A modified Gurson-Tvergaard-Needleman （GTN） model that accounts for the mixed （isotropic and kinematic） hardening of cast steel GS-20Mn5V was developed and implemented in the finite dement program ABAQUS/Standard ...A modified Gurson-Tvergaard-Needleman （GTN） model that accounts for the mixed （isotropic and kinematic） hardening of cast steel GS-20Mn5V was developed and implemented in the finite dement program ABAQUS/Standard via a user-defined material subroutine UMAT. This model couples the stress state and damage evolution （pore volume fraction increase） by a classic method that assumes that the total void volume fraction is divided into a nucleation and a growth part. A parametric study was conducted to assess the effect of modified GTN model parameters on mechanical properties such as the nucleation, growth and coalescence of voids and to obtain the optimal parameter combination by the orthogonal test method. The predicted load-displacement curves of notched specimens with the optimal parameters are favorably compared to the experimental curves. Therefore, the modified GTN model can be used to predict the damage evaluation and fracture behavior of GS-20Mn5V.展开更多
Based on the Gurson-Tvergaard-Needleman(GTN)damage model considering the defect damage evolution,the influence of void defects caused by the casting process on cast steel nodes mechanical properties was studied.Firstl...Based on the Gurson-Tvergaard-Needleman(GTN)damage model considering the defect damage evolution,the influence of void defects caused by the casting process on cast steel nodes mechanical properties was studied.Firstly,based on the GTN damage model,the model s parameter combination of G20Mn5N cast steel was given.Then,the mechanical properties of cast steel nodes were evaluated using the GTN damage model in ABAQUS software,and the influence of model parameters on the failure results was investigated.The results show that the cast steel node considering the GTN damage model fails under 1.93 times of the load.The bearing capacity is lower than that of the bilinear model,and the failure speed is faster.Changes in model parameters will cause a shift in the failure critical point.Meanwhile,the plastic strain index affects the void volume fractions,which shows different variation laws under uniaxial tensile and cyclic loads.Therefore,the GTN damage model establishes the relationship between the micro-defects and macro-mechanical properties of materials,which can better simulate the failure results of structures.展开更多
基金The National Key Research and Development Program of China(No.2017YFC0805103)the National Natural Science Foundation of China(No.51578137,51438002,51108075)the Open Research Fund Program of Jiangsu Key Laboratory of Engineering Mechanics
文摘A modified Gurson-Tvergaard-Needleman （GTN） model that accounts for the mixed （isotropic and kinematic） hardening of cast steel GS-20Mn5V was developed and implemented in the finite dement program ABAQUS/Standard via a user-defined material subroutine UMAT. This model couples the stress state and damage evolution （pore volume fraction increase） by a classic method that assumes that the total void volume fraction is divided into a nucleation and a growth part. A parametric study was conducted to assess the effect of modified GTN model parameters on mechanical properties such as the nucleation, growth and coalescence of voids and to obtain the optimal parameter combination by the orthogonal test method. The predicted load-displacement curves of notched specimens with the optimal parameters are favorably compared to the experimental curves. Therefore, the modified GTN model can be used to predict the damage evaluation and fracture behavior of GS-20Mn5V.
基金The National Key Research and Development Program of China(No.2017YFC0805100)the National Natural Science Foundation of China(No.51578137)the Priority Academic Program Development of Jiangsu Higher Education Institutions,the Open Research Fund Program of Jiangsu Key Laboratory of Engineering Mechanics.
文摘Based on the Gurson-Tvergaard-Needleman(GTN)damage model considering the defect damage evolution,the influence of void defects caused by the casting process on cast steel nodes mechanical properties was studied.Firstly,based on the GTN damage model,the model s parameter combination of G20Mn5N cast steel was given.Then,the mechanical properties of cast steel nodes were evaluated using the GTN damage model in ABAQUS software,and the influence of model parameters on the failure results was investigated.The results show that the cast steel node considering the GTN damage model fails under 1.93 times of the load.The bearing capacity is lower than that of the bilinear model,and the failure speed is faster.Changes in model parameters will cause a shift in the failure critical point.Meanwhile,the plastic strain index affects the void volume fractions,which shows different variation laws under uniaxial tensile and cyclic loads.Therefore,the GTN damage model establishes the relationship between the micro-defects and macro-mechanical properties of materials,which can better simulate the failure results of structures.
基金supported by the National Natural Science Foundation of China (No.51975330)Key Research and Development Program of Shandong Province,China (No.2021ZLGX01)Project of Colleges and Universities Innovation Team of Jinan City,China (No.2021GXRC030)。
