Properties and Application of Oil-well Cement Enhanced with a Novel Composite Toughening Agent

Brittle fracture of cement sheath, induced by perforation and stimulation treatments, can cause cross flow of formation fluid and increase casing damage. A novel agent XL was developed for solving the problem. Experimental results showed that the toughness of the set cement containing XL was improved remarkably. The engineering properties of the slurry containing XL, drag reducer USZ （0.2% BWOC）, filtrate loss additive F 17B （1.2% BWOC） and crystalloid expanding agent F17A （3% BWOC） could meet technical requirements of cementing operation. After perforation, good quality cement sheath enhanced with XL was observed by CBL/VDL logs in a deep well.

FC纤维机场道面混凝土试验研究及施工技术

根据清华大学FC研究中心提供的FC纤维性能,按照某机场道面混凝土中掺加FC纤维的要求,经大量的试验研究并结合现场施工条件,在保证道面混凝土基本性能的前提下,探讨了FC纤维混凝土的配合比、施工工艺及关键技术的质量控制措施,为机场道面混凝土掺加FC纤维的广泛应用奠定了技术基础。

超高强改性合成纤维在机场道面混凝土中的应用研究

为了研究不同掺量的超高强改性合成（FC）纤维对道面混凝土抗折强度和抗裂性能的影响，设计了多组不同的混凝土配合比进行试验。对试验现象及结果进行对比，分析不同纤维掺量对抗折强度和抗裂性能的影响。结果表明：不同掺量的FC纤维对混凝土抗折强度略有提高，但效果不明显；当纤维掺量1—1．6kg／m3，混凝土均未产生裂缝，抗裂效果明显。

SCB试验测试固井水泥断裂力学性能

为了给深部煤层气井固井材料优化、井筒环空结构耐久性提升及封隔能力科学评价预测提供理论依据,利用半圆盘三点弯曲加载(SCB)试验对煤层气井用常规固井水泥(PC)与纤维固井水泥(FC)试样在干燥态、净水及矿化水浸泡条件下的断裂力学性质进行了分析。研究结果表明:①加载位移—载荷曲线与试样断裂速率显示,PC试样断裂形式为脆性断裂,而FC试样呈现类似金属的韧性断裂特征,同等条件下PC试样断裂速率约为FC试样的10倍;②干燥、净水及矿化水浸泡下,PC试样断裂韧度分别为0.53 MPa·m^(0.5)、0.36 MPa·m^(0.5)、0.40 MPa·m^(0.5),FC试样断裂韧度分别为0.49 MPa·m^(0.5)、0.35 MPa·m^(0.5)、0.39 MPa·m^(0.5);③材料断裂能量耗散计算结果显示,相同环境介质条件下FC受压断裂全程耗能为PC的20~30倍;④干燥状态下固井水泥试样优选矿物晶界部位开裂,因而试样断口粗糙或断裂路径曲折,而净水及矿化水浸泡环境下固井水泥试样多沿矿物溶蚀缺陷断裂从而易形成平直裂缝。结论认为,刚度效应与应力集中效应是导致PC断裂韧度略高于FC的关键机制,FC中的纤维通过拉拽和应变协调机制使试样均匀分担外部载荷,从而起到很好的能量分散和载荷缓冲效果,FC表现出的能量耗散性能值得深部煤层气井固井材料优化关注,水的软化作用对于固井水泥材料断裂力学性质的影响非常显著。