This paper provides an investigation of the phase transition and spalling characteristic induced during shock loading and unloading in the pure iron and the FeMnNi alloy. The impact for the pure iron is symmetric and ...This paper provides an investigation of the phase transition and spalling characteristic induced during shock loading and unloading in the pure iron and the FeMnNi alloy. The impact for the pure iron is symmetric and with the same-thickness for both the flyer and the target plate. It is found that an abnormal multiple spalling happens in the pure iron sample as the pressure exceeds the α- ε transition threshold of 13 GPa. In the symmetric and same-thickness impact and reverse impact experiments of the FeMnNi alloy, two abnormal tension regions occur when the pressure exceeds the α - ε transition threshold of 6.3 GPa, and the reverse phase transition s - ~ begins below 4.2 GP. The experimental process is simulated successfully from the non-equilibrium mixture phase and Boettger＇s model. Such abnormal spalling phenomena are believed to relate to the shocked α - ε phase transition. The possible reasons for the abnormal multiple spalling, which occurs during the symmetric and same-thickness impact experiments of pure iron and FeMnNi alloy, are discussed.展开更多
基金Project supported by the National Science Foundations of China (Grant Nos. 10776032 and 10902102)Science Foundation of China Academy of Engineering Physics (Grant Nos. 20060104 and 2009B0201014)
文摘This paper provides an investigation of the phase transition and spalling characteristic induced during shock loading and unloading in the pure iron and the FeMnNi alloy. The impact for the pure iron is symmetric and with the same-thickness for both the flyer and the target plate. It is found that an abnormal multiple spalling happens in the pure iron sample as the pressure exceeds the α- ε transition threshold of 13 GPa. In the symmetric and same-thickness impact and reverse impact experiments of the FeMnNi alloy, two abnormal tension regions occur when the pressure exceeds the α - ε transition threshold of 6.3 GPa, and the reverse phase transition s - ~ begins below 4.2 GP. The experimental process is simulated successfully from the non-equilibrium mixture phase and Boettger＇s model. Such abnormal spalling phenomena are believed to relate to the shocked α - ε phase transition. The possible reasons for the abnormal multiple spalling, which occurs during the symmetric and same-thickness impact experiments of pure iron and FeMnNi alloy, are discussed.