Fused Zirconia

1 Scope This standard specifies the terms, definitions, classification, brands, technical requirements, test methods, inspection rules, packing, marking, trans- portation, storage, and quality certificate of fused zireonia.

Advanced Ramming Mix Based on Fused Zirconia Stabilized by Com-bined Additives of CaO and MgO for Lining of Carbon Black Production Reactor

Fused materials from ZrO2 stabilized by CaO or MgO, or the combined additive consisting of CaO and MgO are made. With using chemical, petrographic, X-ray phase and electron microscopic researches the main characteristics of these materials are determined. It is shown that, the materials of all compositions have low water absorption; they are characterized by equal struc-ture. The materials stabilized by the combined additive consisting of CaO and MgO are presented by generally the cubic phase and a small amount of tetragonal and monoclinic ZrO2 phases. Depending on CaO： MgO ratio in the materials the tetragonal ZrO2 phase settles down in a cubic matrix in the form of separate grains, and sites of net like structure in the form of a ＂woven＂ interlacing （2.9% of CaO and 2. 6% of MgO ）. An influence of the above mentioned fused stabilized ZrO2 materials and quantity of monoclinic zirconia, on the forming of zirconia mix on a phosphate bond and properties of＂ .fired samples is studied. The samples from mix based on ZrO2 stabilized by the combined additive consisting of 2.9% CaO and 2.6% MgO with 20% of monoclinic Zr02 are characterized by the highest properties： after .firing at 1 580 ~C open porosity of 14. 3% - 14. 8%, apparent density of 4. 67 -4. 69 g · cm^-5, cold crushing strength of 62 - 68 MPa, thermal shock resistance （ 1 300℃←→air） of 15 thermal cycles, linear growth of 0. 2%. The manufacturing technology of powders mix-ture for ramming mix based on the new fused material .from ZrO2 stabilized by the combined additive is developed and its production is mastered. From this mixture the large-size, shaped products on the phosphate bond are made at one carbon black production plant, which are installed in the combustion chamber of the carbon black production reactor.

Effect of Zirconia Corundum Addition on Properties of Chrome Corundum Castables

In order to investigate the effect of zirconia corundum on the preparation of chrome corundum castables,samples were prepared using tabular corundum,white fused corundum,active alumina micropowder,chromium oxide micropowder and fused ziconia corundum particles as the main raw materials,and pure calcium aluminate cement as the binder.The effects of the fused zirconia corundum particles addition(1-0.5 mm,0,4.5%,9%,and 18%,by mass)on the linear change rate,the apparent porosity,the cold modulus of rupture,and the thermal shock resistance of chrome corundum castables were studied,and the microstructure of the samples was analyzed.The results show that:(1)with the zirconia corundum addition increasing,the permanent linear change on heating of the samples gradually increases,the apparent porosity gradually increases,the cold modulus of rupture gradually decreases,and the thermal shock resistance gradually increases;(2)according to SEM,it can be found that the phase transformation of ZrO2 after heat treatment leads to a large number of microcracks in the material.On one hand,the cold modulus of rupture of the material is reduced;on the other hand,the thermal shock resistance of the material is improved.