为解决TiO_2光催化纳米材料在使用过程中不易回收的问题,采用直接水解法成功制备了磁性核壳结构Fe_3O_4@TiO_2纳米材料,采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)等对其物理化学...为解决TiO_2光催化纳米材料在使用过程中不易回收的问题,采用直接水解法成功制备了磁性核壳结构Fe_3O_4@TiO_2纳米材料,采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)等对其物理化学特性进行了表征,并且考察了制备工艺条件,如钛酸四丁酯(TBOT)用量、氨水用量、反应温度、反应时间等因素对Fe_3O_4@TiO_2纳米颗粒光催化效果的影响。结果表明,TiO_2在Fe_3O_4颗粒表面进行了有效的包覆,形成了良好的包覆层,优化后制备工艺条件为:TBOT用量1.0 m L、氨水用量0.3 m L、制备温度85℃、制备时间4h,所得Fe_3O_4@TiO_2纳米材料对罗丹明B的催化降解效率明显提高,罗丹明B降解率达到98%。对负载前后纳米颗粒的磁滞回线进行测试发现,TiO_2的包覆并未明显减弱Fe_3O_4的磁性,所制备的可回收磁性Fe_3O_4@TiO_2催化剂具有良好的稳定性和重复利用性能。展开更多
The core-shell Fe2O3@Au particle with spindle morphology were synthesized by three steps.The mean size of the core-shell paricles was about 500 nm by 85 nm.The final single separated spindle particles were attached on...The core-shell Fe2O3@Au particle with spindle morphology were synthesized by three steps.The mean size of the core-shell paricles was about 500 nm by 85 nm.The final single separated spindle particles were attached onto Si substrates.The thiophenol(TP) was served as probe molecule to investigate the pola-rized dependent surface-enhanced Raman scattering(SERS) from single particle.Dramatic variations in SERS intensity was observed when the single core-shell particle was oriented at different angles relative to the polarization of excitation laser.The maximum SERS intensity was detected for TP absorbed on the anisotropic particle which was in the polarization direction parallel to the long axis of the particle,while the minimum intensity was detected at the direction of the incident field that is perpendicular to the long axis of the particle.Our preliminary results provided useful way for obtaining deeper insight to the SERS mechanism.展开更多
文摘为解决TiO_2光催化纳米材料在使用过程中不易回收的问题,采用直接水解法成功制备了磁性核壳结构Fe_3O_4@TiO_2纳米材料,采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)等对其物理化学特性进行了表征,并且考察了制备工艺条件,如钛酸四丁酯(TBOT)用量、氨水用量、反应温度、反应时间等因素对Fe_3O_4@TiO_2纳米颗粒光催化效果的影响。结果表明,TiO_2在Fe_3O_4颗粒表面进行了有效的包覆,形成了良好的包覆层,优化后制备工艺条件为:TBOT用量1.0 m L、氨水用量0.3 m L、制备温度85℃、制备时间4h,所得Fe_3O_4@TiO_2纳米材料对罗丹明B的催化降解效率明显提高,罗丹明B降解率达到98%。对负载前后纳米颗粒的磁滞回线进行测试发现,TiO_2的包覆并未明显减弱Fe_3O_4的磁性,所制备的可回收磁性Fe_3O_4@TiO_2催化剂具有良好的稳定性和重复利用性能。
文摘The core-shell Fe2O3@Au particle with spindle morphology were synthesized by three steps.The mean size of the core-shell paricles was about 500 nm by 85 nm.The final single separated spindle particles were attached onto Si substrates.The thiophenol(TP) was served as probe molecule to investigate the pola-rized dependent surface-enhanced Raman scattering(SERS) from single particle.Dramatic variations in SERS intensity was observed when the single core-shell particle was oriented at different angles relative to the polarization of excitation laser.The maximum SERS intensity was detected for TP absorbed on the anisotropic particle which was in the polarization direction parallel to the long axis of the particle,while the minimum intensity was detected at the direction of the incident field that is perpendicular to the long axis of the particle.Our preliminary results provided useful way for obtaining deeper insight to the SERS mechanism.