Although polyimide fibers are excellent intrinsic flame-retardant fibers, their price is so high that they are rarely used in clothing. To expand their application, the polyimide fibers were blended with flame-retarda...Although polyimide fibers are excellent intrinsic flame-retardant fibers, their price is so high that they are rarely used in clothing. To expand their application, the polyimide fibers were blended with flame-retardant viscose fibers at a ratio of 30∶70, and the blended yarns were woven with flame-retardant polyester filaments. Fabrics with different parameters, including fabric weaves, warp yarn densities, and fabric layers, were designed, and the effects of those fabric parameters on mechanical properties and flame-retardant properties were tested and analyzed. The results show that the tearing load of the fabrics is affected by fabric weaves, warp yarn densities, and fabric layers, and the tearing load of the weft mountain weave fabric and the twill weave fabric is higher than that of the plain weave fabric. The bursting load of the fabric increases with the increase of warp yarn densities and layers. Among the tested fabric samples, the triple-layer twill fabric has the best flame-retardant performance, which meets the standard of flame-retardant protective fabric Grade B1 level. The research of this paper would provide guidance for the development and production of polyimide blended fabrics.展开更多
Based on the analysis of the properties of Nomex 450 and Nomex 462,the thermal properties of Nomex 462/Lenzing Viscose Flame retardent(FR)blending materials were analyzed.It was discovered through burning test and The...Based on the analysis of the properties of Nomex 450 and Nomex 462,the thermal properties of Nomex 462/Lenzing Viscose Flame retardent(FR)blending materials were analyzed.It was discovered through burning test and Thermal Gravity(TG)analysis that the blended material was superior in thermal behaviors to the material made from either Nomex or Viscose FR filament,when the ratio of Nomex and Lenzing Viscose FR reached 80∶20,and excellent thermal properties were achieved with the value of Limiting Oxygen Index(LOI)up to 36.1%.Blending Nomex and Viscose FR filaments may be recommended for better fire retardant property of related fabric.展开更多
基金National Natural Science Foundation of China (No.11802161)Natural Science Foundation of Fujian Province,China (No.2020J05160)Startup Foundation for Doctors of Quanzhou Normal University,China (No.H18012)。
文摘Although polyimide fibers are excellent intrinsic flame-retardant fibers, their price is so high that they are rarely used in clothing. To expand their application, the polyimide fibers were blended with flame-retardant viscose fibers at a ratio of 30∶70, and the blended yarns were woven with flame-retardant polyester filaments. Fabrics with different parameters, including fabric weaves, warp yarn densities, and fabric layers, were designed, and the effects of those fabric parameters on mechanical properties and flame-retardant properties were tested and analyzed. The results show that the tearing load of the fabrics is affected by fabric weaves, warp yarn densities, and fabric layers, and the tearing load of the weft mountain weave fabric and the twill weave fabric is higher than that of the plain weave fabric. The bursting load of the fabric increases with the increase of warp yarn densities and layers. Among the tested fabric samples, the triple-layer twill fabric has the best flame-retardant performance, which meets the standard of flame-retardant protective fabric Grade B1 level. The research of this paper would provide guidance for the development and production of polyimide blended fabrics.
文摘Based on the analysis of the properties of Nomex 450 and Nomex 462,the thermal properties of Nomex 462/Lenzing Viscose Flame retardent(FR)blending materials were analyzed.It was discovered through burning test and Thermal Gravity(TG)analysis that the blended material was superior in thermal behaviors to the material made from either Nomex or Viscose FR filament,when the ratio of Nomex and Lenzing Viscose FR reached 80∶20,and excellent thermal properties were achieved with the value of Limiting Oxygen Index(LOI)up to 36.1%.Blending Nomex and Viscose FR filaments may be recommended for better fire retardant property of related fabric.