Contact Mechanism of Rail Grinding with Open-Structured Abrasive Belt Based on Pressure Grinding Plate

The current research of abrasive belt grinding rail mainly focuses on the contact mechanism and structural design.Compared with the closed structure abrasive belt grinding,open-structured abrasive belt grinding has excellent performance in dynamic stability,consistency of grinding quality,extension of grinding mileage and improvement of working efficiency.However,in the contact structure design,the open-structured abrasive belt grinding rail using a profiling pressure grinding plate and the closed structure abrasive belt using the contact wheel are different,and the contact mechanisms of the two are different.In this paper,based on the conformal contact and Hertz theory,the contact mechanism of the pressure grinding plate,abrasive belt and rail is analyzed.Through finite element simulation and static pressure experiment,the contact behavior of pressure grinding plate,abrasive belt and rail under single concentrated force,uniform force and multiple concentrated force was studied,and the distribution characteristics of contact stress on rail surface were observed.The results show that under the same external load,there are three contact areas under the three loading modes.The outer contour of the middle contact area is rectangular,and the inner contour is elliptical.In the contact area at both ends,the stress is extremely small under a single concentrated force,the internal stress is drop-shaped under a uniform force,and the internal stress under multiple concentration forces is elliptical.Compared with the three,the maximum stress is the smallest and the stress distribution is more uniform under multiple concentrated forces.Therefore,the multiple concentrated forces is the best grinding pressure loading mode.The research provides support for the application of rail grinding with open-structured abrasive belt based on pressure grinding plate,such as contact mechanism and grinding pressure mode selection.

Mechanism of high pressure roll grinding on compression strength of oxidized hematite pellets

The mechanism of high pressure roll grinding on improvement of compression strength of oxidized hematite pellets was researched by considering their roasting properties. The results indicate that oxidized hematite pellets require higher preheating temperature and longer preheating time to attain required compression strength of pellets compared with the common magnetite oxidized pellets. It is found that when the hematite concentrates are pretreated by high pressure roll grinding （HPRG）, the compression strengths of preheated and roasted oxidized hematite pellets get improved even with lower preheating and roasting temperatures and shorter preheating and roasting time. The mechanism for HPRG to improve roasting properties of oxidized pellets were investigated and the cause mainly lies in the increase of micro-sized particles and the decrease of dispersion degree for hematite concentrates, which promotes the hematite concentrate particles to be compacted, the solid-phase crystallization, and finally the formation of Fe203 bonding bridges during subsequent high temperature roasting process.

Strengthening pelletization of manganese ore fines containing high combined water by high pressure roll grinding and optimized temperature elevation system

Pelletization is one of useful processes for the agglomeration of iron ore or concentrates. However, manganese ore fines are mainly agglomerated by sintering due to its high combined water which adversely affects the roasting performance of pellets. In this work, high pressure roll grinding(HPRG) process and optimization of temperature elevation system were investigated to improve the strength of fired manganese ore pellets. It is shown that the manganese ore possesses good ballability after being pretreated by HPRG twice, and good green balls were produced under the conditions of blending 2.0% bentonite in the feed, balling for 7 min at 16.00% moisture. High quality roasted pellets with the compressive strength of 2711 N per pellet were manufactured through preheating at 1050 °C for 10 min and firing at 1335 °C for 15 min by controlling the cracks formation. The fired manganese pellets keep the strength by the solid interconnection of recrystallized pyrolusite grains and the binding of manganite liquid phase which filled the pores and clearance among minerals. The product pellets contain high Mn grade and low impurities, and can be used to smelt ferromanganese, which provides a possible way to use imported manganese ore fines containing high combined water to produce high value ferromanganese.

Fragmentation mechanism of low-grade hematite ore in a high pressure grinding roll

The fragmentation mechanism of low-grade hematite ore in a high pressure grinding roll(HPGR) was studied based on the characteristics of comminuted products at different specific pressure levels. The major properties included the reduction ratio, liberation, specific surface energy, and specific surface area. The results showed that the fracture of low-grade hematite ore in HPGR was an interactive dynamic process in which the interaction between coarse particles of gangue minerals and fine particles of valuable minerals was alternately continuous with increased compactness and compacting strength of materials. Within a range of 2.8–4.4 N/mm^2, valuable minerals were crushed after preferentially absorbing energy, whereas gangue minerals were not completely crushed and only acted as an energy transfer medium. Within a range of 4.4–5.2 N/mm^2, gangue minerals were adequately crushed after absorbing the remaining energy, whereas preferentially crushed valuable minerals acted as an energy transfer medium. Within a range of 5.2–6.0 N/mm^2 range, the low-grade hematite ore was not further comminuted because of the "size effect" on the strength of materials, and the comminution effect of materials became stable.

Effects of high pressure roller grinding on size distribution of vanadium-titanium magnetite concentrate particles and improvement of green pellet strength

The vanadium-titanium magnetite concentrate from Panxi region of China was pretreated by high pressure roller grinding（ HPRG） and then used in pelletization. Size distribution change of the vanadiumtitanium magnetite concentrate after HPRG and the improvement of its green pellet strength were investigated. The results indicated that,besides the increase of fine particles,the vanadium-titanium magnetite concentrate after HPRG had a smaller size ratio of fine particle to coarse particle of 0. 126,meaning a lower porosity,compared with the size ratio of raw material of 0. 157. The concentrate particles were more closely packed when there was a smaller size ratio of fine particle to coarse particle. The particle packing in the green pellets was closer after HPRG,which strengthened the green pellets with an average drop number of 5. 1（ drop height of 0. 5 m） and average compressive strength of 13. 1 N per pellet of 11 mm in diameter.

Roasting Properties of Pellets With Iron Concentrate of Complex Mineral Composition

Investigation was conducted on roasting properties of pellets with an iron concentrate of complex mineral composition. The results indicated that the pellets of complex mineral composition concentrate required higher pre- heating temperature and longer preheating time than that of single magnetite concentrate. Therefore, it is difficult for preheated pellets to withstand the mechanical collision in the roasting process in rotary kiln. It was found that after the iron concentrate being subjected to high pressure roll grinding, the specific surface area reached 2 029. i cm2/g. Consequently, the preheating and roasting temperature of pellets were decreased by 70 and 50 ℃ and preheating and roasting time were decreased by 2 and 4 min, respectively. Meanwhile, the compression strength of preheated and roasted pellets were increased by 200 N for a pellet and 220 N for a pellet, respectively. The mechanism lied in that the increase of specific surface area activated thermal reaction and promoted formation of inter-grain bridge.

Influence of Mechanical Activation on Acid Leaching Dephosphorization of High-phosphorus Iron Ore Concentrates

High pressure roll grinding（HPRG）and ball milling were compared to investigate the influence of mechanical activation on the acid leaching dephosphorization of a high-phosphorus iron ore concentrate,which was manufactured through magnetizing roasting-magnetic separation of high-phosphorus oolitic iron ores.The results indicated that when high-phosphorus iron ore concentrates containing 54.92 mass% iron and 0.76 mass% phosphorus were directly processed through acid leaching,iron ore concentrates containing 55.74mass%iron and 0.33mass%phosphorus with an iron recovery of 84.64%and dephosphorization of 63.79% were obtained.When high-phosphorus iron ore concentrates activated by ball milling were processed by acid leaching,iron ore concentrates containing56.03mass%iron and 0.21mass% phosphorus with an iron recovery of 85.65% and dephosphorization of 77.49%were obtained.Meanwhile,when high-phosphorus iron ore concentrates activated by HPRG were processed by acid leaching,iron ore concentrates containing 58.02mass%iron and 0.10mass% phosphorus were obtained,with the iron recovery reaching 88.42% and the dephosphorization rate reaching 88.99%.Mechanistic studies demonstrated that ball milling can reduce the particle size,demonstrating aprominent reunion phenomenon.In contrast,HPRG pretreatment contributes to the formation of more cracks within the particles and selective dissociation of iron and P bearing minerals,which can provide the favorable kinetic conditions to accelerate the solid-liquid reaction rate.As such,the crystal structure is destroyed and the surface energy of mineral particles is strengthened by mechanical activation,further strengthening the dephosphorization.