Effects of Primary Annealing Condition on Recrystallization Texture in a Grain Oriented Silicon Steel

The recrystallization texture in grain oriented silicon steel sheets, which were annealed at different primary annealingtemperatures with and without an electric field, was investigated. An automated electron backscattered diffraction(EBSD) technique was used to analyze the recrystallization texture. It was found that recovery and application ofelectric field in primary annealing lead to an increase of {001} component and a decrease of {111} component afterannealing at 900℃. The development of recrystallization texture can be explained in terms of the effects of electricfield and primary annealing temperature on recovery.

STUDY ON REDUCING THE CORE LOSS OF GRAIN ORIENTED SILICON STEEL AND IMPROVING ITS AGING PROPERTY BY LASER NITRIDING TECHNIQUE IN ATMOSPHERIC AMBIENT

CW-CO2 laser nitriding technique was applied to improve the properties （such as aging property and the core loss） of grain oriented silicon steel. The samples were nitrided with regular space. Laser power density and scanning speed were chosen as 7.8×10^5W·cm^-2 and 100mm·min^-1. By some laser irradiation, Fe4N and Fe3N were formed in the nitrided zone. The nitrided samples were annealed at the temperatures ranged from 100 to 90℃. The core loss of some interested samples was tested. The results show that the core loss of the nitrided samples with different thickness of 0.23 and 0.30mm decreased by 14.9% and 9.4% respectively, and the aging property were improved up to 800℃. The mechanism of laser nitriding to improve the properties of grain oriented silicon steel is discussed.

Primary Recrystallization of Grain Oriented Silicon Steel Strip Rolled by CSR and Annealed in Magnetic Field

The magnetic properties and textures of grain oriented silicon steel with different thickness rolled by cross shear rolling （CSR） of different mismatched speed ratio （MSR） and annealed in magnetic field under hydrogen were presented.Effects of the factors such as thickness and mismatched speed ratio on the magnetic properties and recrystallization texture were analyzed and the recrystallization principles in magnetic field annealing were discussed. The study would provide a new route for mass production of high quality ultra-thin grain oriented silicon steel strip.

Texture Characteristics of Thin Grain Oriented Silicon Steel Sheet Produced by Cross Shear Rolling

Commercial grain oriented silicon steel was cold rolled to thickness from 0.06 to 0.10 mm by cross shear rolling, then annealed in vacuum or a hydrogen atmosphere furnace. Deformation textures of the sheets were researched by ODF method and reverse pole figure quantitative analyses. The results indicate that: in the condition of the cross shear rolling, the deformation texture of rolled sheet is generally similar to that of conventional rolled sheet, however, the texture distribution through the thickness is asymmetrical. With mismatch speed ratio increasing, the amount of Goss texture increases. With reduction ratio increasing, the intensity of γ-fiber becomes strong.

New process for production of ultra-thin grain oriented silicon steel

The Hi-B silicon steels were cold rolled by cross shear rolling (CSR) with different mismatch speed ratio(MSR)s and conventional rolling(CR) respectively, followed by primary recrystallization annealing. The effects of MSR and annealing temperature on magnetic properties of ultra-thin grain oriented silicon steel were analyzed. Experimental results show that, with the increase of MSR, the magnetic properties can be remarkably improved. The higher the annealing temperature is, the higher the magnetic induction and the lower the iron loss in ultra-thin silicon steel is.

Optimizing Domain Distribution of Grain Oriented Silicon Steel by Using Antimony as the Laser Surface Alloying Element

For reducing the core loss of grain oriented silicon steel and improving its aging property, a new method, the LLSA by using Sb as the laser surface alloying element, was investigated, and at proper technique conditions rather good result was obtained.

Goss Texture Evolution of Grain Oriented Silicon Steel by High-Energy X-ray Diffraction

High energy synchrotron diffraction offers great potential to study the recrystallization kinetics of metallic materials. To study the formation of Goss texture （{ [10}（001）） of grain oriented （GO） silicon steel during secondary recrystallization process, an in situ experiment using hi gh energy X-ray diffraction was designed. The results showed that the secondary recrystallization began when the heating temperature was 1,494 K, and the grains grew rapidly above this temperature. With an increase in annealing temperature, the large grains with 7 orientation [〈111〉//normal direction] formed and gradually occupied the dominant position. As the annealing temperature increased even further, the grains with Goss orientation to a very large size by devouring the 7 orientation grains that formed in the early annealing stage. A single crystal with a Goss orientation was observed in the GO silicon steel when the annealing temperature was 1,540 K.