A slurry dip-coating technique was developed for fabrication of Zr02/Mo-Si/Ni functionally graded material (FGM)on the stainless steel substrate. The rheological behavior of ZrO2-Ni-ethanol slurry was characterized by...A slurry dip-coating technique was developed for fabrication of Zr02/Mo-Si/Ni functionally graded material (FGM)on the stainless steel substrate. The rheological behavior of ZrO2-Ni-ethanol slurry was characterized by viscositytest. The amount of polyvinyl butyral (PVB) additives, which served as the dispersant and binder in ZrO2-Ni-ethanolslurry, was optimized. The results showed that the characters of mixed slurries with added 9 vol. pct (relativelyto total powders) MoSi2 powders prepared by mechanical alloying changed little. The stainless steel substrate wascoated several times by dipping in the slurries, and followed by drying in air every dipping. After debinding in Arin graphite die, the coated FGM plate was finally hot pressed at 1300℃ for 1 h under the pressure of 5 MPa in Arin the same die. Microstructural observations of the sintered FGM specimens revealed that the graded layers wereformed on the stainless steel substrate, in which no cracks were observed.展开更多
X-ray fluorescence （XRF） in combination with partial least-squares （PLS） regression was employed to analyze the ore slurry grade. Using the Monte Carlo simulation code PENELOPE, X-ray fluorescence spectra of ore s...X-ray fluorescence （XRF） in combination with partial least-squares （PLS） regression was employed to analyze the ore slurry grade. Using the Monte Carlo simulation code PENELOPE, X-ray fluorescence spectra of ore samples were obtained. Good accuracy was achieved when this method was used to analyze elements with concentrations of several percent or above. It was demonstrated that the more the number of X-ray fluorescence spectra used to calibrate, the better the obtained accuracy. In this method detector resolution was found to have little or no effect on the results of quantitative analysis. The effect of the concentration of water was investigated as well, and it was found to have little influence on the results.展开更多
文摘A slurry dip-coating technique was developed for fabrication of Zr02/Mo-Si/Ni functionally graded material (FGM)on the stainless steel substrate. The rheological behavior of ZrO2-Ni-ethanol slurry was characterized by viscositytest. The amount of polyvinyl butyral (PVB) additives, which served as the dispersant and binder in ZrO2-Ni-ethanolslurry, was optimized. The results showed that the characters of mixed slurries with added 9 vol. pct (relativelyto total powders) MoSi2 powders prepared by mechanical alloying changed little. The stainless steel substrate wascoated several times by dipping in the slurries, and followed by drying in air every dipping. After debinding in Arin graphite die, the coated FGM plate was finally hot pressed at 1300℃ for 1 h under the pressure of 5 MPa in Arin the same die. Microstructural observations of the sintered FGM specimens revealed that the graded layers wereformed on the stainless steel substrate, in which no cracks were observed.
基金supported by the Ministry of Science and Technology of China (No.2008EG130243)
文摘X-ray fluorescence （XRF） in combination with partial least-squares （PLS） regression was employed to analyze the ore slurry grade. Using the Monte Carlo simulation code PENELOPE, X-ray fluorescence spectra of ore samples were obtained. Good accuracy was achieved when this method was used to analyze elements with concentrations of several percent or above. It was demonstrated that the more the number of X-ray fluorescence spectra used to calibrate, the better the obtained accuracy. In this method detector resolution was found to have little or no effect on the results of quantitative analysis. The effect of the concentration of water was investigated as well, and it was found to have little influence on the results.