Photo-grafting of hydrophilic monomer was used to enhance the hydrophilicity of poly(ether ether ketone) (PEEK) with the aim of extending its applications to biological fields. PEEK sheets were surface modified by...Photo-grafting of hydrophilic monomer was used to enhance the hydrophilicity of poly(ether ether ketone) (PEEK) with the aim of extending its applications to biological fields. PEEK sheets were surface modified by grafting of acrylamide(AAm) with ultraviolet(UV) irradiation in the presence or absence of benzophenone(BP). The effects of BP, irradiation time and monomer concentration on the surface wettability of PEEK were investigated. Characteriza tion of modified PEEK using scanning electron microscopy(SEM), energy-disperse spectrometer(EDS) and water contact angle measurements shows that AAm was successfully grafted on PEEK surface both in presence and absence of BP. With the increase in irradiation time and monomer concentration, contact angles decrease to as low as 30°, demonstrating a significant improvement of surface hydrophilicity. In agreement with the decrease in contact angle, under identical conditions, the nitrogen concentration increases, suggesting the increase in grafting degree of the grafting polymerization. This investigation demonstrates a self-initiation of PEEK due to its BP-like structure in the backbone of the polymer. Though the graft polymerization proceeds more readily in the presence of BP, the self-initiated graft polymerization is clearly observed.展开更多
Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer co...Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.展开更多
Ultraviolet (UV)-induced graft polymerization of acrylamide (AAm) on polypropylene substrates was successfully conducted using dibenzyl trithiocarbonate (DBTTC) as photoinitiator. It was confirmed by chemical an...Ultraviolet (UV)-induced graft polymerization of acrylamide (AAm) on polypropylene substrates was successfully conducted using dibenzyl trithiocarbonate (DBTTC) as photoinitiator. It was confirmed by chemical analysis and surface morphology observation with attenuated total reflectance Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy. A possible mechanism for this graft process was presented, which suggested that, under UV irradiation, the C: S bond in DBTTC could split and abstract a hydrogen from the polypropylene surface and a surface free radical was then formed, and initiated the graft polymerization of AAm.展开更多
By dynamic method under UV irradiation, commercial melt-blown polypropylene (PPMB) filter element was modified with acrylamide (AAm) using benzophenone (BP) as initiator. Attenuated total reflection-Fourier tran...By dynamic method under UV irradiation, commercial melt-blown polypropylene (PPMB) filter element was modified with acrylamide (AAm) using benzophenone (BP) as initiator. Attenuated total reflection-Fourier transform infrared spectroscopy and scanning electron microscope verified that polyacrylamide chain was grafted on the fiber surface of PPMB filter element. Elemental content analysis with energy dispersive X-ray of fibers revealed that the polymerization content in the inner part of filter element was relatively higher than that in the outer. Degree of grafting changed with initiator concentration, monomer concentration, reaction temperature and reached 2.6% at the reaction condition: CBp=0.06 mol/L, CAAm=2.0 mol/L, irradiation time: 80 min, temperature: 60℃. Relative water flux altered with the hydrophilicity and pore size of filter element. In the antifouling test, the modified filter gave greater flux recovery (approximately 70%) after filtration of the water extract of Liuweidihuang, suggesting that the fouling layer was more easily reversible due to the hydrophilic nature of the modified filter.展开更多
Durable superomniphobic surfaces are desirable for their practical applications,including selfcleaning,non-fouling,protective clothing and the separation of liquids.The plasma-induced polymerization of environmentally...Durable superomniphobic surfaces are desirable for their practical applications,including selfcleaning,non-fouling,protective clothing and the separation of liquids.The plasma-induced polymerization of environmentally friendly C6 from a perfluoralkyl methlacrylate copolymer emulsion,AG-E081,was performed and a durable omniphobic fabric was achieved.C6 is an ecological alternative to C8(eight CF2 groups)fluorinated compounds,and it was thereafter successfully incorporated into aramid fabric to achieve a durable superomniphobic surface.The fabric became water and oil repellent with an extremely high water contact angle of 180°.As tested by the water spray AATCC test and hydrocarbon resistance test,the as-prepared fabric gained 100°(ISO 5)and grade number 4 respectively.Furthermore,the fabrics also showed significantly improved washing durability after ten washing cycles.By scanning electron microscopy(SEM),Fourier-transform infrared spectroscopy(FTIR)and x-ray photoelectron spectroscopy(XPS)tests,it is indicated that the durable superomniphobicity can be attributed to the roughness and activation of the aramid surface by the plasma pre-treatment,which induces more adsorption and chemical graft of the C6 copolymer.展开更多
The graft polymerization of acrylic acid(A) and acrylamide(B) was carried out onto bi-oriented polyester BOPET corona film.The influence of monomer concentration,reducer concentration and reaction time on the graft po...The graft polymerization of acrylic acid(A) and acrylamide(B) was carried out onto bi-oriented polyester BOPET corona film.The influence of monomer concentration,reducer concentration and reaction time on the graft polymerization was investigated.The surface tension of the films increased with an increase of monomer concentration,till the concentration of monomer A reached 1.5×10^(-2)g/mL and the concentration of monomer B reached 4.0×10^(-2)g/mL.The surface tension of the films reached a maximum value at 7×10^(-4)M of reducer concentration and subsequently decreased with further increase in reducer concentration.The surface tension of the films increased with the increase of the reaction time apparently within 50min.The grafted corona BOPET films were characterized with IR and XPS.The presence of graft on the film surface was confirmed.The attenuation experiments on grafted corona BOPET films in air at 50℃ and in water were carried out to investigate the persistence of graft polymerization of acrylic acid and arylamide onto BOPET corona films.展开更多
The homopolymerization of 5-methyl-5-hexen-2,4-dione (methacryloylacetone, MAA), a vinyl monomer having beta-diketone group, was carried out in the presence of benzophenone (BP)/N, N-dimenthyl-4-toluidine (DMT) system...The homopolymerization of 5-methyl-5-hexen-2,4-dione (methacryloylacetone, MAA), a vinyl monomer having beta-diketone group, was carried out in the presence of benzophenone (BP)/N, N-dimenthyl-4-toluidine (DMT) system. Graft polymerization of acrylamide initiated by eerie ion onto the homopolymer film was investigated and the mechanism of the grafting reaction was proposed on the basis of ESR study. The grafted copolymer was characterized by means of grafting percentage, water absorption, XPS spectra and scanning electron photomicrographs.展开更多
Methyl methacrylate (MMA) was successfully grafted onto cellulose nanofibers (CNFs) at room temperature in an emulsion system using a diethyl(1,10-<span style="font-family:;" "=""><sp...Methyl methacrylate (MMA) was successfully grafted onto cellulose nanofibers (CNFs) at room temperature in an emulsion system using a diethyl(1,10-<span style="font-family:;" "=""><span style="font-family:Verdana;">phenanthroline </span><i><span style="font-family:Verdana;">N</span></i><sub><span style="font-family:Verdana;">1</span></sub><span style="font-family:Verdana;">,</span><i><span style="font-family:Verdana;">N</span></i><sub><span style="font-family:Verdana;">10</span></sub><span style="font-family:Verdana;">)zinc(</span></span><span style="font-family:Verdana;">II</span><span style="font-family:Verdana;">) complex (Phen</span><span style="font-family:Verdana;">-</span><span style="font-family:Verdana;">DEZ) with oxygen as the radical initiator. The effects of reaction temperature, initiator concentration, and monomer content on the grafting reaction were investigated. The molecular weight of the non-grafted PMMA, which was produced during graft polymerization, was more than 1 million, as determined by size exclusion chromatography. The PMMA-grafted CNFs were analyzed by Fourier transform infrared spectroscopy, thermogravimetric analysis, and scanning electron microscopy, which confirmed the grafting of PMMA on the nanofiber surface. The study presents a strategy for the grafting of high-molecular weight PMMA onto CNFs in an emulsion system</span><span style="font-family:Verdana;"> using</span><span> Phen</span><span>-</span><span><span>DEZ and</span></span><span><span> O</span><sub><span>2</span></sub><span>.</span></span>展开更多
Grafting of poly(methyl methacrylate)from narrow disperse polymer particles by surface-initiated atom transferradical polymerization(ATRP)was investigated.Polydivinylbenzene(PDVB)particles were prepared by dispersionp...Grafting of poly(methyl methacrylate)from narrow disperse polymer particles by surface-initiated atom transferradical polymerization(ATRP)was investigated.Polydivinylbenzene(PDVB)particles were prepared by dispersionpolymerization with poly(N-vinyl pyrrolidone)(PVP)as the stabilizer.Chloromethylated PDVB was used as initiating coresites for subsequent ATRP of methyl methacrylate with CuBr/bpy as catalyst system.It was found that poly(methylmethacrylate)was grafted not only from the particle surfaces but also from within a thin shell layer,leading to particles sizeincreases from 2.38-3.00 μm with a core-shell structure particles.The grafted core-shell particles were characterized withFTIR,SEM,DSC.展开更多
This work aimed at investigating the feasibility of surface modification of cellulose nanocrystals (CNCs) using <em>in situ</em> ring opening polymerization of <em>ε</em>-caprolactone (<em&...This work aimed at investigating the feasibility of surface modification of cellulose nanocrystals (CNCs) using <em>in situ</em> ring opening polymerization of <em>ε</em>-caprolactone (<em>ε</em>-CL) at room temperature. Residues of flax and milkweed (<em>Asclepias syriaca</em>) stem fibers were used as a source of cellulose to obtain and isolate CNCs. The cationic ring opening polymerization (CROP) of the monomer <em>ε</em>-CL was used to covalently graft polycaprolactone (PCL) chains at the CNCs surface. Silver hexafluoroantimonate (AgSbF<sub>6</sub>) was used in combination with the extracted CNCs to initiate, at room temperature, the polymerization and the grafting reactions with no other stimulus. Fourier-Transform InfraRed (FTIR), X-ray Photoelectron Spectrometry (XPS), UV/visible absorption and Gel Permeation Chromatography (GPC) analyses evidenced the presence of PCL chains covalently grafted at CNCs surface, the formation of Ag(0) particles as well as low or moderate molecular weight free PCL chains.展开更多
Membrane fouling is one of the most important challenges faced in membrane ultrafiltration operations. The copolymers of polysulfone-graft-methyl acrylate were synthesized by homogeneous photo-initiated graft copolyme...Membrane fouling is one of the most important challenges faced in membrane ultrafiltration operations. The copolymers of polysulfone-graft-methyl acrylate were synthesized by homogeneous photo-initiated graft copolymerization. The variables affecting the degree of grafting, such as the time of UV (Ultraviolet-visible) irradiation and the concentrations of the methyl acrylate and photoinitiator, were investigated. The graft copolymer membranes were prepared by the phase inversion method. The chemical and morphological changes were characterized by attenuated total reflection-Fourier transform infrared spectroscopy (ATR/FT-IR), scanning electron microscopy, and water contact angles measurements. Results revealed that methyl acrylate groups were present on the membranes and the graft degree of methyl acrylate had remarkable effect on the performance of membranes. Pure water contact angle on the membrane surface decreases with the increase of methyl acrylate graft degree, which indicated that the hydrophilicity of graft copolymer membranes was improved. The permeation fluxes of pure water and bovine serum albumin solution were measured to evaluate the antifouling property of graft copolymer membranes, the results of which have shown an enhancement of antifouling property for graft copolymer membranes.展开更多
Grafting of polymer of methyl methacrylate (PMMA) onto titanium dioxide powder is investigated in this paper. The graft polymerization reaction is induced by dielectric-barrier- discharge produced N2 plasma treatmen...Grafting of polymer of methyl methacrylate (PMMA) onto titanium dioxide powder is investigated in this paper. The graft polymerization reaction is induced by dielectric-barrier- discharge produced N2 plasma treatment of titanium dioxide surfaces. IR, XPS and TGA results show that PMMA is grafted onto the surfaces of titanium dioxide powder. And crystal structure of the titanium dioxide powder observed with XRD spectra is unchanged after plasma graft polymerization.展开更多
Poly(ethylene glycol) methyl ether methacrylate(PEGMA) was grafted on fluorosilicone acrylate rigid gas permissible contact lens surface by means of argon plasma induced polymerization to improve surface hydrophil...Poly(ethylene glycol) methyl ether methacrylate(PEGMA) was grafted on fluorosilicone acrylate rigid gas permissible contact lens surface by means of argon plasma induced polymerization to improve surface hydrophilicity and reduce protein adsorption.The surface properties were characterized by contact angle measurement,x-ray photoelectron spectroscopy(XPS) and atomic force microscopy respectively.The surface protein adsorption was evaluated by lysozyme solution immersion and XPS analysis.The results indicated that a thin layer of PEGMA was successfully grafted.The surface hydrophilicity was bettered and surface free energy increased.The lysozyme adsorption on the lens surface was reduced greatly.展开更多
A new process for lamination of polymer films by 'bulk surface photografting' has been developed. The chemical component of the invention is that the curing of reactive solution between two substrates is initi...A new process for lamination of polymer films by 'bulk surface photografting' has been developed. The chemical component of the invention is that the curing of reactive solution between two substrates is initiated by the surface free radicals produced by aromatic ketones and surface-hydrogen of substrates. Using the new approach, two or more polymer films are bonded together by a grafted polymer network which is grafted to adjacent substrate surfaces. The technique has been applied to film substrates of different polymers such as polyolefins, polyesters, and polyamides which have abstractable hydrogens at the surface. The photolaminated film composites containing carrier films and an intermediate functional film of low permeability give strong laminates with high barrier properties, e.g, for oxygen and air.展开更多
Spherical polyethylene/polypropylene (PE/PP) in-reactor blend granules with various ethylene/propylene molar ratios and high porosity were synthesized using a high yield TiCVMgCl2 supported catalyst. A solution of ben...Spherical polyethylene/polypropylene (PE/PP) in-reactor blend granules with various ethylene/propylene molar ratios and high porosity were synthesized using a high yield TiCVMgCl2 supported catalyst. A solution of benzoyl peroxide (BPO)/maleic anhydride (MAH)/xylene (interfacial reagent) or BPO/MAH/St (comonomer) was absorbed onto the PE/PP in- reactor blend granules, and solid phase graft polymerization of MAH on PE/PP was conducted. The amount of grafted MAH on PE/PP was measured through chemical titration. The results showed that solid phase graft polymerization of MAH in PE/PP in-reactor blend granules produced graft copolymer with high amount of grafted MAH, and the amount of grafted MAH was raised slightly when St was introduced as comonomer. The graft in-reactor blend was fractionated into five fractions through temperature-gradient extraction fractionation (TGEF), and the fractions were analyzed by FTIR. The results revealed that MAH is mainly grafted on the PE segments, whereas MAH was predominantly grafted on the PP segments when St was present in the graft polymerization system. In addition, the final product is still in the form of regular spherical granules, which is beneficial for industrial processing.展开更多
Grafting of polystyrene (PS) onto titanium dioxide powder was investigated. The graft polymerization reaction was induced by high frequency discharge produced N2 plasma treatment of the surfaces of titanium dioxide....Grafting of polystyrene (PS) onto titanium dioxide powder was investigated. The graft polymerization reaction was induced by high frequency discharge produced N2 plasma treatment of the surfaces of titanium dioxide. IR, XPS and TGA results show that PS was grafted on the titanium dioxide powder. And the crystal structure of the titanium dioxide powder observed by XRD was unchanged after plasma treatment.展开更多
An irradiation grafting method was applied for the modification of nanoparticles so that the latter can be added topolymeric materials for improving their mechanical performance using existing compounding techniques. ...An irradiation grafting method was applied for the modification of nanoparticles so that the latter can be added topolymeric materials for improving their mechanical performance using existing compounding techniques. The followingitems are discussed in this paper: (a) chemical interaction between the grafting monomers and the nanoparticles duringirradiation, (b) properties including modulus, yield strength, impact strength and fracture toughness of the resultantcomposites, and (c) possible morphological changes induced by the addition of nanoparticles. Though irradiation graftingpolymerization, nanoparticle agglomerates turn into a nano-composite microstructure (comprised of the nanoparticles and thegrafted, homopolymerized secondary polymer), which in turn builds up a strong interfacial interaction with the surrounding,primary polymeric matrix during the subsequent mixing procedure. Due to the fact that different grafting polymers broughtabout different nanoparticle/matrix interfacial features, microstructures and properties of the ultimate composites could thusbe tailored. It was found that the reinforcing and toughening effects of the nanoparticles on the polymer matrix can be fullybrought into play at a rather low filler loading in comparison to conventional particulate filled composites.展开更多
An investigation of grafting of polymer of styrene (PSt) onto titanium dioxide powder is reported in this paper. The graft polymerization reaction was induced by N2 plasma treatment on the surface of titanium dioxid...An investigation of grafting of polymer of styrene (PSt) onto titanium dioxide powder is reported in this paper. The graft polymerization reaction was induced by N2 plasma treatment on the surface of titanium dioxide. Infrared (IR) spectra and X-ray photospectrum (XPS) results showed that PSt was grafted onto the titanium dioxide powder. An observation by X-ray diffraction (XRD) spectra indicated that the crystal structure of the titanium dioxide powder was unchanged after the plasma treatment.展开更多
In this paper the suitability of a graft polymer nanocomposite hydrogel system for enhanced oil recovery was examined using polyacrylamide graft starch/clay nanocomposite(a laboratory synthesized product) and chromium...In this paper the suitability of a graft polymer nanocomposite hydrogel system for enhanced oil recovery was examined using polyacrylamide graft starch/clay nanocomposite(a laboratory synthesized product) and chromium(III) acetate(crosslinker). X-ray diffraction analysis,Fourier transform infrared spectrometry analysis, field-emission scanning electron microscopy and transmission electron microscopy were carried out to reveal the laboratory synthesized product as a nanocomposite. The effects of various parameters like salt concentration, p H, temperature, polymer concentration and crosslinker concentration on the properties of the developed gel system were systematically evaluated.The thermal stability of the nanocomposite gel and the conventional gel system were also determined by thermogravimetric analysis. The graft polymer nanocomposite gel system exhibited acceptable gel strength, gelation time and gel stability compared with the conventional gel system. The nanocomposite gels prepared using a low crosslinker concentration showed higher gel strength and required longer gelation time than the conventional gel which is more desirable properties for the effective placement of gel during enhanced oil recovery operations. In addition, sand pack flooding experiments show that the graft polymer nanocomposite gels had better plugging capacity than the conventional gel systems under reservoir conditions. Hence, this gel system may be suitable in the water shutoff treatments required for enhanced oil recovery from oilfields.展开更多
基金Supported by the Scientific and Technological Development Programs of Beijing Municipal Education Commission, China (No.KM201010011004)the Scientific Research Foundation for the Returned Overseas Chinese Scholars, Ministry of Education, China, the 2011 Merit-based Research Funding for Picked Returned Overseas Scholars, Beijing Municipality, ChinaBeijing Technology and Business University Through a Research Project Approved for Undergraduates
文摘Photo-grafting of hydrophilic monomer was used to enhance the hydrophilicity of poly(ether ether ketone) (PEEK) with the aim of extending its applications to biological fields. PEEK sheets were surface modified by grafting of acrylamide(AAm) with ultraviolet(UV) irradiation in the presence or absence of benzophenone(BP). The effects of BP, irradiation time and monomer concentration on the surface wettability of PEEK were investigated. Characteriza tion of modified PEEK using scanning electron microscopy(SEM), energy-disperse spectrometer(EDS) and water contact angle measurements shows that AAm was successfully grafted on PEEK surface both in presence and absence of BP. With the increase in irradiation time and monomer concentration, contact angles decrease to as low as 30°, demonstrating a significant improvement of surface hydrophilicity. In agreement with the decrease in contact angle, under identical conditions, the nitrogen concentration increases, suggesting the increase in grafting degree of the grafting polymerization. This investigation demonstrates a self-initiation of PEEK due to its BP-like structure in the backbone of the polymer. Though the graft polymerization proceeds more readily in the presence of BP, the self-initiated graft polymerization is clearly observed.
基金The work was supported by the National Natural Science Foundation of China (Grant No. 20074033) and the High-TechResearch and Development Program of China (Grant no. 2002AA601230).
文摘Surface modification of microporous polypropylene hollow fiber membranes was performed by radical-induced graft polymerization of N,N-dimethylaminoethyl methacrylate (DMAEMA). The influences of temperature, monomer concentration and pre-adsorbed amount of benzoyl peroxide on grafting degree were studied respectively. It was found that the appropriate graft temperature was 75 'C, at which the grafting degree was the highest and the hydrolytic decomposition of DMAEMA the lowest. Scanning electron photomicrography and the average pore diameters of the modified membranes demonstrated that part of the micropores on the membrane surface was plugged by the grafted polyDMAEMA chains, especially at high grafting degree. Contact angle and water swelling experiments showed that a moderate grafting degree could improve the hydrophilicity of the membranes. In the range of 11.3%-12.0% grafting degree, the water swelling percentage reached its maximum (51.1%) and the contact angle reached its minimum (74 degrees). The bovine serum albumin (BSA) adsorption experiment indicated that the grafted polyDMAEMA had a dual effect on protein adsorption. At the first stage, the BSA adsorption decreased with increasing of DMAEMA grafting degree. As the interaction between BSA and polyDMAEMA on membrane surface increased, the BSA adsorption increased with increasing of DMAEMA grafting degree.
基金This work was financed by the National Natural Science Foundation of China(No. 20474054).
文摘Ultraviolet (UV)-induced graft polymerization of acrylamide (AAm) on polypropylene substrates was successfully conducted using dibenzyl trithiocarbonate (DBTTC) as photoinitiator. It was confirmed by chemical analysis and surface morphology observation with attenuated total reflectance Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy. A possible mechanism for this graft process was presented, which suggested that, under UV irradiation, the C: S bond in DBTTC could split and abstract a hydrogen from the polypropylene surface and a surface free radical was then formed, and initiated the graft polymerization of AAm.
基金Project supported by the Natural Science Foundation of Beijing(No.2051002)Science and Technology Programme of Beijing(No.D0205004040421)
文摘By dynamic method under UV irradiation, commercial melt-blown polypropylene (PPMB) filter element was modified with acrylamide (AAm) using benzophenone (BP) as initiator. Attenuated total reflection-Fourier transform infrared spectroscopy and scanning electron microscope verified that polyacrylamide chain was grafted on the fiber surface of PPMB filter element. Elemental content analysis with energy dispersive X-ray of fibers revealed that the polymerization content in the inner part of filter element was relatively higher than that in the outer. Degree of grafting changed with initiator concentration, monomer concentration, reaction temperature and reached 2.6% at the reaction condition: CBp=0.06 mol/L, CAAm=2.0 mol/L, irradiation time: 80 min, temperature: 60℃. Relative water flux altered with the hydrophilicity and pore size of filter element. In the antifouling test, the modified filter gave greater flux recovery (approximately 70%) after filtration of the water extract of Liuweidihuang, suggesting that the fouling layer was more easily reversible due to the hydrophilic nature of the modified filter.
基金supported by the Fundamental Research Funds for the Central Universities 2232019A3-12National Natural Science Foundation of China(No.11375042)。
文摘Durable superomniphobic surfaces are desirable for their practical applications,including selfcleaning,non-fouling,protective clothing and the separation of liquids.The plasma-induced polymerization of environmentally friendly C6 from a perfluoralkyl methlacrylate copolymer emulsion,AG-E081,was performed and a durable omniphobic fabric was achieved.C6 is an ecological alternative to C8(eight CF2 groups)fluorinated compounds,and it was thereafter successfully incorporated into aramid fabric to achieve a durable superomniphobic surface.The fabric became water and oil repellent with an extremely high water contact angle of 180°.As tested by the water spray AATCC test and hydrocarbon resistance test,the as-prepared fabric gained 100°(ISO 5)and grade number 4 respectively.Furthermore,the fabrics also showed significantly improved washing durability after ten washing cycles.By scanning electron microscopy(SEM),Fourier-transform infrared spectroscopy(FTIR)and x-ray photoelectron spectroscopy(XPS)tests,it is indicated that the durable superomniphobicity can be attributed to the roughness and activation of the aramid surface by the plasma pre-treatment,which induces more adsorption and chemical graft of the C6 copolymer.
文摘The graft polymerization of acrylic acid(A) and acrylamide(B) was carried out onto bi-oriented polyester BOPET corona film.The influence of monomer concentration,reducer concentration and reaction time on the graft polymerization was investigated.The surface tension of the films increased with an increase of monomer concentration,till the concentration of monomer A reached 1.5×10^(-2)g/mL and the concentration of monomer B reached 4.0×10^(-2)g/mL.The surface tension of the films reached a maximum value at 7×10^(-4)M of reducer concentration and subsequently decreased with further increase in reducer concentration.The surface tension of the films increased with the increase of the reaction time apparently within 50min.The grafted corona BOPET films were characterized with IR and XPS.The presence of graft on the film surface was confirmed.The attenuation experiments on grafted corona BOPET films in air at 50℃ and in water were carried out to investigate the persistence of graft polymerization of acrylic acid and arylamide onto BOPET corona films.
基金The project was supported by the National Natural Science Foundation of Chna.
文摘The homopolymerization of 5-methyl-5-hexen-2,4-dione (methacryloylacetone, MAA), a vinyl monomer having beta-diketone group, was carried out in the presence of benzophenone (BP)/N, N-dimenthyl-4-toluidine (DMT) system. Graft polymerization of acrylamide initiated by eerie ion onto the homopolymer film was investigated and the mechanism of the grafting reaction was proposed on the basis of ESR study. The grafted copolymer was characterized by means of grafting percentage, water absorption, XPS spectra and scanning electron photomicrographs.
文摘Methyl methacrylate (MMA) was successfully grafted onto cellulose nanofibers (CNFs) at room temperature in an emulsion system using a diethyl(1,10-<span style="font-family:;" "=""><span style="font-family:Verdana;">phenanthroline </span><i><span style="font-family:Verdana;">N</span></i><sub><span style="font-family:Verdana;">1</span></sub><span style="font-family:Verdana;">,</span><i><span style="font-family:Verdana;">N</span></i><sub><span style="font-family:Verdana;">10</span></sub><span style="font-family:Verdana;">)zinc(</span></span><span style="font-family:Verdana;">II</span><span style="font-family:Verdana;">) complex (Phen</span><span style="font-family:Verdana;">-</span><span style="font-family:Verdana;">DEZ) with oxygen as the radical initiator. The effects of reaction temperature, initiator concentration, and monomer content on the grafting reaction were investigated. The molecular weight of the non-grafted PMMA, which was produced during graft polymerization, was more than 1 million, as determined by size exclusion chromatography. The PMMA-grafted CNFs were analyzed by Fourier transform infrared spectroscopy, thermogravimetric analysis, and scanning electron microscopy, which confirmed the grafting of PMMA on the nanofiber surface. The study presents a strategy for the grafting of high-molecular weight PMMA onto CNFs in an emulsion system</span><span style="font-family:Verdana;"> using</span><span> Phen</span><span>-</span><span><span>DEZ and</span></span><span><span> O</span><sub><span>2</span></sub><span>.</span></span>
基金This work was supported by the National Natural Science Foundation of China(No.20274018)Nankai University for their partly financial.
文摘Grafting of poly(methyl methacrylate)from narrow disperse polymer particles by surface-initiated atom transferradical polymerization(ATRP)was investigated.Polydivinylbenzene(PDVB)particles were prepared by dispersionpolymerization with poly(N-vinyl pyrrolidone)(PVP)as the stabilizer.Chloromethylated PDVB was used as initiating coresites for subsequent ATRP of methyl methacrylate with CuBr/bpy as catalyst system.It was found that poly(methylmethacrylate)was grafted not only from the particle surfaces but also from within a thin shell layer,leading to particles sizeincreases from 2.38-3.00 μm with a core-shell structure particles.The grafted core-shell particles were characterized withFTIR,SEM,DSC.
文摘This work aimed at investigating the feasibility of surface modification of cellulose nanocrystals (CNCs) using <em>in situ</em> ring opening polymerization of <em>ε</em>-caprolactone (<em>ε</em>-CL) at room temperature. Residues of flax and milkweed (<em>Asclepias syriaca</em>) stem fibers were used as a source of cellulose to obtain and isolate CNCs. The cationic ring opening polymerization (CROP) of the monomer <em>ε</em>-CL was used to covalently graft polycaprolactone (PCL) chains at the CNCs surface. Silver hexafluoroantimonate (AgSbF<sub>6</sub>) was used in combination with the extracted CNCs to initiate, at room temperature, the polymerization and the grafting reactions with no other stimulus. Fourier-Transform InfraRed (FTIR), X-ray Photoelectron Spectrometry (XPS), UV/visible absorption and Gel Permeation Chromatography (GPC) analyses evidenced the presence of PCL chains covalently grafted at CNCs surface, the formation of Ag(0) particles as well as low or moderate molecular weight free PCL chains.
文摘Membrane fouling is one of the most important challenges faced in membrane ultrafiltration operations. The copolymers of polysulfone-graft-methyl acrylate were synthesized by homogeneous photo-initiated graft copolymerization. The variables affecting the degree of grafting, such as the time of UV (Ultraviolet-visible) irradiation and the concentrations of the methyl acrylate and photoinitiator, were investigated. The graft copolymer membranes were prepared by the phase inversion method. The chemical and morphological changes were characterized by attenuated total reflection-Fourier transform infrared spectroscopy (ATR/FT-IR), scanning electron microscopy, and water contact angles measurements. Results revealed that methyl acrylate groups were present on the membranes and the graft degree of methyl acrylate had remarkable effect on the performance of membranes. Pure water contact angle on the membrane surface decreases with the increase of methyl acrylate graft degree, which indicated that the hydrophilicity of graft copolymer membranes was improved. The permeation fluxes of pure water and bovine serum albumin solution were measured to evaluate the antifouling property of graft copolymer membranes, the results of which have shown an enhancement of antifouling property for graft copolymer membranes.
文摘Grafting of polymer of methyl methacrylate (PMMA) onto titanium dioxide powder is investigated in this paper. The graft polymerization reaction is induced by dielectric-barrier- discharge produced N2 plasma treatment of titanium dioxide surfaces. IR, XPS and TGA results show that PMMA is grafted onto the surfaces of titanium dioxide powder. And crystal structure of the titanium dioxide powder observed with XRD spectra is unchanged after plasma graft polymerization.
基金supported by National Natural Science Foundation of China(No.51273072)
文摘Poly(ethylene glycol) methyl ether methacrylate(PEGMA) was grafted on fluorosilicone acrylate rigid gas permissible contact lens surface by means of argon plasma induced polymerization to improve surface hydrophilicity and reduce protein adsorption.The surface properties were characterized by contact angle measurement,x-ray photoelectron spectroscopy(XPS) and atomic force microscopy respectively.The surface protein adsorption was evaluated by lysozyme solution immersion and XPS analysis.The results indicated that a thin layer of PEGMA was successfully grafted.The surface hydrophilicity was bettered and surface free energy increased.The lysozyme adsorption on the lens surface was reduced greatly.
文摘A new process for lamination of polymer films by 'bulk surface photografting' has been developed. The chemical component of the invention is that the curing of reactive solution between two substrates is initiated by the surface free radicals produced by aromatic ketones and surface-hydrogen of substrates. Using the new approach, two or more polymer films are bonded together by a grafted polymer network which is grafted to adjacent substrate surfaces. The technique has been applied to film substrates of different polymers such as polyolefins, polyesters, and polyamides which have abstractable hydrogens at the surface. The photolaminated film composites containing carrier films and an intermediate functional film of low permeability give strong laminates with high barrier properties, e.g, for oxygen and air.
基金This work was supported by the Special Fund for Major State Basic Research Projects (Grant no. G1999064803).
文摘Spherical polyethylene/polypropylene (PE/PP) in-reactor blend granules with various ethylene/propylene molar ratios and high porosity were synthesized using a high yield TiCVMgCl2 supported catalyst. A solution of benzoyl peroxide (BPO)/maleic anhydride (MAH)/xylene (interfacial reagent) or BPO/MAH/St (comonomer) was absorbed onto the PE/PP in- reactor blend granules, and solid phase graft polymerization of MAH on PE/PP was conducted. The amount of grafted MAH on PE/PP was measured through chemical titration. The results showed that solid phase graft polymerization of MAH in PE/PP in-reactor blend granules produced graft copolymer with high amount of grafted MAH, and the amount of grafted MAH was raised slightly when St was introduced as comonomer. The graft in-reactor blend was fractionated into five fractions through temperature-gradient extraction fractionation (TGEF), and the fractions were analyzed by FTIR. The results revealed that MAH is mainly grafted on the PE segments, whereas MAH was predominantly grafted on the PP segments when St was present in the graft polymerization system. In addition, the final product is still in the form of regular spherical granules, which is beneficial for industrial processing.
文摘Grafting of polystyrene (PS) onto titanium dioxide powder was investigated. The graft polymerization reaction was induced by high frequency discharge produced N2 plasma treatment of the surfaces of titanium dioxide. IR, XPS and TGA results show that PS was grafted on the titanium dioxide powder. And the crystal structure of the titanium dioxide powder observed by XRD was unchanged after plasma treatment.
基金This work was supported by the National Natural Science Foundation of China (No. 50133020), the Team Project of the Natural Science Foundation of Guangdong, China (No. 20003038), and the Key Program of the Science and Technology Department of Guangdong,
文摘An irradiation grafting method was applied for the modification of nanoparticles so that the latter can be added topolymeric materials for improving their mechanical performance using existing compounding techniques. The followingitems are discussed in this paper: (a) chemical interaction between the grafting monomers and the nanoparticles duringirradiation, (b) properties including modulus, yield strength, impact strength and fracture toughness of the resultantcomposites, and (c) possible morphological changes induced by the addition of nanoparticles. Though irradiation graftingpolymerization, nanoparticle agglomerates turn into a nano-composite microstructure (comprised of the nanoparticles and thegrafted, homopolymerized secondary polymer), which in turn builds up a strong interfacial interaction with the surrounding,primary polymeric matrix during the subsequent mixing procedure. Due to the fact that different grafting polymers broughtabout different nanoparticle/matrix interfacial features, microstructures and properties of the ultimate composites could thusbe tailored. It was found that the reinforcing and toughening effects of the nanoparticles on the polymer matrix can be fullybrought into play at a rather low filler loading in comparison to conventional particulate filled composites.
文摘An investigation of grafting of polymer of styrene (PSt) onto titanium dioxide powder is reported in this paper. The graft polymerization reaction was induced by N2 plasma treatment on the surface of titanium dioxide. Infrared (IR) spectra and X-ray photospectrum (XPS) results showed that PSt was grafted onto the titanium dioxide powder. An observation by X-ray diffraction (XRD) spectra indicated that the crystal structure of the titanium dioxide powder was unchanged after the plasma treatment.
基金the Indian Institute of Technology(Indian School of Mines),Dhanbad,India,for providing financial support
文摘In this paper the suitability of a graft polymer nanocomposite hydrogel system for enhanced oil recovery was examined using polyacrylamide graft starch/clay nanocomposite(a laboratory synthesized product) and chromium(III) acetate(crosslinker). X-ray diffraction analysis,Fourier transform infrared spectrometry analysis, field-emission scanning electron microscopy and transmission electron microscopy were carried out to reveal the laboratory synthesized product as a nanocomposite. The effects of various parameters like salt concentration, p H, temperature, polymer concentration and crosslinker concentration on the properties of the developed gel system were systematically evaluated.The thermal stability of the nanocomposite gel and the conventional gel system were also determined by thermogravimetric analysis. The graft polymer nanocomposite gel system exhibited acceptable gel strength, gelation time and gel stability compared with the conventional gel system. The nanocomposite gels prepared using a low crosslinker concentration showed higher gel strength and required longer gelation time than the conventional gel which is more desirable properties for the effective placement of gel during enhanced oil recovery operations. In addition, sand pack flooding experiments show that the graft polymer nanocomposite gels had better plugging capacity than the conventional gel systems under reservoir conditions. Hence, this gel system may be suitable in the water shutoff treatments required for enhanced oil recovery from oilfields.
基金The financial supports by the National Natural Science Foundation of China(Grant:50133020.50273047)the Team Project of the Natural Science Foundation of Guangdong.China(Grant:20003038)the Key Program of the Science and Technology Department of Guangdong,China(Grant:2001A1070201)are acknowledged.