The flow stress behavior of GH4033 superalloy was determined by the hot compression tests at the temperatures of 1223-1473 K and the total strains of 0.6 with the strain rates of 0.001-30.0 s^(-1) by using cylindrical...The flow stress behavior of GH4033 superalloy was determined by the hot compression tests at the temperatures of 1223-1473 K and the total strains of 0.6 with the strain rates of 0.001-30.0 s^(-1) by using cylindrical samples.The processing maps based on the dynamic material model(DMM)combined with the corresponding microstructure observations indicate the reasonable processing domain locating at the strain rates of 0.1-1.0 s^(-1) and the deformation temperature of 1273-1423 K.Meanwhile,the numerical simulation based on finite element model(FEM)described the variation of the effective strain,effective strain rate and the temperature for the core node,and unveiled the influence of the hot rolling parameters considering the initial temperature(T_(0))range of 1223-1473 K and the first-stand biting velocity(v_(0))range of 0.15-0.35 m·s^(-1).Furthermore,the deformation stability of GH4033 superalloy in the round rod hot continuous rolling(HCR)process is described and analyzed by coupling the three-dimensional(3-D)processing map,and the spatial trajectory lines were determined by the numerically simulated temperatures,the strains and the strain rates.Finally,the results show that the hot deformation stability of GH4033 can be achieved by the rolling process parameters located at T_(0)=1423 K and v_(0)=0.25 m·s^(-1).Additionally,the practical HCR processes as T_(0)=1423 K and v_(0)=0.15,0.25,0.35 m·s^(-1) were operated to verify the influence of the hot rolling parameters on the hot deformation stability by the microstructure observation of the final products.展开更多
Based on two-dimensional （2D） rigid-plastic finite element （FE） method, the optimum observation area for metallographic microstructure and the influence of the height-diameter ratio on which were analyzed for the ...Based on two-dimensional （2D） rigid-plastic finite element （FE） method, the optimum observation area for metallographic microstructure and the influence of the height-diameter ratio on which were analyzed for the cylindrical samples with the diameter of 8 mm and different heights from 8 to 16 mm in nonuniform compressive experiments. It is shown that the representative metallographic observation area relevant to the applied deformation condition is located at about 0.835 of the radius from the center of the sample to the solder joint between the sample and the thermocouples. At the same time, the microstructure in that area is more appropriate as the height of the sample is 12 mm. The related parameters of GH4033 superalloy were adopted in the FE analysis, and the validity of this analysis was verified by the compressive experiments.展开更多
基金the National Natural Science Foundation of China(No.52174359)the Key Research and Development Projects of Anhui Province(No.201904a05020068)。
文摘The flow stress behavior of GH4033 superalloy was determined by the hot compression tests at the temperatures of 1223-1473 K and the total strains of 0.6 with the strain rates of 0.001-30.0 s^(-1) by using cylindrical samples.The processing maps based on the dynamic material model(DMM)combined with the corresponding microstructure observations indicate the reasonable processing domain locating at the strain rates of 0.1-1.0 s^(-1) and the deformation temperature of 1273-1423 K.Meanwhile,the numerical simulation based on finite element model(FEM)described the variation of the effective strain,effective strain rate and the temperature for the core node,and unveiled the influence of the hot rolling parameters considering the initial temperature(T_(0))range of 1223-1473 K and the first-stand biting velocity(v_(0))range of 0.15-0.35 m·s^(-1).Furthermore,the deformation stability of GH4033 superalloy in the round rod hot continuous rolling(HCR)process is described and analyzed by coupling the three-dimensional(3-D)processing map,and the spatial trajectory lines were determined by the numerically simulated temperatures,the strains and the strain rates.Finally,the results show that the hot deformation stability of GH4033 can be achieved by the rolling process parameters located at T_(0)=1423 K and v_(0)=0.25 m·s^(-1).Additionally,the practical HCR processes as T_(0)=1423 K and v_(0)=0.15,0.25,0.35 m·s^(-1) were operated to verify the influence of the hot rolling parameters on the hot deformation stability by the microstructure observation of the final products.
基金supported by the National Natural Science Foundation of China (No. 51274062)
文摘Based on two-dimensional （2D） rigid-plastic finite element （FE） method, the optimum observation area for metallographic microstructure and the influence of the height-diameter ratio on which were analyzed for the cylindrical samples with the diameter of 8 mm and different heights from 8 to 16 mm in nonuniform compressive experiments. It is shown that the representative metallographic observation area relevant to the applied deformation condition is located at about 0.835 of the radius from the center of the sample to the solder joint between the sample and the thermocouples. At the same time, the microstructure in that area is more appropriate as the height of the sample is 12 mm. The related parameters of GH4033 superalloy were adopted in the FE analysis, and the validity of this analysis was verified by the compressive experiments.