Temperature-induced resistance transition behaviors of melamine sponge composites wrapped with different graphene oxide derivatives

Temperature-re s ponsive resistance transition behaviors of the melamine sponges wrapped with different graphene oxide derivatives(i.e.nanoribbon,wide-ribbon and sheet)were investigated.Melamine sponge composites coated by three types of GO derivatives were prepared by a simple dip-coating approach.All these composites show good mechanical flexibility and reliability(almost unchanged compressive stress at 70%strain after 100 cycles),high hydrophobicity(water contact angle>120°),excellent flame resistance(self-extinguishing)and structural stability even after burning,which was used to construct the resistance-based fire alarm/warning sensor.Notably,the different resistance response behaviors of such sensors are strongly dependent on the GO size and network formed on the MF skeleton surface.Typically,at a fixed high temperature of~350℃,the three fire alarm sensors show different response time(to trigger the alarm light)of 6.3,8.4 and 11.1 s for nanoribbon,wide-ribbon and sheet at the same concentration,respectively.The structural observation and chemical analysis demonstrated that the discrepancy of temperature-responsive resistance transition behaviors of various GO derivatives was strongly determined by their different thermal reduction degrees during the high-tempe rature or flame treating process.This work offers a design and development for construction of smart fire alarm device for potential fire prevention and safety applications.

One-step co-electrodeposition of graphene oxide doped poly(hydroxymethylated-3,4-ethylenedioxythiophene) film and its electrochemical studies of indole-3-acetic acid

A novel graphene oxide （GO） doped poly（hydroxymethylated-3,4-ethylenedioxythiophene） （PEDOTM） film has been achieved via one-step co-electrodeposition and utilized for electrochemical studies of indole-3-acetic acid （IAA）. The incorporation of GO into PEDOTM film facilitated the electrocatalytic activity and exhibited a favorable interaction between the PEDOTM/GO film and the phytohormone during the oxidation of IAA. Under optimized conditions, differential pulse voltammetry and square wave voltammetry were used for the quantitative analysis of IAA, respectively, each exhibiting a wide linearity range from 0.6 μmol L-1 to 10 μmol L-1 and 0.05 μmol L-1 to 40 μmol L-1, good sensitivity with a low detection Iimit of 0.087 μmol L-1 and 0.033μmol L T, respectively, as well as good stability. With the notable advantages of a green, sensitive method, expeditious response and facile operation, the as-prepared PEDOTM/GO organic-inorganic composite film provides a promising platform for electrochemical studies of IAA.