With the aid of hydrogen permeating devices, the hydrogen permeation behaviors of X52 pipeline steel in NACE A solution with saturated H2S/CO2 were studied under the conditions of different ambient temperatures and pH...With the aid of hydrogen permeating devices, the hydrogen permeation behaviors of X52 pipeline steel in NACE A solution with saturated H2S/CO2 were studied under the conditions of different ambient temperatures and pH values, and the hydrogen permeation behaviors of X52 pipeline steel in weld seam zone were comparatively studied. The experimental results show that the hydrogen permeation coefficient value is directly proportional to the time required for reaching the saturation anode current and inversely proportional to the saturation anode current, and the hydrogen permeation coefficient is influenced by the corrosion scales; the temperature is directly proportional to the saturation anode current, and the hydrogen permeation coefficient is influenced by the temperature and corrosion scales, heat-affected zone and matrix zone in NACE A solution with saturated H2S/CO2 at normal temperature. The hydrogen permeation coefficient in weld seam zone is larger than that in heat-affected zone which is further larger than that in matrix zone.展开更多
The corrosion behavior of the 110S tube steel in the environments of high H2 S and CO2 content was inves- tigated by using a high-temperature and high-pressure autoclave, and the corrosion products were characterized ...The corrosion behavior of the 110S tube steel in the environments of high H2 S and CO2 content was inves- tigated by using a high-temperature and high-pressure autoclave, and the corrosion products were characterized by scanning electron microscopy and X ray diffraction technique. The results showed that all of the corrosion products under the test conditions mainly consisted of different types of iron sulfides such as pyrrhotite of Fe0.95 S, mackinaw- ite of FeS0.9, Fe0. 985 S and FeS, and the absence of iron carbonate in the corrosion scales indicated that the corrosion process was controlled by H2S corrosion. The corrosion rate of the 110S steel decreased firstly and then increased with the rising of temperature. The minimum corrosion rate occurred at 110 ℃. When the H2 S partial pressure PH2s below 9 MPa, the corrosion rate declined with the increase of PH2s. While over 9 MPa, a higher PH2s resulted in a faster corrosion process. With the increasing of the CO2 partial pressure, the corrosion rate had an increasing trend. The morphologies of the corrosion scales had a good accordance with the corrosion rates.展开更多
基金Funded by the Program for National Science Foundation for Distinguished Young Scholars (No.51125019)the National Natural Science Foundation of China (No.50904050)+2 种基金the Basic Projects of Sichuan Province of China(No.2011JY0106)Postdoctoral Science Foundation(No.20110490810)the Special Fund of China's Central Government for the Development of Local Colleges and Universities-the Project of National First-level Discipline in Oil and Gas Engineering
文摘With the aid of hydrogen permeating devices, the hydrogen permeation behaviors of X52 pipeline steel in NACE A solution with saturated H2S/CO2 were studied under the conditions of different ambient temperatures and pH values, and the hydrogen permeation behaviors of X52 pipeline steel in weld seam zone were comparatively studied. The experimental results show that the hydrogen permeation coefficient value is directly proportional to the time required for reaching the saturation anode current and inversely proportional to the saturation anode current, and the hydrogen permeation coefficient is influenced by the corrosion scales; the temperature is directly proportional to the saturation anode current, and the hydrogen permeation coefficient is influenced by the temperature and corrosion scales, heat-affected zone and matrix zone in NACE A solution with saturated H2S/CO2 at normal temperature. The hydrogen permeation coefficient in weld seam zone is larger than that in heat-affected zone which is further larger than that in matrix zone.
基金Sponsored by Key National Science and Technology Specific Projects of China(2008ZX05017-002)
文摘The corrosion behavior of the 110S tube steel in the environments of high H2 S and CO2 content was inves- tigated by using a high-temperature and high-pressure autoclave, and the corrosion products were characterized by scanning electron microscopy and X ray diffraction technique. The results showed that all of the corrosion products under the test conditions mainly consisted of different types of iron sulfides such as pyrrhotite of Fe0.95 S, mackinaw- ite of FeS0.9, Fe0. 985 S and FeS, and the absence of iron carbonate in the corrosion scales indicated that the corrosion process was controlled by H2S corrosion. The corrosion rate of the 110S steel decreased firstly and then increased with the rising of temperature. The minimum corrosion rate occurred at 110 ℃. When the H2 S partial pressure PH2s below 9 MPa, the corrosion rate declined with the increase of PH2s. While over 9 MPa, a higher PH2s resulted in a faster corrosion process. With the increasing of the CO2 partial pressure, the corrosion rate had an increasing trend. The morphologies of the corrosion scales had a good accordance with the corrosion rates.