cm^2 to 31 830 W/cm^2. As the output power of the laser is increasing, its porosity is increasing and cracks are appearing and spreading quickly, And also the phase will transform from γ-Al2O3 to a-Al2O3 in the damaged areas. When the energy density is 17 507 W/cm^2, the coatings are destroyed completely. The thermal infection field on substrate is rather small. The laser energy is depleted by the phase transformation and cracks in Al2O3 coatings during the laser thermal shock.展开更多
NiCoCrAlY-ZrO2·Y2O3 coatings were deposited on the substrates by using a technology of combining electron,atom and ion beams （three beams）. Isothermal oxidation for these samples was performed at 1100℃ for 100...NiCoCrAlY-ZrO2·Y2O3 coatings were deposited on the substrates by using a technology of combining electron,atom and ion beams （three beams）. Isothermal oxidation for these samples was performed at 1100℃ for 100-300 h. The results show that a thermally grown oxide （TGO） layer was formed between NiCoCrAlY layer and oxidation. The TGO contains α-Al2O3 and Y4Al2O9 etc. oxides. The intensity ratio of α-Al2O3/Y4Al2O9 was monotonously decreased with increasing oxidation time based on XRD （X-ray diffraction） analysis. The Y4Al2O9 phase plays the most important role in high temperature oxidation resistance at 1100℃. The related mechanism was also discussed.展开更多
The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influenc...The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influences of contents and sizes of AlOon the structure and wearability were investigated.The results show that the wear resistance of the coating would be increased greatly by adding AlO,but the spray weldability decreases with increasing AlOcontent.So there is an optimal content of AlOpowder.The composite coating with AlOnano or sub-micron powder of 0.5% has the best abrasive resistance,while the optimal content of AlOmicron powder is 1 %.展开更多
To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composi...To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.展开更多
Al2O3p/Al composite coatings were prepared on the surface of AZ31 magnesium alloy by plasma spraying technology with mixed powders of Al and Al2O3. An orthogonal test containing six factors and five levels was carried...Al2O3p/Al composite coatings were prepared on the surface of AZ31 magnesium alloy by plasma spraying technology with mixed powders of Al and Al2O3. An orthogonal test containing six factors and five levels was carried out to acquire the optimum technical parameters. Mierostruetures and properties of the composite coatings were studied. The results show that the coatings consist of Al2O3 particulates distributed uniformly and Al matrix, and the interface between the particulate and matrix is continuous, compact and clean. With increasing the mass fraction of Al2O3 in the mixed powders, the volume fraction of Al2O3 in the coatings iacreases. The Al2O3p/Al composite coating with 14% Al2O3 volume fraction has more compact microstrueture and more satisfactory properties.展开更多
基金Project (50572090) supported by the National Natural Science Foundation of ChinaProject (KP200901) supported by the States Key Laboratory of Solidification Processing in NWPU, China
文摘Molybdenum disilicide （MoSi2） sheath and aluminum oxide （Al2O3） core blended powders were fabricated by spray drying. A derived coating material was produced for the application as microwave absorbers using the as prepared powders by atmospheric plasma spray （APS） technology. The effects of MoSi2/Al2O3 mass ratio on the dielectric and physical mechanical properties of the composite coatings were investigated. When the MoSi2 content of the composites increases from 0 to 45%, the flexure strength and fracture toughness improve from 198 to 324 MPa and 3.05 to 4.82 MPa-m1/2 then decline to 310 MPa and 4.67 MPa-m1/2, respectively. The dielectric loss tangent increases with increasing MoSi2 content, and the real part of permittivity decreases conversely over the frequency range of 8.2-12.4 GHz. These effects are due to the agglomeration of early molten MoSi2 particles and the increase of the electrical conductivity with increasing MoSi2 content.
基金Project (51072165) supported by the National Natural Science Foundation of ChinaProject (KP200901) supported by the Fund of the State Key Laboratory of Solidification Processing,China
文摘The pyrolytic carbon （PyC） coatings were fabricated on A1203 fiber fabrics by the method of chemical vapor deposition （CVD）. The microstructures of A1203 fibers with and without PyC coatings were characterized by SEM and Raman spectroscopy. The influence of deposition time of PyC on the DC conductivity （ad） of A1203 filaments and complex permittivity of fabrics at X band （8.2-12.4 GHz） were investigated. The values of Crd and complex permittivity increase with increasing deposition time of PyC. The electron relaxation polarization and conductance loss were supposed to be contributed to the increase of ε＇ and ε＂, respectively. In addition, the reflection loss （RL） of fabrics was calculated. The results show that the microwave absorbing properties of Al2O3 fiber fabrics can be improved by PyC coatings. The best RL results are for 60 min-deposition sample, of which the minimum value is about -40.4 dB at about 9.5 GHz and the absorbing frequency band （AFB） is about 4 GHz.
基金Project (59975046) supported by the National Natural Science Foundation of China
文摘Al2O3-13%TiO2 （mass fraction） coatings, prepared by laser cladding on nickel-based alloy, were heated using high frequency induction sources. The coating microstructure and the interface between bond coating and ceramic coating were characterized by SEM, XRD and EDS. The results show that two-layer substructure exists in the ceramic coating： one layer evolving from fully melted region where the sintered grains grow fully; another layer resembling the liquid-phase-sintered structure consisting of three-dimensional net where the melted Al2O3 particles are embedded in the TiO2-rich matrix. The mechanism of the two-layer substructure formation is also explained in terms of the melting and flattening behavior of the powders during laser cladding processing. The spinel compounds NiAl2O4 and acicular compounds Cr2O3 are discovered in the interface between bond coating and ceramic coating. It proves that the chemical reactions in the laser cladding process will significantly enhance the coating adhesion.
基金Project (50771021) supported by the National Natural Science Foundation of China
文摘Al2O3/Au nano-laminated composite coatings were prepared by means of magnetron sputtering. The coating was compact and comprised of nano-laminated Al2O3 and Au layers. High temperature cyclic oxidation test was employed to investigate the oxidation resistance of the composite coatings. The results revealed that the applied Al2O3/Au nano-laminated composite coatings improved the oxidation and spallation resistance of the stainless steel substrate significantly. The mechanism accounting for oxidation resistance was related with the suppression of inward oxygen diffusion and selective oxidation of Cr in the substrate. The mechanism accounting for spallation resistance was attributed to the relaxation of thermal stress by the nano-laminated structure.
基金Project supported by Governor's Foundation of Guizhou Province (2004-07)
文摘To eliminate thermal stress and cracks in the process of laser cladding, a kind of bioceramic coating with gradient compositional design was prepared on the surface of Ti alloy by using wide-band laser cladding. And effect of Y2O3 content on gradient bioceramic composite coating was studied. The experimental results indicate that adding rare earth can refine grain. Different rare earth contents affect formation of HA and β-TCP in bioceramic coating. When the content of rare earth ranges from 0.4% to 0.6%, the active extent of rare earth in synthesizing HA and β-TCP is the best, which indicates that “monosodium glutamate” effect of rare earth plays a dominant role. However, when rare earth content is up to 0.8%, the amount of synthesizing HA and β-TCP in coating conversely goes down, which demonstrates that rare earth gradually losts its catalysis in manufacturing HA and β-TCP.
文摘Cored wires for electric arc spraying of Al/Al 2 O 3 MMC coatings were developed, with Al 2 O 3 powder as the core material and commercial aluminium strip as the retaining sheath. The bond strength, Al 2 O 3 content, microstructure, micro-hardness and wear resistance of coatings produced by arc spraying of the cored wires were experimentally investigated and were compared with those of pure aluminum coating.
基金Project(2017YFB0306100) supported by the National Key Research&Development Plan of ChinaProjects(51801034,51771059) supported by the National Natural Science Foundation of China+3 种基金Projects(2018GDASCX-0949,2018GDASCX-0950,2017GDASCX-0111) supported by the Guangdong Academy of Sciences,ChinaProjects(2017B090916002,2017A070701027) supported by the Guangdong Technical Research Program,ChinaProjects(2016A030312015,2017A030310315) supported by the Natural Science Foundation of Guangdong Province,ChinaProjects(201605131008557,201707010385) supported by the Technical Research Program of Guangzhou City,China
文摘The commonly-employed material for thermal barrier coatings(TBCs)is 7 wt.%Y2O3 ZrO2(7YSZ),generally deposited by electron beam-physical vapor deposition(EB-PVD).Due to the increasing demand for higher operating temperature in aero-derivative gas turbines,a lot of effort has been made to prevent the premature failure of columnar 7YSZ TBCs,which is induced by the microstructure degradation,sintering and spallation after the deposition of infiltrated siliceous mineral(consisting of calcium magnesium aluminum silicate(CaO MgO Al2O3 SiO2,i.e.,CMAS)).A new method called Al-modification for columnar 7YSZ TBCs against CMAS corrosion was present.The Al film was magnetron-sputtered on the surface of the columnar 7YSZ TBCs,followed by performing vacuum heat treatment of the Al-deposited TBCs.During the heat treatment,the molten Al reacted with ZrO2 to formα-Al2O3 overlay that effectively hindered CMAS infiltration.Moreover,the Al film could evaporate and re-nucleate,leading to the generation of Al2O3 nanowires,which further restrained the moving of molten CMAS.
文摘Two types of plasma sprayed coatings (NiCrAlY and NiCrAlY-A12O3) were remelted by a 5 kW cw CO2 laser. With increasing laser power and decreasing traverse speed in the ranges of 200-700 W and 5-30 mm/s respectively, the melted track grew in width and depth. In the optimum range of laser parameters, a homogeneous remelted layer without voids, cavities, unmelted particles and microcracks was formed. On the surface of remelted layers, Al203 and YAIO3 were detected. As a result of isothermal oxidation tests, weight gains of laser remelted coatings were obviously lower than that only plasma sprayed, especially laser remelted NiCrAlY-Al2O3 coatings. The effects of laser remelting and incorporation of A12O3 second phase in N1CrAlY matrix on high temperature oxidation resistance were discussed.
文摘ZrO2, Al2O3, ZrO2/Al2O3 and Al2O3/ZrO2 coatings were fabricated on low carbon steel using atmospheric plasma spraying technique. The microstructure and phase composition of the as-sprayed coatings were examined by scanning electron microscopy （SEM） and X-ray diffraction （XRD）, respectively. The polarization test, salt spray test and immersion test were used to investigate the corrosion behavior of the coatings in 3.5% NaCl solution. The results suggested that the bilayered Al2O3/ZrO2 coating exhibits superior corrosion resistance when compared with the other coatings. This is ascribed to the presence of very few interconnected pores and stable phases in the coating.
基金the Ministerial Level Advanced Research Foundation (1040020440703)
文摘Rules and mechanism of damage in Al2O3 coatings irradiated by CO2 CW laser are studied in order to improve the ability of parts of equipment standing against the high power laser. Al2O3 coatings were sprayed by air plasma spray（APS） on the 45^# steel substrate, and then were irradiated by CO2 CW laser from 795 W/cm^2 to 31 830 W/cm^2. As the output power of the laser is increasing, its porosity is increasing and cracks are appearing and spreading quickly, And also the phase will transform from γ-Al2O3 to a-Al2O3 in the damaged areas. When the energy density is 17 507 W/cm^2, the coatings are destroyed completely. The thermal infection field on substrate is rather small. The laser energy is depleted by the phase transformation and cracks in Al2O3 coatings during the laser thermal shock.
基金financial supports from the National High-Tech Research and Development Program of China("863"Program,863-715-23-01-02)the National Natural Science Foundation of China(No.59441009).
文摘NiCoCrAlY-ZrO2·Y2O3 coatings were deposited on the substrates by using a technology of combining electron,atom and ion beams （three beams）. Isothermal oxidation for these samples was performed at 1100℃ for 100-300 h. The results show that a thermally grown oxide （TGO） layer was formed between NiCoCrAlY layer and oxidation. The TGO contains α-Al2O3 and Y4Al2O9 etc. oxides. The intensity ratio of α-Al2O3/Y4Al2O9 was monotonously decreased with increasing oxidation time based on XRD （X-ray diffraction） analysis. The Y4Al2O9 phase plays the most important role in high temperature oxidation resistance at 1100℃. The related mechanism was also discussed.
基金Item Sponsored by Provincial Natural Science Foundation of Jiangsu of China(BK2000012)
文摘The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influences of contents and sizes of AlOon the structure and wearability were investigated.The results show that the wear resistance of the coating would be increased greatly by adding AlO,but the spray weldability decreases with increasing AlOcontent.So there is an optimal content of AlOpowder.The composite coating with AlOnano or sub-micron powder of 0.5% has the best abrasive resistance,while the optimal content of AlOmicron powder is 1 %.
基金Funded by the national Natural Science Foundation of China (No. 51075293)the Foundation for Development of Science and Technology of Taiyuan University of Technology,China(No.K201014)
文摘To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.
基金This research was supported by Jilin Province Science Foundation （No. 20090552）.
文摘Al2O3p/Al composite coatings were prepared on the surface of AZ31 magnesium alloy by plasma spraying technology with mixed powders of Al and Al2O3. An orthogonal test containing six factors and five levels was carried out to acquire the optimum technical parameters. Mierostruetures and properties of the composite coatings were studied. The results show that the coatings consist of Al2O3 particulates distributed uniformly and Al matrix, and the interface between the particulate and matrix is continuous, compact and clean. With increasing the mass fraction of Al2O3 in the mixed powders, the volume fraction of Al2O3 in the coatings iacreases. The Al2O3p/Al composite coating with 14% Al2O3 volume fraction has more compact microstrueture and more satisfactory properties.