In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was inve...In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was investigated.The rolled Mg-3Zn-0.5Zr-0.6Nd alloy exhibited an ultimate tensile strength of 386 MPa,a yield strength of 361 MPa,and an elongation of 7.1%.Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both alloys.Optimal mechanical properties for the Mg-3Zn-0.5Zr-0.6Nd alloy were achieved after annealing at 200℃,with an ultimate tensile strength of 287 MPa,a yield strength of 235 MPa,and an elongation of 26.1%.The numerous deformed microstructures,twins,and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening rate.After annealing,a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains,and the increased volume fraction of precipitated phases,which significantly improved the elongation of the alloy.Additionally,the addition of Nd element could enhance the annealing recrystallization rate,reduce the Schmid factor difference between basal and prismatic slip systems,facilitate multi-system slip initiation and improve the alloy plasticity.展开更多
Effect of controlled rolling and cooling process on the mechanical properties of low carbon cold forging steel was investigated for different processing parameters of a laboratory hot rolling mill. The results show th...Effect of controlled rolling and cooling process on the mechanical properties of low carbon cold forging steel was investigated for different processing parameters of a laboratory hot rolling mill. The results show that the specimens with fast cooling after hot rolling exhibit very good mechanical properties, and the improvement of the mechanical properties can be attributed mainly to the ferrite-grain refinement. The mechanical properties increase with decreasing final cooling temperature within the range from 670 ℃ to 570 ℃ due to the finer interlamellar spacing of pearlite colony. The specimen with fast cooling after low temperature rolling shows the highest values of the mechanical properties. The effect of the ferrite grain size on the mechanical properties was greater than that of pearlite morphology in the present study. The mechanical properties of specimens by controlled rolling and cooling process without thermal treatment were greatly superior to that of the same specimens by the conventional rolling, and their tensile strength reached 490 MPa grade even in the case of low temperature rolling without controlled rolling. It might be expected to realize the substitution medium-carbon by low-carbon for 490 MPa grade cold forging steel with controlled rolling and cooling process.展开更多
The strength-to-weight ratio is an important property of high-strength low-alloy(HSLA)steel in pipeline,whose precipitation strengthening can be improved.The final rolling temperature(FRT)and coiling temperature(CT)ar...The strength-to-weight ratio is an important property of high-strength low-alloy(HSLA)steel in pipeline,whose precipitation strengthening can be improved.The final rolling temperature(FRT)and coiling temperature(CT)are the key process parameters in the control of precipitates and microstructure.Continuous cooling rate was fixed at 10℃/s,and the effects of deformation and coiling temperatures on precipitates and microstructure of Ti-Nb microalloyed HSLA steel were investigated through thermo-mechanical controlled processing on Gleeble 3500.The microstructure is mainly acicular ferrite with high density dislocation and several microns scale.The size and volume fraction of the precipitates were studied under transmission electron microscopy.The results showed that the diameter of the precipitates was in the range between 4 and 240 nm.The optimized combination of parameters is FRT of 820℃and CT of 550℃,and the volume fraction of precipitates obtained under this process is 0.59%.展开更多
基金Project(202203021221088)supported by the Fundamental Research Program of Shanxi Province,ChinaProject(20230010)supported by the Fund Program for the Scientific Activities of Selected Returned Overseas Professionals in Shanxi Province,China+5 种基金Project(202201050201012)supported by the Shanxi Provincial Science and Technology Major Special Project Plan of Taking the Lead in Unveiling the List,ChinaProject(2023-063)supported by the Research Project Supported by Shanxi Scholarship Council of ChinaProjects(51771129,52271109)supported by the National Natural Science Foundation of ChinaProject(2021YFB3703300)supported by the National Key Research and Development Program for Young Scientists,ChinaProject(YDZJSX2021B019)supported by the Special Fund Project for Guiding Local Science and Technology Development by the Central Government,ChinaProject(SKL-YSJ202103)supported by the Open Foundation of State Key Laboratory of High-end Compressor and System Technology,China。
文摘In this study,the Mg-3Zn-0.5Zr-χNd(χ=0,0.6)alloys were subjected to final rolling treatment with large deformation of 50%.The impact of annealing temperatures on the microstructure and mechanical properties was investigated.The rolled Mg-3Zn-0.5Zr-0.6Nd alloy exhibited an ultimate tensile strength of 386 MPa,a yield strength of 361 MPa,and an elongation of 7.1%.Annealing at different temperatures resulted in reduced strength and obviously increased elongation for both alloys.Optimal mechanical properties for the Mg-3Zn-0.5Zr-0.6Nd alloy were achieved after annealing at 200℃,with an ultimate tensile strength of 287 MPa,a yield strength of 235 MPa,and an elongation of 26.1%.The numerous deformed microstructures,twins,and precipitated phases in the rolled alloy could impede the deformation at room temperature and increase the work hardening rate.After annealing,a decrease in the work hardening effect and an increase in the dynamic recovery effect were obtained due to the formation of fine equiaxed grains,and the increased volume fraction of precipitated phases,which significantly improved the elongation of the alloy.Additionally,the addition of Nd element could enhance the annealing recrystallization rate,reduce the Schmid factor difference between basal and prismatic slip systems,facilitate multi-system slip initiation and improve the alloy plasticity.
基金Funded by Shenyang City Application Basic Research Project (No. 1071198-1-00)
文摘Effect of controlled rolling and cooling process on the mechanical properties of low carbon cold forging steel was investigated for different processing parameters of a laboratory hot rolling mill. The results show that the specimens with fast cooling after hot rolling exhibit very good mechanical properties, and the improvement of the mechanical properties can be attributed mainly to the ferrite-grain refinement. The mechanical properties increase with decreasing final cooling temperature within the range from 670 ℃ to 570 ℃ due to the finer interlamellar spacing of pearlite colony. The specimen with fast cooling after low temperature rolling shows the highest values of the mechanical properties. The effect of the ferrite grain size on the mechanical properties was greater than that of pearlite morphology in the present study. The mechanical properties of specimens by controlled rolling and cooling process without thermal treatment were greatly superior to that of the same specimens by the conventional rolling, and their tensile strength reached 490 MPa grade even in the case of low temperature rolling without controlled rolling. It might be expected to realize the substitution medium-carbon by low-carbon for 490 MPa grade cold forging steel with controlled rolling and cooling process.
基金supported by Science and Technology Innovation Cooperation Project between China and South Africa(2017YFE0113400).
文摘The strength-to-weight ratio is an important property of high-strength low-alloy(HSLA)steel in pipeline,whose precipitation strengthening can be improved.The final rolling temperature(FRT)and coiling temperature(CT)are the key process parameters in the control of precipitates and microstructure.Continuous cooling rate was fixed at 10℃/s,and the effects of deformation and coiling temperatures on precipitates and microstructure of Ti-Nb microalloyed HSLA steel were investigated through thermo-mechanical controlled processing on Gleeble 3500.The microstructure is mainly acicular ferrite with high density dislocation and several microns scale.The size and volume fraction of the precipitates were studied under transmission electron microscopy.The results showed that the diameter of the precipitates was in the range between 4 and 240 nm.The optimized combination of parameters is FRT of 820℃and CT of 550℃,and the volume fraction of precipitates obtained under this process is 0.59%.