Solubilities and properties (density, conductivity and pH value) of solutions in the quaternary system Li +,K +//CO 2- 3,B 4O 2- 7-H 2O at 288 K were experimentally studied with the isothermal equilibrium method. The ...Solubilities and properties (density, conductivity and pH value) of solutions in the quaternary system Li +,K +//CO 2- 3,B 4O 2- 7-H 2O at 288 K were experimentally studied with the isothermal equilibrium method. The phase diagram of the system consisted of two invariant points E and F, five univariant curves, and four crystallization fields that belonged to K 2CO 3·3/2H 2O,Li 2 B 4O 7·3H 2O, K 2 B 4O 7 ·4H 2O and Li 2CO 3. The composition of the solution corresponding to E was w(CO 2- 3)=2.27 %, w(B 4O 2- 7) =6.05 %, w(K + ) =4.30%,w(Li + )=0.30 % and the equilibrium solids were Li 2 B 4O 7· 3H 2O+K 2 B 4O 7·4H 2O+Li 2CO 3;The composition of the solution for F was w(CO 2- 3) =22.45%,w(B 4O 2- 7)=1.88%,w(K + )=29.96%,w(Li + )=0.03% and the equilibrium solids were K 2CO 3·3/2H 2O+ K 2 B 4O 7·4H 2O+Li 2CO 3. K 2CO 3 possesses strong salting-out effect on K 2 B 4O 7,Li 2CO 3 and Li 2 B 4O 7.展开更多
The supersaturated solution of MgO· 3B2O3 18% MgSO4 H2O was prepared and then reacted under hydrothermal condition at 120℃ . The solid phases of the different time were identified by means of chemical analysis, ...The supersaturated solution of MgO· 3B2O3 18% MgSO4 H2O was prepared and then reacted under hydrothermal condition at 120℃ . The solid phases of the different time were identified by means of chemical analysis, XRD, FT IR, SEM. The results show that the solid phases are spherical and sheet szaibelyite, which is different from those of non hydrothermal condition. On these grounds we suggested the crystallization mechanism of szaibelyite under the hydrothermal condition and then discussed the effects of hydrothermal properties on the crystallization mechanism.展开更多
文摘Solubilities and properties (density, conductivity and pH value) of solutions in the quaternary system Li +,K +//CO 2- 3,B 4O 2- 7-H 2O at 288 K were experimentally studied with the isothermal equilibrium method. The phase diagram of the system consisted of two invariant points E and F, five univariant curves, and four crystallization fields that belonged to K 2CO 3·3/2H 2O,Li 2 B 4O 7·3H 2O, K 2 B 4O 7 ·4H 2O and Li 2CO 3. The composition of the solution corresponding to E was w(CO 2- 3)=2.27 %, w(B 4O 2- 7) =6.05 %, w(K + ) =4.30%,w(Li + )=0.30 % and the equilibrium solids were Li 2 B 4O 7· 3H 2O+K 2 B 4O 7·4H 2O+Li 2CO 3;The composition of the solution for F was w(CO 2- 3) =22.45%,w(B 4O 2- 7)=1.88%,w(K + )=29.96%,w(Li + )=0.03% and the equilibrium solids were K 2CO 3·3/2H 2O+ K 2 B 4O 7·4H 2O+Li 2CO 3. K 2CO 3 possesses strong salting-out effect on K 2 B 4O 7,Li 2CO 3 and Li 2 B 4O 7.
文摘The supersaturated solution of MgO· 3B2O3 18% MgSO4 H2O was prepared and then reacted under hydrothermal condition at 120℃ . The solid phases of the different time were identified by means of chemical analysis, XRD, FT IR, SEM. The results show that the solid phases are spherical and sheet szaibelyite, which is different from those of non hydrothermal condition. On these grounds we suggested the crystallization mechanism of szaibelyite under the hydrothermal condition and then discussed the effects of hydrothermal properties on the crystallization mechanism.