A novel unsymmetrical fluorinated diamine monomer with kink non-coplanar heterocyclic structures, 1,2-dihydro- 2-（4-amino-2-trifluoromethyophenyo）-4-[4-（4-amino-2-trifluoromethyophenoxy）phenyo]（2H）phthaoazin-1-o...A novel unsymmetrical fluorinated diamine monomer with kink non-coplanar heterocyclic structures, 1,2-dihydro- 2-（4-amino-2-trifluoromethyophenyo）-4-[4-（4-amino-2-trifluoromethyophenoxy）phenyo]（2H）phthaoazin-1-oneo was prepared through the nucleophilic substitution reaction of 1-trifluromethyl-2-chloro-5-nitrobenzene with 1,2-dihydro-4-（4- hydroxyphenyl）（2H）phthalazin-l-one in the presence of potassium carbonate, followed by catalytic reduction with hydrazine and Pd-C. A series of new fluorinated polyarnides were synthesized by the phosphorylation polyamidation of the fluorinated diamine with various dicarboxylic acids. The prepared polymers were obtained in quantitative yields with moderately and high inherent viscosities （0.47-0.87 dL/g）. They were all amorphous and readily soluble in various polar aprotic solvents such as N-methyl-2-pyrrolidone （NMP）, N,N-dimethylformamide （DMF）, N,N-dimethylacctamide （DMAc）, pyridine （Py） and m-cresol at room temperature. These fluorinated polyamides have excellent thermal properties. The glass transition temperatures were all above 300℃. The 5% and 10% weight loss temperatures were in the range of 437-466℃ and 482-525℃ in nitrogen atmosphere, respectively.展开更多
A new fluorinated poly(ether amide) bearing xanthene group was prepared from 9,9-bis[4-(2-trifluoromethyl-4-aminophenox- y)phenyl]xanthene (BTFAPX) with 9,9-bis[4-(4-carboxyphenoxy)phenyl]xanthene (BCAPX) in the prese...A new fluorinated poly(ether amide) bearing xanthene group was prepared from 9,9-bis[4-(2-trifluoromethyl-4-aminophenox- y)phenyl]xanthene (BTFAPX) with 9,9-bis[4-(4-carboxyphenoxy)phenyl]xanthene (BCAPX) in the presence of triphenyl phos- phate and pyridine (Py). The polymer had the weight-average molecular weight (Mw) of 69,000 and number-average molecular weight (Mn) of 39,000, showed the glass transition temperature (Tg) of 267 ℃, 5% weight loss temperature (Tds) over 460 ℃ both in N2 and air, and char yield of 62% at 800 ℃ in N2. This polymer was amorphous and readily soluble in amide-type solvents such as N,N-dimethylacetamide (DMAc), and even in m-cressol, Py and tetrahydrofuran (THF) at room temperature, and exhibited tensile strength of 74 MPa, elongation at break of 6%, tensile moduli of 2.2 GPa. The polymer had low dielectric constant of 3.69 (100 Hz), low moisture absorption of 0.56%, and high transparency with an ultraviolet-visible absorption cut-off wavelength at 334 nm.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No. 50673031)the Key Natural Science Foundation of Fujian Province (No. E0320003)State Key Laboratory of Polymer Physics and Chemistry in Institute of Chemistry of CAS (No. 200602).
文摘A novel unsymmetrical fluorinated diamine monomer with kink non-coplanar heterocyclic structures, 1,2-dihydro- 2-（4-amino-2-trifluoromethyophenyo）-4-[4-（4-amino-2-trifluoromethyophenoxy）phenyo]（2H）phthaoazin-1-oneo was prepared through the nucleophilic substitution reaction of 1-trifluromethyl-2-chloro-5-nitrobenzene with 1,2-dihydro-4-（4- hydroxyphenyl）（2H）phthalazin-l-one in the presence of potassium carbonate, followed by catalytic reduction with hydrazine and Pd-C. A series of new fluorinated polyarnides were synthesized by the phosphorylation polyamidation of the fluorinated diamine with various dicarboxylic acids. The prepared polymers were obtained in quantitative yields with moderately and high inherent viscosities （0.47-0.87 dL/g）. They were all amorphous and readily soluble in various polar aprotic solvents such as N-methyl-2-pyrrolidone （NMP）, N,N-dimethylformamide （DMF）, N,N-dimethylacctamide （DMAc）, pyridine （Py） and m-cresol at room temperature. These fluorinated polyamides have excellent thermal properties. The glass transition temperatures were all above 300℃. The 5% and 10% weight loss temperatures were in the range of 437-466℃ and 482-525℃ in nitrogen atmosphere, respectively.
基金National Natural Science Foundation of China(No.20664001)the Research Program of Jiangxi Province Department of Education(No.2007-123,GJJ08166 and GJJ09138) for the financial support
文摘A new fluorinated poly(ether amide) bearing xanthene group was prepared from 9,9-bis[4-(2-trifluoromethyl-4-aminophenox- y)phenyl]xanthene (BTFAPX) with 9,9-bis[4-(4-carboxyphenoxy)phenyl]xanthene (BCAPX) in the presence of triphenyl phos- phate and pyridine (Py). The polymer had the weight-average molecular weight (Mw) of 69,000 and number-average molecular weight (Mn) of 39,000, showed the glass transition temperature (Tg) of 267 ℃, 5% weight loss temperature (Tds) over 460 ℃ both in N2 and air, and char yield of 62% at 800 ℃ in N2. This polymer was amorphous and readily soluble in amide-type solvents such as N,N-dimethylacetamide (DMAc), and even in m-cressol, Py and tetrahydrofuran (THF) at room temperature, and exhibited tensile strength of 74 MPa, elongation at break of 6%, tensile moduli of 2.2 GPa. The polymer had low dielectric constant of 3.69 (100 Hz), low moisture absorption of 0.56%, and high transparency with an ultraviolet-visible absorption cut-off wavelength at 334 nm.