The effects of thickness and types of gold plating on the resistance to hightemperature discoloration of gold plating on cavity surface of ceramic package were investigated. Itwas found that the thicker gold plating, ...The effects of thickness and types of gold plating on the resistance to hightemperature discoloration of gold plating on cavity surface of ceramic package were investigated. Itwas found that the thicker gold plating, the less discoloration degree for ceramic packages.Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide goldplating. The relationship between the gold plating thickness and the amount of diffused Ni to thegold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃ for 15 minwas also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Coplating systems, respectively, no discoloration was observed on the gold plating surface of cavity,and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Coto the gold plating is 0.04%.展开更多
The effects of thickness and types of gold plating on the resistance to high temperature discoloration of gold plating on cavity surface of ceramic package were investigated. It was found that the thicker gold plating...The effects of thickness and types of gold plating on the resistance to high temperature discoloration of gold plating on cavity surface of ceramic package were investigated. It was found that the thicker gold plating, the less discoloration degree for ceramic packages. Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide gold plating. The relationship between the gold plating thickness and the amount of diffused Ni to the gold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃for 15 min was also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Co plating systems, respectively, no discoloration was observed on the gold plating surface of cavity, and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Co to the gold plating is 0.04%.展开更多
The use of more and more electron products requires interior wood products to have the performance of electromagnetic shielding. One of the ways to realize it is to introduce the chemical plating which has already bee...The use of more and more electron products requires interior wood products to have the performance of electromagnetic shielding. One of the ways to realize it is to introduce the chemical plating which has already been developed in electron industry into wood processing. The paper clarifies the mechanism of electroless copper and gold plating and its application to wood. It emphasizes the development and technology of electroless copper and gold plating on wood. Meanwhile, it points out that it is highly feasible to take this technology into effect.展开更多
Two small-size package methods, thin stainless steel tube based package method and plating gold based package method for fiber Bragg grating(FBG) temperature sensors, are designed. The characteristics of the FBG tempe...Two small-size package methods, thin stainless steel tube based package method and plating gold based package method for fiber Bragg grating(FBG) temperature sensors, are designed. The characteristics of the FBG temperature sensors in the environment temperature between 203K and 243K are investigated. The wavelengths of the FBG temperature sensors as a function of the temperature are examined experimentally. The experiment results of the two different small-size package sensors in identical conditions are compared with each other. The transmission spectrum of the sensors is analyzed at the temperature of 273K and 213K. The temperature sensitive factors of the sensors are derived analytically and are verified by experiments. Linear fitting to the wavelength-temperature curve is carried out.展开更多
文摘The effects of thickness and types of gold plating on the resistance to hightemperature discoloration of gold plating on cavity surface of ceramic package were investigated. Itwas found that the thicker gold plating, the less discoloration degree for ceramic packages.Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide goldplating. The relationship between the gold plating thickness and the amount of diffused Ni to thegold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃ for 15 minwas also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Coplating systems, respectively, no discoloration was observed on the gold plating surface of cavity,and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Coto the gold plating is 0.04%.
文摘The effects of thickness and types of gold plating on the resistance to high temperature discoloration of gold plating on cavity surface of ceramic package were investigated. It was found that the thicker gold plating, the less discoloration degree for ceramic packages. Non-cyanide gold plating performed better resistance to high-temperature aging than cyanide gold plating. The relationship between the gold plating thickness and the amount of diffused Ni to the gold plating of ceramic packages with Au/Ni and Au/Ni-Co platings after heating at 420℃for 15 min was also studied. When the gold plating thickness reach 2.0 μm and 1.6 μm for Au/Ni and Au/Ni-Co plating systems, respectively, no discoloration was observed on the gold plating surface of cavity, and the corresponding diffused Ni amounts (mass fraction) are 1.0% and 0.4%, while the diffused Co to the gold plating is 0.04%.
文摘The use of more and more electron products requires interior wood products to have the performance of electromagnetic shielding. One of the ways to realize it is to introduce the chemical plating which has already been developed in electron industry into wood processing. The paper clarifies the mechanism of electroless copper and gold plating and its application to wood. It emphasizes the development and technology of electroless copper and gold plating on wood. Meanwhile, it points out that it is highly feasible to take this technology into effect.
基金National Natural Science Foundation of China(50179029)
文摘Two small-size package methods, thin stainless steel tube based package method and plating gold based package method for fiber Bragg grating(FBG) temperature sensors, are designed. The characteristics of the FBG temperature sensors in the environment temperature between 203K and 243K are investigated. The wavelengths of the FBG temperature sensors as a function of the temperature are examined experimentally. The experiment results of the two different small-size package sensors in identical conditions are compared with each other. The transmission spectrum of the sensors is analyzed at the temperature of 273K and 213K. The temperature sensitive factors of the sensors are derived analytically and are verified by experiments. Linear fitting to the wavelength-temperature curve is carried out.