Germanium-tin films with rather high Sn content （28.04% and 29.61%） are deposited directly on Si （100） and Si （111） substrates by magnetron sputtering. The mechanism of the effect of rapid thermal annealing on t...Germanium-tin films with rather high Sn content （28.04% and 29.61%） are deposited directly on Si （100） and Si （111） substrates by magnetron sputtering. The mechanism of the effect of rapid thermal annealing on the Sn surface segregation of Ge1-xSnx films is investigated by x-ray photoelectron spectroscopy （XPS） and atomic force microscopy （AFM）. The x-ray diffraction （XRD） is also performed to determine the crystallinities of the Ge1-xSnx films. The experimental results indicate that root mean square （RMS） values of the annealed samples are comparatively small and have no noticeable changes for the as-grown sample when annealing temperature is below 400℃. The diameter of the Sn three-dimensional （3D） island becomes larger than that of an as-grown sample when the annealing temperature is 700℃. In addition, the Sn surface composition decreases when annealing temperature ranges from 400℃ to 700℃. However, Sn bulk compositions in samples A and B are kept almost unchanged when the annealing temperature is below 600℃. The present investigation demonstrates that the crystallinity of Ge1-xSnx/Si （111） has no obvious advantage over that of Ge1-xSnx/Si （100） and the selection of Si （111） substrate is an effective method to improve the surface morphologies of Ge1-xSnx films. We also find that more severe Sn surface segregation occurs in the Ge1-xSnx/Si （111） sample during annealing than in the Ge1-xSnx/Si （100） sample.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.61474085 and 61704130)the Science Research Plan in Shaanxi Province,China(Grant No.2016GY-085)+1 种基金the Opening Project of Key Laboratory of Microelectronic Devices&Integrated Technology,Institute of Microelectronics,Chinese Academy of Sciences(Grant No.90109162905)the Fundamental Research Funds for the Central Universities,China(Grant No.61704130)
文摘Germanium-tin films with rather high Sn content （28.04% and 29.61%） are deposited directly on Si （100） and Si （111） substrates by magnetron sputtering. The mechanism of the effect of rapid thermal annealing on the Sn surface segregation of Ge1-xSnx films is investigated by x-ray photoelectron spectroscopy （XPS） and atomic force microscopy （AFM）. The x-ray diffraction （XRD） is also performed to determine the crystallinities of the Ge1-xSnx films. The experimental results indicate that root mean square （RMS） values of the annealed samples are comparatively small and have no noticeable changes for the as-grown sample when annealing temperature is below 400℃. The diameter of the Sn three-dimensional （3D） island becomes larger than that of an as-grown sample when the annealing temperature is 700℃. In addition, the Sn surface composition decreases when annealing temperature ranges from 400℃ to 700℃. However, Sn bulk compositions in samples A and B are kept almost unchanged when the annealing temperature is below 600℃. The present investigation demonstrates that the crystallinity of Ge1-xSnx/Si （111） has no obvious advantage over that of Ge1-xSnx/Si （100） and the selection of Si （111） substrate is an effective method to improve the surface morphologies of Ge1-xSnx films. We also find that more severe Sn surface segregation occurs in the Ge1-xSnx/Si （111） sample during annealing than in the Ge1-xSnx/Si （100） sample.
