A formula is derived for determining the influence of temperature and loading rate on dynamic fracture toughness of a high strength low alloy steel (HQ785C) from thermal activation analysis of the experimental results...A formula is derived for determining the influence of temperature and loading rate on dynamic fracture toughness of a high strength low alloy steel (HQ785C) from thermal activation analysis of the experimental results of three-point bend specimens as well as introducing an Arrhenius formula. It is shown that the results obtained by the given formula are in good agreement with the experimental ones in the thermal activation region. The present method is also valuable to describe the relationship between dynamic fracture toughness and temperature and loading rate of other high strength low alloy steels.展开更多
Three types of composite materials were designed and fabricated by hot pressing powder blends of alumina with 20 vol. pct nickel particles. The composites differ in the shape, size and distribution of the nickel parti...Three types of composite materials were designed and fabricated by hot pressing powder blends of alumina with 20 vol. pct nickel particles. The composites differ in the shape, size and distribution of the nickel particles. Composite microstructures are described and measurements of density, hardness, flexure strength, and fracture toughness are reported. The results showed that the fracture strength of the composite with dispersed nickel particles is higher than the other two composites （network microstructure and mixed microstructure） and the alumina matrix. For all the composites studied, tougher materials than the monolithic alumina were produced. The fracture toughness of the composite with a network microstructure is much higher than that of the other composites. The toughening mechanisms were described based on the observation of the fracture surfaces and the crack-particle interactions. Moreover, the parameters for microstructural tailoring of these materials have been deduced. The toughening of the produced composites was explained in light of the interracial bond strength.展开更多
文摘A formula is derived for determining the influence of temperature and loading rate on dynamic fracture toughness of a high strength low alloy steel (HQ785C) from thermal activation analysis of the experimental results of three-point bend specimens as well as introducing an Arrhenius formula. It is shown that the results obtained by the given formula are in good agreement with the experimental ones in the thermal activation region. The present method is also valuable to describe the relationship between dynamic fracture toughness and temperature and loading rate of other high strength low alloy steels.
文摘Three types of composite materials were designed and fabricated by hot pressing powder blends of alumina with 20 vol. pct nickel particles. The composites differ in the shape, size and distribution of the nickel particles. Composite microstructures are described and measurements of density, hardness, flexure strength, and fracture toughness are reported. The results showed that the fracture strength of the composite with dispersed nickel particles is higher than the other two composites （network microstructure and mixed microstructure） and the alumina matrix. For all the composites studied, tougher materials than the monolithic alumina were produced. The fracture toughness of the composite with a network microstructure is much higher than that of the other composites. The toughening mechanisms were described based on the observation of the fracture surfaces and the crack-particle interactions. Moreover, the parameters for microstructural tailoring of these materials have been deduced. The toughening of the produced composites was explained in light of the interracial bond strength.