Spinel lithium manganese oxide ion-sieves have been considered the most promising adsorbents to extract Li^+ from brines and sea water.Here,we report a lithium ion-sieve which was successfully loaded onto tubular α-A...Spinel lithium manganese oxide ion-sieves have been considered the most promising adsorbents to extract Li^+ from brines and sea water.Here,we report a lithium ion-sieve which was successfully loaded onto tubular α-Al2 O3 ceramic substrates by dipping crystallization and post-calcination method.The lithium manganese oxide Li4 Mn5 O(12)was first synthesized onto tubular α-Al2 O3 ceramic substrates as the ion-sieve precursor(i.e.L-AA),and the corresponding lithium ion-sieve(i.e.H-AA) was obtained after acid pickling.The chemical and morphological properties of the ion-sieve were confirmed by X-ray diffraction(XRD) and scanning electron microscopy(SEM).Both L-AA and H-AA showed characteristic peaks of α-Al2 O3 and cubic phase Li4 Mn5 O(12) and the peaks representing cubic phase could still exist after pickling.The lithium manganese oxide Li4 Mn5 O(12) could be uniformly loaded not only on the surface of α-Al2 O3 ubstrates but also inside the pores.Moreover,we found that the equilibrium adsorption capacity of H-AA was 22.9 mg·g^-1.After 12 h adsorption,the adsorption balance was reached.After 5 cycles of adsorption,the adsorption capacity of H-AA was 60.88% of the initial adsorption capacity.The process of H-AA adsorption for Li^+correlated with pseudo-second order kinetic model and Langmuir model.Adsorption thermodynamic parameters regarding enthalpy(△N), Gibbs free energy(△G) and entropy(AS) were calculated.For the dynamic adsorptiondesorption process of H-AA,the H-AA exhibited excellent adsorption performance to Li^+ with the Li^+ dynamic adsorption capacity of 9.74 mg·g^-1 and the Mn^2+dissolution loss rate of 0.99%.After 3 dynamic adsorption-desorption cycles,80% of the initial dynamic adsorption capacity was still kept.展开更多
Nanostructured TiO2 has applications in solar cells, photocatalysts, and fast- charging, safe lithium ion batteries （LIBs）. To meet the demand of high-capacity and high-rate LIBs with TiO2-based anodes, it is import...Nanostructured TiO2 has applications in solar cells, photocatalysts, and fast- charging, safe lithium ion batteries （LIBs）. To meet the demand of high-capacity and high-rate LIBs with TiO2-based anodes, it is important to fine-tune the nanoarchitecture using a well-controlled synthesis approach. Herein, we report a new approach that involves epitaxial growth combined with topotactic conversion to synthesize a unique type of three-dimensional （3D） TiO2 nano- architecture that is assembled by well-oriented ultrathin nanobelts. The whole nanoarchitecture displays a 3D Chinese knot-like morphology; the core consists of robust perpendicular interwoven nanobelts and the shell is made of extended nanobelts. The nanobelts oriented in three perpendicular [001]A directions facilitate Li＋ penetration and diffusion. Abundant anatase/TiO2-B interfaces provide a large amount of interfacial pseudocapacitance. A high and stable capacity of 130 mA.h.g-1 was obtained after 3,000 cycles at 10 A·g-1 （50 C）, and the high-rate property of our material was greater than that of many recently reported high-rate TiO2 anodes. Our result provides, not only a novel synthesis strategy, but also a new type of 3D anatase TiO2 anode that may be useful in developing long-lasting and fast-charging batteries.展开更多
基金This work was financially supported by National Key Research and Development Program(2018YFE0203502),ChinaPrimary Research and Development Plan ofJiangsu Province(BE2019117),China and National Students'Platform for Innovation and Entrepreneurship Training(201910291051Z),China.
文摘Spinel lithium manganese oxide ion-sieves have been considered the most promising adsorbents to extract Li^+ from brines and sea water.Here,we report a lithium ion-sieve which was successfully loaded onto tubular α-Al2 O3 ceramic substrates by dipping crystallization and post-calcination method.The lithium manganese oxide Li4 Mn5 O(12)was first synthesized onto tubular α-Al2 O3 ceramic substrates as the ion-sieve precursor(i.e.L-AA),and the corresponding lithium ion-sieve(i.e.H-AA) was obtained after acid pickling.The chemical and morphological properties of the ion-sieve were confirmed by X-ray diffraction(XRD) and scanning electron microscopy(SEM).Both L-AA and H-AA showed characteristic peaks of α-Al2 O3 and cubic phase Li4 Mn5 O(12) and the peaks representing cubic phase could still exist after pickling.The lithium manganese oxide Li4 Mn5 O(12) could be uniformly loaded not only on the surface of α-Al2 O3 ubstrates but also inside the pores.Moreover,we found that the equilibrium adsorption capacity of H-AA was 22.9 mg·g^-1.After 12 h adsorption,the adsorption balance was reached.After 5 cycles of adsorption,the adsorption capacity of H-AA was 60.88% of the initial adsorption capacity.The process of H-AA adsorption for Li^+correlated with pseudo-second order kinetic model and Langmuir model.Adsorption thermodynamic parameters regarding enthalpy(△N), Gibbs free energy(△G) and entropy(AS) were calculated.For the dynamic adsorptiondesorption process of H-AA,the H-AA exhibited excellent adsorption performance to Li^+ with the Li^+ dynamic adsorption capacity of 9.74 mg·g^-1 and the Mn^2+dissolution loss rate of 0.99%.After 3 dynamic adsorption-desorption cycles,80% of the initial dynamic adsorption capacity was still kept.
基金This research was supported financially by the National Natural Science Foundation of China （NSFC） （Nos. 51672315, U1301242, 21271190, and 21403106）, the government of Guangzhou city for an international joint-project （No. 201704030020）, the Government of Guangdong Province for NSF （No. S2012020011113） and the provincial Ministry of Cooperative funded special funds （Nos. 2013A090100010, 2016B090932005, and 2015B090927002）, the Fundamental Research Funds for the Central Universities （No. 161gpy18）. The authors acknowledge Prof. Hong Jin Fan from Nanyang Technological University for helpful discussions.
文摘Nanostructured TiO2 has applications in solar cells, photocatalysts, and fast- charging, safe lithium ion batteries （LIBs）. To meet the demand of high-capacity and high-rate LIBs with TiO2-based anodes, it is important to fine-tune the nanoarchitecture using a well-controlled synthesis approach. Herein, we report a new approach that involves epitaxial growth combined with topotactic conversion to synthesize a unique type of three-dimensional （3D） TiO2 nano- architecture that is assembled by well-oriented ultrathin nanobelts. The whole nanoarchitecture displays a 3D Chinese knot-like morphology; the core consists of robust perpendicular interwoven nanobelts and the shell is made of extended nanobelts. The nanobelts oriented in three perpendicular [001]A directions facilitate Li＋ penetration and diffusion. Abundant anatase/TiO2-B interfaces provide a large amount of interfacial pseudocapacitance. A high and stable capacity of 130 mA.h.g-1 was obtained after 3,000 cycles at 10 A·g-1 （50 C）, and the high-rate property of our material was greater than that of many recently reported high-rate TiO2 anodes. Our result provides, not only a novel synthesis strategy, but also a new type of 3D anatase TiO2 anode that may be useful in developing long-lasting and fast-charging batteries.