Microstructures and magnetic properties of Fe84Nb7B9,Fe80Ti8B 12 and Fe32Ni36（Nb/V）7Si8B17 powders and their bulk alloys prepared by mechanical alloying（MA） method and hot-press sintering were studied. The results...Microstructures and magnetic properties of Fe84Nb7B9,Fe80Ti8B 12 and Fe32Ni36（Nb/V）7Si8B17 powders and their bulk alloys prepared by mechanical alloying（MA） method and hot-press sintering were studied. The results show that: 1) After MA for 20 h,nanocrystalline bcc singl e phase supersaturated solid solution forms in Fe84-Nb7B9 and Fe8 0Ti8B12 alloys,amorphous structure forms in Fe32Ni36Nb7 Si8B17 alloy,duplex microstructure composed of nanocrystalline γ- （FeNi） supersaturated solid solution and trace content of Fe2B phase forms in Fe32Ni36-V7Si8B17 alloy. 2) The decomposition process of supersaturated solid solution phases in Fe84Nb7B9 and Fe80Ti8B 12 alloys happens at 710780 ℃,crystallization reaction in Fe （32）Ni36Nb7Si8B17 alloy happens at 530 ℃（the temperature of peak value） and residual amorphous crystallized further happens at 760 ℃ （the temperature of peak value）,phase decomposition process of supersaturated solid solution at 780 ℃ （the temperature of peak value） and crystallization reaction at 431 ℃ （the temperature of peak value） happens in Fe32Ni36V7S i8B17 alloy. 3) under 900 ℃,30 MPa,（0.5 h） hot-press sintering conditions,bulk alloys with high relative density（94.7%95.8%） can be ob tained. Except that the grain size of Fe84Nb7B9 bulk alloy is large,s uperfine grains （grain size 50200 nm） are obtained in other alloys. Exc ept that single phase microstructure is obtained in Fe80Ti8B12 bul k alloy,multi-phase microstructures are obtained in other alloys. 4) The magne tic properties of Fe80Ti8B12bulk alloy（Bs=1.74 T,Hc= 4.35 kA/m） are significantly superior to those of other bulk alloys,which is r elated to the different phases of nanocrystalline or amorphous powder formed dur ing hot-press sintering process and grain size.展开更多
Fe-based amorphous alloys with high iron content of 76at%-80at%were synthesized in the Fe-Mo-Si-P-C-B alloy system by the single roller melt-spinning technique.The amorphous ribbons exhibit high Vickers microhardness ...Fe-based amorphous alloys with high iron content of 76at%-80at%were synthesized in the Fe-Mo-Si-P-C-B alloy system by the single roller melt-spinning technique.The amorphous ribbons exhibit high Vickers microhardness and good ductility,which can be indented and bent 180°without breaking.A number of shear bands could be observed around the indents and the bending traces.Studies on the magnetic properties of the amorphous alloys show that they possess high saturation magnetizations of 1.34-1.6 T,which increases with the increase of iron content.The core losses of these Fe-based amorphous alloys at various magnetic inductions were tested and found to be significantly dependent on their components.The Fe-Mo-Si-P-C-B amorphous alloys with excellent mechanical properties and soft magnetic properties have promising potential in functional applications.展开更多
Bulk amorphous crystal and microcrystal for Pr60Cu(20-x)Ni10Al10Fex (x=0, 8, 15, 20) with the diameter of Φ 2～6 mm were manufactured by electric arc smelting, high frequency heating and copper mold upper suction cas...Bulk amorphous crystal and microcrystal for Pr60Cu(20-x)Ni10Al10Fex (x=0, 8, 15, 20) with the diameter of Φ 2～6 mm were manufactured by electric arc smelting, high frequency heating and copper mold upper suction casting, and its structure was analyzed by X-ray diffract meter. It showed soft magnetic characteristic gradually when Fe content in it was up to 8%. The material was applied to magnetic-electric sensor as key component, output signal of which was measured with the change of Fe content. It shows that the signal changes from weak to strong with the increase of Fe content and presents the largest peak value when Fe is replaced by Cu completely.展开更多
The thermal stability of milling Fe86Zr11-xNbxB3（x=5.5, 6） melt-spun strip powders and the influence of high-pressure sintering conditions on phase component and grain size of bulk alloys were investigated by X-ray ...The thermal stability of milling Fe86Zr11-xNbxB3（x=5.5, 6） melt-spun strip powders and the influence of high-pressure sintering conditions on phase component and grain size of bulk alloys were investigated by X-ray diffractometry（XRD）, differential scanning calorimetry（DSC） and scanning electron microscopy（SEM）. The results show that milling melt-spun powder remains in the amorphous state, and the crystallization temperature of which is 480530℃, the apparent activation energy Ep of crystallization process is 294.1219.5kJ/mol. The increasing Nb content can increase crystallization temperature and decrease Ep. Under the sintering conditions of 5.5GPa/3min, when Pw is 1150W, single phase α-Fe nanocrystalline （20.626.7nm） bulk alloy with relative density higher than 99.0% can be obtained. Under the sintering conditions of 5.5GPa/1150W/3min, the magnetic properties of these nanocrystalline bulk alloys are Fe86Zr5.5Nb5.5B3 alloy, Bs=1.15T, Hc=5.08kA·m-1; Fe86Zr5Nb6B3 alloy, Bs=1.26T, Hc=4.27kA·m-1.展开更多
文摘Microstructures and magnetic properties of Fe84Nb7B9,Fe80Ti8B 12 and Fe32Ni36（Nb/V）7Si8B17 powders and their bulk alloys prepared by mechanical alloying（MA） method and hot-press sintering were studied. The results show that: 1) After MA for 20 h,nanocrystalline bcc singl e phase supersaturated solid solution forms in Fe84-Nb7B9 and Fe8 0Ti8B12 alloys,amorphous structure forms in Fe32Ni36Nb7 Si8B17 alloy,duplex microstructure composed of nanocrystalline γ- （FeNi） supersaturated solid solution and trace content of Fe2B phase forms in Fe32Ni36-V7Si8B17 alloy. 2) The decomposition process of supersaturated solid solution phases in Fe84Nb7B9 and Fe80Ti8B 12 alloys happens at 710780 ℃,crystallization reaction in Fe （32）Ni36Nb7Si8B17 alloy happens at 530 ℃（the temperature of peak value） and residual amorphous crystallized further happens at 760 ℃ （the temperature of peak value）,phase decomposition process of supersaturated solid solution at 780 ℃ （the temperature of peak value） and crystallization reaction at 431 ℃ （the temperature of peak value） happens in Fe32Ni36V7S i8B17 alloy. 3) under 900 ℃,30 MPa,（0.5 h） hot-press sintering conditions,bulk alloys with high relative density（94.7%95.8%） can be ob tained. Except that the grain size of Fe84Nb7B9 bulk alloy is large,s uperfine grains （grain size 50200 nm） are obtained in other alloys. Exc ept that single phase microstructure is obtained in Fe80Ti8B12 bul k alloy,multi-phase microstructures are obtained in other alloys. 4) The magne tic properties of Fe80Ti8B12bulk alloy（Bs=1.74 T,Hc= 4.35 kA/m） are significantly superior to those of other bulk alloys,which is r elated to the different phases of nanocrystalline or amorphous powder formed dur ing hot-press sintering process and grain size.
基金supported by the China Postdoctoral Science Foundation(CPSF)(No.2007CB613900)the National Basic Research Priorities Program of China(No.2007CB613905)+1 种基金the Program for New Century Excellent Talents in the University,the Ministry of Education of China(No.50671050)the National Natural Science Foundation of China(Nos.50671050 and 50971073).
文摘Fe-based amorphous alloys with high iron content of 76at%-80at%were synthesized in the Fe-Mo-Si-P-C-B alloy system by the single roller melt-spinning technique.The amorphous ribbons exhibit high Vickers microhardness and good ductility,which can be indented and bent 180°without breaking.A number of shear bands could be observed around the indents and the bending traces.Studies on the magnetic properties of the amorphous alloys show that they possess high saturation magnetizations of 1.34-1.6 T,which increases with the increase of iron content.The core losses of these Fe-based amorphous alloys at various magnetic inductions were tested and found to be significantly dependent on their components.The Fe-Mo-Si-P-C-B amorphous alloys with excellent mechanical properties and soft magnetic properties have promising potential in functional applications.
文摘Bulk amorphous crystal and microcrystal for Pr60Cu(20-x)Ni10Al10Fex (x=0, 8, 15, 20) with the diameter of Φ 2～6 mm were manufactured by electric arc smelting, high frequency heating and copper mold upper suction casting, and its structure was analyzed by X-ray diffract meter. It showed soft magnetic characteristic gradually when Fe content in it was up to 8%. The material was applied to magnetic-electric sensor as key component, output signal of which was measured with the change of Fe content. It shows that the signal changes from weak to strong with the increase of Fe content and presents the largest peak value when Fe is replaced by Cu completely.
基金Project(0452NM086) supported by the Tackling Key Science and Technology Programof Shanghai , China
文摘The thermal stability of milling Fe86Zr11-xNbxB3（x=5.5, 6） melt-spun strip powders and the influence of high-pressure sintering conditions on phase component and grain size of bulk alloys were investigated by X-ray diffractometry（XRD）, differential scanning calorimetry（DSC） and scanning electron microscopy（SEM）. The results show that milling melt-spun powder remains in the amorphous state, and the crystallization temperature of which is 480530℃, the apparent activation energy Ep of crystallization process is 294.1219.5kJ/mol. The increasing Nb content can increase crystallization temperature and decrease Ep. Under the sintering conditions of 5.5GPa/3min, when Pw is 1150W, single phase α-Fe nanocrystalline （20.626.7nm） bulk alloy with relative density higher than 99.0% can be obtained. Under the sintering conditions of 5.5GPa/1150W/3min, the magnetic properties of these nanocrystalline bulk alloys are Fe86Zr5.5Nb5.5B3 alloy, Bs=1.15T, Hc=5.08kA·m-1; Fe86Zr5Nb6B3 alloy, Bs=1.26T, Hc=4.27kA·m-1.