The Fe-based alloy coatings reinforced with in situ synthesized TiB2-TiC were prepared on Q235 steel by reactive plasma cladding using Fe901 alloy, Ti, B4C, and graphite (C) powders us raw materials. The effects of ...The Fe-based alloy coatings reinforced with in situ synthesized TiB2-TiC were prepared on Q235 steel by reactive plasma cladding using Fe901 alloy, Ti, B4C, and graphite (C) powders us raw materials. The effects of C/B4C weight percentage ratio (0 - 1. 38 ) on the microstructure , microhardness , and wet sand abrasion resistance of the coatings were investigated. The results show that the coatings consist of ( Fe, Cr ) solid solution, TiC, TiB2, Ti8C5 , and Fe3 C phases. The decrease of C/B4 C ratio is propitious to the formation of TiB2 and Tis C5. Increasing the C/B4 C ratio can help to refine the microstructure of the coatings. However, the microhardness of the middle-upper of the coatings and the wet sand abrasion resistance of the coatings degenerate with the increase of C/B4C ratio. The coating exhibits the best wet sand abrasion resistance at C/BaC =0 and its average mass loss rate per unit wear distance is 0. 001 2%/m. The change of the wet sand abrasion resistance of the coatings with the C/B4C ratio can be mainly attributed to the combined action of the changes of microhardness and the volume percentage of the ceramic reinforcements containing titanium in the coatings.展开更多
Fe-based Prussian blue(Fe-PB)cathode material shows great application potential in sodium(Na)-ion batteries due to its high theoretical capacity,long cycle life,low cost,and simple preparation process.However,the crys...Fe-based Prussian blue(Fe-PB)cathode material shows great application potential in sodium(Na)-ion batteries due to its high theoretical capacity,long cycle life,low cost,and simple preparation process.However,the crystalline water and vacancies of Fe-PB lattice,the low electrical conductivity,and the dissolution of metal ions lead to limited capacity and poor cycling stability.In this work,a perylene tetracarboxylic dianhydride amine(PTCDA)coating layer is successfully fabricated on the surface of Fe-PB by a liquid-phase method.The aminated PTCDA(PTCA)coating not only increases the specific surface area and electronic conductivity but also effectively reduces the crystalline water and vacancies,which avoids the erosion of Fe-PB by electrolyte.Consequently,the PTCA layer reduces the charge transfer resistance,enhances the Na-ion diffusion coefficient,and improves the structure stability.The PTCA-coated Fe-PB exhibits superior Na storage performance with a first discharge capacity of 145.2 mAh g^(−1) at 100 mA g^(−1).Long cycling tests exhibit minimal capacity decay of 0.027%per cycle over 1000 cycles at 1 A g^(−1).Therefore,this PTCA coating strategy has shown promising competence in enhancing the electrochemical performance of Fe-PB,which can potentially serve as a universal electrode coating strategy for Na-ion batteries.展开更多
A Ni–P alloy gradient coating consisting of multiple electroless Ni–P layers with various phosphorus contents was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were...A Ni–P alloy gradient coating consisting of multiple electroless Ni–P layers with various phosphorus contents was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were used to characterize the different Ni–P coatings’ morphologies, phase structures, elemental compositions, and corrosion protection. The gradient coating showed good adhesion and high corrosion and wear resistance, enabling the application of aluminum alloy in harsh environments. The results showed that the double zinc immersion was vital in obtaining excellent adhesion (81.2 N). The optimal coating was not peeled and shredded even after bending tests with angles higher than 90°and was not corroded visually after 500 h of neutral salt spray test at 35℃. The high corrosion resistance was attributed to the misaligning of these micro defects in the three different nickel alloy layers and the amorphous structure of the high P content in the outer layer. These findings guide the exploration of functional gradient coatings that meet the high application requirement of aluminum alloy parts in complicated and harsh aviation environments.展开更多
The poor corrosion and wear resistances of Mg alloys seriously limit their potential applications in various industries.The conventional epoxy coating easily forms many intrinsic defects during the solidification proc...The poor corrosion and wear resistances of Mg alloys seriously limit their potential applications in various industries.The conventional epoxy coating easily forms many intrinsic defects during the solidification process,which cannot provide sufficient protection.In the current study,we design a double-layer epoxy composite coating on Mg alloy with enhanced anti-corrosion/wear properties,via the spin-assisted assembly technique.The outer layer is functionalized graphene(FG)in waterborne epoxy resin(WEP)and the inner layer is Ce-based conversion(Ce)film.The FG sheets can be homogeneously dispersed within the epoxy matrix to fill the intrinsic defects and improve the barrier capability.The Ce film connects the outer layer with the substrate,showing the transition effect.The corrosion rate of Ce/WEP/FG composite coating is 2131 times lower than that of bare Mg alloy,and the wear rate is decreased by~90%.The improved corrosion resistance is attributed to the labyrinth effect(hindering the penetration of corrosive medium)and the obstruction of galvanic coupling behavior.The synergistic effect derived from the FG sheet and blocking layer exhibits great potential in realizing the improvement of multi-functional integration,which will open up a new avenue for the development of novel composite protection coatings of Mg alloys.展开更多
Titanium alloys are excellent structural materials in engineering fields,but their poor tribological properties limit their further applications.Electroless plating is an effective method to enhance the tribological p...Titanium alloys are excellent structural materials in engineering fields,but their poor tribological properties limit their further applications.Electroless plating is an effective method to enhance the tribological performance of alloys,but it is difficult to efficiently apply to titanium alloys,due to titanium alloy’s strong chemical activity.In this work,the electroless Nickel-Boron(Ni-B)coating was successfully deposited on the surface of titanium alloy(Ti-6AL-4V)via a new pre-treatment process.Then,linearly reciprocating sliding wear tests were performed to evaluate the tribological behaviors of titanium alloy and its electroless Ni-B coatings.It was found that the Ni-B coatings can decrease the wear rate of the titanium alloy from 19.89×10^(−3)mm^(3)to 0.41×10^(−3)mm^(3),which attributes to the much higher hardness of Ni-B coatings.After heat treatment,the hardness of Ni-B coating further increases corresponding to coating crystallization and hard phase formation.However,heat treatment does not improve the tribological performance of Ni-B coating,due to the fact that higher brittleness and more severe oxidative wear exacerbate the damage of heat-treated coatings.Furthermore,the Ni-B coatings heat-treated both in air and nitrogen almost present the same tribological performance.The finding of this work on electroless coating would further extend the practical applications of titanium alloys in the engineering fields.展开更多
Constructing a functional hybrid coating appears to be a promising strategy for addressing the poor corrosion resistance and insufficient endothelialization of Mg-based stents.Nevertheless,the steps for preparing comp...Constructing a functional hybrid coating appears to be a promising strategy for addressing the poor corrosion resistance and insufficient endothelialization of Mg-based stents.Nevertheless,the steps for preparing composite coatings are usually complicated and time-consuming.Herein,a novel composite coating,composed of bioactive magnesium thioctic acid(MTA)layer formed by deposition and corrosion-resistant magnesium hydroxide(Mg(OH)_(2))layer grown in situ,is simply fabricated on ZE21B alloys via one-step electrodeposition.Scanning electron microscopy(SEM)shows that the electrodeposited coating has a compact and uniform structure.And the high adhesion of the MTA/Mg(OH)_(2)hybrid coating is also confirmed by the micro-scratch test.Electrochemical test,scanning kelvin probe(SKP),and hydrogen evolution measurement indicate that the hybrid coating effectively reduces the degradation rate of Mg substrates.Haemocompatibility experiment and cell culture trial detect that the composite coating is of fine biocompatibility.Finally,the preparation mechanism of MTA/Mg(OH)_(2)hybrid coatings is discussed and proposed.This coating shows a great potential application for cardiovascular stents.展开更多
Magnesium(Mg)alloys are lightweight materials with excellent mechanical properties,making them attractive for various applications,including aerospace,automotive,and biomedical industries.However,the practical applica...Magnesium(Mg)alloys are lightweight materials with excellent mechanical properties,making them attractive for various applications,including aerospace,automotive,and biomedical industries.However,the practical application of Mg alloys is limited due to their high susceptibility to corrosion.Plasma electrolytic oxidation(PEO),or micro-arc oxidation(MAO),is a coating method that boosts Mg alloys'corrosion resistance.However,despite the benefits of PEO coatings,they can still exhibit certain limitations,such as failing to maintain long-term protection as a result of their inherent porosity.To address these challenges,researchers have suggested the use of inhibitors in combination with PEO coatings on Mg alloys.Inhibitors are chemical compounds that can be incorporated into the coating or applied as a post-treatment to further boost the corrosion resistance of the PEO-coated Mg alloys.Corrosion inhibitors,whether organic or inorganic,can act by forming a protective barrier,hindering the corrosion process,or modifying the surface properties to reduce susceptibility to corrosion.Containers can be made of various materials,including polyelectrolyte shells,layered double hydroxides,polymer shells,and mesoporous inorganic materials.Encapsulating corrosion inhibitors in containers fully compatible with the coating matrix and substrate is a promising approach for their incorporation.Laboratory studies of the combination of inhibitors with PEO coatings on Mg alloys have shown promising results,demonstrating significant corrosion mitigation,extending the service life of Mg alloy components in aggressive environments,and providing self-healing properties.In general,this review presents available information on the incorporation of inhibitors with PEO coatings,which can lead to improved performance of Mg alloy components in demanding environments.展开更多
A novel design of micro-aluminum(μAl)powder coated with bi-/tri-component alloy layer,such as:Ni-P and Ni-P-Cu(namely,Al@Ni-P,Al@Ni-P-Cu,respectively),as combustion catalysts,were introduced to release its huge energ...A novel design of micro-aluminum(μAl)powder coated with bi-/tri-component alloy layer,such as:Ni-P and Ni-P-Cu(namely,Al@Ni-P,Al@Ni-P-Cu,respectively),as combustion catalysts,were introduced to release its huge energy inside Al-core and promote rapid pyrolysis of ammonium perchlorate(AP)at a lower temperature in aluminized propellants.The microstructure of Al@Ni-P-Cu demonstrates that a three-layer Ni-P-Cu shell,with the thickness of~100 nm,is uniformly supported byμAl carrier(fuel unit),which has an amorphous surface with a thickness of~2.3 nm(catalytic unit).The peak temperature of AP with the addition of Al@Ni-P-Cu(3.5%)could significantly drop to 316.2℃ at high-temperature thermal decomposition,reduced by 124.3℃,in comparison to that of pure AP with 440.5℃.It illustrated that the introduction of Al@Ni-P-Cu could weaken or even eliminate the obstacle of AP pyrolysis due to its reduction of activation energy with 118.28 kJ/mol.The laser ignition results showed that the ignition delay time of Al@Ni-P-Cu/AP mixture with 78 ms in air is shorter than that of Al@Ni-P/AP(118 ms),decreased by 33.90%.Those astonishing breakthroughs were attributed to the synergistic effects of adequate active sites on amorphous surface and oxidation exothermic reactions(7597.7 J/g)of Al@Ni-P-Cu,resulting in accelerated mass and/or heat transfer rate to catalyze AP pyrolysis and combustion.Moreover,it is believed to provide an alternative Al-based combustion catalyst for propellant designer,to promote the development the propellants toward a higher energy.展开更多
The Fe-based amorphous alloy coatings with different porosities were deposited on Q235 steel substrates by means of atmospheric plasma spraying(APS).The as-sprayed coatings were remelted by the facility of a Nd:YAG la...The Fe-based amorphous alloy coatings with different porosities were deposited on Q235 steel substrates by means of atmospheric plasma spraying(APS).The as-sprayed coatings were remelted by the facility of a Nd:YAG laser to further enhance their compactness and bonding strength via orthogonal experiment design.The effects of laser remelting on the microstructure,phase compositions and mechanical properties of the as-sprayed coatings were investigated by optical microscopy,scanning electron microscope,X-ray diffraction and Vickers microhardness tester.The corrosion performance of the coatings was evaluated by both potential dynamic measurements(PDM)and electrochemical impedance spectroscopy(EIS)in a 10%NaOH solution.The results indicate that laser power of 700 W,scanning velocity of 4 mm/s,beam size of 3 mm and porosity of 1.19%are the optimized remelting process parameters.The laser-remelted coatings exhibite more homogenous structure as strong metallurgical bonding to substrates.The amorphous phases in the as-sprayed coatings crystallize toα-Fe,Fe2Si,Fe3.5B,and Fe2W phases for the high temperature and rapid solidification in the remelting process.The microhardness values of as-sprayed are in the range of 700-800 HV0.1,while the microhardness values of the remelted coatings are enhanced slightly to 750-850 HV0.1.Both PDM and EIS analysis results show that the remelted coatings exhibite relatively excellent corrosion resistance compared with the stainless steel 1Cr18Ni9Ti,however the corrosion resistance of the remelted coatings is inferior to the as-sprayed amorphous coatings.展开更多
Mierostrueture of the Fe-based alloy hardfaeing coating reinforced by TiC-VC particles was investigated by means of SEM, TEM, XRD and EPMA. The thermodynamics and effect of elements on the carbides were discussed. The...Mierostrueture of the Fe-based alloy hardfaeing coating reinforced by TiC-VC particles was investigated by means of SEM, TEM, XRD and EPMA. The thermodynamics and effect of elements on the carbides were discussed. The result shows that TiC-VC carbides can be formed during arc welding. Carbides with particle size of 2 ~4μm are uniformly dispersed in the matrix. Evidently the covering components and their amount affect the microstrueture and hardness of the coatings. An excellent microstructure and hardness of hardfacing coating were obtained, while the amount of graphite, FeTi and FeV was controlled within the range of 8%- 10%, 15%- 18% and 8%- 12%, respectively.展开更多
A gradient coating of Fe-based alloy was manufactured with rare earths (RE) by plasma surfacing on Q235 steel substrate. The coatings were studied by using X-ray diffraction(XRD), scanning electron microscope(SEM), di...A gradient coating of Fe-based alloy was manufactured with rare earths (RE) by plasma surfacing on Q235 steel substrate. The coatings were studied by using X-ray diffraction(XRD), scanning electron microscope(SEM), differential thermal analyzer(DTA), and electron probe micro-analyzer (EPMA). The results show that the phases of the two kinds of coatings(with and without RE) both include α-Fe, Fe7C3, Fe3C, Cr2B, Fe2B and FeB. The microstructure of F314 coating is mainly hypereutectic, the pro-phases Cr7C3 and Cr2B are loose, crassi, spiculate and contain microcracks. The brittleness of the coating is high, and the average hardness is 787 HV. When 0.8wt% RE was added into the F314 alloy, the microstructure varied from hypoeutectic to hypereutectic continuously, The hardness appears as gradient distribution with the highest value of 773 HV, meanwhile, the brittleness decreases significantly. The formation of gradient structure depends on the fallowing factors: (i) the conversion of RE. The addition of RE lowers the elements point and Fe-C eutectic temperature, thus the base metal melting acutely. (ii) the heating of plasma arc. Graded temperature results in directional solidification, thus the gradient structure forms easily. The main reasons for the hardness decrease with RE addition in the alloy are the ratio of hard phase lowering and the hardness of the hard phase decreasing.展开更多
The Fe_(949.7)Cr_(18)Mn_(1.9)Mo_(7.4)W_(1.6)B_(15.2)C_(3.8)Si_(2) amorphous coating was deposited on T91 steel substrate by using the high-velocity oxygen fuel(HVOF)spray technique to enhance the corrosion resistance ...The Fe_(949.7)Cr_(18)Mn_(1.9)Mo_(7.4)W_(1.6)B_(15.2)C_(3.8)Si_(2) amorphous coating was deposited on T91 steel substrate by using the high-velocity oxygen fuel(HVOF)spray technique to enhance the corrosion resistance of T91 stainless steel in liquid lead-bismuth eutectic(LBE).The corrosion behavior of the T91 steel and coating exposed to oxygen-saturated LBE at 400℃ for 500 h was investigated.Results showed that the T91 substrate was severely corroded and covered by a homogeneously distributed dual-layer oxide on the interface contacted to LBE,consisting of an outer magnetite layer and an inner Fe-Cr spinel layer.Meanwhile,the amorphous coating with a high glass transition temperature(Tg=550℃)and crystallization temperature(T_(x)=600℃)exhibited dramatically enhanced thermal stability and corrosion resistance.No visible LBE penetration was observed,although small amounts of Fe_(3)O_(4),Cr_(2)O_(3),and PbO were found on the coating surface.In addition,the amorphicity and interface bonding of the coating layer remained unchanged after the LBE corrosion.The Fe-based amorphous coating can act as a stable barrier layer in liquid LBE and have great application potential for long-term service in LBE-cooled fast reactors.展开更多
Mg alloys are considered the most promising engineering materials because of their unique properties.However,the uncontrolled corrosion rate of these alloys limits their applications.Therefore,in this study,a micro-ar...Mg alloys are considered the most promising engineering materials because of their unique properties.However,the uncontrolled corrosion rate of these alloys limits their applications.Therefore,in this study,a micro-arc oxidation layer was used as a transition layer to“directly”grow a zinc-based metal-organic framework(MOF)composite coating on the surface of a Mg alloy(AZ91D).Herein,the two zeolitic imidazolate framework(ZIF-8)coatings with different morphologies were separately prepared by homologous metal oxide induction and a one-step in-situ growth method.The superhydrophobic composite coating showed strong hydrophobicity and self-cleaning properties,which could prevent the penetration of water and corrosive ions(Cl^(−))into the surface of AZ91D.Electrochemical tests demonstrated that the super-hydrophobic composite coatings greatly enhanced the corrosion resistance of AZ91D,and the corrosion current density decreased from 10^(−5)to 10^(−9)A/cm^(2).These results indicate that the ZIF-8 coatings are beneficial for improving the hydrophobicity and enhancing the corrosion resistance of Mg alloys.Therefore,MOF composite coatings provide a new strategy that can be used to prepare multifunctional anticorrosion coatings on metal substrates.展开更多
Magnesium(Mg)alloys,the lightest metal construction material used in industry,play a vital role in future development.However,the poor corrosion resistance of Mg alloys in corrosion environments largely limits their p...Magnesium(Mg)alloys,the lightest metal construction material used in industry,play a vital role in future development.However,the poor corrosion resistance of Mg alloys in corrosion environments largely limits their potential wide applications.Therefore,a micro-arc oxidation/graphene oxide/stearic acid(MAO/GO/SA)superhydrophobic composite coating with superior corrosion resistance was fabricated on a Mg alloy AZ91D through micro-arc oxidation(MAO)technology,electrodeposition technique,and self-assembly technology.The composition and microstructure of the coating were characterized by scanning electron microscopy,X-ray diffraction,energy dispersive spectroscopy,and Raman spectroscopy.The effective protection of the MAO/GO/SA composite coating applied to a substrate was evaluated using potentiodynamic polarization,electrochemical impedance spectroscopy tests,and salt spray tests.The results showed that the MAO/GO/SA composite coating with a petal spherical structure had the best superhydrophobicity,and it attained a contact angle of 159.53°±2°.The MAO/GO/SA composite coating exhibited high resistance to corrosion,according to electrochemical and salt spray tests.展开更多
Biodegradable implants are critical for regenerative orthopaedic procedures,but they may suffer from too fast corrosion in human-body environment.This necessitates the synthesis of a suitable coating that may improve ...Biodegradable implants are critical for regenerative orthopaedic procedures,but they may suffer from too fast corrosion in human-body environment.This necessitates the synthesis of a suitable coating that may improve the corrosion resistance of these implants without compromising their mechanical integrity.In this study,an AZ91 magnesium alloy,as a representative for a biodegradable Mg implant material,was modified with a thin reduced graphene oxide(RGO)-calcium carbonate(CaCO_(3))composite coating.Detailed analytical and in-vitro electrochemical characterization reveals that this coating significantly improves the corrosion resistance and mechanical integrity,and thus has the potential to greatly extend the related application field.展开更多
Formation of super-hydrophobic and corrosion-resistant coatings can provide significant corrosion protection to magnesium alloys.However,it remains a grand challenge to produce such coatings for magnesium-lithium allo...Formation of super-hydrophobic and corrosion-resistant coatings can provide significant corrosion protection to magnesium alloys.However,it remains a grand challenge to produce such coatings for magnesium-lithium alloys due to their high chemical reactivity.Herein,a one-step hydrothermal processing was developed using a stearic-acid-based precursor medium,which enables the hydrothermal conversion and the formation of low surface energy materials concurrently to produce the super-hydrophobic and corrosion-resistant coating.The multiscale microstructures with nanoscale stacks and microscale spheres on the surface,as well as the through-thickness stearates,lead to the super-hydrophobicity and excellent corrosion resistance of the obtained coating.展开更多
A longstanding quest in material science has been the development of superhydrophobic coating based on a single material, without the requirement of fluorination or silane treatment. In this work, the micro-arc oxidat...A longstanding quest in material science has been the development of superhydrophobic coating based on a single material, without the requirement of fluorination or silane treatment. In this work, the micro-arc oxidation(MAO) coating as transition layer can effectively enhance the bonding force of the superhydrophobic coating. The semiconductor@metal organic frameworks(MOFs) core-shell structure was synthesized by a simple self-templating method, and obtained ZnO@2-methylimidazole zinc salt(ZIF-8) nanorods array on magnesium(Mg)alloy. ZnO nanorods not only act as the template but also provide Zn^(2+) for ZIF-8. In addition, we proved that the ligand concentration,synthesis time and temperature are the keys to the preparation of ZnO@ZIF-8 nanorods. As we expect, the ZnO@ZIF-8 nanorods array can trap air in the gaps to form an air layer, and the coating exhibits superhydrophobic properties(154.81°). Excitingly, ZnO@ZIF-8 nanorods array shown a superhydrophobic property, without the requirement of fluorination or silane treatment. The results shown that the coating has good chemical stability and self-cleaning performance. Meanwhile, the corrosion resistance has been significantly improved, R_(ct) was increased from 1.044×10^(3) to 1.414×10^(6) Ω/cm^(2) and I_(corr) was reduced from 4.275×10^(-5) to 5.611×10^(-9)A/cm^2. Therefore, the semiconductor@MOFs core-shell structure has broad application prospects in anti-corrosion.展开更多
A V/Ce conversion coating was deposited in the surface of AZ31B magnesium alloy in a solution containing vanadate and cerium nitrate.The coating composition and morphology were examined.The conversion coating appears ...A V/Ce conversion coating was deposited in the surface of AZ31B magnesium alloy in a solution containing vanadate and cerium nitrate.The coating composition and morphology were examined.The conversion coating appears to consist of a thin and cracked coating with a scattering of spherical particles.The corrosion behavior of the substrate and conversion coating was studied by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS).Compared with AZ31B magnesium alloy,the corrosion current density of the conversion coating is decreased by two orders of magnitude.The total impedance of the V/Ce conversion coating rise to 1.6×10^(3)Ω·cm^(2)in contrast with2.2×10^(2)Ω·cm^(2)of the bare AZ31B.In addition,the electrical conductivity of the coating was assessed by conductivity meter and Mott-Schottky measurement.The results reveal a high dependence of the conductivity of the coating on the semiconductor properties of the phase compositions.展开更多
In this study,the effects of intermetallic compounds(Mg_(17)Al_(12)and Al_(8)Mn_(5))on the Mg-Al layered double hydroxide(LDH)formation mechanism and corrosion behavior of an in-situ LDH/Mg(OH)_(2)steam coatings on AZ...In this study,the effects of intermetallic compounds(Mg_(17)Al_(12)and Al_(8)Mn_(5))on the Mg-Al layered double hydroxide(LDH)formation mechanism and corrosion behavior of an in-situ LDH/Mg(OH)_(2)steam coatings on AZ80 Mg alloy were investigated.Citric acid(CA)was used to activate the alloy surface during the pretreatment process.The alloy was first pretreated with CA and then subjected to a hydrothermal process using ultrapure water to produce Mg-Al-LDH/Mg(OH)_(2)steam coating.The effect of different time of acid pretreatment on the activation of the intermetallic compounds was investigated.The microstructure and elemental composition of the obtained coatings were analyzed using FE-SEM,EDS,XRD and FT-IR.The corrosion resistance of the coated samples was evaluated using different techniques,i.e.,potentiodynamic polarization(PDP),electrochemical impedance spectrum(EIS)and hydrogen evolution test.The results indicated that the CA pretreatment significantly influenced the activity of the alloy surface by exposing the intermetallic compounds.The surface area fraction of Mg_(17)Al_(12)and Al_(8)Mn_(5)phases on the surface of the alloy was significantly higher after the CA pretreatment,and thus promoted the growth of the subsequent Mg-Al-LDH coatings.The CA pretreatment for 30 s resulted in a denser and thicker LDH coating.Increase in the CA pretreatment time significantly led to the improvement in corrosion resistance of the coated AZ80 alloy.The corrosion current density of the coated alloy was lower by three orders of magnitude as compared to the uncoated alloy.展开更多
A novel combined method for the formation of composite coatings on the Mg-Mn-Ce alloy is developed.Ceramic like matrix was formed on the Mg alloy surface by the plasma electrolytic oxidation.Then the samples were subs...A novel combined method for the formation of composite coatings on the Mg-Mn-Ce alloy is developed.Ceramic like matrix was formed on the Mg alloy surface by the plasma electrolytic oxidation.Then the samples were subsequently processed by dip-coating in an alcohol suspension of superdispersed polytetrafluoroethylene and spraying with the tetrafluoroethylene telomers solution.SEM,OSP,and SPM was used to study structure of formed surfaces.It was established by measurements of CA and CAH,as well as surface free energy calculations that formed coatings demonstrate superhydrophobic properties due to the presence of an irregular hierarchical surface structure and low surface free energy of fluoropolymers.The coating preserves its hydrophobic properties after exposure to high and low temperatures,for a long time as well as being in corrosive environments.EDS and XRD data analysis confirmed the presence of organofluorine compounds in the composite layers,including in the form of crystalline polytetrafluoroethylene.Using potentiodynamic polarization test and EIS,it was found that the resulting coatings significantly increase the corrosion resistance of Mg material.These data are also confirmed by salt spray tests for 40 days.Incorporation of fluoropolymers additionally decrease coatings coefficient of friction.展开更多
基金This work is supported by the National Natural Science Foundation of China (Grant No. 51101051 ), the Natural Science Foundation of Jiangsu Province (Grant No. BK2011250), and Jiangsu Planned Projects for Postdoctoral Research Funds (Grant No. 1101017 C).
文摘The Fe-based alloy coatings reinforced with in situ synthesized TiB2-TiC were prepared on Q235 steel by reactive plasma cladding using Fe901 alloy, Ti, B4C, and graphite (C) powders us raw materials. The effects of C/B4C weight percentage ratio (0 - 1. 38 ) on the microstructure , microhardness , and wet sand abrasion resistance of the coatings were investigated. The results show that the coatings consist of ( Fe, Cr ) solid solution, TiC, TiB2, Ti8C5 , and Fe3 C phases. The decrease of C/B4 C ratio is propitious to the formation of TiB2 and Tis C5. Increasing the C/B4 C ratio can help to refine the microstructure of the coatings. However, the microhardness of the middle-upper of the coatings and the wet sand abrasion resistance of the coatings degenerate with the increase of C/B4C ratio. The coating exhibits the best wet sand abrasion resistance at C/BaC =0 and its average mass loss rate per unit wear distance is 0. 001 2%/m. The change of the wet sand abrasion resistance of the coatings with the C/B4C ratio can be mainly attributed to the combined action of the changes of microhardness and the volume percentage of the ceramic reinforcements containing titanium in the coatings.
基金National Key Research and Development Program of China,Grant/Award Number:2022YFB3807700Hubei Natural Science Foundation Innovation Group Project,Grant/Award Number:2022CFA020+2 种基金Joint Funds of the Hubei Natural Science Foundation Innovation and Development,Grant/Award Number:2022CFD034Major Technological Innovation Project of Hubei Science and Technology Department,Grant/Award Number:2019AAA164National Natural Science Foundation of China,Grant/Award Number:2022CFD034。
文摘Fe-based Prussian blue(Fe-PB)cathode material shows great application potential in sodium(Na)-ion batteries due to its high theoretical capacity,long cycle life,low cost,and simple preparation process.However,the crystalline water and vacancies of Fe-PB lattice,the low electrical conductivity,and the dissolution of metal ions lead to limited capacity and poor cycling stability.In this work,a perylene tetracarboxylic dianhydride amine(PTCDA)coating layer is successfully fabricated on the surface of Fe-PB by a liquid-phase method.The aminated PTCDA(PTCA)coating not only increases the specific surface area and electronic conductivity but also effectively reduces the crystalline water and vacancies,which avoids the erosion of Fe-PB by electrolyte.Consequently,the PTCA layer reduces the charge transfer resistance,enhances the Na-ion diffusion coefficient,and improves the structure stability.The PTCA-coated Fe-PB exhibits superior Na storage performance with a first discharge capacity of 145.2 mAh g^(−1) at 100 mA g^(−1).Long cycling tests exhibit minimal capacity decay of 0.027%per cycle over 1000 cycles at 1 A g^(−1).Therefore,this PTCA coating strategy has shown promising competence in enhancing the electrochemical performance of Fe-PB,which can potentially serve as a universal electrode coating strategy for Na-ion batteries.
基金financially supported by the National Natural Science Foundation of China (No.52271073)。
文摘A Ni–P alloy gradient coating consisting of multiple electroless Ni–P layers with various phosphorus contents was prepared on the aviation aluminum alloy. Several characterization and electrochemical techniques were used to characterize the different Ni–P coatings’ morphologies, phase structures, elemental compositions, and corrosion protection. The gradient coating showed good adhesion and high corrosion and wear resistance, enabling the application of aluminum alloy in harsh environments. The results showed that the double zinc immersion was vital in obtaining excellent adhesion (81.2 N). The optimal coating was not peeled and shredded even after bending tests with angles higher than 90°and was not corroded visually after 500 h of neutral salt spray test at 35℃. The high corrosion resistance was attributed to the misaligning of these micro defects in the three different nickel alloy layers and the amorphous structure of the high P content in the outer layer. These findings guide the exploration of functional gradient coatings that meet the high application requirement of aluminum alloy parts in complicated and harsh aviation environments.
基金the National Natural Science Foundation of China(Grant number 51771178)Shaanxi Outstanding Youth Fund project(Grant number 2021JC-45)+2 种基金Key international cooperation projects in Shaanxi Province(Grant number 2020KWZ-007)the Major Program of Science and Technology in Shaanxi Province(Grant number20191102006)Open Fund of State Key Laboratory of Advanced Design and Manufacturing for Vehicle Body(Grant number 32115019)。
文摘The poor corrosion and wear resistances of Mg alloys seriously limit their potential applications in various industries.The conventional epoxy coating easily forms many intrinsic defects during the solidification process,which cannot provide sufficient protection.In the current study,we design a double-layer epoxy composite coating on Mg alloy with enhanced anti-corrosion/wear properties,via the spin-assisted assembly technique.The outer layer is functionalized graphene(FG)in waterborne epoxy resin(WEP)and the inner layer is Ce-based conversion(Ce)film.The FG sheets can be homogeneously dispersed within the epoxy matrix to fill the intrinsic defects and improve the barrier capability.The Ce film connects the outer layer with the substrate,showing the transition effect.The corrosion rate of Ce/WEP/FG composite coating is 2131 times lower than that of bare Mg alloy,and the wear rate is decreased by~90%.The improved corrosion resistance is attributed to the labyrinth effect(hindering the penetration of corrosive medium)and the obstruction of galvanic coupling behavior.The synergistic effect derived from the FG sheet and blocking layer exhibits great potential in realizing the improvement of multi-functional integration,which will open up a new avenue for the development of novel composite protection coatings of Mg alloys.
基金Supported by Sichuan Provincial Science and Technology Program of China(Grant No.2018JY0245)National Natural Science Foundation of China(Grant No.51975492)Natural Science Foundation of Southwest University of Science and Technology of China(Grant No.19xz7163).
文摘Titanium alloys are excellent structural materials in engineering fields,but their poor tribological properties limit their further applications.Electroless plating is an effective method to enhance the tribological performance of alloys,but it is difficult to efficiently apply to titanium alloys,due to titanium alloy’s strong chemical activity.In this work,the electroless Nickel-Boron(Ni-B)coating was successfully deposited on the surface of titanium alloy(Ti-6AL-4V)via a new pre-treatment process.Then,linearly reciprocating sliding wear tests were performed to evaluate the tribological behaviors of titanium alloy and its electroless Ni-B coatings.It was found that the Ni-B coatings can decrease the wear rate of the titanium alloy from 19.89×10^(−3)mm^(3)to 0.41×10^(−3)mm^(3),which attributes to the much higher hardness of Ni-B coatings.After heat treatment,the hardness of Ni-B coating further increases corresponding to coating crystallization and hard phase formation.However,heat treatment does not improve the tribological performance of Ni-B coating,due to the fact that higher brittleness and more severe oxidative wear exacerbate the damage of heat-treated coatings.Furthermore,the Ni-B coatings heat-treated both in air and nitrogen almost present the same tribological performance.The finding of this work on electroless coating would further extend the practical applications of titanium alloys in the engineering fields.
基金the National Key Research and Development Program of China(2018YFC1106703)the National Natural Science Foundation of China(No.U1804251)。
文摘Constructing a functional hybrid coating appears to be a promising strategy for addressing the poor corrosion resistance and insufficient endothelialization of Mg-based stents.Nevertheless,the steps for preparing composite coatings are usually complicated and time-consuming.Herein,a novel composite coating,composed of bioactive magnesium thioctic acid(MTA)layer formed by deposition and corrosion-resistant magnesium hydroxide(Mg(OH)_(2))layer grown in situ,is simply fabricated on ZE21B alloys via one-step electrodeposition.Scanning electron microscopy(SEM)shows that the electrodeposited coating has a compact and uniform structure.And the high adhesion of the MTA/Mg(OH)_(2)hybrid coating is also confirmed by the micro-scratch test.Electrochemical test,scanning kelvin probe(SKP),and hydrogen evolution measurement indicate that the hybrid coating effectively reduces the degradation rate of Mg substrates.Haemocompatibility experiment and cell culture trial detect that the composite coating is of fine biocompatibility.Finally,the preparation mechanism of MTA/Mg(OH)_(2)hybrid coatings is discussed and proposed.This coating shows a great potential application for cardiovascular stents.
文摘Magnesium(Mg)alloys are lightweight materials with excellent mechanical properties,making them attractive for various applications,including aerospace,automotive,and biomedical industries.However,the practical application of Mg alloys is limited due to their high susceptibility to corrosion.Plasma electrolytic oxidation(PEO),or micro-arc oxidation(MAO),is a coating method that boosts Mg alloys'corrosion resistance.However,despite the benefits of PEO coatings,they can still exhibit certain limitations,such as failing to maintain long-term protection as a result of their inherent porosity.To address these challenges,researchers have suggested the use of inhibitors in combination with PEO coatings on Mg alloys.Inhibitors are chemical compounds that can be incorporated into the coating or applied as a post-treatment to further boost the corrosion resistance of the PEO-coated Mg alloys.Corrosion inhibitors,whether organic or inorganic,can act by forming a protective barrier,hindering the corrosion process,or modifying the surface properties to reduce susceptibility to corrosion.Containers can be made of various materials,including polyelectrolyte shells,layered double hydroxides,polymer shells,and mesoporous inorganic materials.Encapsulating corrosion inhibitors in containers fully compatible with the coating matrix and substrate is a promising approach for their incorporation.Laboratory studies of the combination of inhibitors with PEO coatings on Mg alloys have shown promising results,demonstrating significant corrosion mitigation,extending the service life of Mg alloy components in aggressive environments,and providing self-healing properties.In general,this review presents available information on the incorporation of inhibitors with PEO coatings,which can lead to improved performance of Mg alloy components in demanding environments.
基金supported by the National Natural Science Foundation of China,China(Grant Nos.U20B2018,U21B2086,11972087)。
文摘A novel design of micro-aluminum(μAl)powder coated with bi-/tri-component alloy layer,such as:Ni-P and Ni-P-Cu(namely,Al@Ni-P,Al@Ni-P-Cu,respectively),as combustion catalysts,were introduced to release its huge energy inside Al-core and promote rapid pyrolysis of ammonium perchlorate(AP)at a lower temperature in aluminized propellants.The microstructure of Al@Ni-P-Cu demonstrates that a three-layer Ni-P-Cu shell,with the thickness of~100 nm,is uniformly supported byμAl carrier(fuel unit),which has an amorphous surface with a thickness of~2.3 nm(catalytic unit).The peak temperature of AP with the addition of Al@Ni-P-Cu(3.5%)could significantly drop to 316.2℃ at high-temperature thermal decomposition,reduced by 124.3℃,in comparison to that of pure AP with 440.5℃.It illustrated that the introduction of Al@Ni-P-Cu could weaken or even eliminate the obstacle of AP pyrolysis due to its reduction of activation energy with 118.28 kJ/mol.The laser ignition results showed that the ignition delay time of Al@Ni-P-Cu/AP mixture with 78 ms in air is shorter than that of Al@Ni-P/AP(118 ms),decreased by 33.90%.Those astonishing breakthroughs were attributed to the synergistic effects of adequate active sites on amorphous surface and oxidation exothermic reactions(7597.7 J/g)of Al@Ni-P-Cu,resulting in accelerated mass and/or heat transfer rate to catalyze AP pyrolysis and combustion.Moreover,it is believed to provide an alternative Al-based combustion catalyst for propellant designer,to promote the development the propellants toward a higher energy.
基金National Natural Science Foundation of China(50805104)
文摘The Fe-based amorphous alloy coatings with different porosities were deposited on Q235 steel substrates by means of atmospheric plasma spraying(APS).The as-sprayed coatings were remelted by the facility of a Nd:YAG laser to further enhance their compactness and bonding strength via orthogonal experiment design.The effects of laser remelting on the microstructure,phase compositions and mechanical properties of the as-sprayed coatings were investigated by optical microscopy,scanning electron microscope,X-ray diffraction and Vickers microhardness tester.The corrosion performance of the coatings was evaluated by both potential dynamic measurements(PDM)and electrochemical impedance spectroscopy(EIS)in a 10%NaOH solution.The results indicate that laser power of 700 W,scanning velocity of 4 mm/s,beam size of 3 mm and porosity of 1.19%are the optimized remelting process parameters.The laser-remelted coatings exhibite more homogenous structure as strong metallurgical bonding to substrates.The amorphous phases in the as-sprayed coatings crystallize toα-Fe,Fe2Si,Fe3.5B,and Fe2W phases for the high temperature and rapid solidification in the remelting process.The microhardness values of as-sprayed are in the range of 700-800 HV0.1,while the microhardness values of the remelted coatings are enhanced slightly to 750-850 HV0.1.Both PDM and EIS analysis results show that the remelted coatings exhibite relatively excellent corrosion resistance compared with the stainless steel 1Cr18Ni9Ti,however the corrosion resistance of the remelted coatings is inferior to the as-sprayed amorphous coatings.
文摘Mierostrueture of the Fe-based alloy hardfaeing coating reinforced by TiC-VC particles was investigated by means of SEM, TEM, XRD and EPMA. The thermodynamics and effect of elements on the carbides were discussed. The result shows that TiC-VC carbides can be formed during arc welding. Carbides with particle size of 2 ~4μm are uniformly dispersed in the matrix. Evidently the covering components and their amount affect the microstrueture and hardness of the coatings. An excellent microstructure and hardness of hardfacing coating were obtained, while the amount of graphite, FeTi and FeV was controlled within the range of 8%- 10%, 15%- 18% and 8%- 12%, respectively.
文摘A gradient coating of Fe-based alloy was manufactured with rare earths (RE) by plasma surfacing on Q235 steel substrate. The coatings were studied by using X-ray diffraction(XRD), scanning electron microscope(SEM), differential thermal analyzer(DTA), and electron probe micro-analyzer (EPMA). The results show that the phases of the two kinds of coatings(with and without RE) both include α-Fe, Fe7C3, Fe3C, Cr2B, Fe2B and FeB. The microstructure of F314 coating is mainly hypereutectic, the pro-phases Cr7C3 and Cr2B are loose, crassi, spiculate and contain microcracks. The brittleness of the coating is high, and the average hardness is 787 HV. When 0.8wt% RE was added into the F314 alloy, the microstructure varied from hypoeutectic to hypereutectic continuously, The hardness appears as gradient distribution with the highest value of 773 HV, meanwhile, the brittleness decreases significantly. The formation of gradient structure depends on the fallowing factors: (i) the conversion of RE. The addition of RE lowers the elements point and Fe-C eutectic temperature, thus the base metal melting acutely. (ii) the heating of plasma arc. Graded temperature results in directional solidification, thus the gradient structure forms easily. The main reasons for the hardness decrease with RE addition in the alloy are the ratio of hard phase lowering and the hardness of the hard phase decreasing.
基金financially supported by the National Natural Science Foundation of China (Nos. 52061135207, 51871016, 51921001, 5197011039, 5197011018, and U20b200318)the China Nuclear Power Technology Research Institute Co., Ltd
文摘The Fe_(949.7)Cr_(18)Mn_(1.9)Mo_(7.4)W_(1.6)B_(15.2)C_(3.8)Si_(2) amorphous coating was deposited on T91 steel substrate by using the high-velocity oxygen fuel(HVOF)spray technique to enhance the corrosion resistance of T91 stainless steel in liquid lead-bismuth eutectic(LBE).The corrosion behavior of the T91 steel and coating exposed to oxygen-saturated LBE at 400℃ for 500 h was investigated.Results showed that the T91 substrate was severely corroded and covered by a homogeneously distributed dual-layer oxide on the interface contacted to LBE,consisting of an outer magnetite layer and an inner Fe-Cr spinel layer.Meanwhile,the amorphous coating with a high glass transition temperature(Tg=550℃)and crystallization temperature(T_(x)=600℃)exhibited dramatically enhanced thermal stability and corrosion resistance.No visible LBE penetration was observed,although small amounts of Fe_(3)O_(4),Cr_(2)O_(3),and PbO were found on the coating surface.In addition,the amorphicity and interface bonding of the coating layer remained unchanged after the LBE corrosion.The Fe-based amorphous coating can act as a stable barrier layer in liquid LBE and have great application potential for long-term service in LBE-cooled fast reactors.
基金supported by Guangxi Natural Science Foundation of China(No.2020GXNSFAA159011)National Natural Science Foundation of China(No.51664011)Guangxi Key Laboratory Foundation of China(No.EMFM20211120).
文摘Mg alloys are considered the most promising engineering materials because of their unique properties.However,the uncontrolled corrosion rate of these alloys limits their applications.Therefore,in this study,a micro-arc oxidation layer was used as a transition layer to“directly”grow a zinc-based metal-organic framework(MOF)composite coating on the surface of a Mg alloy(AZ91D).Herein,the two zeolitic imidazolate framework(ZIF-8)coatings with different morphologies were separately prepared by homologous metal oxide induction and a one-step in-situ growth method.The superhydrophobic composite coating showed strong hydrophobicity and self-cleaning properties,which could prevent the penetration of water and corrosive ions(Cl^(−))into the surface of AZ91D.Electrochemical tests demonstrated that the super-hydrophobic composite coatings greatly enhanced the corrosion resistance of AZ91D,and the corrosion current density decreased from 10^(−5)to 10^(−9)A/cm^(2).These results indicate that the ZIF-8 coatings are beneficial for improving the hydrophobicity and enhancing the corrosion resistance of Mg alloys.Therefore,MOF composite coatings provide a new strategy that can be used to prepare multifunctional anticorrosion coatings on metal substrates.
基金financially supported by the Guangxi Natural Science Foundation,China(No.2020GXNSFAA 159011)the National Natural Science Foundation of China(No.51664011).
文摘Magnesium(Mg)alloys,the lightest metal construction material used in industry,play a vital role in future development.However,the poor corrosion resistance of Mg alloys in corrosion environments largely limits their potential wide applications.Therefore,a micro-arc oxidation/graphene oxide/stearic acid(MAO/GO/SA)superhydrophobic composite coating with superior corrosion resistance was fabricated on a Mg alloy AZ91D through micro-arc oxidation(MAO)technology,electrodeposition technique,and self-assembly technology.The composition and microstructure of the coating were characterized by scanning electron microscopy,X-ray diffraction,energy dispersive spectroscopy,and Raman spectroscopy.The effective protection of the MAO/GO/SA composite coating applied to a substrate was evaluated using potentiodynamic polarization,electrochemical impedance spectroscopy tests,and salt spray tests.The results showed that the MAO/GO/SA composite coating with a petal spherical structure had the best superhydrophobicity,and it attained a contact angle of 159.53°±2°.The MAO/GO/SA composite coating exhibited high resistance to corrosion,according to electrochemical and salt spray tests.
文摘Biodegradable implants are critical for regenerative orthopaedic procedures,but they may suffer from too fast corrosion in human-body environment.This necessitates the synthesis of a suitable coating that may improve the corrosion resistance of these implants without compromising their mechanical integrity.In this study,an AZ91 magnesium alloy,as a representative for a biodegradable Mg implant material,was modified with a thin reduced graphene oxide(RGO)-calcium carbonate(CaCO_(3))composite coating.Detailed analytical and in-vitro electrochemical characterization reveals that this coating significantly improves the corrosion resistance and mechanical integrity,and thus has the potential to greatly extend the related application field.
基金support from the Fundamental Research Funds for the Central Universities of Hohai university(B200202122)National Natural Science Foundation of China(51878246 and 51979099)+1 种基金the Natural Science Foundation of Jiangsu Province of China(BK20191303)Key Research and Development Project of Jiangsu Province of China(BE2017148).
文摘Formation of super-hydrophobic and corrosion-resistant coatings can provide significant corrosion protection to magnesium alloys.However,it remains a grand challenge to produce such coatings for magnesium-lithium alloys due to their high chemical reactivity.Herein,a one-step hydrothermal processing was developed using a stearic-acid-based precursor medium,which enables the hydrothermal conversion and the formation of low surface energy materials concurrently to produce the super-hydrophobic and corrosion-resistant coating.The multiscale microstructures with nanoscale stacks and microscale spheres on the surface,as well as the through-thickness stearates,lead to the super-hydrophobicity and excellent corrosion resistance of the obtained coating.
基金financially supported by Guangxi Natural Science Foundation of China (No.2020GXNSFAA159011)National Natural Science Foundation of China (No.51664011)。
文摘A longstanding quest in material science has been the development of superhydrophobic coating based on a single material, without the requirement of fluorination or silane treatment. In this work, the micro-arc oxidation(MAO) coating as transition layer can effectively enhance the bonding force of the superhydrophobic coating. The semiconductor@metal organic frameworks(MOFs) core-shell structure was synthesized by a simple self-templating method, and obtained ZnO@2-methylimidazole zinc salt(ZIF-8) nanorods array on magnesium(Mg)alloy. ZnO nanorods not only act as the template but also provide Zn^(2+) for ZIF-8. In addition, we proved that the ligand concentration,synthesis time and temperature are the keys to the preparation of ZnO@ZIF-8 nanorods. As we expect, the ZnO@ZIF-8 nanorods array can trap air in the gaps to form an air layer, and the coating exhibits superhydrophobic properties(154.81°). Excitingly, ZnO@ZIF-8 nanorods array shown a superhydrophobic property, without the requirement of fluorination or silane treatment. The results shown that the coating has good chemical stability and self-cleaning performance. Meanwhile, the corrosion resistance has been significantly improved, R_(ct) was increased from 1.044×10^(3) to 1.414×10^(6) Ω/cm^(2) and I_(corr) was reduced from 4.275×10^(-5) to 5.611×10^(-9)A/cm^2. Therefore, the semiconductor@MOFs core-shell structure has broad application prospects in anti-corrosion.
基金financially supported by the National Key Research and Development Program of China (Nos. 2016YFB0301105 and 2017YFB0702100)。
文摘A V/Ce conversion coating was deposited in the surface of AZ31B magnesium alloy in a solution containing vanadate and cerium nitrate.The coating composition and morphology were examined.The conversion coating appears to consist of a thin and cracked coating with a scattering of spherical particles.The corrosion behavior of the substrate and conversion coating was studied by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS).Compared with AZ31B magnesium alloy,the corrosion current density of the conversion coating is decreased by two orders of magnitude.The total impedance of the V/Ce conversion coating rise to 1.6×10^(3)Ω·cm^(2)in contrast with2.2×10^(2)Ω·cm^(2)of the bare AZ31B.In addition,the electrical conductivity of the coating was assessed by conductivity meter and Mott-Schottky measurement.The results reveal a high dependence of the conductivity of the coating on the semiconductor properties of the phase compositions.
基金This work was supported by the National Natural Science Foundation of China(Grant Nos.51601108 and 52071191)the Natural Science Foundation of Shandong Province(ZR2020ME011).
文摘In this study,the effects of intermetallic compounds(Mg_(17)Al_(12)and Al_(8)Mn_(5))on the Mg-Al layered double hydroxide(LDH)formation mechanism and corrosion behavior of an in-situ LDH/Mg(OH)_(2)steam coatings on AZ80 Mg alloy were investigated.Citric acid(CA)was used to activate the alloy surface during the pretreatment process.The alloy was first pretreated with CA and then subjected to a hydrothermal process using ultrapure water to produce Mg-Al-LDH/Mg(OH)_(2)steam coating.The effect of different time of acid pretreatment on the activation of the intermetallic compounds was investigated.The microstructure and elemental composition of the obtained coatings were analyzed using FE-SEM,EDS,XRD and FT-IR.The corrosion resistance of the coated samples was evaluated using different techniques,i.e.,potentiodynamic polarization(PDP),electrochemical impedance spectrum(EIS)and hydrogen evolution test.The results indicated that the CA pretreatment significantly influenced the activity of the alloy surface by exposing the intermetallic compounds.The surface area fraction of Mg_(17)Al_(12)and Al_(8)Mn_(5)phases on the surface of the alloy was significantly higher after the CA pretreatment,and thus promoted the growth of the subsequent Mg-Al-LDH coatings.The CA pretreatment for 30 s resulted in a denser and thicker LDH coating.Increase in the CA pretreatment time significantly led to the improvement in corrosion resistance of the coated AZ80 alloy.The corrosion current density of the coated alloy was lower by three orders of magnitude as compared to the uncoated alloy.
基金The study was supported by the Russian Science Foundation grant no.22-73-10149,https://rscf.ru/project/22-73-10149/.
文摘A novel combined method for the formation of composite coatings on the Mg-Mn-Ce alloy is developed.Ceramic like matrix was formed on the Mg alloy surface by the plasma electrolytic oxidation.Then the samples were subsequently processed by dip-coating in an alcohol suspension of superdispersed polytetrafluoroethylene and spraying with the tetrafluoroethylene telomers solution.SEM,OSP,and SPM was used to study structure of formed surfaces.It was established by measurements of CA and CAH,as well as surface free energy calculations that formed coatings demonstrate superhydrophobic properties due to the presence of an irregular hierarchical surface structure and low surface free energy of fluoropolymers.The coating preserves its hydrophobic properties after exposure to high and low temperatures,for a long time as well as being in corrosive environments.EDS and XRD data analysis confirmed the presence of organofluorine compounds in the composite layers,including in the form of crystalline polytetrafluoroethylene.Using potentiodynamic polarization test and EIS,it was found that the resulting coatings significantly increase the corrosion resistance of Mg material.These data are also confirmed by salt spray tests for 40 days.Incorporation of fluoropolymers additionally decrease coatings coefficient of friction.