Magnetic Cu^0/Fe3O4 submicron composites were prepared using a hydrothermal method and used as heterogeneous catalysts for the activation of peroxymonosulfate（PMS） and the degradation of organic pollutants.The as-pr...Magnetic Cu^0/Fe3O4 submicron composites were prepared using a hydrothermal method and used as heterogeneous catalysts for the activation of peroxymonosulfate（PMS） and the degradation of organic pollutants.The as-prepared magnetic Cu^0/Fe3O4 submicron composites were composed of Cu^0 and Fe3O4 crystals and had an average size of approximately 220 nm.The Cu^0/Fe3O4 composites could efficiently catalyze the activation of PMS to generate singlet oxygen,and thus induced the rapid degradation of rhodamine B,methylene blue,orange Ⅱ,phenol and 4-chlorophenol.The use of0.1 g/L of the Cu^0/Fe3O4 composites induced the complete removal of rhodamine B（20 μmol/L） in15 min,methylene blue（20 μmol/L） in 5 min,orange Ⅱ（20 μmol/L） in 10 min,phenol（0.1mmol/L） in 30 min and 4-chlorophenol（0.1 mmol/L） in 15 min with an initial pH value of 7.0 and a PMS concentration of 0.5 mmol/L.The total organic carbon（TOC） removal higher than 85%for all of these five pollutants was obtained in 30 min when the PMS concentration was 2.5 mmol/L.The rate of degradation was considerably higher than that obtained with Cu^0 or Fe3O4 particles alone.The enhanced catalytic activity of the Cu^0/Fe3O4 composites in the activation of PMS was attributed to the synergistic effect of the Cu^0 and Fe3O4 crystals in the composites.Singlet oxygen was identified as the primary reactive oxygen species responsible for pollutant degradation by electron spin resonance and radical quenching experiments.A possible mechanism for the activation of PMS by Cu^0/Fe3O4 composites is proposed as electron transfer from the organic pollutants to PMS induces the activation of PMS to generate ^1O2,which induces the degradation of the organic pollutants.As a magnetic catalyst,the Cu^0/Fe3O4 composites were easily recovered by magnetic separation,and exhibited excellent stability over five successive degradation cycles.The present study provides a facile and green heterogeneous catalysis method for the oxidative removal of organic pollutants.展开更多
The modification of graphitic carbon nitride can significantly improve the photocatalytic performance of graphitic carbon nitride(g-C3N4).Fe2O3/nitrogen-deficient g-C3N4-x composite catalysts were prepared with dicyan...The modification of graphitic carbon nitride can significantly improve the photocatalytic performance of graphitic carbon nitride(g-C3N4).Fe2O3/nitrogen-deficient g-C3N4-x composite catalysts were prepared with dicyandiamide as the precursor and Fe3+doped in this study.The composite catalysts were characterized by XRD,SEM,FT-IR,XPS and photocurrent measurements.Close interaction occurred between Fe2O3 and nitrogen deficient g-C3N4-x,more photogenerated electrons were created and effectively separated from the holes,resulting in a decrease of photocarrier recombination,and thus enhancing the photocurrent.Photocatalytic performance experiments showed that Fe2O3/nitrogen deficient g-C3N4-x could utilize lowenergy visible light more efficiently than pure g-C3N4,and the removal rate was 92%in 60 minutes.展开更多
Objective： To establish a method of genomic DNA extraction from whole blood using Fe3O4/Au composite particles as a carrier. Methods： Two crucial conditions （sodium chloride concentration and amount of the magnetic...Objective： To establish a method of genomic DNA extraction from whole blood using Fe3O4/Au composite particles as a carrier. Methods： Two crucial conditions （sodium chloride concentration and amount of the magnetic particles） were optimized and 8 different human whole blood samples were used to purify genomic DNA under the optimal condition. Then agarose gel electrophoresis and polymerase cbain reaction （PCR） were performed. Results： The optimal binding condition was 1.5 mol/L NaC1/10% PEG, and the optimal amount of Fe3O4/Au composite particles was 600μg. The yields of the genomic DNA from 100μl of different whole blood samples were 2-5 μg, and the ratio of A260/A280 was in the range of 1.70-1.90. The size of genomic DNA was about 23 kb and the PCR was valid. Conclusion： The purification system using Fe3O4/Au composite microparticles has advantages in high yield, high purity, ease of operating, time saving and avoiding centrifugation. The purified sample was found to function satisfactorily in PCR amplification.展开更多
The Fe3O4@SiO2 composite nanoparticles were obtained from as-synthesized magnetite (Fe3O4) nanoparticles through the modified St?ber method. Then, the Fe3O4 nanoparticles and Fe3O4@SiO2 composite nanoparticles were ch...The Fe3O4@SiO2 composite nanoparticles were obtained from as-synthesized magnetite (Fe3O4) nanoparticles through the modified St?ber method. Then, the Fe3O4 nanoparticles and Fe3O4@SiO2 composite nanoparticles were characterized by means of X-ray diffraction (XRD), Raman spectra, scanning electron microscope (SEM) and vibrating sample magnetometer (VSM). Recently, the studies focus on how to improve the dispersion of composite particle and achieve good magnetic performance. Hence effects of the volume ratio of tetraethyl orthosilicate (TEOS) and magnetite colloid on the structural, morphological and magnetic properties of the composite nanoparticles were systematically investi-gated. The results revealed that the Fe3O4@SiO2 had better thermal stability and dispersion than the magnetite nanoparticles. Furthermore, the particle size and magnetic property of the Fe3O4@SiO2 composite nanoparticles can be adjusted by changing the volume ratio of TEOS and magnetite colloid.展开更多
One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT...One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.展开更多
A special Fe3O4nanoparticles–graphene（Fe3O4–GN） composite as a magnetic label was employed for biodetection using giant magnetoresistance（GMR） sensors with a Wheatstone bridge. The Fe3O4–GN composite exhibits a...A special Fe3O4nanoparticles–graphene（Fe3O4–GN） composite as a magnetic label was employed for biodetection using giant magnetoresistance（GMR） sensors with a Wheatstone bridge. The Fe3O4–GN composite exhibits a strong ferromagnetic behavior with the saturation magnetization MS of approximately 48 emu/g, coercivity HC of 200 Oe, and remanence Mr of 8.3 emu/g, leading to a large magnetic fringing field. However, the Fe3O4 nanoparticles do not aggregate together, which can be attributed to the pinning and separating effects of graphene sheet to the magnetic particles. The Fe3O4–GN composite is especially suitable for biodetection as a promising magnetic label since it combines two advantages of large fringing field and no aggregation. As a result, the concentration x dependence of voltage difference ｜？V｜ between detecting and reference sensors undergoes the relationship of ｜？V｜ = 240.5 lgx ＋ 515.2 with an ultralow detection limit of 10 ng/mL（very close to the calculated limit of 7 ng/mL） and a wide detection range of 4 orders.展开更多
Transition metal oxides have been actively exploited for application in lithium ion batteries due to their facile synthesis,high specific capacity,and environmental-friendly.In this paper,Fe3O4@TiO2@C yolk-shell(Y-S)s...Transition metal oxides have been actively exploited for application in lithium ion batteries due to their facile synthesis,high specific capacity,and environmental-friendly.In this paper,Fe3O4@TiO2@C yolk-shell(Y-S)spheres,used as anode material for lithium ion batteries,were successfully fabricated by Stober method.XRD patterns reveal that Fe3O4@TiO2@C Y-S spheres possess a good crystallinity.But the diffraction peaks’intensity of Fe3O4 crystals in the composites is much weaker than that of bare Fe3O4 spheres,indicating that the outer anatase TiO2@C layer can cover up the diffraction peaks of inner Fe3O4 spheres.The yolk-shell structure of Fe3O4@TiO2@C spheres is further characterized by TEM,HAADFSTEM,and EDS mapping.The yolk-shell structure is good for improving the cycling stability of the inner Fe3O4 spheres during lithium ions insertion-extraction processes.When tested at 200 mA/g,the Fe3O4@TiO2@C Y-S spheres can provide a stable discharge capacity of 450 mAh/g over 100 cycles,which is much better than that of bare Fe3O4 spheres and TiO2@C spheres.Furthermore,cyclic voltammetry curves show that the composites have a good cycling stability compared to bare Fe3O4 spheres.展开更多
We describes a controllable synthesis procedure for growing a-Ee2O3 and Ee3O4 nanowires. High magnetic hematite a-Fe2O3 nanowires are successfully grown on Fe0.5Ni0.5 alloy substrates via an oxide assisted vapor-solid...We describes a controllable synthesis procedure for growing a-Ee2O3 and Ee3O4 nanowires. High magnetic hematite a-Fe2O3 nanowires are successfully grown on Fe0.5Ni0.5 alloy substrates via an oxide assisted vapor-solid process. Experimental results also indicate that previous immersion of the substrates in a solution of oxalic acid causes the grown nanowires to convert gradually into magnetite （Fe3O4） nanowires. Additionally, the saturated state of Fe3O4 nanowires is achieved as the oxalic acid concentration reaches 0.75 mol/L. The average diameter and length of nanowires expands with an increasing operation temperature and the growth density of nanowires accumulates with an increasing gas flux in the vapor-solid process. The growth mechanism of a-Fe2O3 and Fe3O4 nanowires is also discussed. The results demonstrate that the entire synthesis of nanowires can be completed within 2 h.展开更多
A Fe modified Na2WO4 compound was synthesized by a solution impregnation method and was ball-milled with MgH2 to constitute a novel MgH2-Fe2O3/Na2WO4 composite. The effects of the Fe2O3/Na2WO4 additive on the hydrogen...A Fe modified Na2WO4 compound was synthesized by a solution impregnation method and was ball-milled with MgH2 to constitute a novel MgH2-Fe2O3/Na2WO4 composite. The effects of the Fe2O3/Na2WO4 additive on the hydrogen storage properties of MgH2 together with the corresponding mechanism were investigated. At 423 K, within the first 200 seconds, the hydrogen absorption amount of MgH2+20 wt% Fe2O3/Na2WO4 was almost 5 times that of pure MgH2. And at 573 K, its total hydrogen desorption amount was 7 times that for pure MgH2. Meanwhile, its onset dehydrogenation temperature was 110 K lower than that of pure MgH2. It was worth noting that the MgH2+20 wt% Fe/Na2WO4 presented the lower dehydrogenation reaction activation energy(Ea) of 35.9 kJ·mol^-1 compared to that of pure MgH2. The active MgWO4, Mg2 FeH6 and MgO formed during the milling process were responsible for the improvement of the hydrogen storage properties for MgH2.展开更多
Carbon-encapsulated Fe3O4 composites were successfully fabricated via hydrothermal method and ex- amined by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The Fe3O4@C nanocomposi...Carbon-encapsulated Fe3O4 composites were successfully fabricated via hydrothermal method and ex- amined by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The Fe3O4@C nanocomposite as an anode material with novel structure demonstrated excellent electrochemical performance, with enhanced specific reversible current density of 50 mA/g capacity （950 mAh/g at the after 50 cycles）, remarkable rate capability （more than 650 mAh/g even at the current density of 1,000 mAJg） and good cycle ability with less capacity fading （2.4 % after 50 cycles）. Two factors have been attributed to the ultrahigh electrochemical perfor- mance： Firstly, the 30- to 50-nm spherical structure with a short diffusion pathway and the amorphous carbon layer could not only provide extra space for buffering the volumetric change during the continuous charging-dis- charging but also improve the whole conductivity of the Fe3O4@C nanocomposite electrode; secondly, the syner- gistic effects of Fe304 and carbon could avoid Fe304 direct exposure to the electrolyte and maintain the structural stabilization of Fe3O4@C nanocomposite. It was suggested that the Fe3O4@C nanocomposite could be suitable as analternative anode for lithium-ion batteries with a high ap- plication potential.展开更多
In this investigation micron-sized monodisperse magnetic composite polymer particles with amino and amide functional groups were prepared considering their applications in biotechnology. First, polystyrene/poly (acryl...In this investigation micron-sized monodisperse magnetic composite polymer particles with amino and amide functional groups were prepared considering their applications in biotechnology. First, polystyrene/poly (acrylic acid-acrylam- ide-N-N-methylene-bis-acrylamide) [PS/P(AA-AAm-MBAAm)] composite polymer particles were prepared by seeded copolymerization. The carboxyl groups present on or near the particles surface were modified by amine-nucleophile, ethylene diamine (EDA), through pre-activation with dicyclohexyl carbodiimide as coupling agent. The aminated particles were then magnetically modified and named as aminated-Fe3O4 composite particles. Formation of such magnetic composite particles was confirmed by scanning electron micrographs, FTIR-spectra and magnetic susceptibility measurement. The produced composite particles were paramagnetic. To see the relative hydrophilic character of the particles surface the adsorption behavior of trypsin (TR) as biomolecule was studied on PS particles and aminated-Fe3O4 composite particles. The magnitude of adsorbed TR on PS particles was higher than that on aminated-Fe3O4 composite particles.展开更多
基金supported by the National Natural Science Foundation of China (21377169, 21507168)the Fundamental Research Funds for the Central Universities (CZW15078)the Natural Science Foundation of Hubei Province of China (2014CFC1119, 2015CFB505)~~
文摘Magnetic Cu^0/Fe3O4 submicron composites were prepared using a hydrothermal method and used as heterogeneous catalysts for the activation of peroxymonosulfate（PMS） and the degradation of organic pollutants.The as-prepared magnetic Cu^0/Fe3O4 submicron composites were composed of Cu^0 and Fe3O4 crystals and had an average size of approximately 220 nm.The Cu^0/Fe3O4 composites could efficiently catalyze the activation of PMS to generate singlet oxygen,and thus induced the rapid degradation of rhodamine B,methylene blue,orange Ⅱ,phenol and 4-chlorophenol.The use of0.1 g/L of the Cu^0/Fe3O4 composites induced the complete removal of rhodamine B（20 μmol/L） in15 min,methylene blue（20 μmol/L） in 5 min,orange Ⅱ（20 μmol/L） in 10 min,phenol（0.1mmol/L） in 30 min and 4-chlorophenol（0.1 mmol/L） in 15 min with an initial pH value of 7.0 and a PMS concentration of 0.5 mmol/L.The total organic carbon（TOC） removal higher than 85%for all of these five pollutants was obtained in 30 min when the PMS concentration was 2.5 mmol/L.The rate of degradation was considerably higher than that obtained with Cu^0 or Fe3O4 particles alone.The enhanced catalytic activity of the Cu^0/Fe3O4 composites in the activation of PMS was attributed to the synergistic effect of the Cu^0 and Fe3O4 crystals in the composites.Singlet oxygen was identified as the primary reactive oxygen species responsible for pollutant degradation by electron spin resonance and radical quenching experiments.A possible mechanism for the activation of PMS by Cu^0/Fe3O4 composites is proposed as electron transfer from the organic pollutants to PMS induces the activation of PMS to generate ^1O2,which induces the degradation of the organic pollutants.As a magnetic catalyst,the Cu^0/Fe3O4 composites were easily recovered by magnetic separation,and exhibited excellent stability over five successive degradation cycles.The present study provides a facile and green heterogeneous catalysis method for the oxidative removal of organic pollutants.
基金Supported by the Fuling Shale Gas Environmental Exploration Technology of National Science and Technology Special Project(No.2016ZX05060)the Demonstration of Integrated Management of Rocky Desertification and Enhancement of Ecological Service Function in Karst Peak-cluster Depression(No.2016YFC0502400)National Natural Science Foundation of China(No.51709254)
文摘The modification of graphitic carbon nitride can significantly improve the photocatalytic performance of graphitic carbon nitride(g-C3N4).Fe2O3/nitrogen-deficient g-C3N4-x composite catalysts were prepared with dicyandiamide as the precursor and Fe3+doped in this study.The composite catalysts were characterized by XRD,SEM,FT-IR,XPS and photocurrent measurements.Close interaction occurred between Fe2O3 and nitrogen deficient g-C3N4-x,more photogenerated electrons were created and effectively separated from the holes,resulting in a decrease of photocarrier recombination,and thus enhancing the photocurrent.Photocatalytic performance experiments showed that Fe2O3/nitrogen deficient g-C3N4-x could utilize lowenergy visible light more efficiently than pure g-C3N4,and the removal rate was 92%in 60 minutes.
基金Supported by the National High Technology Research and Development Program of China (2006AA020705)
文摘Objective： To establish a method of genomic DNA extraction from whole blood using Fe3O4/Au composite particles as a carrier. Methods： Two crucial conditions （sodium chloride concentration and amount of the magnetic particles） were optimized and 8 different human whole blood samples were used to purify genomic DNA under the optimal condition. Then agarose gel electrophoresis and polymerase cbain reaction （PCR） were performed. Results： The optimal binding condition was 1.5 mol/L NaC1/10% PEG, and the optimal amount of Fe3O4/Au composite particles was 600μg. The yields of the genomic DNA from 100μl of different whole blood samples were 2-5 μg, and the ratio of A260/A280 was in the range of 1.70-1.90. The size of genomic DNA was about 23 kb and the PCR was valid. Conclusion： The purification system using Fe3O4/Au composite microparticles has advantages in high yield, high purity, ease of operating, time saving and avoiding centrifugation. The purified sample was found to function satisfactorily in PCR amplification.
文摘The Fe3O4@SiO2 composite nanoparticles were obtained from as-synthesized magnetite (Fe3O4) nanoparticles through the modified St?ber method. Then, the Fe3O4 nanoparticles and Fe3O4@SiO2 composite nanoparticles were characterized by means of X-ray diffraction (XRD), Raman spectra, scanning electron microscope (SEM) and vibrating sample magnetometer (VSM). Recently, the studies focus on how to improve the dispersion of composite particle and achieve good magnetic performance. Hence effects of the volume ratio of tetraethyl orthosilicate (TEOS) and magnetite colloid on the structural, morphological and magnetic properties of the composite nanoparticles were systematically investi-gated. The results revealed that the Fe3O4@SiO2 had better thermal stability and dispersion than the magnetite nanoparticles. Furthermore, the particle size and magnetic property of the Fe3O4@SiO2 composite nanoparticles can be adjusted by changing the volume ratio of TEOS and magnetite colloid.
基金Funded by the National Natural Science Foundation of China (No. 50674048)Research Fund for the Doctoral Program of Higher Education of China(No.20103227110006)
文摘One-dimensional and quasi-one-dimensional nanostructure materials are promising building blocks for electromagnetic devices and nanosystems.In this work,the composite Ni0.5Zn0.5Fe2O4（NZFO）/ Pb（Zr0.52Ti0.48）O3（PZT） nanofibers with average diameters about 65 nm are prepared by electrospinning from poly（vinyl pyrrolidone） （PVP） and metal salts.The precursor composite NZFO/PZT/PVP nanofibers and the subsequent calcined NZFO/PZT nanofibers are investigated by Fourier transform infrared spectroscopy （FT- IR） ,X-ray diffraction （XRD）,scanning electron microscopy （SEM）.The magnetic properties for nanofibers are measured by vibrating sample magnetometer（VSM）.The NZFO/PZT nanofibers obtained at calcination temperature of 900 °C for 2 h consist of the ferromagnetic spinel NZFO and ferroelectric perovskite PZT phases,which are constructed from about 37 nm NZFO and 17 nm PZT grains.The saturation magnetization of these NZFO/PZT nanofibers increases with increasing calcination temperature and contents of NZFO in the composite.
基金supported by the National Natural Science Foundation of China(Grant Nos.11074040,11504192,11674187,11604172,and 51403114)the Natural Science Foundation of Shandong Province,China(Grant Nos.ZR2012FZ006 and BS2014CL010)the China Postdoctoral Science Foundation(Grant Nos.2014M551868 and 2015M570570)
文摘A special Fe3O4nanoparticles–graphene（Fe3O4–GN） composite as a magnetic label was employed for biodetection using giant magnetoresistance（GMR） sensors with a Wheatstone bridge. The Fe3O4–GN composite exhibits a strong ferromagnetic behavior with the saturation magnetization MS of approximately 48 emu/g, coercivity HC of 200 Oe, and remanence Mr of 8.3 emu/g, leading to a large magnetic fringing field. However, the Fe3O4 nanoparticles do not aggregate together, which can be attributed to the pinning and separating effects of graphene sheet to the magnetic particles. The Fe3O4–GN composite is especially suitable for biodetection as a promising magnetic label since it combines two advantages of large fringing field and no aggregation. As a result, the concentration x dependence of voltage difference ｜？V｜ between detecting and reference sensors undergoes the relationship of ｜？V｜ = 240.5 lgx ＋ 515.2 with an ultralow detection limit of 10 ng/mL（very close to the calculated limit of 7 ng/mL） and a wide detection range of 4 orders.
基金supported by the Tianjin Committee of Science and Technology (No.14JCZDJC32400)Tianjin Science and Technology Innovation Platform Program (No.14TXGCCX00017)
文摘Transition metal oxides have been actively exploited for application in lithium ion batteries due to their facile synthesis,high specific capacity,and environmental-friendly.In this paper,Fe3O4@TiO2@C yolk-shell(Y-S)spheres,used as anode material for lithium ion batteries,were successfully fabricated by Stober method.XRD patterns reveal that Fe3O4@TiO2@C Y-S spheres possess a good crystallinity.But the diffraction peaks’intensity of Fe3O4 crystals in the composites is much weaker than that of bare Fe3O4 spheres,indicating that the outer anatase TiO2@C layer can cover up the diffraction peaks of inner Fe3O4 spheres.The yolk-shell structure of Fe3O4@TiO2@C spheres is further characterized by TEM,HAADFSTEM,and EDS mapping.The yolk-shell structure is good for improving the cycling stability of the inner Fe3O4 spheres during lithium ions insertion-extraction processes.When tested at 200 mA/g,the Fe3O4@TiO2@C Y-S spheres can provide a stable discharge capacity of 450 mAh/g over 100 cycles,which is much better than that of bare Fe3O4 spheres and TiO2@C spheres.Furthermore,cyclic voltammetry curves show that the composites have a good cycling stability compared to bare Fe3O4 spheres.
文摘We describes a controllable synthesis procedure for growing a-Ee2O3 and Ee3O4 nanowires. High magnetic hematite a-Fe2O3 nanowires are successfully grown on Fe0.5Ni0.5 alloy substrates via an oxide assisted vapor-solid process. Experimental results also indicate that previous immersion of the substrates in a solution of oxalic acid causes the grown nanowires to convert gradually into magnetite （Fe3O4） nanowires. Additionally, the saturated state of Fe3O4 nanowires is achieved as the oxalic acid concentration reaches 0.75 mol/L. The average diameter and length of nanowires expands with an increasing operation temperature and the growth density of nanowires accumulates with an increasing gas flux in the vapor-solid process. The growth mechanism of a-Fe2O3 and Fe3O4 nanowires is also discussed. The results demonstrate that the entire synthesis of nanowires can be completed within 2 h.
基金Funded by the National Natural Science Foundation of China(No.51771164)Scientific Research Projects in Colleges and Universities in Hebei Province,China(No.ZD2019307)+2 种基金the Fundamental Research Funds for the Central Universities(No.3142019013)the Natural Science Foundation of Hebei Province of China(No.E2019508214)the Program for Top-notch Young Talents in University of Hebei Province(No.BJ2016043)
文摘A Fe modified Na2WO4 compound was synthesized by a solution impregnation method and was ball-milled with MgH2 to constitute a novel MgH2-Fe2O3/Na2WO4 composite. The effects of the Fe2O3/Na2WO4 additive on the hydrogen storage properties of MgH2 together with the corresponding mechanism were investigated. At 423 K, within the first 200 seconds, the hydrogen absorption amount of MgH2+20 wt% Fe2O3/Na2WO4 was almost 5 times that of pure MgH2. And at 573 K, its total hydrogen desorption amount was 7 times that for pure MgH2. Meanwhile, its onset dehydrogenation temperature was 110 K lower than that of pure MgH2. It was worth noting that the MgH2+20 wt% Fe/Na2WO4 presented the lower dehydrogenation reaction activation energy(Ea) of 35.9 kJ·mol^-1 compared to that of pure MgH2. The active MgWO4, Mg2 FeH6 and MgO formed during the milling process were responsible for the improvement of the hydrogen storage properties for MgH2.
基金supported by the National Natural Science Foundation of China(51201066 and 51171065)the Natural Science Foundation of Guangdong Province(S2012020010937 and 10351063101000001)+1 种基金the Scientific and Technological Plan of Guangdong Province(2013B010403032)the Education Department of Guangdong Province Science and Technology Innovation Project(2013KJCX0183)
文摘Carbon-encapsulated Fe3O4 composites were successfully fabricated via hydrothermal method and ex- amined by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The Fe3O4@C nanocomposite as an anode material with novel structure demonstrated excellent electrochemical performance, with enhanced specific reversible current density of 50 mA/g capacity （950 mAh/g at the after 50 cycles）, remarkable rate capability （more than 650 mAh/g even at the current density of 1,000 mAJg） and good cycle ability with less capacity fading （2.4 % after 50 cycles）. Two factors have been attributed to the ultrahigh electrochemical perfor- mance： Firstly, the 30- to 50-nm spherical structure with a short diffusion pathway and the amorphous carbon layer could not only provide extra space for buffering the volumetric change during the continuous charging-dis- charging but also improve the whole conductivity of the Fe3O4@C nanocomposite electrode; secondly, the syner- gistic effects of Fe304 and carbon could avoid Fe304 direct exposure to the electrolyte and maintain the structural stabilization of Fe3O4@C nanocomposite. It was suggested that the Fe3O4@C nanocomposite could be suitable as analternative anode for lithium-ion batteries with a high ap- plication potential.
文摘In this investigation micron-sized monodisperse magnetic composite polymer particles with amino and amide functional groups were prepared considering their applications in biotechnology. First, polystyrene/poly (acrylic acid-acrylam- ide-N-N-methylene-bis-acrylamide) [PS/P(AA-AAm-MBAAm)] composite polymer particles were prepared by seeded copolymerization. The carboxyl groups present on or near the particles surface were modified by amine-nucleophile, ethylene diamine (EDA), through pre-activation with dicyclohexyl carbodiimide as coupling agent. The aminated particles were then magnetically modified and named as aminated-Fe3O4 composite particles. Formation of such magnetic composite particles was confirmed by scanning electron micrographs, FTIR-spectra and magnetic susceptibility measurement. The produced composite particles were paramagnetic. To see the relative hydrophilic character of the particles surface the adsorption behavior of trypsin (TR) as biomolecule was studied on PS particles and aminated-Fe3O4 composite particles. The magnitude of adsorbed TR on PS particles was higher than that on aminated-Fe3O4 composite particles.