High Cycle Fatigue Properties of Die-Cast Magnesium Alloy AZ91D with Addition of Different Concentrations of Cerium

The effect of addition of different concentrations of Ce on high-cycle fatigue behavior of die-cast magnesium alloy AZ91D was investigated. Mechanical fatigue tests were conducted at the stress ratio of R = 0.1, and fatigue strength was evaluated using up-and-down loading method. The results show that the grain size of AZ91D alloy is remarkably refined, and the amount of porosity decreases and evenly distributes with the addition of Ce. The fatigue strength of AZ91D alloy at room temperature increases from 96.7 up to 116.3 MPa （ 1% Ce） and 105.5 MPa （2 % Ce）, respectively, at the number of cycles to failure, Nf = 1 × 10^7. The fatigue crack of AZ91D alloy initiates at porosities and inclusions, and propagates along grain boundaries. The fatigue striations on fractured surface appear with Ce addition. The fatigue fracture surface of test specimens shows mixed-fracture characteristics of quasi-cleavage and dimple.

Cutting Performance of WC-Co Alloys Modified by Nano-Additives

In this paper,the microstructure of WC-Co alloys with and without nano-additives was characterized by scanning electron microscopy（SEM） and transmission electron microscopy（TEM）.The hardness and fracture toughness was tested by using a Vickers hardness tester and a universal testing machine.The cutting test was carried out at different feed velocities（250 r/min and 320 r/min）,and the contact pairs are cutting tools and 45# steel bars.Results showed that the hardness and fracture toughness of WC-Co cemented carbides with nano-additives are higher than that of WC-Co cemented carbides without nano-additives,and they are increased 10.21% and 19.69%,respectively.The flank worn width and crater width of cutting tools decrease greatly with the addition of nano-additives.For the nano-modified specimen with WC grain size of 7 μm,both the flank worn width and crater width are the minimum after the cutting process.And there are little built-up layers and some pile-up regions on the flank face leading to high cutting performance for the nano-modified cemented carbides.There are some melted regions on the flank face of cutting tools without nano-additives,and the WC grains on the cross section of alloys without nano-additives show severe fragmentation.The wear type of WC-Co is flank wear,and the wear mechanism is abrasive,adhesion and oxidation wear.