A Zr-Gd alloy with neutron poisoning properties and resistance to boiling concentrated HNO3 corrosion was developed based on a corrosion-resistant Zr-702 alloy to meet the demand for neutron shielding in the closed-lo...A Zr-Gd alloy with neutron poisoning properties and resistance to boiling concentrated HNO3 corrosion was developed based on a corrosion-resistant Zr-702 alloy to meet the demand for neutron shielding in the closed-loop treatment of spent fuel and the nuclear chemical industry.In this study,1 wt.%,3 wt.%,5 wt.%,7 wt.%,and 9 wt.%Zr-Gd alloys were designed and fabricated with Zr-702 as the control element.The electrochemical behavior of the Zr-Gd alloys in boiling concentrated HNO3 was investigated,and the neutron shielding effect on plate thickness and Gd content was simulated.The experimental results demonstrate that the corrosion resistance of the alloy decreased slightly before~7-9 wt.%with increasing Gd content;this is the inflection point of its corrosion resistance.The alloy uniformly dissolved the Gd content that could not be dissolved in the Zr lattice,resulting in numerous micropores on the passivation coating,which deteriorated and accelerated the corrosion rate.The MCNP simulation demonstrated that when the Gd content was increased to 5 wt.%,a 2-mm-thick plate can shield 99.9%neutrons;an alloy with a Gd content≥7 wt.%required only a 1-mm-thick plate,thereby showing that the addition of Gd provides an excellent neutron poisoning effect.Thus,the corrosion resistance and neutron shielding performance of the Zr-Gd alloy can meet the harsh service requirements of the nuclear industry.展开更多
The AA5052 aluminum alloy is widely used in automobile and aerospace manufacturing,and with the development of light-weight alloys,it is required that these materials exhibit better mechanical properties.Previous stud...The AA5052 aluminum alloy is widely used in automobile and aerospace manufacturing,and with the development of light-weight alloys,it is required that these materials exhibit better mechanical properties.Previous studies have demonstrated that the addition of Sc to aluminum alloys can improve both the microstructure and properties of the alloys.In this study,the effect of Sc on the Fe-rich phase and properties of the AA5052 aluminum alloy was studied by adding 0%,0.05%,0.2%,and 0.3%Sc.The results show that with the increase of Sc,the coarse needle-like Fe-rich phase gradually transforms into Chinese-script and then nearly spherical particles,reduce the size of Fe-rich phase,and refine the grain with increase of high angle grain boundaries(HAGBs).These microstructure changes enhance the strength of the AA5052 alloy through Sc addition.The ductility of the alloy is obviously improved because the addition of a lower amount of Sc changes the morphology of Fe-rich phase from needle-like into a Chinese-script,and it is subsequently reduced as a result of significant increase in HAGBs with increasing Sc content.展开更多
基金supported by the National Natural Science Foundation of China (Nos.52201021 and 52101099)Key Research and Development Program of Shaanxi (2021GY-249,2021GY-233)+1 种基金Natural Science Basic Research Program of Shaanxi (No.2020JC-50)Shaanxi Provincial Natural Science Youth Foundation (2022JQ-410).
文摘A Zr-Gd alloy with neutron poisoning properties and resistance to boiling concentrated HNO3 corrosion was developed based on a corrosion-resistant Zr-702 alloy to meet the demand for neutron shielding in the closed-loop treatment of spent fuel and the nuclear chemical industry.In this study,1 wt.%,3 wt.%,5 wt.%,7 wt.%,and 9 wt.%Zr-Gd alloys were designed and fabricated with Zr-702 as the control element.The electrochemical behavior of the Zr-Gd alloys in boiling concentrated HNO3 was investigated,and the neutron shielding effect on plate thickness and Gd content was simulated.The experimental results demonstrate that the corrosion resistance of the alloy decreased slightly before~7-9 wt.%with increasing Gd content;this is the inflection point of its corrosion resistance.The alloy uniformly dissolved the Gd content that could not be dissolved in the Zr lattice,resulting in numerous micropores on the passivation coating,which deteriorated and accelerated the corrosion rate.The MCNP simulation demonstrated that when the Gd content was increased to 5 wt.%,a 2-mm-thick plate can shield 99.9%neutrons;an alloy with a Gd content≥7 wt.%required only a 1-mm-thick plate,thereby showing that the addition of Gd provides an excellent neutron poisoning effect.Thus,the corrosion resistance and neutron shielding performance of the Zr-Gd alloy can meet the harsh service requirements of the nuclear industry.
基金supported by the Key Research&Development Program of Yunnan Province(Grant numbers 202103AA080017,202203AE140011).
文摘The AA5052 aluminum alloy is widely used in automobile and aerospace manufacturing,and with the development of light-weight alloys,it is required that these materials exhibit better mechanical properties.Previous studies have demonstrated that the addition of Sc to aluminum alloys can improve both the microstructure and properties of the alloys.In this study,the effect of Sc on the Fe-rich phase and properties of the AA5052 aluminum alloy was studied by adding 0%,0.05%,0.2%,and 0.3%Sc.The results show that with the increase of Sc,the coarse needle-like Fe-rich phase gradually transforms into Chinese-script and then nearly spherical particles,reduce the size of Fe-rich phase,and refine the grain with increase of high angle grain boundaries(HAGBs).These microstructure changes enhance the strength of the AA5052 alloy through Sc addition.The ductility of the alloy is obviously improved because the addition of a lower amount of Sc changes the morphology of Fe-rich phase from needle-like into a Chinese-script,and it is subsequently reduced as a result of significant increase in HAGBs with increasing Sc content.