ETHYLENE POLYMERIZATION AND COPOLYMERIZATION WITH POLAR MONOMERS BY A NEUTRAL NICKEL CATALYST COMBINED WITH CO-CATALYST OF Ni(COD)_2 OR AL(i-Bu)_3

A neutral nickel(Ⅱ)catalyst D,{[O-(3-cyclohexyl)(5-Cl)C_6H_2-ortho-C(H)=N-2,6-C_6H_3(i-Pr)_2]Ni(Ph_3P)(Ph)}hasbeen synthesized and characterized by IH-NMR,FTIR and elemental analysis.The results indicate that Al(i-Bu)_3 is aneffective cocatalyst for the neutral nickel catalyst.With bis(1,5-cyclooctadiene)nickel(0)[Ni(COD)_2]or Al(i-Bu)_3 as a co-catalyst,the neutral nickel catalyst D is active for ethylene polymerisation and copolymerisation with polar monomers(tert-butyl 10-undecenoate(BU),methyl 10-undecenoate(MU),allyl alcohol(AA)and 4-penten-1-ol(PO))under mild conditions.The resulting polymers were characterized by (?)H-NMR,FTIR,DSC,and GPC.From the comparative studies,Ni(COD)_2 ismore active than Al(i-Bu)_3 for ethylene homopolymerization,while Al(i-Bu)_3 is more effective than Ni(COD)_2 for ethylenecopolymerisation with polar monomers.The polymerization parameters which affect both the catalytic activity and propertiesof the resulting polyethylene were investigated in detail.Under the conditions of 20 μmol catalyst D and Ni(COD)_2/D=3(molar ratio) in 30 mL toluene solution at 45℃,12×105 Pa ethylene for 20 min,the polymerization activity reaches ashigh as 7.29×105 gPE.(mol.Ni.h)^(-1) and M_η,is 7.16×104 g.mol^(-1).For ethylene copolymerization with polar monomers,theeffect of comonomer concentrations was examined.As high as 0.97 mol% of MU,1.06 mol% of BU,1.04 mol% of AA and1.37 mol% of PO were incorporated into the polymer,respectively,catalyzed by D/Al(i-Bu)_3 system.

Copolymerization of Ethylene with 10-Undecen-1-ol Using Highly Active Vanadium(Ⅲ) Precatalysts Bearing Bis(imino)pyrrolyl Ligands

The copolymerizations of ethylene with 10-undecen-1-ol have been investigated using vanadium precatalysts, bis（imino）pyrrolyl vanadium（Ⅲ） complexes 1-3, 2,5-C4H2N（CH=NR）2VCl2（THF）2 [R = C6H5 （1）, 2,6-iPr2C6H3 （2）, C6F5 （3）], and the iminopyrrolyl and b-diketiminate ones for comparison. The polar monomer was pretreated by diethylaluminium chloride （present also as the cocatalyst） before the copolymerization. The monomer reactivity ratios were evaluated using the Fineman-Ross method. The ligand structure considerably influenced the catalytic activity and tolerance towards the polar monomer, the polar monomer incorporation and the molecular weights of the resultant copolymers. The bis（imino）pyrrolyl vanadium complexes exhibited promising catalytic performance for the copolymerization, and a high catalytic activity up to 3.84 kg/mmolv·h with a high comonomer incorporation of 14.0 mol% was achieved by complex 3 under mild conditions.