Clay materials from Thicky in Thiès district (Senegal) are very abundant and could be used for the production of clay brick for the construction industry in Senegal and the surrounding countries. The geophysical,...Clay materials from Thicky in Thiès district (Senegal) are very abundant and could be used for the production of clay brick for the construction industry in Senegal and the surrounding countries. The geophysical, geotechnical, and thermal studies carried out did lead to a better comprehension of the potential of the area for clay production. It also allowed determining the physical and chemical characteristics of the clays for their use in order to make fired clay bricks. Different types of fired clay brick were produced with Thicky’s clays. The study of the physical, mechanical and thermal parameters of these raw materials and bricks has given very satisfactory results compared to the standards in use. It is noted a good ceramic behavior, and there is no deterioration observed after firing at 900°C until low residual moisture of about 3% (on a dry basis), a smooth texture with a beautiful appearance, a low loss on ignition, a low shrinkage value of less than 1% (dry), moderate water absorption and also good compressive strength. The study of thermal properties on a brick wall by the asymmetric lime plane method gives satisfactory effusivity and thermal conductivity values which are respectively equal to 746.48 J<span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>K<sup>-1</sup><span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>m<sup>-2</sup><span style="white-space:nowrap;">·</span>s<sup>-1/2</sup> and 0.42 W<span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>m<sup>-1</sup><span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>k<sup>-1</sup> with a thermal resistance of 0.0028 m<sup>2</sup><span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>K<span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>W<sup>-1</sup>.展开更多
High cost has been pointed among factors that limit the promotion of geopolymers. To contribute to the reduction of the use of costly industrial sodium silicate in activators for geopolymers, a gel obtained with RHA a...High cost has been pointed among factors that limit the promotion of geopolymers. To contribute to the reduction of the use of costly industrial sodium silicate in activators for geopolymers, a gel obtained with RHA and concentrated sodium hydroxide was used in the present study to develop an alkaline activator with 8 M NaOH and to produce geopolymers with crushed fired clay bricks wastes (FCBW). Characteristics of the gel were compared to that of commercial sodium silicate which was also mixed with 8 M NaOH in the ratio 1:1 to produce geopolymers. Chemical and mineralogical analyses were done on raw materials. Fourier Transformed Infrared Spectroscopy (FTIR) was done on the gel, commercial sodium silicate and products. Biaxial four point flexural strength, bulk density, water absorption and scanning electron microscopy (SEM) tests were also done on products. Results showed that RHA-NaOH alkaline activator has good potential in consolidating FCBW powder through geopolymerization process which gave products that had characteristics not far from that when the commercial sodium silicate was used. The gel obtained by mixing RHA and NaOH can contribute to the reduction of the use of costly commercial sodium silicate in the production process of geopolymers. However, appropriate filtration process is needed for the RHA-NaOH gel to reduce its impurities as undissolved entities, which will consequently contribute to improve the flexural strength, the density and the microstructure of its products which were low compared to when commercial sodium silicate was used.展开更多
Peculiar color and form of Leizhou red-brick folk dwelling distinguishes it from other vernacular dwellings in Lingnan region(south of the Five Ridges, referring to the current Guangdong and Guangxi). The fi re-sealin...Peculiar color and form of Leizhou red-brick folk dwelling distinguishes it from other vernacular dwellings in Lingnan region(south of the Five Ridges, referring to the current Guangdong and Guangxi). The fi re-sealing gable wall(hereinafter referred to as fi re-sealing wall) in brilliant colors, diversifi ed forms and exaggerated shapes is a remarkable symbol of local dwellings. Originating from Fulao traditional vernacular dwelling and inheriting its advantages, fi re-sealing wall of Leizhou red-brick vernacular dwelling has shown diversity for the infl uence of immigrants, regional cultures, social background and economic status, and formed its own features in color, form and decoration. On the basis of fi eld investigation, this paper described diversifi ed features of the fi re-sealing wall of Leizhou red-brick vernacular dwelling, analyzed the causes of its diversity from the perspectives of aesthetics, function and technology, and explored the harmonious living philosophy implied by its function, form and art.展开更多
文摘Clay materials from Thicky in Thiès district (Senegal) are very abundant and could be used for the production of clay brick for the construction industry in Senegal and the surrounding countries. The geophysical, geotechnical, and thermal studies carried out did lead to a better comprehension of the potential of the area for clay production. It also allowed determining the physical and chemical characteristics of the clays for their use in order to make fired clay bricks. Different types of fired clay brick were produced with Thicky’s clays. The study of the physical, mechanical and thermal parameters of these raw materials and bricks has given very satisfactory results compared to the standards in use. It is noted a good ceramic behavior, and there is no deterioration observed after firing at 900°C until low residual moisture of about 3% (on a dry basis), a smooth texture with a beautiful appearance, a low loss on ignition, a low shrinkage value of less than 1% (dry), moderate water absorption and also good compressive strength. The study of thermal properties on a brick wall by the asymmetric lime plane method gives satisfactory effusivity and thermal conductivity values which are respectively equal to 746.48 J<span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>K<sup>-1</sup><span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>m<sup>-2</sup><span style="white-space:nowrap;">·</span>s<sup>-1/2</sup> and 0.42 W<span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>m<sup>-1</sup><span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>k<sup>-1</sup> with a thermal resistance of 0.0028 m<sup>2</sup><span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>K<span style="white-space:nowrap;"><span style="white-space:nowrap;">·</span></span>W<sup>-1</sup>.
文摘High cost has been pointed among factors that limit the promotion of geopolymers. To contribute to the reduction of the use of costly industrial sodium silicate in activators for geopolymers, a gel obtained with RHA and concentrated sodium hydroxide was used in the present study to develop an alkaline activator with 8 M NaOH and to produce geopolymers with crushed fired clay bricks wastes (FCBW). Characteristics of the gel were compared to that of commercial sodium silicate which was also mixed with 8 M NaOH in the ratio 1:1 to produce geopolymers. Chemical and mineralogical analyses were done on raw materials. Fourier Transformed Infrared Spectroscopy (FTIR) was done on the gel, commercial sodium silicate and products. Biaxial four point flexural strength, bulk density, water absorption and scanning electron microscopy (SEM) tests were also done on products. Results showed that RHA-NaOH alkaline activator has good potential in consolidating FCBW powder through geopolymerization process which gave products that had characteristics not far from that when the commercial sodium silicate was used. The gel obtained by mixing RHA and NaOH can contribute to the reduction of the use of costly commercial sodium silicate in the production process of geopolymers. However, appropriate filtration process is needed for the RHA-NaOH gel to reduce its impurities as undissolved entities, which will consequently contribute to improve the flexural strength, the density and the microstructure of its products which were low compared to when commercial sodium silicate was used.
基金Sponsored by General Program of National Natural Science Foundation of China(51278194)
文摘Peculiar color and form of Leizhou red-brick folk dwelling distinguishes it from other vernacular dwellings in Lingnan region(south of the Five Ridges, referring to the current Guangdong and Guangxi). The fi re-sealing gable wall(hereinafter referred to as fi re-sealing wall) in brilliant colors, diversifi ed forms and exaggerated shapes is a remarkable symbol of local dwellings. Originating from Fulao traditional vernacular dwelling and inheriting its advantages, fi re-sealing wall of Leizhou red-brick vernacular dwelling has shown diversity for the infl uence of immigrants, regional cultures, social background and economic status, and formed its own features in color, form and decoration. On the basis of fi eld investigation, this paper described diversifi ed features of the fi re-sealing wall of Leizhou red-brick vernacular dwelling, analyzed the causes of its diversity from the perspectives of aesthetics, function and technology, and explored the harmonious living philosophy implied by its function, form and art.