The C 3N 4 film on Al 2O 3 formed by dynamic catalytic at low energy Ar + ion sputtering C 3H 6N 6+Ni target. The ratio of nitroge atoms to carbon in the films is 4∶3. C(1 s ) peakes for graphite, diamond and C≡N no...The C 3N 4 film on Al 2O 3 formed by dynamic catalytic at low energy Ar + ion sputtering C 3H 6N 6+Ni target. The ratio of nitroge atoms to carbon in the films is 4∶3. C(1 s ) peakes for graphite, diamond and C≡N not have observed. above results are obtained by XPS. The main peak appears at 1275cm -1 in the Raman spectrum. Results of SEM cant observed that sample is consist of cluter type crystal, but is no needle type. The colour is yellow but is no white. The experimental result indicated films consist of inorganic cavalent solid carbon nitride. The results from XRF observed sample contain Fe and Ni elements. It has been illustrated that Fe and Ni responsible for one C 3N 4 polymerization.展开更多
The title complex Cu[C5H3N(CCH3=N-C6H5)2]2(PF6)2 has been synthesized by r eaction of Schiff base C5H3N(CCH3=N-C6H5)2 and cupric sulfate in toluene solut ion. The crystal structure was determined by X-ray diffraction ...The title complex Cu[C5H3N(CCH3=N-C6H5)2]2(PF6)2 has been synthesized by r eaction of Schiff base C5H3N(CCH3=N-C6H5)2 and cupric sulfate in toluene solut ion. The crystal structure was determined by X-ray diffraction method and the chemical formula weight of the complex is 1041.85. The crystal structure belongs to triclinic system with spacegroup and cell parameters: a=12.6470(10) , b=14. 123(2) , c=15.613(2);á=66.150(10)a=79.470(10)?=78.290(10)穖-3 and F(000)=1064. The final R:R1=0.0668, wR 2=0.1927; R(all data): R1=0.1133, wR2=0.2357. The Cu was coordinated by six nitrogen, at the same time the Cu formed a distorted octahedron, besides the angles and pl anes of this compound were discussed . The result of kinetics of the thermal dec omposition indicated that the first step of it is 2 series chemical reactions, t he function of machanism is f(a)=(1-a)2, and the activation energy is 144.64E/ kJ. CCDC: 180872.展开更多
A novel porous coordination polymer [La(C8H6NO2)3]n was synthesized by hydrothermal reaction of flexible ligands 3 (3 pyridyl)acrylate and La(NO3)3· 6H2O. The structure was characterized by elemental analysis, IR...A novel porous coordination polymer [La(C8H6NO2)3]n was synthesized by hydrothermal reaction of flexible ligands 3 (3 pyridyl)acrylate and La(NO3)3· 6H2O. The structure was characterized by elemental analysis, IR spectroscopy and X ray single crystal diffraction. X ray single crystal analysis reveals the structure consists of [La(C8H6NO2)3]n. It crystallizes in monoclinic crystal system with space group P2(1)/c. Crystallographic date: a=0. 7889(3)nm, b=2.5916(9)nm, c=1.1489(4)nm, α =90.00° , β =95.219(6)° , γ =90.00° , V=2.3393(15)nm3, Z=4, Dc=1.656g· cm- 3, μ =1.871mm- 1, F(000)=1152, R1=0.0328, wR2=0.0522. CCDC: 211700.展开更多
文摘The C 3N 4 film on Al 2O 3 formed by dynamic catalytic at low energy Ar + ion sputtering C 3H 6N 6+Ni target. The ratio of nitroge atoms to carbon in the films is 4∶3. C(1 s ) peakes for graphite, diamond and C≡N not have observed. above results are obtained by XPS. The main peak appears at 1275cm -1 in the Raman spectrum. Results of SEM cant observed that sample is consist of cluter type crystal, but is no needle type. The colour is yellow but is no white. The experimental result indicated films consist of inorganic cavalent solid carbon nitride. The results from XRF observed sample contain Fe and Ni elements. It has been illustrated that Fe and Ni responsible for one C 3N 4 polymerization.
文摘The title complex Cu[C5H3N(CCH3=N-C6H5)2]2(PF6)2 has been synthesized by r eaction of Schiff base C5H3N(CCH3=N-C6H5)2 and cupric sulfate in toluene solut ion. The crystal structure was determined by X-ray diffraction method and the chemical formula weight of the complex is 1041.85. The crystal structure belongs to triclinic system with spacegroup and cell parameters: a=12.6470(10) , b=14. 123(2) , c=15.613(2);á=66.150(10)a=79.470(10)?=78.290(10)穖-3 and F(000)=1064. The final R:R1=0.0668, wR 2=0.1927; R(all data): R1=0.1133, wR2=0.2357. The Cu was coordinated by six nitrogen, at the same time the Cu formed a distorted octahedron, besides the angles and pl anes of this compound were discussed . The result of kinetics of the thermal dec omposition indicated that the first step of it is 2 series chemical reactions, t he function of machanism is f(a)=(1-a)2, and the activation energy is 144.64E/ kJ. CCDC: 180872.
文摘A novel porous coordination polymer [La(C8H6NO2)3]n was synthesized by hydrothermal reaction of flexible ligands 3 (3 pyridyl)acrylate and La(NO3)3· 6H2O. The structure was characterized by elemental analysis, IR spectroscopy and X ray single crystal diffraction. X ray single crystal analysis reveals the structure consists of [La(C8H6NO2)3]n. It crystallizes in monoclinic crystal system with space group P2(1)/c. Crystallographic date: a=0. 7889(3)nm, b=2.5916(9)nm, c=1.1489(4)nm, α =90.00° , β =95.219(6)° , γ =90.00° , V=2.3393(15)nm3, Z=4, Dc=1.656g· cm- 3, μ =1.871mm- 1, F(000)=1152, R1=0.0328, wR2=0.0522. CCDC: 211700.