Fe-based amorphous coating prepared using high-velocity oxygen fuel and its corrosion behavior in static lead-bismuth eutectic alloy

The Fe_(949.7)Cr_(18)Mn_(1.9)Mo_(7.4)W_(1.6)B_(15.2)C_(3.8)Si_(2) amorphous coating was deposited on T91 steel substrate by using the high-velocity oxygen fuel(HVOF)spray technique to enhance the corrosion resistance of T91 stainless steel in liquid lead-bismuth eutectic(LBE).The corrosion behavior of the T91 steel and coating exposed to oxygen-saturated LBE at 400℃ for 500 h was investigated.Results showed that the T91 substrate was severely corroded and covered by a homogeneously distributed dual-layer oxide on the interface contacted to LBE,consisting of an outer magnetite layer and an inner Fe-Cr spinel layer.Meanwhile,the amorphous coating with a high glass transition temperature(Tg=550℃)and crystallization temperature(T_(x)=600℃)exhibited dramatically enhanced thermal stability and corrosion resistance.No visible LBE penetration was observed,although small amounts of Fe_(3)O_(4),Cr_(2)O_(3),and PbO were found on the coating surface.In addition,the amorphicity and interface bonding of the coating layer remained unchanged after the LBE corrosion.The Fe-based amorphous coating can act as a stable barrier layer in liquid LBE and have great application potential for long-term service in LBE-cooled fast reactors.

Effect of Kerosene Flowing Rate on Microstructure and Wearing Properties for Fe-based Amorphous Coatings

The effects of kerosene flow rate on the microstructure and wearing properties were investigated for Fe-based amorphous coatings sprayed by High Velocity Oxygen Fuel (HVOF).The microstructures and wearing properties of the Fe-based amorphous coatings were analyzed with scanning electron microscope (SEM),X-ray diffraction analyzer (XRD),and ball-on-disc tribometer (CFT-1),respectively.The experimental results show that the well interfacial bonding can be observed between the amorphous coating layer and the substrate,and the porosity in amorphous coating layer is less to 1%.Only some crystalline a-Fe and FeO phases can be detected by XRD in the amorphous coatings,while the amorphous content is up to 99.4%.The wearing coefficient is near to 0.15,which is superior to SUS316 of 0.28.As the increasing of wearing loads,the failure mode is changed from oxidation wear to the composite of oxidation and abrasive wear.

Superhydrophobic Fe-based amorphous coating fabricated by detonation spraying with excellent anti-corrosion and self-cleaning properties

Amorphous alloys without crystalline defects(dislocation,crystal boundary)are ideal hydrophobic coating materials due to their low surface energy.This work used a synergistic method of detonation spraying and surface modification to obtain the superhydrophobic Febased amorphous coatings with high hardness and dense structure on the Q 235 substrate.The results showed that the water contact angles(WCA)of the superhydrophobic coating was 160°±3.6°,and water droplets could bounce off the superhydrophobic coating surface,illustrating the excellent self-cleaning performance of coating.Notably,the corrosion current density(i_(corr))of the superhydrophobic coating further decreased by 2 orders of magnitude down to8.008×10^(-8)A·cm^(-2)compared to the as-deposited coating with 5.473×10^(-6)A·cm^(-2);the corrosion potential(E_(corr))of the superhydrophobic coating shifted by 34 mV to the positive side compared with that of the as-deposited coating(-310 mV).Likewise,the impedance modulus|Z|values of the superhydrophobic coating increased by nearly2 orders of magnitude up to 1×10^(5.6)compared to the asdeposited coating with 1×10^(3.8).Even through lasting immersion in NaCl for 10 days,|Z|values of the superhydrophobic coating were still much higher than those of the as-deposited coating.The superhydrophobic Fe-based amorphous coatings could respond to their applications under extreme conditions due to their excellent hydrophobicity and self-cleaning properties,illustrating their promising future in aerospace,automotive,and machinery industries.

Hot corrosion behaviors of 921A alloy and HVAF-sprayed Fe-based amorphous coating covered with KCl-ZnCl_(2) salts

Hot corrosion behaviors of the 921A alloy and Fe-based amorphous coating induced by KCl-10% ZnCl_(2) and KCl-55% ZnCl_(2) salts at 450℃ in air for 40 h were investigated.Results show that the 921A alloy suffers more serious corrosion damage than the coating and KCl-55% ZnCl_(2) salts are more corrosive than KCl-10% ZnCl_(2) salts.In the two salts,an Fe_(2)O_(3) layer is formed on the 921A alloy surface,while an outer Fe-rich oxide layer and an inner Cr-rich oxide layer are formed on the surface of the coating.Moreover,a certain amount of metal chloride can be found at the oxide/alloy(coating)interface,which can be explained by "active oxidation".However,the corrosion resistance of the Fe-based amorphous coating did not achieve the desired results,probably because the intersplats in the coating serve as corrosion diffusing channels,which facilitate the corrosion damage rate.Nevertheless,the coating is still in amorphous state after hot corrosion exposure.

Achieving a superior Na storage performance of Fe-based Prussian blue cathode by coating perylene tetracarboxylic dianhydride amine

Fe-based Prussian blue(Fe-PB)cathode material shows great application potential in sodium(Na)-ion batteries due to its high theoretical capacity,long cycle life,low cost,and simple preparation process.However,the crystalline water and vacancies of Fe-PB lattice,the low electrical conductivity,and the dissolution of metal ions lead to limited capacity and poor cycling stability.In this work,a perylene tetracarboxylic dianhydride amine(PTCDA)coating layer is successfully fabricated on the surface of Fe-PB by a liquid-phase method.The aminated PTCDA(PTCA)coating not only increases the specific surface area and electronic conductivity but also effectively reduces the crystalline water and vacancies,which avoids the erosion of Fe-PB by electrolyte.Consequently,the PTCA layer reduces the charge transfer resistance,enhances the Na-ion diffusion coefficient,and improves the structure stability.The PTCA-coated Fe-PB exhibits superior Na storage performance with a first discharge capacity of 145.2 mAh g^(−1) at 100 mA g^(−1).Long cycling tests exhibit minimal capacity decay of 0.027%per cycle over 1000 cycles at 1 A g^(−1).Therefore,this PTCA coating strategy has shown promising competence in enhancing the electrochemical performance of Fe-PB,which can potentially serve as a universal electrode coating strategy for Na-ion batteries.

Corrosion resistance of Fe-based amorphous metallic matrix coating fabricated by HVOF thermal spraying

The Fe-based amorphous metallic matrix coating （Fe-AMMC） was fabricated with the powder mixtures of Fe-based metallic glass synthesized with industrial raw materials, NiCr alloy and WC particle by high velocity oxy-fuel （HVOF） spraying. The corrosion resistance of Fe-AMMC was investigated by potentiodynamic polarization tests in 1 mol/L HCl, NaCl, H2SO4 and NaOH solutions, respectively. The surface morphologies corroded were observed by SEM. The results indicate that Fe-AMMC exhibits excellent corrosion resistance, higher corrosion resistance than 304L stainless steel in the chloride solutions. The low corrosion current density and passive current density of Fe-AMMC with a wide spontaneous passivation region are about 132.0μA/cm2 and 9.0 mA/cm2 in HCl solution, and about 2.5 μA/cm2 and 2.3 mA/cm2 in NaCl solution. The excellent corrosion resistance demonstrates that Fe-based amorphous metallic matrix powder is a viable engineering material in practical anti-corrosion and anti-wear coating applications.

Corrosion and irradiation behavior of Fe-based amorphous coating in lead-bismuth eutectic liquids

Lead-bismuth eutectics (LBE) have considerable potential as a candidate material for accelerator-driven sub-critical systems(ADS).However,LBE corrosion and irradiation damage are two urgent challenges remaining to be solved for impellers of primary pumps.In this study,we have explored the possibility of using Fe-based amorphous coatings to overcome LBE corrosion and concurrently to sustain irradiation damage.Specifically,the Fe_(54)Cr_(18)Mo_(2)Zr_(8)B_(18)amorphous coating was prepared by high-velocity oxygen-fuel (HVOF) spraying on 316L steel and exposed to saturated oxygen static LBE for 500 h at 400℃.The coating with high thermal stability (T_(g)=615℃ and T_(x)=660℃) effectively prevented the substrate steel from being corroded by LBE owing to its unique long-range disordered atomic packing.The coating also exhibited strong irradiation resistance when being subjected to 45 dpa (displacement per atom) Au ion irradiation at room temperature,with no sign of crystallization even at the maximum implantation depth of 300 nm.Consequently,the hardness of the coatings before and after irradiation increased slightly.The current findings shed new insights into understanding corrosion mechanism and irradiation behavior of amorphous solids in LBE and expand the application range of amorphous materials.

Microstructure and Wear Properties of Fe-based Amorphous Coatings Deposited by High-velocity Oxygen Fuel Spraying

Fe-based powder with a composition of Fe_（42.87）Cr_（15.98）Mo_（16.33）C_（15.94）B_（8.88）（at.%）was used to fabricate coatings by high-velocity oxygen fuel spraying.The effects of the spraying parameters on the microstructure and the wear properties of the Fe-based alloy coatings were systematically studied.The results showed that the obtained Fe-based coatings with a thickness of about 400μm consisted of a large-volume amorphous phase and some nanocrystals.With increasing the fuel and oxygen flow rates,the porosity of the obtained coatings decreased.The coating deposited under optimized parameters exhibited the lowest porosity of 2.8%.The excellent wear resistance of this coating was attributed to the properties of the amorphous matrix and the presence of nanocrystals homogeneously distributed within the matrix.The wear mechanism of the coatings was discussed on the basis of observations of the worn surfaces.

Formation and corrosion behavior of Fe-based amorphous metallic coatings prepared by detonation gun spraying

Amorphous metallic coatings with a composition of Fe48Cr15Mo14C15B6Y2 were prepared by detonation gun spraying process. Microstructural studies show that the coatings present a densely layered structure typical of thermally sprayed deposits with the porosity below 2%. Both crystallization and oxidation occurred obviously during spraying process, so that the amorphous fraction of the coatings decreased to 54% compared with fully amorphous alloy ribbons of the same component. Corrosion behavior of the amorphous coatings was investigated by electrochemical measurement. The results show that the coatings exhibit extremely wide passive region and low passive current density in 3.5% NaCl (mass fraction) and 1 mol/L HCl solutions, which illustrates excellent ability to resist localized corrosion.

Fabrication and microstructure of Fe-based amorphous composite coatings by laser cladding

Fe-based amorphous composite coatings were fabricated on AISI 1045 steel by laser cladding. The results of the X- ray diffraction and transmission electron microscopy analyses .show the coating is composed of an amorphous phase in majority and a nanocrystaUine phuse in m,inority. Phase composition of the coating changes along the depth of the coating. The reasonable scanning speed for fabricating an amorphous composite coating is 3 500 mm/min when the laser power is 4 800 W and the laser beam diameter is 2 mm. If the scanning speed is lower than 3 500 mm/min, the intensity of the two main diffraction peaks in X-ray diffraction patterns of the coatings decreases with the scanning speeds increasing. At the same time, a broad halo peak emerges and enlarges. High laser power and fast scanning speed are the essential conditions of amorphization. The coating exhibits high microhardness.

Effects of Annealing Below Glass Transition Temperature on the Wettability and Corrosion Performance of Fe-based Amorphous Coatings

This study investigated the effect of annealing below glass transition temperature(T_(g))on the microstructural characteristics,mechanical property,wettability,and electrochemical performance of activated combustion-high velocity air fuel(AC-HVAF)-sprayed Fe-Cr-Mo-W-C-B-Y amorphous coatings(ACs).Results showed that Fe-based ACs with a thickness of~300μm exhibited a fully amorphous structure with low oxidization.Originating from the reduced free volume,sub-T_(g) annealing increased the thermal stability,hardness,and surface hydrophobicity of Fe-based ACs.The enhanced corrosion resistance of sub-T_(g) annealed ACs in 3.5 wt%NaCl solution was attributed to the increased surface hydrophobicity and passivation capability.This finding elucidates the correlation between sub-T_(g) annealing and the properties of Fe-based ACs,which promotes ameliorating ACs with superior performance.

Microstructure characteristics of coating with amorphous phases prepared from Fe-based alloy powders by plasma spray

In this paper, alloy powders mixed with a molar ratio of Fe ： P ： C of 80 ： 13 ： 7 were sprayed on Q235 steel by plasma spray method to prepare coating with amorphous phases. The phase composition of the mixed alloy powders and prepared coating were characterized by X-ray diffraction （ XRD ）. The morphology and the composition cf the coating were analyzed by scanning eleetron microscopy （SEM） nnd energy dispersive apectroscopy （ EDS ）. In addition, the thermal stability ef the coating with amorphous phases was characterized by differential thermal analyzer （ DTA ）. Tile results showed that, usirtg mixed alloy powders with a molar ratio of Fe： P： C of 80：13：7, the coating containing certain amount of amorphous alloys was suceessathlly prepared through atmospheric plasma spray technique. In the coating, the main phases were determined to be Fe, FeP aad Fe2P. The crystallization of the coating started from about 461°. Tile coating was mechanically adhered to the substrate.

Clean production of Fe-based amorphous soft magnetic alloys via smelting reduction of high-phosphorus iron ore and apatite

Separated preparation of prealloys and amorphous alloys results in severe solidification-remelting and beneficial element removal-readdition contradictions,which markedly increase energy consumption and emissions.This study offered a novel strategy for the direct production of FePC amorphous soft magnetic alloys via smelting reduction of high-phosphorus iron ore(HPIO)and apatite.First,the thermodynamic conditions and equilibrium states of the carbothermal reduction reactions in HPIO were calculated,and the element content in reduced alloys was theoretically determined.The phase and structural evolutions,as well as element migration and enrichment behaviors during the smelting reduction of HPIO and Ca_(3)(PO_(4))_(2),were then experimentally verified.The addition of Ca_(3)(PO_(4))_(2)in HPIO contributes to the enrichment of the P element in reduced alloys and the subsequent development of Fe_(3)P and Fe_(2)P phases.The content of P and C elements in the range of 1.52 wt% -14.63 wt% and 0.62 wt% -2.47 wt%,respectively,can be well tailored by adding 0-50 g Ca_(3)(PO_(4))_(2)and controlling the C/O mole ratio of 0.8-1.1,which is highly consistent with the calculated results.These FePC alloys were then successfully formed into amorphous ribbons and rods.The energy consumption of the proposed strategy was estimated to be 2.00×10^(8) kJ/t,which is reduced by 30% when compared with the conventional production process.These results are critical for the comprehensive utilization of mineral resources and pave the way for the clean production of Fe-based amorphous soft magnetic alloys.

Microstructure and tribological properties of laser cladding Fe-based coating on pure Ti substrate

Fe-based coating was produced on pure Ti substrate by the laser cladding technology. The composition and microstructure of the fabricated coating were analyzed by scanning electron microscopy （SEM）, X-ray diffraction （XRD） and transmission electron microscopy （TEM） technique. The tribological properties were tested through sliding against AISI52100 steel ball at different normal loads and sliding speeds. Besides, the morphologies of the worn surfaces and wear debris were analyzed by scanning electron microscopy （SEM） and three dimensional （3D） non-contact surface mapping. The results show that the prepared Fe-based coating has a high hardness of about 860 HV0.2 and exhibits an average wear rate of （0.70-2.32）×10-6 mm3/（N-m）, showing that the Fe-based coating can greatly improve the wear resistance of pure Ti substrate. The wear mechanism of the coating involves moderate adhesive and abrasive wear.

Long-term corrosion behavior of HVOF sprayed FeCrSiBMn amorphous/nanocrystalline coating

A FeCrSiBMn amorphous/nanocrystalline coating with 700 μm in thickness and 0.65% in porosity, was prepared by high velocity oxygen fuel(HVOF) spraying process. The long-term corrosion behavior of the FeCrSiBMn coating was evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy(EIS) tests in a 3.5% NaCl solution with a hard chromium coating as a reference. The FeCrSiBMn coating exhibited higher corrosion potential and lower corrosion current density than the hard chromium coating. The pore resistance(Rp) and charge transfer resistance(Rct) of FeCrSiBMn coating were higher than those of the hard chromium coating. In addition, after immersion in the Na Cl solution for 28 d, only small pores in the FeCrSiBMn coating were observed. All the results indicated that the FeCrSiBMn coating held superior corrosion resistance to the hard chromium coating. This could be attributed to the dense structure, low porosity and amorphous/nanocrystalline phases of the FeCrSiBMn coating.

Fabrication, tribological and corrosion behaviors of detonation gun sprayed Fe-based metallic glass coating

A metallic glass coating with the composition of Fe51.33Cr14.9Mo25.67Y3.4C3.44B1.26 （mole fraction, %） on the Q235 stainless steel was developed by the detonation gun （D-gun） spraying process. The microstructure and the phase aggregate were analyzed by scanning electron microscopy and X-ray diffractometry, respectively. Microhardness, wear resistance and corrosion behavior were assessed using a Vickers microhardness tester, a ball-on-disk wear testing machine and the electrochemical measurement method, respectively. Microstructural studies show that the coatings possess a densely layered structure with the porosity less than 2.1%. The tribological behavior of the coatings examined under dry conditions shows that their relative wear resistance is five times higher than that of the substrate material. Both adhesive wear and abrasive wear contribute to the friction, but the former is the dominant wear mechanism of the metallic glass coatings. The coatings exhibit low passive current density and extremely wide passive region in 3.5% NaCl solution, thus indicating excellent corrosion resistance.

Identifying the optimal HVOF spray parameters to attain minimum porosity and maximum hardness in iron based amorphous metallic coatings

Flow based Erosion e corrosion problems are very common in fluid handling equipments such as propellers, impellers, pumps in warships, submarine. Though there are many coating materials available to combat erosionecorrosion damage in the above components, iron based amorphous coatings are considered to be more effective to combat erosionecorrosion problems. High velocity oxy-fuel(HVOF)spray process is considered to be a better process to coat the iron based amorphous powders. In this investigation, iron based amorphous metallic coating was developed on 316 stainless steel substrate using HVOF spray technique. Empirical relationships were developed to predict the porosity and micro hardness of iron based amorphous coating incorporating HVOF spray parameters such as oxygen flow rate, fuel flow rate, powder feed rate, carrier gas flow rate, and spray distance. Response surface methodology(RSM) was used to identify the optimal HVOF spray parameters to attain coating with minimum porosity and maximum hardness.

Microstructure and corrosion resistance of Fe/Mo composite amorphous coatings prepared by air plasma spraying

Fe/Mo composite coatings were prepared by air plasma spraying （APS） using Fe-based and Mo-based amorphous and nanocrys- talline mixed powders. Microstructural studies show that the composite coatings present a layered structure with low porosity due to adding the self-bonded Mo-based alloy. Corrosion behaviors of the composite coatings, the Fe-based coatings and the Mo-based coatings were in- vestigated by electrochemical measurements and salt spray tests. Electrochemical results show that the composite coatings exhibit a lower polarization current density and higher corrosion potentials than the Fe-based coating when tested in 3.5wt% NaC1 solutions, indicating supe- rior corrosion resistance compared with the Fe-based coating. Also with the increase in addition of the Mo-based alloy, a raised corrosion re- sistance, inferred by an increase in corrosion potential and a decrease in polarization current density, can be found. The results of salt spray tests again show that the corrosion resistance is enhanced by adding the Mo-based alloy, which helps to reduce the porosity of the composite coatings and enhance the stability of the passive films.

PROPERTIES OF ELECTRODEPOSITED AMORPHOUS Ni-W-P-SiC COMPOSITE COATINGS

The Effects of heat treatment temperature on the hardness,wear resistance and structure of the amorphous Ni-W-P-SiC composite coatings have been investigated.The results show that Ni-W-P-SiC composite coatings are amorphous under 300℃, partially crystalline at 300-400℃,and crystalline when heat treatment temperature reaches 400℃,the crystals being fine Ni3P phase particles.The hardness,wear resistance and the crystallization temperature of the composite coatings increase when an additive is added into the bath.The hardness and wear resistance of the coatings increase with increasing heat treatment temperature,and they will reach their peak values when the heat treatment temperature reaches 400℃.Corrosion experiment indicates that the corrosion resistance of amorphous Ni-W-P-SiC composite coatings in various kinds of corrosive media except nitric acid is better than that of stainless steel 1Cr18Ni9Ti.Scanning electron microscopy observation shows that the additive has no effect on the surface appearance of the coatings,but the current density and the pH value have considerable effects on the surface appearance.

Microstructure of Cu-based Amorphous Composite Coatings on AZ91D Magnesium Alloy by Laser Cladding

To improve the sliding wear resistance of AZ91D magnesium alloy, Cu-based amorphous composite coatings made of CuaTTi34Zr11Nis and Cu47Ti34Zr11Ni8＋20 wt pct SiC powders were fabricated on AZ91D magnesium alloy by laser cladding, respectively. SEM （scanning electron microscopy）, EDS （energy dispersive X-ray spectroscopy）, XRD （X-ray diffraction） and TEM （transmission electron microscopy） techniques were employed to study the phases of the coatings. The results show that the coatings mainly consist of amorphous phase and different intermetallic compounds. The reason of formation of amorphous phase and the function of SiC particles were explained in details.