In this paper,chemical co-precipitation method was employed to synthesize Fe3O4 nanoparticles which can be well dispersed in water by using citric acid as a surfactant.Afterwards,by using Fe3O4 nanoparticles as seeds ...In this paper,chemical co-precipitation method was employed to synthesize Fe3O4 nanoparticles which can be well dispersed in water by using citric acid as a surfactant.Afterwards,by using Fe3O4 nanoparticles as seeds in a Triton X-100/hexanol/cyclohexane/water reverse microemulsion system,the core-shell structural Fe3O4@SiO2 nanocomposite particles were prepared via hydrolysis and condensation of tetraethyl orthosilicate(TEOS) under the catalysis of alkali.The effects of different stirring methods and the concentration of TEOS on the morphology of Fe3O4@SiO2 nanoparticles were investigated.The results show that the mechanical stirring can effectively control the morphology of composite nanoparticles to form a good dispersion and spherical morphology of core-shell nanoparticles.With the increase of TEOS concentration,the thickness of the SiO2 shell increases,and the morphology of the composite particles becomes more uniform.展开更多
为解决TiO_2光催化纳米材料在使用过程中不易回收的问题,采用直接水解法成功制备了磁性核壳结构Fe_3O_4@TiO_2纳米材料,采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)等对其物理化学...为解决TiO_2光催化纳米材料在使用过程中不易回收的问题,采用直接水解法成功制备了磁性核壳结构Fe_3O_4@TiO_2纳米材料,采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)等对其物理化学特性进行了表征,并且考察了制备工艺条件,如钛酸四丁酯(TBOT)用量、氨水用量、反应温度、反应时间等因素对Fe_3O_4@TiO_2纳米颗粒光催化效果的影响。结果表明,TiO_2在Fe_3O_4颗粒表面进行了有效的包覆,形成了良好的包覆层,优化后制备工艺条件为:TBOT用量1.0 m L、氨水用量0.3 m L、制备温度85℃、制备时间4h,所得Fe_3O_4@TiO_2纳米材料对罗丹明B的催化降解效率明显提高,罗丹明B降解率达到98%。对负载前后纳米颗粒的磁滞回线进行测试发现,TiO_2的包覆并未明显减弱Fe_3O_4的磁性,所制备的可回收磁性Fe_3O_4@TiO_2催化剂具有良好的稳定性和重复利用性能。展开更多
利用三步法（热溶剂还原法,硅烷化和氨基功能化）制备了Fe3O4@SiO2-NH2磁性纳米复合材料用于水体中全氟化合物的萃取,结合超高效液相色谱-串联三重四极杆质谱（UPLC-MS/MS）技术,建立了水体中7种典型全氟化合物的检测方法。通过扫描电镜...利用三步法（热溶剂还原法,硅烷化和氨基功能化）制备了Fe3O4@SiO2-NH2磁性纳米复合材料用于水体中全氟化合物的萃取,结合超高效液相色谱-串联三重四极杆质谱（UPLC-MS/MS）技术,建立了水体中7种典型全氟化合物的检测方法。通过扫描电镜（SEM）、透射电镜（TEM）和傅立叶红外光谱（FT-IR）等手段对材料进行表征,详细研究了解析溶剂、解析溶剂体积、解析时间、吸附时间和p H值等因素对萃取效率的影响。结果表明：氨基被成功修饰在Fe3O4@SiO2纳米粒子的表面,Fe3O4@SiO2-NH2磁性纳米材料对目标全氟化合物有较好的萃取效果,在萃取时间为20 min,解析溶剂为3 m L×4含0.28%氨水的甲醇,解析时间为5 min,p H 5.0时,萃取效率最佳。在最优实验条件下,全氟化合物的检出限为0.2~0.5 ng/L,线性范围为1~500 ng/L。方法用于实际水体中目标全氟化合物的检测,样品的加标回收率不低于82.0%。展开更多
文摘In this paper,chemical co-precipitation method was employed to synthesize Fe3O4 nanoparticles which can be well dispersed in water by using citric acid as a surfactant.Afterwards,by using Fe3O4 nanoparticles as seeds in a Triton X-100/hexanol/cyclohexane/water reverse microemulsion system,the core-shell structural Fe3O4@SiO2 nanocomposite particles were prepared via hydrolysis and condensation of tetraethyl orthosilicate(TEOS) under the catalysis of alkali.The effects of different stirring methods and the concentration of TEOS on the morphology of Fe3O4@SiO2 nanoparticles were investigated.The results show that the mechanical stirring can effectively control the morphology of composite nanoparticles to form a good dispersion and spherical morphology of core-shell nanoparticles.With the increase of TEOS concentration,the thickness of the SiO2 shell increases,and the morphology of the composite particles becomes more uniform.
文摘为解决TiO_2光催化纳米材料在使用过程中不易回收的问题,采用直接水解法成功制备了磁性核壳结构Fe_3O_4@TiO_2纳米材料,采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X-射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)等对其物理化学特性进行了表征,并且考察了制备工艺条件,如钛酸四丁酯(TBOT)用量、氨水用量、反应温度、反应时间等因素对Fe_3O_4@TiO_2纳米颗粒光催化效果的影响。结果表明,TiO_2在Fe_3O_4颗粒表面进行了有效的包覆,形成了良好的包覆层,优化后制备工艺条件为:TBOT用量1.0 m L、氨水用量0.3 m L、制备温度85℃、制备时间4h,所得Fe_3O_4@TiO_2纳米材料对罗丹明B的催化降解效率明显提高,罗丹明B降解率达到98%。对负载前后纳米颗粒的磁滞回线进行测试发现,TiO_2的包覆并未明显减弱Fe_3O_4的磁性,所制备的可回收磁性Fe_3O_4@TiO_2催化剂具有良好的稳定性和重复利用性能。
文摘利用三步法（热溶剂还原法,硅烷化和氨基功能化）制备了Fe3O4@SiO2-NH2磁性纳米复合材料用于水体中全氟化合物的萃取,结合超高效液相色谱-串联三重四极杆质谱（UPLC-MS/MS）技术,建立了水体中7种典型全氟化合物的检测方法。通过扫描电镜（SEM）、透射电镜（TEM）和傅立叶红外光谱（FT-IR）等手段对材料进行表征,详细研究了解析溶剂、解析溶剂体积、解析时间、吸附时间和p H值等因素对萃取效率的影响。结果表明：氨基被成功修饰在Fe3O4@SiO2纳米粒子的表面,Fe3O4@SiO2-NH2磁性纳米材料对目标全氟化合物有较好的萃取效果,在萃取时间为20 min,解析溶剂为3 m L×4含0.28%氨水的甲醇,解析时间为5 min,p H 5.0时,萃取效率最佳。在最优实验条件下,全氟化合物的检出限为0.2~0.5 ng/L,线性范围为1~500 ng/L。方法用于实际水体中目标全氟化合物的检测,样品的加标回收率不低于82.0%。