Dielectric barrier discharge plasma synthesis of Ag/γ-Al_(2)O_(3) catalysts for catalytic oxidation of CO

In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.

Monolithic Mesh-Type Fe-Pd/γ-Al₂O₃/Al Bifunctional Catalysts for Electro-Fenton Degradation of Rhodamine B

A novel Fe-Pd bifunctional catalyst supported on mesh-type γ-Al2O3/Al was prepared and applied in the degradation of Rhodamine B (RhB). The monolithic mesh-type Fe-Pd/γ-Al2O3/Al bifunctional catalyst could be separated from the solution directly and could synthesize H2O2 in situ. The characterization results showed that Fe could improve the dispersion of Pd0, and the electronic interactions between Pd and Fe could increase the Pd0 contents on the catalyst, which increased the productivity of H2O2. Furthermore, DFT calculations proved that the addition of Fe could inhibit the dissociation of O2 and promote the nondissociative hydrogenation of O2 on the surface of Fe-Pd/γ-Al2O3/Al, which resulted in the increasement of H2O2 selectivity. Finally, the in-situ synthesized H2O2 by Pd was furtherly decomposed in situ by Fe to generateOH radicals to degrade organic pollutants. Therefore, Fe-Pd/ γ-Al2O3/Al catalysts exhibited excellent catalytic activity in the in-situ synthesis of H2O2 and the degradation of RhB due to the synergistic effects between Pd and Fe on the catalyst. It provided a new idea for the design of bifunctional electro-Fenton catalysts. Ten cycles of experiments showed that the catalytic activity of Fe-Pd/γ-Al2O3/Al catalyst could be maintained for a long time.

Investigation of the characteristics and deactivation of catalytic active center of Cr-Al_2O_3 catalysts for isobutane dehydrogenation

Deactivation mechanism of Cr-Al2O3catalyst and the interaction of Cr-A1 in the dehydrogenation of isobutane, as well as the nature of the catalytic active center, were studied using XRD, SEM, XPS, H2-TPR, isobutane-TPR and TPO techniques. The results revealed that the deactivation of Cr-Al2O3 catalyst was mainly caused by carbon deposition on its surface. The Cr3＋ ion could not be reduced by hydrogen but could be reduced to Cr2＋ by hydrocarbons and monoxide carbon. The active center for isobutane dehydrogenation could be Cr2＋/Cr3＋ produced from Cr6＋ by the on line reduction of hydrocarbon and carbon monoxide. The binding energy of Al3＋ was strongly affected by the state of chromium cations in the catalysts.

Support Effects on Thiophene Hydrodesulfurization over Co-Mo-Ni/Al_2O_3 and Co-Mo-Ni/TiO_2-Al_2O_3 Catalysts

A carbon-based sulfonated catalyst was prepared by direct sulfonation and carbonization （in moderate conditions：200 ＆#176;C, 12 h） of red liquor solids, a by-product of paper-making process. The prepared sulfonated cata-lyst （SC） had aromatic structure, composed of carbon enriched inner core, and oxygen-containing （SO3H, COOH, OH） groups enriched surface. The SO3H, COOH, OH groups amounted to 0.74 mmol·g^-1, 0.78 mmol·g^-1, 2.18 mmol·g^-1, respectively. The fresh SC showed much higher catalytic activity than that of the traditional solid acid catalysts （strong-acid 732 cation exchange resin, hydrogen type zeolite socony mobile-five （HZSM-5）, sulfated zir-conia） in esterification of oleic acid. SC was deactivated during the reactions, through the mechanisms of leaching of sulfonated species and formation of sulfonate esters. Two regeneration methods were developed, and the catalytic activity can be mostly regenerated by regeneration Method 1 and be fully regenerated by regeneration Method 2, respectively.

Oligomerization of 1-Decene: Catalyzation by Immobilized AlCl_3/γ-Al_2O_3 Catalyst in Fixed-bed Reactor

1-Decene was oligomerized over the supported AlCl3/γ-Al2O3 catalyst in a fixed-bed reactor. The effects of temperature and LHSV on oligomerization of 1-decene were investigated and the synthetic PAO was characterized with GC technique. Furthermore, the life of immobilized catalyst was tested and the mechanism of catalyst deactivation was discussed. The results showed that with an increasing temperature, the PAO yield increased and the kinematic viscosity of oil decreased. The GC results indicated that the synthesized PAO was a mixture consisting of dimers, trimers, tetramers and pentamers. The results of chloride content measurements and BET tests showed that catalyst deactivation could be mainly attributed to the loss of active components.

CeO_2-ZrO_2-La_2O_3-Al_2O_3 composite oxide and its supported palladium catalyst for the treatment of exhaust of natural gas engined vehicles

Composite supports CeO2-ZrO2-Al2O3（CZA） and CeO2-ZrO2-Al2O3-La2O3（CZALa） were prepared by co-precipitation method. Palladium catalysts were prepared by impregnation and their purification ability for CH4, CO and NOx in the mixture gas simulated the exhaust from natural gas vehicles （NGVs） operated under stoichiometric condition was investigated. The effect of La2O3 on the physicochemical properties of supports and catalysts was characterized by various techniques. The characterizations with X-ray diffraction （XRD） and Raman spectroscopy revealed that the doping of La2O3 restrained effectively the sintering of crystallite particles, maintained the crystallite particles in nanoscale and stabilized the crystal phase after calcination at 1000 ℃. The results of N2-adsorption, H2-temperatnre-programmed reduction （H2-TPR） and oxygen storage capacity （OSC） measurements indicated that La2O3 improved the textural properties, reducibility and OSC of composite supports. Activity testing results showed that the catalysts exhibit excellent activities for the simultaneous removal of methane, CO and NOx in the simulated exhaust gas. The catalysts supported on CZALa showed remarkable thermal stability and catalytic activity for the three pollutants, especially for NOx. The prepared palladium catalysts have high ability to remove NOx, CH4 and CO, and they can be used as excellent catalysts for the purification of exhaust from NGVs operated under stoichiometric condition. The catalysts reported in this work also have significant potential in industrial application because of their high performance and low cost.

DBD coupled with MnOx/γ-Al2O3 catalysts for the degradation of chlorobenzene

This paper investigates the degradation of chlorobenzene by dielectric barrier discharge(DBD)coupled with MnOx/γ-Al2O3 catalysts.MnOx/γ-Al2O3 catalysts were prepared using the impregnation method and were characterized in detail by N2 adsorption/desorption,x-ray diffraction and x-ray photoelectron spectroscopy.Compared with the single DBD reactor,the coupled reactor has a better performance on the removal rate of chlorobenzene,the selectivity of COx,and the inhibition of ozone production,especially at low discharge voltages.The degradation rate of chlorobenzene and selectivity of COx can reach 96.3%and 53.0%,respectively,at the specific energy density of 1350 J l-1.Moreover,the ozone concentration produced by the discharge is significantly reduced because the MnOx/Al2O3 catalysts contribute to the decomposition of ozone to form oxygen atoms for the oxidation of chlorobenzene.In addition,based on analysis of the byproducts,the decomposition mechanism of chlorobenzene in the coupled reactor is also discussed.

Preparation and characterization of Fe_2O_3-CeO_2-TiO_2/γ-Al_2O_3 catalyst for degradation dye wastewater

In order to develop a catalyst with high activity for catalytic wet oxidation （CWO） process at room temperature and atmospheric pressure, Fe2O3-CeO2-TiO2/γ-Al2O3 catalyst was prepared by consecutive impregnation method and the prepared parameters were optimized. The structure of the catalyst was characterized by BET, XRF, SEM and XPS technologies, and the actual wastewater was used to investigate the catalytic activity of Fe2O3-CeO2-TiO2/γ-Al2O3 in CWO process. The experimental results showed that the prepared catalyst exhibited good catalytic activity when the doping amount of Ti was 1.0 wt% （the weight ratio of Ti to carriers）, and the middle product, Fe2O3-CeO2-TiO2/γ-Al2O3, was calcined in 450℃ for 2 h. The CWO experiment for treating actual dye wastewater indicated that the COD, color and TOC of actual wastewater were decreased by 62.23%, 50.12% and 41.26% in 3 h, respectively, and the ratio of BOD5/COD was increased from 0.19 to 0.30.

Syngas production by combined carbon dioxide reforming and partial oxidation of methane over Ni/α-Al_2O_3 catalysts

Ni/α-Al2O3 catalysts were found to be active in the temperature range 600 ～ 900℃ for both CO2 reforming and partial oxidation of methane.The effects of Ni loading,reaction temperature and feed gas ratio for the combination of CO2 reforming and partial oxidation of CH4 over Ni/α-Al2O3 were investigated.Catalysts of xwt%Ni/α-Al2O3（x=2.5,5,8 and 12） were prepared by wet impregnating the calcined support with a solution of nickel nitrate.XRD patterns and activity tests have verified that the 5wt%Ni/α-Al2O3 was the most active catalyst,as compared with the other prepared catalyst samples.An increase of the Ni loading to more than 5wt% led to a reduction in the Ni dispersion.In addition,by combining the endothermic carbon dioxide reforming reaction with the exothermic partial oxidation reaction,the loss of catalyst activity with time on stream was reduced with the amount of oxygen added to the feed.

Effect of Fe_2O_3 Loading Amount on Catalytic Properties of Monolithic Fe_2O_3/Ce_(0.67)Zr_(0.33)O_2-Al_2O_3 Catalyst for Methane Combustion

Ce0.67Zr0.33O2-Al2O3 solid solution was prepared by the co-precipitation method. Fe2O3-based catalysts supported on the solid solution were obtained by the impregnation method. The article revealed that the optimal loading amount of Fe2O3 on Ce0.67Zr0.33 O2-Al2O3 in our experimental condition for catalytic combustion of methane was 8% （ mass fraction）. The prepared catalysts were characterized by BET, TPR, XRD analyses, and their catalytic activity was investigated after being calcined at 873 K and after being aged in water gas at 1273 K. When the loading amount of Fe203 was 8% （ mass fraction）, the catalyst held the highest activity, and the best temperature speciality and thermal stability. The complete-conversion temperature of methane for fresh and aged sample was 788 and 838 K, respectively. The range between the light-off temperature and the complete-conversion temperature was only 15 K. The characterization results of XRD indicated that Fe2O3 was well dispersed on the Ce0.67Zr0.33O2-Al2O3 matrix. The results of BET and TPR were in good harmony with the catalytic activity results.

催化精馏专用填料型固体酸SO_4^(2-)/ZrO_2-Al_2O_3-Al的研究

为了研制催化精馏专用催化剂 ,采用铝阳极氧化法制备了Al2 O3 Al一体型载体 ,并将活性固体超强酸SO42 -/ZrO2 引入到Al2 O3 Al上 ,得到一种新型催化精馏专用填料式固体酸SO42 -/ZrO2 Al2 O3 Al催化剂 .利用XRD、SEM、BET、XPS、NH3 TPD等手段对其进行了表征 .结果表明 ,所制得的阳极氧化铝膜厚为 5 6 μm ,SO42 -/ZrO2 Al2 O3 Al固体酸具有比表面积大、酸强度适中的特点 .XRD结果表明 ,ZrO2 在Al2 O3 Al上处于高度分散状态 .将该固体酸用于乙酸 /乙醇酯化反应中 ,显示出较高的催化活性 。

NOx storage and reduction assisted by non-thermal plasma over Co/Pt/Ba/γ-Al2O3 catalyst using CH_(4) as reductant

NOx storage and reduction(NSR)technology has been regarded as one of the most promising strategies for the removal of nitric oxides(NOx)from lean-burn engines,and the potential of the plasma catalysis method for NOx reduction has been confirmed in the past few decades.This work reports the NSR of nitric oxide(NO)by combining non-thermal plasma(NTP)and Co/Pt/Ba/γ-Al2O3(Co/PBA)catalyst using methane as a reductant.The experimental results reveal that the NOx conversion of NSR assisted by NTP is notably enhanced compared to the catalytic efficiency obtained from NSR in the range of 150°C–350°C,and NOx conversion of the 8%Co/PBA catalyst reaches 96.8%at 350°C.Oxygen(O_(2))has a significant effect on the removal of NOx,and the NOx conversion increases firstly and then decreases when the O_(2)concentration ranges from 2%to 10%.Water vapor reduces the NOx storage capacity of Co/PBA catalysts on account of the competition for adsorption sites on the surface of Co/PBA catalysts.There is a negative correlation between sulfur dioxide(SO_(2))and NOx conversion in the NTP system,and the 8%Co/PBA catalyst exhibits higher NOx conversion compared to other catalysts,which shows that Co has a certain SO_(2)resistance.

新型填料式固体酸SO_4^(2-)/Al_2O_3-Al催化合成乙酸乙酯

为了制备催化精馏用填料式催化剂 ,采用铝阳极氧化法和浸渍法制备了新型填料式SO2 -4/Al2 O3 Al固体酸催化剂 ,并用于催化乙醇和乙酸的酯化反应。最佳反应条件为 :醇酸摩尔比 1∶8,催化剂 2 .0 g ,反应温度90～ 10 0℃ ,反应时间 6 .0h ,酯化率 90 .4 0 % ,选择性 10 0 % 。

溶胶-凝胶法制备致密α-Al_2O_3涂层的研究

以异丙醇铝为前驱物,水为溶剂,硝酸为胶溶剂,用分散法制得了稳定透明的氧化铝溶胶,并用降液法制得了氧化铝凝胶涂层,经热处理后最终获得Al2O3涂层.利用TG-DTA分析了氧化铝凝胶向Al2O3的转变过程.XRD分析表明所获得的涂层为α-Al2O3晶型结构.SEM分析表明所制得的涂层致密均匀,无开裂,并且涂层与基底结合良好.因而该法是一种简单易行的制备致密α-Al2O3涂层的好方法.

Effect of Calcination Temperature on La-Modified Al2O3 Catalysts for Vapor Phase Hydrofluorination of Acetylene to Vinyl Fluoride

A La-modified Al2O3 catalyst was prepared with deposition-precipitation method. The effect of calcination temperature on the reactivity for vapor phase hydrofluorination of acetylene to vinyl fluoride. The catalysts calcined at different temperatures were characterized using NH3-TPD, pyridine-FTIR, X-ray diffraction, and Raman techniques. It was found that the calcination process could not only change the structure of these catalysts but also modify the amount of surface acidity on the catalysts. The catalyst calcined at 400 ℃ exhibited the highest conversion of acetylene （94.6%） and highest selectivity to vinyl fluoride （83.4%） and lower coke deposition selectivity （0.72%）. The highest activity was related to the largest amount of surface acidity on the catalyst, and the coke deposition was also related to the total amount of surface acidic sites.

纳米α-Al_2O_3对HMX撞击感度的影响

比较了单质炸药HMX和混合炸药HMX／纳米Al2O3落锤撞击试验,研究纳米α-Al2O3对HMX撞击感度的影响,并对纳米Al2O3在混合炸药中作用机理进行了探讨。结果表明,纳米α-Al2O3具有润滑作用,HMX／纳米Al2O3混合炸药的撞击感度随纳米α-Al2O3添加量的增加而降低,添加2.0％(质量分数)纳米α-Al2O3混合炸药与单质炸药HMX相比,2.5kg落锤测试的50％爆炸特性落高(H50)提高了13.1cm。

利用纳米铝和沉淀法制备纳米α-Al_2O_3粉体

以Al(NO3)3·9H2O、氨水和纳米铝粉为原料,采用液相沉淀法制备出Al(OH)3溶胶,经过真空抽滤和高温煅烧获得了纳米α-Al2O3粉体.研究了反应体系pH值、纳米铝粉添加和煅烧温度对Al(OH)3溶胶质量以及Al2O3晶型转化温度的影响.结果表明,反应体系pH值为9时可以获得团聚少、分散性好的Al(OH)3溶胶,添加摩尔分数为3%的纳米铝粉作为籽晶可以使α-Al2O3的转变温度降至1000°C左右.实验获得的纳米α-Al2O3粉体粒度分布均匀,无明显团聚,近似球形,平均粒径约为20nm.

Cu-Fe-Ru-La/γ-Al_2O_3湿式氧化催化剂的制备、表征及机理(英文)

采用等量浸渍法以γ-Al2O3为载体,制备过渡金属Cu和Fe、贵金属Ru、稀土金属La的复合催化剂。采用催化湿式空气氧化法处理模拟印染废水,研究金属离子配比、焙烧温度对催化剂活性及稳定性的影响,并对催化剂CWAO反应机理进行探讨:权衡催化剂的活性和稳定性,催化剂的组分质量配比和焙烧温度分别为Cu∶Fe∶Ru∶La=1∶1∶1∶3、450℃。对催化剂进行XRD、XPS、孔结构、FT-IR、TG-DTA、SEM、TEM表征,结果表明:焙烧使催化剂组成物质分解为氧化物,元素Cu、Fe、Ru、La分别以CuO、Fe2O3、RuO2、La2O3形式存在;焙烧温度升高,晶粒长大结晶趋于完整,催化剂孔容孔径增大但比表面积减小,晶粒尺寸分布在5～20 nm;Cu-Fe-Ru-La/γ-Al2O3催化剂使用前后结构无明显变化且反应后溶出的金属浓度低,催化剂具有较高的稳定性。

熔铝氧化渗透合成SiC_p/Al_2O_3-Al复合材料的微观结构分析

以低成本的熔铝氧化渗透合成新方法制备了SiCp/Al2 O3 Al复合材料。借助X光电子谱 (XPS)、光学金相显微镜、透射电镜 (TEM)、X射线衍射 (XRD)等手段研究了该种复合材料的微观结构 ,并分析了影响微观结构的主要因素及其影响规律。结果表明 ,Al2 O3 和Al作为复合材料基体呈双连续分布 ,它们各自的含量可在较大范围内受SiC颗粒的粒度所控制。在熔铝氧化渗透合成的SiCp/Al2 O3 Al复合材料中 ,各组成相之间无界面反应 ,也无晶间相 ,Al2 O3 在SiC颗粒表面二次形核并直接生长的现象普遍存在 ,并由此形成了具有良好物理冶金结合的Al2 O3

Relationship between Cr-Al Interaction and the Performance of Cr-Al₂O₃Catalysts for Isobutane Dehydrogenation

A series of catalysts were prepared using the kneading molding method and the impregnation method as well as the dry mix method by using different raw materials. By using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and temperature-programmed reduction (TPR) techniques, we studied the relationship between the catalyst performance and the Cr-Al interaction in the catalytic dehydrogenation of isobutane. The results demonstrated that the Cr-Al interaction in the catalyst had a direct influence on the catalytic activity and the selectivity of isobutene. The catalysts prepared using the kneading molding method had higher catalytic activity and isobutene selectivity than those prepared using the dry mix method. By comparison, XRD, XPS, and TPR results showed that the greater the Cr-Al interaction in the catalyst was, the higher the catalytic activity was. Here, we propose a mechanism of isobutane dehydrogenation.