Optimization on microstructure,mechanical properties and damping capacities of duplex structured Mg–8Li–4Zn–1Mn alloys

Optimizing the mechanical properties and damping capacity of the duplex-structured Mg–Li–Zn–Mn alloy by tailoring the microstructure via hot extrusion was investigated.The results show that the Mg–8Li–4Zn–1Mn alloy is mainly composed ofα-Mg,β-Li,Mg–Li–Zn and Mn phases.The microstructure of the test alloy is refined owing to dynamic recrystallization(DRX)during hot extrusion.After hot extrusion,the crushed precipitates are uniformly distributed in the test alloy.The yield strength(YS),ultimate tensile strength(UTS),and elongation(EL)of as-extruded alloy reach 156 MPa,208 MPa,and 32.3%,respectively,which are much better than that of as-cast alloy.Furthermore,the as-extruded and as-cast alloys both exhibit superior damping capacities,with the damping capacity(Q^(-1))of 0.030 and 0.033 at the strain amplitude of 2×10^(-3),respectively.The mechanical properties of the test alloy can be significantly improved by hot extrusion,whereas the damping capacities have no noticeable change,which indicates that the duplex-structured Mg–Li alloys with appropriate mechanical properties and damping properties can be obtained by alloying and hot extrusion.

Design optimization of cast Cu-Al-Be-B alloys for high damping capacity

This paper investigated high-damping Cu-Al-Be-B cast alloys using metallographic analysis, X-ray diffraction (XRD) and electrical resistance measurements for transformation temperatures. The results showed that beryllium can stabilize β phase, resulting in a thermo-elastic martensite microstructure leading to high-damping capacity in cast Cu-Al-Be-B alloys. Trace additions of boron to Cu-Al-Be alloys can significantly refine the grains, providing high strength and ductility to the alloys. A factorial design of experiment method was used to optimize the composition and properties of cast Cu-Al-Be-B alloys. The optimal microstructure for thermo-elastic martensite can be obtained by adjusting the amounts of aluminum and beryllium to eutectoid or pseudo-eutectoid compositions. An optimized cast Cu-Al-Be-B alloy was developed to provide excellent mechanical properties, tensile strength σ_b=767MPa, elongation δ=7.62%, and damping capacity S. D. C=18.70%.

INFLUENCE OF Al-5Ti-1B MASTER ALLOY ON MICROSTRUCTURE AND DAMPING CAPACITY OF ZA27 ALLOY

１ＩＮＴＲＯＤＵＣＴＩＯＮＴｈｅｄａｍｐｉｎｇｃａｐａｃｉｔｙｏｆａｍａｔｅｒｉａｌｉｓａｍｅａｓｕｒｅｏｆｔｈｅｅｎｅｒｇｙｔｈａｔｉｓｄｉｓｓｉｐａｔｅｄｉｎｔｈｅｍａｔｅｒｉａｌｄｕｒｉｎｇｍｅｃｈａｎｉｃａｌｖｉｂｒａｔｉｏｎｕｎｄｅｒｃｙｃ...

Effects of Y and Zn on mechanical properties and damping capacity of Mg-Cu-Mn alloy

Optical microscope,X-ray diffractometer,scanning electron microscope,tensile tester and dynamic mechanical analyzer(DMA) were applied to investigate the effects of Y and Zn additions on microstructure,mechanical properties and damping capacity of Mg-3Cu-1Mn(CM31) alloy.The results show that with the increase of Y and Zn contents,the secondary dendrite arm spacing of alloys is reduced;meanwhile,the yield strength is increased.In low strain amplitude,the damping capacity of alloys with Y and Zn addition is lower than that of CM31 alloy.However,in strain amplitude over 5×10-3,the damping capacity of alloy with a trace of Y and Zn addition(1%Y and 2%Zn,mass fraction) increases abnormally with the increase of strain amplitude and is near to that of pure Mg,probably due to the increase of dislocation density caused by the precipitation of secondary phase.The temperature dependence of damping capacity of above alloy was also tested and discussed.

Influence of RE Content on Damping Capacity of Alloy ZA27

The modification mechanism and damping capacity(Q-1) of conventional ascast ZA27 alloy modified by Al10%RE were investigated. Cantilever beam technique was used to measure the damping capacity. The experimental results show that the addition of RE to the ZA27 alloy can refine microstructure and improve the damping capacity, the best modification effect and the highest damping capacity can be obtained at 03%RE content. It is believed that the damping mechanism of ZA27 alloy is associated with the viscous sliding or slipping of grain boundaries and interfaces, and the more the grain boundaries and interfaces, the higher the damping capacity of ZA27 alloy can be obtained.

Solid solution strengthening and damping capacity of Mg-Ga binary alloys

The mechanical behaviors and damping capacities of the binary Mg−Ga alloys with the Ga content ranging from 1 to 5 wt.%were investigated by means of optical microscope(OM),scanning electron microscope(SEM),X-ray diffraction(XRD),hardness test,tensile test and dynamic mechanical analyzer(DMA).The hardness(HV_(0.5))increases with the increase of Ga content,which can be described as HV_(0.5)=41.61+10.35c,and the solid solution strengthening effect∆σ_(s)of the alloy has a linear relationship with c^(n),where c is the molar fraction of solute atoms and n=1/2 or 2/3.Ga exhibits a stronger solid solution strengthening effect than Al,Zn or Sn due to the large atomic radius difference and the modulus mismatch between Ga and Mg atoms.The addition of Ga makes the Mg−Ga alloys have better damping capacity,and this phenomenon can be explained by the Granato−Lücke dislocation model.The lattice distortion and the modulus mismatch generated because of the addition of Ga increase the resistance to motion of the dislocation in the process of swinging or moving,and thus the better damping capacity is acquired.

Effects of Y on mechanical properties and damping capacity of ZK60 magnesium alloys

The microstructure,mechanical properties and damping capacity of ZK60-xY(x=0,1.5%,2.5%,4.0%,mass fraction) magnesium alloys were investigated by using the optical microscope(OM),X-ray diffractometer(XRD),universal tensile testing machine and dynamic mechanical analyzer(DMA).The mechanisms for damping capacity of referred alloys were discussed by Granato-Lücke theory.The results show that Y additions remarkably reduce grain size(the average grain size is 21.6,13.0,8.6 and 4.0μm,respectively),and the tensile properties are enhanced with grain refining(the yield tensile strength increases to 292 MPa from 210 MPa and ultimate tensile strength increases to 330 MPa from 315 MPa).For the ZK60-xY(x=0,1.5%,4.0%)alloys,the damping capacity decreases with the increase of Y content.However,for the ZK60-xY(x=2.5%)alloy,the damping capacity improves abnormally,which is possibly related to the formation of Mg3Y2Zn3(W)FCC phase in this alloy.

Effects of Ce on damping capacity of AZ91D magnesium alloy

The microstructures and damping capacity of AZ91D cast alloys containing various Ce contents were investigated. Damping capacity (Q-1) of the alloys was measured by cantilever beam technique, and the relationship between damping capacity and strain amplitude was investigated. The results show that Al4Ce phase is formed in AZ91D alloy after adding a certain quantity of Ce contents, then as-cast microstructures of the alloys are refined. Meanwhile the damping capacity of the alloys is also improved. When the mass fraction of Ce is 0.7%, the most obvious refinement effect and the maximum damping capacity can be obtained. When the damping capacity (Q-1) is )2.728)×10-3, 61% increment can be obtained compared with unmodified AZ91D alloy. The damping capacity of the alloys is relative to strain amplitude, and the damping behavior can be explained by the theory of Granato and Lücke.

Effects of Cu and Mn on mechanical properties and damping capacity of Mg-Cu-Mn alloy

The effects of Cu and Mn additions on mechanical properties and damping capacity of Mg-Cu-Mn alloy were investigated. The tensile properties and damping capacity at room temperature of as-cast Mg-Cu-Mn alloy were tested.The microstructurc was studied using optical microscope,X-ray diffraction and scanning electron microscope.The Hall-Perch relation and Granato-Lücke model were used to explain the influences of Cu and Mn additions on the tensile properties and damping capacity of Mg-Cu-Mn alloy.The results show that Cu and Mn additions remarkably reduce the grain size of Mg-Cu-Mn alloy,but have little influence on phase composition and solute atoms concentration,the tensile properties increase obviously and the internal friction of Mg-Cu-Mn alloy decreases with grain refining.

Effect of environmental temperature on damping capacity of Cu-Al-Mn alloy

The effect of environmental temperature on the damping capacity of Cu-7.66Al-9.52Mn (mass fraction, %) alloy was studied. The result shows that with increasing the environmental temperature, the logarithmic decrement increases firstly and reaches the maximal value of 0.118. The reason is that more phase interfaces and twinning boundaries can move at a higher temperature, leading to higher consumption of energy, in despite of the decreasing of the amount of martensite. When the environmental temperature is above Ms, with further increase in the environmental temperature, the logarithmic decrement decreases sharply mainly because there is little martensite remaining in the alloy.

DAMPING CAPACITY OF HIGH SILICON ALLOY ZA27 PREPAREDBY SPRM DEPOSITION

The damping capacities (Q-1) of high silicon (6wt%) Zinc-27wt% Aluminia alloy prepared by spray deposition and conventional casting process were investigated. Three methods, free-decay, half-power band width and phase angles difference, have been ased to measure the damping capacities of the experimental materiale. The experimental results indicate that the damping capacity of spray deposited material is 3.7times larger than that of the conventional casting alloy ZA27 The machanism for its improvement was aiso investigated from a microstructvre viempoint.

INFLUENCE OF ZIRCONIUM ON MICROSTRUCTURE AND DAMPING CAPACITY OF ZA27 ALLOY

To improve the damping capacities of metals and alloys, the microstructures and damping capacities of ZA27 alloy modified by Zr were studied, and the damping capacities at room tempemture were measured by using cantilever beam techniques. The experiment results show that Zr can refine the Al-rich primary phase and improve the damping Capacities saliently. Compared with the un-modified one, the damping capacity of ZA27 alloy modified by 0.3wt%Zr received 90 percent increment. The high damping capacities are attributed primarily to grain ablement and the increasing of phase interfaces.

Influence of CaO on damping capacity and mechanical properties of Mg alloy

For developing cost effective damping Mg alloys with high damping capacity and better mechanical properties, the microstructures, the mechanical properties at room temperature and the damping capacity of Mg alloy adding CaO were investigated and compared with those of K1A alloy. CaO adding into pure Mg maintains the damping capacity and increases the ultimate tensile strength compared with those of pure Mg. Mg-CaO alloy can be regarded as cost-effective damping alloy with high damping and mechanical properties as well as with the advantages of improving oxidation and burning resistances.

Numerical modeling of damping capacity of Zn-Al alloys with fully lamellar microstructures

The damping behaviors of Zn-Al alloys with fully lamellar microstructures were simulated with the cell method. The influences of the grain boundary condition, the strain amplitude, the number of the lamellae in the grain (N) and the content ratio of Zn and Al in Zn-Al alloys on the damping capacity were investigated. The results indicate that the grain boundary condition has great influence on the damping capacity of Zn-Al alloys, and also affects the relationship between the damping capacity and the number of lamellae (N). The variation of damping capacity with the strain amplitude is increasing exponentially with the strain amplitude and the damping capacity increases with the increasing of content of Zn.

Mechanical properties and damping capacities of magnesium alloys processed by equal channel angular extrusion(ECAE)

Equal channel angular extrusion (ECAE) was applied to commercial pure magnesium and AZ91D alloy. Microstructures of these magnesium alloys before and after ECAE process were observed by optical microscopy (OM). The ultimate tensile strength of pure magnesium and AZ91D alloy processed by ECAE is about 130 and 260MPa, respectively, and it is much higher than that of the as cast alloys. The elongation of them is increased from about 2% to 8%. The strain amplitude dependence damping capacities of these magnesium alloys were investigated by dynamic mechanical analyzer (DMA). ECAE process largely decreases the damping capacities of pure magnesium from 0.033 to about 0.012 (ε=1×10 -4), but does not show obvious influence on that of AZ91D alloy, which is about 0.0015.

EFFECT OF ANNEALING ON DAMPING CAPACITIES OF AS-CAST ZA27 ALLOY

ZA27 alloy was prepared by casting with permanent mold and then annealed at 250℃ for 1-4h. The damping capaciG of the alloy was measured using a testing apparatus based on the cantilever beam technique. It was found that the as-cast ZA27 alloy possesses high damping capacity with the value of 1.3 × 10^4 at 320Hz. After annealed at 250℃ for lh, the damping capacity decreases to 1.1 × 10^-3 and then remains constant even when the annealing time is increased to 4h. The microstructure of the as-cast ZA27 alloy consists of large dendrites of Al-rich PrimaG （x-phases, eutectoid （α ＋ η） and nonequilibrium eutectic phases （α ＋ η ＋ ε）. After annealing at 250℃ for lh, the e phase disappears due to dissolution into the matrix, and the spacing between the flakes of eutectoid increases. The further increase in the annealing time has little effect on the spacing. The damping mechanism of the alloy was discussed considering the thermoelastic damping and defect damping. The value of thermoelastic damping accounts only for 7%-8% in the overall damping in cantilever beam damping measurements and the damping capacity of the ZA27 alloy came mainly from defect damping.

Effects of Y content and temperature on the damping capacity of extruded Mg-Y sheets

The damping behavior of extruded Mg-xY(x=0.5,1.0,3.0 wt.%)sheets were investigated in detail concerning the effects of Y addition and temperature,and the relationship between damping capacity and yield strength was discussed.At room temperature(RT),with Y content increasing from 0.5%to 3.0%,the damping capacity(Q-1)significantly decreased from 0.037 to 0.015.For all the studied sheets,the relationship between strain amplitude and Q-1 fitted well with the Granato and Liicke(G-L)dislocation damping model.With temperature increased,the G-L plots deviated from linearity indicating that the dislocation damping was not the only dominate mechanism,and the grain boundary sliding(GBS)could contribute to damping capacity.Consequently,the Q-1 increased remarkably above the critical temperature,and the critical temperature increased significantly from 50℃ to 290℃ with increasing Y contents from 0 to 3.0wt.%.This result implied that the segregation of Y solutes at grain boundary could depress the GBS,which was consistent with the recent finding of segregation tendency for rare-earth solutes.The extruded Mg-IY sheet exhibited slightly higher yield strength(Rp0.2)and Q-1 comparing with high-damping Mg-0.6Zr at RT.At an elevated temperature of 325℃,the Mg-IY sheet had similar Q-1 but over 3 times larger Rp0.2 than that of the pure Mg.The present study indicated that the extruded Mg-Y based alloys exhibited promising potential for developing high-performance damping alloys,especially for the elevated-temperature application.

Effect of small tensile deformation on damping capacities of Mg-1%Al alloy

Tensile tests with small deformation amounts of 0.5%,1%,3%and 5%were performed at room temperature on as cast Mg-1%Al alloy.Microstructures of the Mg-1%Al alloys before and after deformation were observed by optical microscopy(OM) and transmission electron microscopy(TEM).The strain amplitude dependent and temperature dependent damping capacities of the as-cast and deformed Mg-1%Al alloys were investigated by dynamic mechanical analysis(DMA).The mechanism of deformation on damping capacity of Mg-1%Al alloy was discussed.The results show that the as-cast Mg-1%Al alloy has high damping value at high strain.When the tensile elongation is higher than 3%,the damping values of this alloy in high strain region are significantly decreased at room temperature.But the large amount of dislocations produced by tensile deformation are activated by heat,and then increase the damping value at high temperature.

Optimization of mechanical and damping properties of Mg-0.6Zr alloy by different extrusion processing

In this study,the optimization of mechanical and damping capacities of Mg-0.6 wt.%Zr alloys by controlling the recrystallized(DRXed)grain size under varying extrusion processing parameters including extrusion temperature T and strain rate was investigated.The relationship between the DRXed grain size and damping properties of the studied alloy was also discussed.The DRXed grain size of the as-extruded Mg-Zr alloys decreased as the extrusion temperature T decreased and the strain rateεincreased.As the DRXed grain size decreased,the strength and elongation of the as-extruded alloys exhibited improved performance through the grain refinement mechanism,while the damping properties deteriorated.The extrusion temperature of the Mg-Zr alloy had relatively greater effects on the mechanical and damping properties than the strain rate.The results of the present work indicate that alloys with appropriate mechanical and damping properties may be obtained from controlling the DRXed grain size by careful tailoring of the extrusion process parameters.

Damping behavior and mechanical properties of Mg-Cu-Mn alloy processed by equal channel angular pressing

Equal channel angular pressing(ECAP) was conducted at 250℃for 4 passes to the as-extruded Mg-3%Cu-1%Mn alloy with high strength and high damping capacity.After ECAP processing,the grain of as-extruded alloy is significantly refined to about 4μm,both yield strength and tensile strength of the as-extruded Mg-Cu-Mn alloy are decreased,but the ductility is improved.After the ECAP processing,the damping capacity of Mg-Cu-Mn alloy is decreased at room temperature,while is substantially increased at elevated temperatures,After annealing at 300℃for 1 h,both yield strength and tensile strength of the ECAPed alloy are further decreased,but the ductility is significantly improved.The damping capacity of the as-annealed alloy is increased at room temperature, while is decreased at elevated temperatures.The mechanisms for damping capacity of the alloy at ambient and elevated temperatures were discussed.