New Ge/SiO_2 glasses have been synthesized by heating the GeO_2/SiO_2 dry gels under H_2gas at 700℃. The resulting fluorescence spectra show that this kind of Ge/SiO_2 glasses emit strongphotoluminescence at 392 nm (...New Ge/SiO_2 glasses have been synthesized by heating the GeO_2/SiO_2 dry gels under H_2gas at 700℃. The resulting fluorescence spectra show that this kind of Ge/SiO_2 glasses emit strongphotoluminescence at 392 nm (3.12 eV), medium strong photoluminescence at 600 nm (2.05 eV)and weak photoluminescence at 770 nm (1.60 eV) respectively. Possible photoluminescencemechanisms are also discussed based on the results of X-ray diffraction (XRD) and X-rayphotoelectron spectra(XPS).展开更多
Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with t...Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with the addition of Ga2S3, two main structural transformations were deduced ： the gradual enhancement of ethane- like structural units S3 Ge- GeS3 （ 250 cm ^- 1） and S3 Ga- GaS3 （270 cm ^- 1 ） and the appearance of charge imbalanced units [ Ga2 S2 （ S1/2 ）4 ]^2- and [Ga（ S1/2 ）4 ]^- . And this change of structural aspect seems to give as a clue to understanding the cause of the increased rare-earth solubility.展开更多
An improved sol-gel method was used to prepare Eu3+ ions doped SiO-Y2O3 nanocomposites. Systematic study on the effect of post-annealling treatment on photoluminescence (PL) properties of the samples under various eur...An improved sol-gel method was used to prepare Eu3+ ions doped SiO-Y2O3 nanocomposites. Systematic study on the effect of post-annealling treatment on photoluminescence (PL) properties of the samples under various europium ions doping concentrations were carried out. XRD patterns indicate that the samples show an amorphous matrix structure, and the SEM patterns show that the samples present a multi-hole loosen structure, and a rod structure after high-temperature annealling treatment (800 ℃) for 3 h. Raman spectra demonstrate that Y3+ and Eu3+ ions were incorporated into the composites successfully through the sol-gel and post-anneal process. Under the excitation of 387 nm (7F0→5G2) violet light (but not 394 nm (7F0→5L6)), the strongest emission spectrum, the red light, was observed at around 616 nm (5D0→7F2) when the samples were re-treated by annealing at high temperature after 3 months laying aside. Without annealing treatment, the optimized doping mole ratio of Eu ions is about 9%, which is much higher than that doped in SiOglass with the concentration of 3.5%, and it then becomes 5% when the samples are treated by high temperature annealing. In addition, the excitation of 532 nm (7F0→5D1) light can also arouse a comparatively strong emission.展开更多
文摘New Ge/SiO_2 glasses have been synthesized by heating the GeO_2/SiO_2 dry gels under H_2gas at 700℃. The resulting fluorescence spectra show that this kind of Ge/SiO_2 glasses emit strongphotoluminescence at 392 nm (3.12 eV), medium strong photoluminescence at 600 nm (2.05 eV)and weak photoluminescence at 770 nm (1.60 eV) respectively. Possible photoluminescencemechanisms are also discussed based on the results of X-ray diffraction (XRD) and X-rayphotoelectron spectra(XPS).
文摘Roman scattering measurement of （ 1 - x ） GeS2-x Ga2S3 system glasses was conducted in order to understand the microstructural change caused by the addition of Ga2S3 . According to the change of Raman spectra with the addition of Ga2S3, two main structural transformations were deduced ： the gradual enhancement of ethane- like structural units S3 Ge- GeS3 （ 250 cm ^- 1） and S3 Ga- GaS3 （270 cm ^- 1 ） and the appearance of charge imbalanced units [ Ga2 S2 （ S1/2 ）4 ]^2- and [Ga（ S1/2 ）4 ]^- . And this change of structural aspect seems to give as a clue to understanding the cause of the increased rare-earth solubility.
基金NSFC (50272063)The Sci-Tec Project of Jiangmen City Nanocomposites (2006-10 &No .2007-11)
文摘An improved sol-gel method was used to prepare Eu3+ ions doped SiO-Y2O3 nanocomposites. Systematic study on the effect of post-annealling treatment on photoluminescence (PL) properties of the samples under various europium ions doping concentrations were carried out. XRD patterns indicate that the samples show an amorphous matrix structure, and the SEM patterns show that the samples present a multi-hole loosen structure, and a rod structure after high-temperature annealling treatment (800 ℃) for 3 h. Raman spectra demonstrate that Y3+ and Eu3+ ions were incorporated into the composites successfully through the sol-gel and post-anneal process. Under the excitation of 387 nm (7F0→5G2) violet light (but not 394 nm (7F0→5L6)), the strongest emission spectrum, the red light, was observed at around 616 nm (5D0→7F2) when the samples were re-treated by annealing at high temperature after 3 months laying aside. Without annealing treatment, the optimized doping mole ratio of Eu ions is about 9%, which is much higher than that doped in SiOglass with the concentration of 3.5%, and it then becomes 5% when the samples are treated by high temperature annealing. In addition, the excitation of 532 nm (7F0→5D1) light can also arouse a comparatively strong emission.
基金Project(50974090)supported by the National Natural Science Foundation of ChinaProjects(JCYJ20140418182819155,JCYJ20130329113849606)supported by the Shenzhen Dedicated Funding of Strategic Emerging Industry Development Program,China