A spiral fluidity test model of superalloys with 10 mm in height and 3 mm in thickness was designed to evaluate the fluidity of two distinct Ni-based superalloys IN718 and IN939.The factors influencing fluidity are as...A spiral fluidity test model of superalloys with 10 mm in height and 3 mm in thickness was designed to evaluate the fluidity of two distinct Ni-based superalloys IN718 and IN939.The factors influencing fluidity are ascertained through comparative analysis utilizing methodologies such as JMat Pro,differential scanning calorimetry and high-temperature confocal laser scanning microscopy.The results show that under identical testing conditions,the fluidity of the IN939 superalloy surpasses that of the IN718 superalloy.When subjected to the same temperature,the melt viscosity and surface tension of IN939 superalloy are considerably reduced relative to those of IN718 superalloy,which is beneficial to improving the melt fluidity.Furthermore,the liquidus temperature and solidification range for the IN939 superalloy are both smaller compared with those of the IN718 superalloy.This condition proves advantageous in delaying dendrite coherency,thereby improving fluidity.展开更多
The crystallization has significant influence on fluidity of slag and slag discharge of entrained-flow-bed(EFB) gasifier. The crystallization characteristics and fluidity of five synthetic slags with different MgO/CaO...The crystallization has significant influence on fluidity of slag and slag discharge of entrained-flow-bed(EFB) gasifier. The crystallization characteristics and fluidity of five synthetic slags with different MgO/CaO ratios prepared on the basis of the range of oxide contents of Zhundong coal ash were investigated in this study. The results show that with the MgO/CaO ratio increase, the initial crystallization temperature increases, and the main temperature range of crystallization ratio growth moves to higher temperature range gradually which causes Tp25(Tp25is the temperature corresponding to the viscosity of 25 Pa·s)to increase. Mg-rich crystals are formed preferentially than Ca-rich crystals when adding the same amount of MgO and CaO during cooling. The effective slagging operating temperature range decrease from 217 ℃ for the slag with a 0:4 MgO/CaO ratio to 44 ℃ for the slag with a 4:0 MgO/CaO ratio with the MgO/CaO ratio increase. The slags with 2:2 and 1:3 MgO/CaO ratios show similar effective slagging operating temperature range, Tp25and the temperature corresponding to the viscosity of 2 Pa·s.However, compared with the slag with a 1:3 MgO/CaO ratio, the crystallization ratio and rate of slag with a 2:2 MgO/CaO ratio are lower within lower temperature range(1300–1200 ℃), causing its lower critical viscosity temperature and wider actual operating temperature range. Of the five slags, the widest effective slagging operating temperature range and the lowest Tp25of the slag with a 0:4 MgO/CaO ratio due to its low crystallization ratio, and wider actual operating temperature range of the slag with a 2:2 MgO/CaO ratio make the two slags suitable for slag discharge of EFB gasifier.展开更多
由于油层非均质性强,井间、层间、层内差异大,均一化设计注入方案满足不了所有井的需要,更满足不了所有层的需要,因此需从单井入手。在ZN区块PⅠ5~PⅡ10层段选取三类油层中渗透率级别为0.5~0.7μm^(2)的三类井组为研究对象,研究该井组...由于油层非均质性强,井间、层间、层内差异大,均一化设计注入方案满足不了所有井的需要,更满足不了所有层的需要,因此需从单井入手。在ZN区块PⅠ5~PⅡ10层段选取三类油层中渗透率级别为0.5~0.7μm^(2)的三类井组为研究对象,研究该井组驱替段塞前段注入参数界限。通过改变聚合物黏度、注入速度和段塞大小设计了不同注入方案。使用数值模拟方法对比各个注入方案,综合考虑开发效果、经济效益以及注入压力情况等因素,确定聚合物最优注入黏度、段塞大小和注入速度分别为33 m Pa·s、0.25 PV和0.16 PV·a^(-1);与常规水驱相比,采收率提高了14.24%,优化结果更好地指导了现场变流度聚合物驱的实施。展开更多
H +_ATPase activity of tonoplast in roots of Hordeum vulgare L. cv. 'Tanyin 2' (salt_tolerant cultivar) increased when the roots were exposed to 50-200 mmol/L NaCl for 2 d, and decreased when NaCl concentrati...H +_ATPase activity of tonoplast in roots of Hordeum vulgare L. cv. 'Tanyin 2' (salt_tolerant cultivar) increased when the roots were exposed to 50-200 mmol/L NaCl for 2 d, and decreased when NaCl concentration was increased to 600 mmol/L. In 'Kepin 7' (salt_sensitive cultivar), tonoplast H +_ATPase activity in roots also increased at lower levels of NaCl (50-100 mmol/L), but decreased at higher levels of NaCl (200-600 mmol/L). Tonoplast fluidity in roots of 'Tanyin 2' decreased at 50-200 mmol/L NaCl, and increased significantly at 600 mmol/L NaCl. Under salt stress, the change of tonoplast fluidity was identical with that of the ratio of unsaturated fatty acids to saturated fatty acids in tonoplast lipid of barley roots. It is proposed that the increase of tonoplast fluidity due to increased degree of unsaturation of fatty acids is one of the reasons leading to the decrease of H +_ATPase activity under higher level of NaCl stress.展开更多
基金support from the National Natural Science Foundation of China(Nos.52031012,51904218)。
文摘A spiral fluidity test model of superalloys with 10 mm in height and 3 mm in thickness was designed to evaluate the fluidity of two distinct Ni-based superalloys IN718 and IN939.The factors influencing fluidity are ascertained through comparative analysis utilizing methodologies such as JMat Pro,differential scanning calorimetry and high-temperature confocal laser scanning microscopy.The results show that under identical testing conditions,the fluidity of the IN939 superalloy surpasses that of the IN718 superalloy.When subjected to the same temperature,the melt viscosity and surface tension of IN939 superalloy are considerably reduced relative to those of IN718 superalloy,which is beneficial to improving the melt fluidity.Furthermore,the liquidus temperature and solidification range for the IN939 superalloy are both smaller compared with those of the IN718 superalloy.This condition proves advantageous in delaying dendrite coherency,thereby improving fluidity.
基金supported by the National Natural Science Foundation of China(21878082).
文摘The crystallization has significant influence on fluidity of slag and slag discharge of entrained-flow-bed(EFB) gasifier. The crystallization characteristics and fluidity of five synthetic slags with different MgO/CaO ratios prepared on the basis of the range of oxide contents of Zhundong coal ash were investigated in this study. The results show that with the MgO/CaO ratio increase, the initial crystallization temperature increases, and the main temperature range of crystallization ratio growth moves to higher temperature range gradually which causes Tp25(Tp25is the temperature corresponding to the viscosity of 25 Pa·s)to increase. Mg-rich crystals are formed preferentially than Ca-rich crystals when adding the same amount of MgO and CaO during cooling. The effective slagging operating temperature range decrease from 217 ℃ for the slag with a 0:4 MgO/CaO ratio to 44 ℃ for the slag with a 4:0 MgO/CaO ratio with the MgO/CaO ratio increase. The slags with 2:2 and 1:3 MgO/CaO ratios show similar effective slagging operating temperature range, Tp25and the temperature corresponding to the viscosity of 2 Pa·s.However, compared with the slag with a 1:3 MgO/CaO ratio, the crystallization ratio and rate of slag with a 2:2 MgO/CaO ratio are lower within lower temperature range(1300–1200 ℃), causing its lower critical viscosity temperature and wider actual operating temperature range. Of the five slags, the widest effective slagging operating temperature range and the lowest Tp25of the slag with a 0:4 MgO/CaO ratio due to its low crystallization ratio, and wider actual operating temperature range of the slag with a 2:2 MgO/CaO ratio make the two slags suitable for slag discharge of EFB gasifier.
文摘由于油层非均质性强,井间、层间、层内差异大,均一化设计注入方案满足不了所有井的需要,更满足不了所有层的需要,因此需从单井入手。在ZN区块PⅠ5~PⅡ10层段选取三类油层中渗透率级别为0.5~0.7μm^(2)的三类井组为研究对象,研究该井组驱替段塞前段注入参数界限。通过改变聚合物黏度、注入速度和段塞大小设计了不同注入方案。使用数值模拟方法对比各个注入方案,综合考虑开发效果、经济效益以及注入压力情况等因素,确定聚合物最优注入黏度、段塞大小和注入速度分别为33 m Pa·s、0.25 PV和0.16 PV·a^(-1);与常规水驱相比,采收率提高了14.24%,优化结果更好地指导了现场变流度聚合物驱的实施。
文摘H +_ATPase activity of tonoplast in roots of Hordeum vulgare L. cv. 'Tanyin 2' (salt_tolerant cultivar) increased when the roots were exposed to 50-200 mmol/L NaCl for 2 d, and decreased when NaCl concentration was increased to 600 mmol/L. In 'Kepin 7' (salt_sensitive cultivar), tonoplast H +_ATPase activity in roots also increased at lower levels of NaCl (50-100 mmol/L), but decreased at higher levels of NaCl (200-600 mmol/L). Tonoplast fluidity in roots of 'Tanyin 2' decreased at 50-200 mmol/L NaCl, and increased significantly at 600 mmol/L NaCl. Under salt stress, the change of tonoplast fluidity was identical with that of the ratio of unsaturated fatty acids to saturated fatty acids in tonoplast lipid of barley roots. It is proposed that the increase of tonoplast fluidity due to increased degree of unsaturation of fatty acids is one of the reasons leading to the decrease of H +_ATPase activity under higher level of NaCl stress.