基于蠕变损伤力学理论的HK40炉管焊接接头的蠕变损伤研究

The accurate prediction of damage behavior of welded components at high temperature is becoming incresasingly important in order to realize an optimised design and maintenance of a plant life.In the present paper,the creep properties of the weld of HK40 furnace tube are determined by means of a local deformation measuring technique.A damage mechanics approach is introduced to simulate the damage development and creep rupture of HK-40 furnace tubes due to the presence of a weld.Metallographical research also indicates that the weld has a higher damage rank.It has been illustrated that damage is prone to the weld in the later period of service life.It is thus concluded that the weldments may become the weak link in HK-40 furnace tubes.

石化装置用HK40炉管的焊接

对HK40炉管焊接易产生热裂纹及保证800℃左右使用的热强性及热稳定性,提出了保证焊缝质量的措施,通过焊接试验与评定,确定了施焊工艺,并成功地用于转化炉管的焊接。

焊接对HK40高温炉管的蠕变损伤与断裂的影响

采用含有局部效应的蠕变损伤力学方法 ,计及材料不均匀性 ,建立母材和焊缝金属两材料有限元模型 ,分析了具有缺口的 HK40带焊缝试样以及实际 HK40炉管焊接接头的蠕变损伤发展与断裂。蠕变损伤模拟结果表明 ,虽然焊缝金属为蠕变硬焊缝 ,但在服役寿命的后期 ,焊缝损伤较母材严重 ,出现损伤局部化特征 ,最终的失效发生在焊缝中。服役 10年的 HK40炉管的金相剖析也表明焊缝比母材具有较高的损伤级别 ,这预示着焊缝在长期服役过程中是最薄弱的环节之一。

HK—40炉管与15CrMo法兰的焊接

锦西石化分公司制氢装置转化炉检修中,施工单位进行了HK—40炉管与15Cr Mo法兰的焊接。结合这次焊接,本文叙述了HK—40钢和15Cr Mo钢的焊接特点;介绍了焊材的选择、焊接方法和检查方法;通过焊接实践,给出了焊条选择、焊接和检查要点。

HK40转化炉管超声检测中的影响因素

HK40炉管系离心铸造的大晶粒奥氏体不锈钢 ,用普通的无损检测方法很难对其进行可靠的检测。理论和实践都表明双探头透射法是检测 HK40炉管的行之有效的方法。本文探讨透射法检测过程中的影响因素。

高温构件材料临界A参数的定量测定

通过对服役材料HK40炉管损伤状态的实验测定和分析 ,认为在受损材料的裂纹前端存在临界损伤状态。使用A参数方法 ,通过定量金相分析 ,首次获得了裂纹前端的临界参数值Acr。临界参数值Acr的确定为临界损伤值的确定提供了基础 ,为高温构件的寿命预测。