The selection of appropriate materials for the transportation pipelines is of vital importance to ensure the safety operation in Carbon Capture,Utilisation and Storage(CCUS).To clarify the effects of Cr content in ste...The selection of appropriate materials for the transportation pipelines is of vital importance to ensure the safety operation in Carbon Capture,Utilisation and Storage(CCUS).To clarify the effects of Cr content in steel on the resistance against general and localised corrosion,electrochemistry methods combined with pH measurements and various surface analysis techniques were implemented on X65,1Cr,3Cr and 5Cr steel samples in a CO_(2)-saturated solution at 60°C and pH 6.6 during 192 h of immersion.Additionally,thermodynamic and kinetic analyses of the formation of the corrosion products on carbon steel and low-Cr steels were performed.The results show that the general corrosion resistance increased with rising Cr content without the presence of significant corrosion products formation.However,with the formation and development of the corrosion products,the general corrosion resistance reduced with the increase in Cr content.The formation of the compact crystalline FeCO3 on X65 and 1Cr steel surfaces offered superior general corrosion protection,while cannot provide enough localised corrosion protection.By contrast,the double-structural corrosion product layers on 3Cr and 5Cr steels notably suppressed the localised corrosion,but providing poor protection against general corrosion over long immersion periods.This study reveals the contributions of Cr content on general and localised corrosion resistance at various periods,providing references for material selection and evaluation in CO_(2) environments relevant for CCUS.展开更多
The effect of Na-excess content in the precursor on the structural and electrochemical performances of sodium nickel manganese oxide(NNMO)prepared by sol-gel and electrospinning methods is investigated in this paper.X...The effect of Na-excess content in the precursor on the structural and electrochemical performances of sodium nickel manganese oxide(NNMO)prepared by sol-gel and electrospinning methods is investigated in this paper.X-ray diffraction results of the prepared NNMO without adding Na-excess content indicate sodium loss,while the mixed phase of P2/O′3-type layered NNMO presented after adding Na-excess content.Compared with the sol-gel method,the secondary phase of NiO is more suppressed by using the electrospinning method,which is further confirmed by field emission scanning electron microscope images.N_(2) adsorption-desorption isotherms show no remarkably difference in specific surface areas between different preparation methods and Na-excess contents.The analysis of X-ray absorption near edge structure indicates that the oxidation states of Ni and Mn are+2 and+4,respectively.For the electrochemical properties,superior electrochemical performance is observed in the NNMO electrode with a low Na-excess content of 5wt%.The highest specific capacitance is 36.07 F·g^(-1)at0.1 A·g^(-1)in the NNMO electrode prepared by using the sol-gel method.By contrast,the NNMO electrode prepared using the electrospinning method with decreased Na-excess content shows excellent cycling stability of 100%after charge-discharge measurements for 300 cycles.Therefore,controlling the Na excess in the precursor together with the preparation method is important for improving the electrochemical performance of Na-based electrode materials in supercapacitors.展开更多
基金supported by the National Key R&D Program of China(2021YFB4001601)the Natural Science Foundation of Shandong Province(ZR2021QE036)+3 种基金the Fundamental Research Funds for the Central Universities(22CX06052A)the Postgraduate Innovation Funding Project of China University of Petroleum(East China)(YCX2020070)the Fundamental Research Funds for the Central Universities(20CX02405A)the Development Fund of Shandong Key Laboratory of Oil&Gas Storage and Transportation Safety.
文摘The selection of appropriate materials for the transportation pipelines is of vital importance to ensure the safety operation in Carbon Capture,Utilisation and Storage(CCUS).To clarify the effects of Cr content in steel on the resistance against general and localised corrosion,electrochemistry methods combined with pH measurements and various surface analysis techniques were implemented on X65,1Cr,3Cr and 5Cr steel samples in a CO_(2)-saturated solution at 60°C and pH 6.6 during 192 h of immersion.Additionally,thermodynamic and kinetic analyses of the formation of the corrosion products on carbon steel and low-Cr steels were performed.The results show that the general corrosion resistance increased with rising Cr content without the presence of significant corrosion products formation.However,with the formation and development of the corrosion products,the general corrosion resistance reduced with the increase in Cr content.The formation of the compact crystalline FeCO3 on X65 and 1Cr steel surfaces offered superior general corrosion protection,while cannot provide enough localised corrosion protection.By contrast,the double-structural corrosion product layers on 3Cr and 5Cr steels notably suppressed the localised corrosion,but providing poor protection against general corrosion over long immersion periods.This study reveals the contributions of Cr content on general and localised corrosion resistance at various periods,providing references for material selection and evaluation in CO_(2) environments relevant for CCUS.
基金financially supported by (i) Suranaree University of Technology,(ii) Thailand Science Research and Innovation,and (iii) National Science,Research and Innovation Fund(project codes 90464 and 160363)。
文摘The effect of Na-excess content in the precursor on the structural and electrochemical performances of sodium nickel manganese oxide(NNMO)prepared by sol-gel and electrospinning methods is investigated in this paper.X-ray diffraction results of the prepared NNMO without adding Na-excess content indicate sodium loss,while the mixed phase of P2/O′3-type layered NNMO presented after adding Na-excess content.Compared with the sol-gel method,the secondary phase of NiO is more suppressed by using the electrospinning method,which is further confirmed by field emission scanning electron microscope images.N_(2) adsorption-desorption isotherms show no remarkably difference in specific surface areas between different preparation methods and Na-excess contents.The analysis of X-ray absorption near edge structure indicates that the oxidation states of Ni and Mn are+2 and+4,respectively.For the electrochemical properties,superior electrochemical performance is observed in the NNMO electrode with a low Na-excess content of 5wt%.The highest specific capacitance is 36.07 F·g^(-1)at0.1 A·g^(-1)in the NNMO electrode prepared by using the sol-gel method.By contrast,the NNMO electrode prepared using the electrospinning method with decreased Na-excess content shows excellent cycling stability of 100%after charge-discharge measurements for 300 cycles.Therefore,controlling the Na excess in the precursor together with the preparation method is important for improving the electrochemical performance of Na-based electrode materials in supercapacitors.