The synthesis of Friedel＇s salt （FS： 3CaO·Al2O3·CaCl2·10H2O） by the reaction of calcium chloride with sodium aluminate was investigated. Factors affecting the preparation of Friedel＇s salt, such as...The synthesis of Friedel＇s salt （FS： 3CaO·Al2O3·CaCl2·10H2O） by the reaction of calcium chloride with sodium aluminate was investigated. Factors affecting the preparation of Friedel＇s salt, such as reaction temperature, initial concentration, titration speed, aging time and molar Ca/Al ratio were studied in detail. XRD, SEM images and particle size distribution show that the reaction temperature, aging time and molar Ca/Al ratio have significant effect on the composition, crystal morphology, and average particle size of the obtained samples. In addition, the initial CaCl2 concentration and NaAlO2 titration speed do not significantly influence the morphology and particle size distribution of Friedel＇s salt. With the optimization of the operating conditions, the crystals can grow up to a average size of about 28 μm, showing flat hexagonal （or pseudo- hexagonal） crystal morphology. Moreover, two potential mechanisms of Friedel＇s salt formation including adsorption mechanism and anion-exchange mechanism were discussed. In the adsorption mechanism, Friedel＇s salt forms due to the adsorption of the bulk C1- ions present in the solution into the interlayers of the principal layers, [Ca2Al（OH-）6·2H2O]＋, in order to balance the charge. In the anion-exchange mechanism, the freechloride ions bind with the AFro （a family of hydrated compounds found in cement） hydrates to form Friedel＇s salt by anion-exchange with the ions present in the interlayers of the principal layer, [Ca2Al（OH-）6. 2H2O]＋- OH-.展开更多
基金Funded by International Science&Technology Cooperation Program of China(No.2013DFB70220)the National Natural Science Foundation of China(No.21076212)the Natural Science Foundation of Guizhou Province of China(No.[2014]2003)
文摘The synthesis of Friedel＇s salt （FS： 3CaO·Al2O3·CaCl2·10H2O） by the reaction of calcium chloride with sodium aluminate was investigated. Factors affecting the preparation of Friedel＇s salt, such as reaction temperature, initial concentration, titration speed, aging time and molar Ca/Al ratio were studied in detail. XRD, SEM images and particle size distribution show that the reaction temperature, aging time and molar Ca/Al ratio have significant effect on the composition, crystal morphology, and average particle size of the obtained samples. In addition, the initial CaCl2 concentration and NaAlO2 titration speed do not significantly influence the morphology and particle size distribution of Friedel＇s salt. With the optimization of the operating conditions, the crystals can grow up to a average size of about 28 μm, showing flat hexagonal （or pseudo- hexagonal） crystal morphology. Moreover, two potential mechanisms of Friedel＇s salt formation including adsorption mechanism and anion-exchange mechanism were discussed. In the adsorption mechanism, Friedel＇s salt forms due to the adsorption of the bulk C1- ions present in the solution into the interlayers of the principal layers, [Ca2Al（OH-）6·2H2O]＋, in order to balance the charge. In the anion-exchange mechanism, the freechloride ions bind with the AFro （a family of hydrated compounds found in cement） hydrates to form Friedel＇s salt by anion-exchange with the ions present in the interlayers of the principal layer, [Ca2Al（OH-）6. 2H2O]＋- OH-.
