Bulk metallic glass（BMG） rods Fe71Mo5-xNbxP12C10B2（x=1,2,3,4 and 5） with diameter of 1 or 2 mm were synthesized by copper mold casting.The effects of Nb substitution for Mo on the structure,thermal and mechanical ...Bulk metallic glass（BMG） rods Fe71Mo5-xNbxP12C10B2（x=1,2,3,4 and 5） with diameter of 1 or 2 mm were synthesized by copper mold casting.The effects of Nb substitution for Mo on the structure,thermal and mechanical properties of Fe71Mo5-xNbxP12C10B2 alloys were studied by X-ray diffraction,differential scanning calorimetry and compressive testing.The results show that the substitution of Nb for Mo leads to a decreased glass forming ability,but with plasticity of 1.0%,the fracture strength of Fe71Mo2Nb3P12C10B2 alloy increases up to 4.0 GPa.The improvement of the fracture strength is discussed in terms of the enhancement of atomic bonding nature and the favorite formation of a network-like structure due to the substitution of Nb for Mo.展开更多
由单一还原剂 NaH_2PO_2或 NaH_2PO_3与 KBH_4的复合还原剂分别在类镍溶液中获得 Ni-Fe-P 以及 Ni-Fe-P-B 合金膜,研究了这些新型合金膜的磁性。结果发现,铁磁性元素 Fe 含量增加导致原子平均磁矩及饱和磁化强度 Ms 增大;结构为非晶态...由单一还原剂 NaH_2PO_2或 NaH_2PO_3与 KBH_4的复合还原剂分别在类镍溶液中获得 Ni-Fe-P 以及 Ni-Fe-P-B 合金膜,研究了这些新型合金膜的磁性。结果发现,铁磁性元素 Fe 含量增加导致原子平均磁矩及饱和磁化强度 Ms 增大;结构为非晶态的合金膜具有较优的矫顽力 Hc 值;合金膜磁滞回线出现较低的矩形比说明化学镀制备态样品不够均匀;热处理温度高于400℃后,合金膜的饱和磁化强度连续减小,矫顽力急剧增大;同时,镀层的均匀性明显得到改善。展开更多
采用硼酸为缓冲剂,柠檬酸钠为络合剂在碱性介质中化学沉积Ni Fe P合金.考察了工艺条件如pH、FeSO4·7H2O浓度和温度对沉积速度的影响.获得了沉积速度快,镀液稳定性好的工艺条件.采用差示扫描量热和X射线衍射研究了Ni Fe P合金的晶...采用硼酸为缓冲剂,柠檬酸钠为络合剂在碱性介质中化学沉积Ni Fe P合金.考察了工艺条件如pH、FeSO4·7H2O浓度和温度对沉积速度的影响.获得了沉积速度快,镀液稳定性好的工艺条件.采用差示扫描量热和X射线衍射研究了Ni Fe P合金的晶化行为.结果表明,镀层在镀态呈非晶结构,镀层在200.5℃晶化为亚稳的Ni Fe合金,310℃晶化为立方FeNi3合金,369.2℃晶化为四方的Ni3P,而491.3℃为继续生成FeNi3的吸热峰.展开更多
采用自制的析磷助剂EA P作为Zn Fe P合金镀层中的磷源 ,研究了Zn Fe P合金镀液组成及工艺条件对镀层中磷、铁含量的影响。在最佳工艺条件下 ,可得到磷、铁含量分别为 0 .6 %左右和 0 .4%Zn Fe P合金镀层。腐蚀试验证明 ,经银白色钝化后...采用自制的析磷助剂EA P作为Zn Fe P合金镀层中的磷源 ,研究了Zn Fe P合金镀液组成及工艺条件对镀层中磷、铁含量的影响。在最佳工艺条件下 ,可得到磷、铁含量分别为 0 .6 %左右和 0 .4%Zn Fe P合金镀层。腐蚀试验证明 ,经银白色钝化后的Zn Fe P合金镀层的耐蚀性能是Zn Fe合金镀层的 2倍以上。展开更多
基金Project (SWU110046) supported by the Doctorate Foundation of Southwest University,China
文摘Bulk metallic glass（BMG） rods Fe71Mo5-xNbxP12C10B2（x=1,2,3,4 and 5） with diameter of 1 or 2 mm were synthesized by copper mold casting.The effects of Nb substitution for Mo on the structure,thermal and mechanical properties of Fe71Mo5-xNbxP12C10B2 alloys were studied by X-ray diffraction,differential scanning calorimetry and compressive testing.The results show that the substitution of Nb for Mo leads to a decreased glass forming ability,but with plasticity of 1.0%,the fracture strength of Fe71Mo2Nb3P12C10B2 alloy increases up to 4.0 GPa.The improvement of the fracture strength is discussed in terms of the enhancement of atomic bonding nature and the favorite formation of a network-like structure due to the substitution of Nb for Mo.
文摘由单一还原剂 NaH_2PO_2或 NaH_2PO_3与 KBH_4的复合还原剂分别在类镍溶液中获得 Ni-Fe-P 以及 Ni-Fe-P-B 合金膜,研究了这些新型合金膜的磁性。结果发现,铁磁性元素 Fe 含量增加导致原子平均磁矩及饱和磁化强度 Ms 增大;结构为非晶态的合金膜具有较优的矫顽力 Hc 值;合金膜磁滞回线出现较低的矩形比说明化学镀制备态样品不够均匀;热处理温度高于400℃后,合金膜的饱和磁化强度连续减小,矫顽力急剧增大;同时,镀层的均匀性明显得到改善。
文摘采用硼酸为缓冲剂,柠檬酸钠为络合剂在碱性介质中化学沉积Ni Fe P合金.考察了工艺条件如pH、FeSO4·7H2O浓度和温度对沉积速度的影响.获得了沉积速度快,镀液稳定性好的工艺条件.采用差示扫描量热和X射线衍射研究了Ni Fe P合金的晶化行为.结果表明,镀层在镀态呈非晶结构,镀层在200.5℃晶化为亚稳的Ni Fe合金,310℃晶化为立方FeNi3合金,369.2℃晶化为四方的Ni3P,而491.3℃为继续生成FeNi3的吸热峰.
文摘采用自制的析磷助剂EA P作为Zn Fe P合金镀层中的磷源 ,研究了Zn Fe P合金镀液组成及工艺条件对镀层中磷、铁含量的影响。在最佳工艺条件下 ,可得到磷、铁含量分别为 0 .6 %左右和 0 .4%Zn Fe P合金镀层。腐蚀试验证明 ,经银白色钝化后的Zn Fe P合金镀层的耐蚀性能是Zn Fe合金镀层的 2倍以上。