A seed-directed approach to synthesizing Fe ZSM-22 zeolite without organic structure directing agent(OSDA)was developed by using Fe-rich diatomite as all aluminum and iron sources.The Fe ZSM-22zeolite with optimal cry...A seed-directed approach to synthesizing Fe ZSM-22 zeolite without organic structure directing agent(OSDA)was developed by using Fe-rich diatomite as all aluminum and iron sources.The Fe ZSM-22zeolite with optimal crystallinity and purity can be obtained by systematically adjusting feed composition and synthesis conditions.Characterizations show that Fe ZSM-22 zeolite synthesized with OSDA-free owns high crystallinity,obvious thin needle-shaped morphology and high Bronsted/Lewis acid ratio.Significantly,when used for n-octane hydroisomerization reaction,its derived catalyst exhibits the best catalytic performance reflected by the highest selectivity to C_(8)isomers compared to the two reference catalysts prepared based on a Fe-containing and a Fe-free ZSM-22 synthesized through an OSDA-directed route from natural diatomite and conventional chemicals,respectively.This work provides an alternative route to sustainably synthesizing heteroatomic zeolites with high performance.展开更多
Hydroisomerization catalysts Pt/ZSM-22, Pt/ZSM-23, and Pt/ZSM-22/ZSM-23 were prepared by supporting Pt on ZSM-22, ZSM-23, and intergrowth zeolite ZSM-22/ZSM-23, respectively. The typical physicochemical properties of ...Hydroisomerization catalysts Pt/ZSM-22, Pt/ZSM-23, and Pt/ZSM-22/ZSM-23 were prepared by supporting Pt on ZSM-22, ZSM-23, and intergrowth zeolite ZSM-22/ZSM-23, respectively. The typical physicochemical properties of these catalysts were characterized by X-Ray Diffraction (XRD), N2 absorption-desorption, Pyridine-Fourier Transform Infrared (Py-FTIR), Transmission Electron Microscopy (TEM), X-Ray Fluorescence (XRF), Scanning Electron Microscopy (SEM) and NH3- Temperature Programmed Desorption (NH3-TPD), and the performance of these catalysts in n-dodecane hydroisomerization was evaluated in a continuous down-flow fixed bed with a stainless steel tubular reactor. The characterization results indicated that the intergrowth zeolite ZSM-22/ZSM-23 possessed the dual structure of ZSM-22 and ZSM-23, and the catalyst Pt/ZSM-22/ZSM-23 had similar pores and weak acidity to Pt/ZSM-22 and Pt/ZSM-23 catalysts. Moreover, Pt/ZSM-22/ZSM-23 catalyst showed a high selectivity in hydroisomerization of long chain n-alkanes to mono-branched isomers. The evaluation results for n-dodecane hydroisomerization indicated that the activity of Pt/ZSM-22/ZSM-23 was the lowest, while the hydroisomerization selectivity was the highest among the three catalysts. The maximum yield of i-dodecane product was 68.3% over Pt/ZSM-22/ZSM-23 at 320 ℃.展开更多
The performance of MCM-22 zeolite for catalytic isomerization of 1-hexene has been studied. At a n(H2)/n(1-hexene) ratio of 8, the influence of steam treatment temperature, reaction temperature and reaction pressure o...The performance of MCM-22 zeolite for catalytic isomerization of 1-hexene has been studied. At a n(H2)/n(1-hexene) ratio of 8, the influence of steam treatment temperature, reaction temperature and reaction pressure on the performance of MCM-22 zeolite for catalytic skeletal isomerization of 1-hexene was examined. The experimental results showed that at a steam treatment temperature of 500℃, a reaction temperature of 270℃, a space velocity of 1.0 h-1 and a reaction pressure of 0.2 MPa, the MCM-22 zeolite exhibited excellent performance for catalytic skeletal isomerization of 1-hexene with the i-hexene yield reaching 66.15%. Compared with other commonly used molecular sieve catalysts, the MCM-22 zeolite catalyst exhibited better catalytic performance for skeletal isomerization of 1-hexene.展开更多
基金the financial supports from the National Natural Science Foundation of China(22322803,22178059,22208054,22221005,22072019)Key Technologies Innovation and Industrialization Projects of Fujian Province(2022G031)Qingyuan Innovation Laboratory(00121002,00523005)。
文摘A seed-directed approach to synthesizing Fe ZSM-22 zeolite without organic structure directing agent(OSDA)was developed by using Fe-rich diatomite as all aluminum and iron sources.The Fe ZSM-22zeolite with optimal crystallinity and purity can be obtained by systematically adjusting feed composition and synthesis conditions.Characterizations show that Fe ZSM-22 zeolite synthesized with OSDA-free owns high crystallinity,obvious thin needle-shaped morphology and high Bronsted/Lewis acid ratio.Significantly,when used for n-octane hydroisomerization reaction,its derived catalyst exhibits the best catalytic performance reflected by the highest selectivity to C_(8)isomers compared to the two reference catalysts prepared based on a Fe-containing and a Fe-free ZSM-22 synthesized through an OSDA-directed route from natural diatomite and conventional chemicals,respectively.This work provides an alternative route to sustainably synthesizing heteroatomic zeolites with high performance.
基金the financial supports form Petrochina(050508-04-02)the National Natural Science Foundation of China(No.21073235,and 20833011)
文摘Hydroisomerization catalysts Pt/ZSM-22, Pt/ZSM-23, and Pt/ZSM-22/ZSM-23 were prepared by supporting Pt on ZSM-22, ZSM-23, and intergrowth zeolite ZSM-22/ZSM-23, respectively. The typical physicochemical properties of these catalysts were characterized by X-Ray Diffraction (XRD), N2 absorption-desorption, Pyridine-Fourier Transform Infrared (Py-FTIR), Transmission Electron Microscopy (TEM), X-Ray Fluorescence (XRF), Scanning Electron Microscopy (SEM) and NH3- Temperature Programmed Desorption (NH3-TPD), and the performance of these catalysts in n-dodecane hydroisomerization was evaluated in a continuous down-flow fixed bed with a stainless steel tubular reactor. The characterization results indicated that the intergrowth zeolite ZSM-22/ZSM-23 possessed the dual structure of ZSM-22 and ZSM-23, and the catalyst Pt/ZSM-22/ZSM-23 had similar pores and weak acidity to Pt/ZSM-22 and Pt/ZSM-23 catalysts. Moreover, Pt/ZSM-22/ZSM-23 catalyst showed a high selectivity in hydroisomerization of long chain n-alkanes to mono-branched isomers. The evaluation results for n-dodecane hydroisomerization indicated that the activity of Pt/ZSM-22/ZSM-23 was the lowest, while the hydroisomerization selectivity was the highest among the three catalysts. The maximum yield of i-dodecane product was 68.3% over Pt/ZSM-22/ZSM-23 at 320 ℃.
文摘The performance of MCM-22 zeolite for catalytic isomerization of 1-hexene has been studied. At a n(H2)/n(1-hexene) ratio of 8, the influence of steam treatment temperature, reaction temperature and reaction pressure on the performance of MCM-22 zeolite for catalytic skeletal isomerization of 1-hexene was examined. The experimental results showed that at a steam treatment temperature of 500℃, a reaction temperature of 270℃, a space velocity of 1.0 h-1 and a reaction pressure of 0.2 MPa, the MCM-22 zeolite exhibited excellent performance for catalytic skeletal isomerization of 1-hexene with the i-hexene yield reaching 66.15%. Compared with other commonly used molecular sieve catalysts, the MCM-22 zeolite catalyst exhibited better catalytic performance for skeletal isomerization of 1-hexene.