The effect of rare earth metals(REM)on the characteristics of auto-tempering and decomposition of martensite for low-carbon and low-alloy steels(20SiMn2V and 20SiMn2VRE)was investigated using TEM,dilatometer and micro...The effect of rare earth metals(REM)on the characteristics of auto-tempering and decomposition of martensite for low-carbon and low-alloy steels(20SiMn2V and 20SiMn2VRE)was investigated using TEM,dilatometer and microhardness test.Results show that both ε.and θ carbides,during auto-tempering, may precipitate from the low-carbon martensite matrix at the same time in the 20SiMn2V steel,however,the precipitation of the ε-carbides can be inhibited by the REM contained in the 20SiMn2 VRE steel,resulting in change of the type of precipitated carbides and decrease of the extent of auto-tempering.The“in-situ”ob- servations show that the decomposition of martensite is also inhibited by the REM contained in the 20SiMn2 VRE steel during low temperature tempering.展开更多
In this paper,the microstructure and hydrogen embrittlement(HE) susceptibility of an Fe-Ni-Co based superalloy with different contents of trace elements,P and Mn,have been investigated.The results indicated that by lo...In this paper,the microstructure and hydrogen embrittlement(HE) susceptibility of an Fe-Ni-Co based superalloy with different contents of trace elements,P and Mn,have been investigated.The results indicated that by lowering the contents of trace elements P and Mn,the size and distribution of γ' become more homogeneous,and the precipitation of stable phase η can be retarded to longer ageing time.As a result,the hydrogen resistant properties of the alloy are obviously improved.展开更多
Hot compression tests were performed to investigate the hot deformation behavior of Fe–27.34Mn–8.63Al–1.03C lightweight steel and optimize the hot workability parameters. The temperature range was 900–1150℃ and t...Hot compression tests were performed to investigate the hot deformation behavior of Fe–27.34Mn–8.63Al–1.03C lightweight steel and optimize the hot workability parameters. The temperature range was 900–1150℃ and the strain rate range was 0.01–5 s^(-1)on a Gleeble-3800 thermal simulator machine. The results showed that the flow stress increased with decreasing deformation temperature and increasing strain rate. According to the constitutive equation, the activation energy of hot deformation was 422.88 kJ·mol^(-1). The relationship between the critical stress and peak stress of the tested steel was established, and a dynamic recrystallization kinetic model was thus obtained. Based on this model, the effects of strain rate and deformation temperature on the volume fraction of dynamically recrystallized grains were explored. The microstructural examination and processing map results revealed that the tested steel exhibited a good hot workability at deformation temperatures of 1010–1100℃ and strain rate of 0.01 s^(-1).展开更多
基金financially supported by the Fundamental Research Funds for the Central Universities,China(No.2020CDJDPT001)the Chongqing Natural Science Foundation,China(No.cstc2021jcyj-msxm X0699)。
文摘The effect of rare earth metals(REM)on the characteristics of auto-tempering and decomposition of martensite for low-carbon and low-alloy steels(20SiMn2V and 20SiMn2VRE)was investigated using TEM,dilatometer and microhardness test.Results show that both ε.and θ carbides,during auto-tempering, may precipitate from the low-carbon martensite matrix at the same time in the 20SiMn2V steel,however,the precipitation of the ε-carbides can be inhibited by the REM contained in the 20SiMn2 VRE steel,resulting in change of the type of precipitated carbides and decrease of the extent of auto-tempering.The“in-situ”ob- servations show that the decomposition of martensite is also inhibited by the REM contained in the 20SiMn2 VRE steel during low temperature tempering.
文摘In this paper,the microstructure and hydrogen embrittlement(HE) susceptibility of an Fe-Ni-Co based superalloy with different contents of trace elements,P and Mn,have been investigated.The results indicated that by lowering the contents of trace elements P and Mn,the size and distribution of γ' become more homogeneous,and the precipitation of stable phase η can be retarded to longer ageing time.As a result,the hydrogen resistant properties of the alloy are obviously improved.
基金financially supported by the National Natural Science Foundation of China (Nos. 52071300 and 51904278)the Special Funding Projects for Local Science and Technology Development guided by the Central Committee (No. YDZX20191400004587)+1 种基金the Key Research and Development Project of Zhejiang Province, China (No.2020C01131)the Innovation projects of colleges and universities in Shanxi Province, China (No. 2019L0577)。
文摘Hot compression tests were performed to investigate the hot deformation behavior of Fe–27.34Mn–8.63Al–1.03C lightweight steel and optimize the hot workability parameters. The temperature range was 900–1150℃ and the strain rate range was 0.01–5 s^(-1)on a Gleeble-3800 thermal simulator machine. The results showed that the flow stress increased with decreasing deformation temperature and increasing strain rate. According to the constitutive equation, the activation energy of hot deformation was 422.88 kJ·mol^(-1). The relationship between the critical stress and peak stress of the tested steel was established, and a dynamic recrystallization kinetic model was thus obtained. Based on this model, the effects of strain rate and deformation temperature on the volume fraction of dynamically recrystallized grains were explored. The microstructural examination and processing map results revealed that the tested steel exhibited a good hot workability at deformation temperatures of 1010–1100℃ and strain rate of 0.01 s^(-1).