Dissimilar material joining of 6008 aluminum alloy to H220 YD galvanized high strength steel was performed by resistance spot welding with especial electrodes that were a flat tip electrode against the steel surface a...Dissimilar material joining of 6008 aluminum alloy to H220 YD galvanized high strength steel was performed by resistance spot welding with especial electrodes that were a flat tip electrode against the steel surface and a domed tip electrode upon the aluminum alloy surface. An intermetallic compound layer composed of Fe2Al5 and FeAl3 was formed at the steel/ aluminum interface in the welded joint. The thickness of the intermetallic compound layer increased with increasing welding current and welding time, and the maximum thickness being 7. 0 μm was obtained at 25 kA and 300 ms. The weld nugget diameter and tensile shear load of the welded joint had increased tendencies first with increasing welding current ( 18 -22 kA) and welding time ( 50 - 300 ms), then changed little with further increasing welding current ( 22 - 25 kA) and welding time (300 -400 ms). The maximum tensile shear load reached 5.4 kN at 22 kA and 300 ms. The welded joint fractured through brittle intermetallic compound layer and aluminum alloy nugget.展开更多
In the present work, N 2, N 2+H 2, Ar and Ar+H 2, were used as the sintering atmosphere of Metal Injection Molded 316L stainless steel respectively. The influences of the sintering atmospheres on C, O, N contents of t...In the present work, N 2, N 2+H 2, Ar and Ar+H 2, were used as the sintering atmosphere of Metal Injection Molded 316L stainless steel respectively. The influences of the sintering atmospheres on C, O, N contents of the sintered specimens, sintered density, grain morphology and mechanical properties were investigated. The results show that C, O, N contents of the sintered specimens can be controlled in permitted low values. The ultimate tensile strength and elongation of the specimen sintered in N 2+H 2 atmosphere are 765 MPa and 32% respectively. Using Ar and Ar+H 2 as the sintering atmosphere, the density of the sintered specimens is 98% of the theoretical density; the pores are uniformly distributed as small spherical shape and the grain size is about 50 μm. The mechanical properties of the specimen, i.e. ultimate tensile strength 630 MPa, yield strength 280 MPa, elongation 52%, HRB 71, are much better than those of the American Metal Powder Industries Federation(MPIF) 35 Standard after being sintered in Ar+H 2.展开更多
The mechanical behavior and microstructural evolution of an Fe-30Mn-3Al-3Si twinninginduced plasticity(TWIP)steel processed using warm forging was investigated.It is found that steel processed via warm forging improve...The mechanical behavior and microstructural evolution of an Fe-30Mn-3Al-3Si twinninginduced plasticity(TWIP)steel processed using warm forging was investigated.It is found that steel processed via warm forging improves comprehensive mechanical properties compared to the TWIP steel processed via cold rolling,with a high tensile strength(R_(m))of 793 MPa,a yield strength(R_(P))of 682 MPa,an extremely large R_(P)/R_(m)ratio as high as 0.86 as well as an excellent elongation rate of 46.8%.The microstructure observation demonstrates that steel processed by warm forging consists of large and elongated grains together with fine,equiaxed grains.Complicated micro-defect configurations were also observed within the steel,including dense dislocation networks and a few coarse deformation twins.As the plastic deformation proceeds,the densities of dislocations and deformation twins significantly increase.Moreover,a great number of slip lines could be observed in the elongated grains.These findings reveal that a much more dramatic interaction between microstructural defect and dislocations glide takes place in the forging sample,wherein the fine and equiaxed grains propagated dislocations more rapidly,together with initial defect configurations,are responsible for enhanced strength properties.Meanwhile,larger,elongated grains with more prevalently activated deformation twins result in high plasticity.展开更多
Three types of steels were designed on the basis of GX40CrNiSi25-12 austenitic heat resistant steel by adding different Mn contents(2wt.%,6wt.%,and 12wt.%).Thermodynamic calculation,microstructure characterization and...Three types of steels were designed on the basis of GX40CrNiSi25-12 austenitic heat resistant steel by adding different Mn contents(2wt.%,6wt.%,and 12wt.%).Thermodynamic calculation,microstructure characterization and mechanical property tests were conducted to investigate the effect of Mn addition on the microstructure and mechanical properties of the austenitic heat resistant steel.Results show that the matrix structure in all the three types of steels at room temperature is completely austenite.Carbides NbC and M_(23)C_(6)precipitate at grain boundaries of austenite matrix.With the increase of Mn content,the number of carbides increases and their distribution becomes more uniform.With the Mn content increases from 1.99%to 12.06%,the ultimate tensile strength,yield strength and elongation increase by 14.6%,8.0%and 46.3%,respectively.The improvement of the mechanical properties of austenitic steels can be explained by utilizing classic theories of alloy strengthening,including solid solution strengthening,precipitation strengthening,and grain refinement.The increase in alloy strength can be attributed to solid solution strengthening and precipitation strengthening caused by the addition of Mn.The improvement of the plasticity of austenitic steels can be explained from two aspects:grain refinement and homogenization of precipitated phases.展开更多
The characteristics of microstructure, mechanical property and corrosion behavior of Cr26Mo3.5 super stainless steel joints by pulse tungsten inert gas(P-TIG)welding and laser welding were investigated. The results in...The characteristics of microstructure, mechanical property and corrosion behavior of Cr26Mo3.5 super stainless steel joints by pulse tungsten inert gas(P-TIG)welding and laser welding were investigated. The results indicate that the widths of the center equiaxed grain zone(EGZ)and the columnar grain zone(CGZ)increase with the increase of heat input in both welding processes. The precipitates of Nb and Ti carbides and nitrides are formed in the weld metal(WM)and the heat affected zone(HAZ). The joints by laser welding show better tensile and corrosion resistance properties than those by P-TIG welding due to the heat concentration and lower heat input. The tensile strength and elongation increase with the decrease of heat input, and the fracture mode of the joints turns into ductile-brittle mixed fracture from ductile fracture when the welding method turns into P-TIG welding from laser welding. Moreover, the corrosion resistance of all joints declines slightly with the increase of heat input. Hence, laser welding is more suitable for welding Cr26Mo3.5 super stainless steel in engineering applications.展开更多
Ar-N_(2)-O_(2)ternary shielding gas is employed in dissimilar welding between high nitrogen steel and low alloy steel.The effect of O_(2)and N_(2)is investigated based on the systematical analysis of the metal transfe...Ar-N_(2)-O_(2)ternary shielding gas is employed in dissimilar welding between high nitrogen steel and low alloy steel.The effect of O_(2)and N_(2)is investigated based on the systematical analysis of the metal transfer,nitrogen escape phenomenon,weld appearance,nondestructive detection,nitrogen content distribution,microstructure and mechanical properties.There are two nitrogen sources of the nitrogen in the weld:high nitrogen base material and shielding gas.The effect of shielding gas is mainly reflected in these two aspects.The change of the droplet transfer mode affects the fusion ratio,N2in the shielding gas can increase nitrogen content and promote the nitrogen uniform distribution.The addition of 2%O_(2)to Ar matrix can change the metal transfer from globular transfer to spray transfer,high nitrogen base material is thereby dissolved more to the molten pool,making nitrogen content increase,ferrite decrease and the mechanical properties improve.When applying N2-containing shielding gas,arc stability becomes poor and short-circuiting transfer frequency increases due to the nitrogen escape from droplets and the molten pool.Performance of the joints is improved with N_(2)increasing,but internal gas pores are easier to appear because of the poor capacity of low alloy steel to dissolve nitrogen,The generation of pores will greatly reduce the impact resistance.4-8%N2content in shielding gas is recommended in this study considering the integrated properties of the dissimilar welded joint.展开更多
The microstructure and mechanical properties of titanium(Ti)-bearing medium-carbon nonquenched and tempered steel with different nitrogen content before and after hot forging were investigated through smelting,forging...The microstructure and mechanical properties of titanium(Ti)-bearing medium-carbon nonquenched and tempered steel with different nitrogen content before and after hot forging were investigated through smelting,forging,and laboratory tests.The results show that the grain size of nonquenched and tempered steel was gradually refined,and the ferrite content gradually increased with an increase in nitrogen content.The grain size of the material with low nitrogen content increased abnormally,and its impact properties significantly decreased after hot forging.The grain size of nonquenched and tempered steel with higher nitrogen content was slightly larger than that before forging,and the tensile and yield strength increased,but the impact toughness was not significantly reduced.The Ti-bearing nonquenched and tempered steel showed better strength and toughness after hot forging with the addition of 0.010%0.015%nitrogen.展开更多
A new thermomechanical process consisting of heavy cold rolling(HCR)and short-time heat treatment(STH)is developed to fabricate fine-grained martensite microstructure in a low-cost plain low-carbon steel.To achieve th...A new thermomechanical process consisting of heavy cold rolling(HCR)and short-time heat treatment(STH)is developed to fabricate fine-grained martensite microstructure in a low-cost plain low-carbon steel.To achieve the optimal mechanical properties after STH,three different ferrite-pearlite(F-P)dual-phase microstructures are prepared via hot rolling(HR),HR and austenitizing,and HR and HCR.The microstructure evolution and the comprehensive mechanical properties of the alloy during STH are then investigated.We find that the volume fractions of transformed martensite after STH increase with decreasing grain sizes of the pre-STH F-P dual phases.The rapid heating and short-time holding of STH promote grain nucleation and inhibit grain growth,resulting in microstructure refinement.The formation of martensites with different morphologies and different carbon concentrations in the HR and HCR+STH alloy is identified,owing to the inhomogeneous carbon distribution by STH.Tensile experiments demonstrate that STH greatly improves the comprehension mechanical properties of the alloy.Excellent mechanical properties,with a yield strength of 1224 MPa,a tensile strength of 1583 MPa,a uniform elongation of 4.0%and a total elongation of 7.3%are achieved in the HR and HCR+STH alloy.These excellent mechanical properties are principally attributed to the microstructure refinement and martensite formation induced by STH,with a yield strength improvement of 134%and a tensile strength improvement of 150%relative to the HR alloy.展开更多
The mechanical properties and microstructure evolution of cold-deformed CrMnN austenitic stainless steel annealed in a temperature ranging from 50 ℃ to 650 ℃ for 90 min and at 550 ℃ for different time were investig...The mechanical properties and microstructure evolution of cold-deformed CrMnN austenitic stainless steel annealed in a temperature ranging from 50 ℃ to 650 ℃ for 90 min and at 550 ℃ for different time were investigated by tensile test, micro hardness test, and Transmission Electron Microscope (TEM). The steel was strengthened when it got annealed at temperatures ranging from 100 ℃ to 550 ℃, while it was softened when it got annealed at temperatures ranging from 550 ℃ to 650 ℃. Annealing temperature had stronger effect on mechanical properties than annealing time. TEM observations showed that nano-sized precipitates formed when the steel was annealed at 150 ℃ for 90 min, but the size and density of precipitates had no noticeable change with annealing temperature and time. Recrystallization occurred when the steel was annealed at temperatures above 550 ℃ for 90 min, and its scale increased with annealing temperature. Nano-sized annealing twins were observed. The mechanisms that controlled the mechanical behaviors of the steel were discussed.展开更多
The effects of the microalloying element niobium(Nb) on the microstructure and mechanical properties of the hot stamped steel 38 Mn B5 were investigated. The impact of Nb addition on the microstructure was studied thr...The effects of the microalloying element niobium(Nb) on the microstructure and mechanical properties of the hot stamped steel 38 Mn B5 were investigated. The impact of Nb addition on the microstructure was studied through scanning electron microscopy(SEM), transmission electron microscopy(TEM), and X-ray diffraction(XRD). The experimental results indicated that the microstructures of the steel containing Nb were finer than those of the steel without Nb. Moreover, Nb mainly presented as a second-phase particle in 38MnB5 steel, and the particles included Nb carbonitrides. In addition, the tensile strength and elongation of the hot rolled and hot stamped steels were also measured, and they demonstrated that the appropriate addition of Nb was beneficial to the mechanical properties of 38 MnB5. Under the same conditions, the tensile strength of 38 MnB5 Nb was higher than that of 38 MnB5, which increased from 2011 to 2179 MPa. The yield strength also increased from 1316 to 1476 MPa, and the elongation increased from 5.92% to 6.64%. Overall, Nb had a positive effect on the performance of the hot stamped steel.展开更多
The microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and tens...The microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and tensile test. The results show that Si can promote the transformation of austenite (γ) to ferrite (α), enlarge the (α+γ) region, and increase the aging stability of martensite by inhibiting carbide precipitation. Adding Cr leads to the formation of retained austenite and martensite/austenite (M/A) constituents, as well as the decomposi- tion of martensite during the overaging stage. Both of the steels show higher initial strain-hardening rates and two-stage strain-hardening characteristics. The C-Mn-Si-Nb steel shows the higher strain-hardening rate than the C-Mn-Cr-Nb steel in the first stage; however, there is no significant difference in the second stage. Although the tensile strength and elongation of the two steels both exceed 1000 MPa and 15%, respectively, the comprehensive mechanical properties of the C-Mn-Si-Nb steel are superior.展开更多
Thermomechanical experiments were carried out to reproduce the hot stamping process and to investigate the effects of process parameters on the microstructure and mechanical properties of stamped parts. The process pa...Thermomechanical experiments were carried out to reproduce the hot stamping process and to investigate the effects of process parameters on the microstructure and mechanical properties of stamped parts. The process parameters, such as austenitizing temperature, soaking time, initial deformation temperature and cooling rate, are studied. The resulting microstructures of specimens were observed and analyzed. To evaluate the mechanical properties of specimens, tensile and hardness tests were also performed at room temperature. The op-timum parameters to achieve the highest tensile strength and the desired microstructure were acquired by comparing and analyzing the results. It is indicated that hot deformation changes the transformation characteristics of 22MnB5 steel. Austenite deformation promotes the austen-ite-to-ferrite transformation and elevates the critical cooling rate to induce a fully martensitic transformation.展开更多
Uniaxial tension tests and hole-expansion tests were carried out to determine the influence of silicon on the microstructures, mechanical properties, and stretch-flangeability of conventional dual-phase steels. Compar...Uniaxial tension tests and hole-expansion tests were carried out to determine the influence of silicon on the microstructures, mechanical properties, and stretch-flangeability of conventional dual-phase steels. Compared to 0.03wt% silicon, the addition of 1.08wt% silicon induced the formation of finer ferrite grains (6.8μm ) and a higher carbon content of martensite (Cm≈ 0.32wt%). AS the silicon level increased, the initial strain-hardening rate (n value) and the uniform elongation increased, whereas the yield strength, yield ratio, and stretch-flangeability decreased. The microstructures were observed after hole-expansion tests. The results showed that low carbon content martensite (Cm ≈ 0.19wt%) can easily deform in coordination with ferrite. The relationship between the mechanical properties and stretch-flangeability indicated that the steel with large post-uniform elongation has good stretch-flangeability due to a closer plastic incom- patibility of the ferrite and martensite phases, which can effectively delay the production and decohesion of microvoids.展开更多
Nitrogen can increase the strength of steels without weakening the toughness and improve the corrosion resistance at the same time. Compared with conventional nitrogen-free die steels, a new type of nitrogen-containin...Nitrogen can increase the strength of steels without weakening the toughness and improve the corrosion resistance at the same time. Compared with conventional nitrogen-free die steels, a new type of nitrogen-containing die steel was developed with many superior properties, such as high strength, high hardness, and good toughness. This paper focused on the effects of heat treatment on the microstruc- tures and mechanical properties of the new type of nitrogen-containing die steel, which were investigated by the optimized deformation process and heat treatment. Isothermal spheroidal annealing and high-temperature quenching as well as high-temperature tempering were ap- plied in the experiment by means of an orthogonal method after the steel was multiply forged. The mechanical properties of nitro- gen-containing die steel forgings are better than the standard of NADCA #207-2003.展开更多
The tempering microstructure and mechanical properties of X80 steel used for heating-bent pipe were analyzed. The results show that the microstructure of X80 steel tempered at 550 ℃ and 600 ℃ is bainitic ferrite (BF...The tempering microstructure and mechanical properties of X80 steel used for heating-bent pipe were analyzed. The results show that the microstructure of X80 steel tempered at 550 ℃ and 600 ℃ is bainitic ferrite (BF)+granular bainite (GB), and partial ferrite laths in BF merge and broaden. The interior sub-lath boundary of some GB begins to disappear due to merging, the M/A constituent (a mixture of martensite plus retained austenite) in GB is orbicular. At the two tempering temperatures the tested X80 steel shows a certain degree of tempering stability. After being tempered at 650 ℃, the microstructure of X80 steel is GB+quasi-polygonal ferrite(QF), and the original BF laths have merged to form smaller GB crystal grains. The reason is that the steel shows better match of strength and toughness. After being tempered at 700 ℃ , the microstructure of X80 steel is composed mainly of QF, which can improve the plasticity but decline severely the yield strength of X80, and the M/A constituent assembles and grows up at the grain boundary of QF, resulting in excellent lower low-temperature toughness of X80.展开更多
TiC based steel bonded carbides with the addition of nano TiN were prepared by vacuum sintering techniques.The microstructure was investigated using scanning electron microscopy(SEM) and transmission electron micros...TiC based steel bonded carbides with the addition of nano TiN were prepared by vacuum sintering techniques.The microstructure was investigated using scanning electron microscopy(SEM) and transmission electron microscopy(TEM),and the mechanical properties,such as bending strength,impact toughness,hardness,and density,were measured.The results indicate that the grain size becomes small and there is uniformity in the steel bonded carbide with nano addition;several smaller carbide particles are also found to be inlaid in the rim of the larger carbide grains and prevent the coalescence of TiC grains.The smaller and larger carbide grains joint firmly,and then the reduction of the average size of the grains leads to the increase in the mechanical properties of the steel bonded carbides with nano addition.But the mechanical properties do not increase monotonously with an increase in nano addition.When the nano TiN addition accounts for 6-8 wt.% of the amount of steel bonded carbides,the mechanical properties reach the maximum values and then decrease with further increase in nano TiN addition.展开更多
The mechanical properties of transformation induced plasticity (TRIP) steel are strongly affected by the conditions of iso-thermal bainitic processing. The multiphase microstructure of TRIP steel under different con...The mechanical properties of transformation induced plasticity (TRIP) steel are strongly affected by the conditions of iso-thermal bainitic processing. The multiphase microstructure of TRIP steel under different conditions of isothermal bainitic processing was investigated using OM,SEM,XRD and TEM. The volume fraction of retained austenite and the carbon content in austenite were determined quantitatively using X-ray diffraction patterns. The relationship between mechanical properties and isothermal bainitic processing parameters was investigated. The stability of retained austenite was analyzed by the volume fraction of retained austenite and the carbon content in retained austenite. The experimental results show that the multiphase microstructure consists of ferrite,bainite and metastable retained austenite.To obtain good mechanical properties,the optimal conditions of isothermal bainitic temperature and holding time are 410-430°C and 180-240 s,respectively. After isothermal bainitic processing under the optimal conditions,the corresponding volume fraction of retained austenite is 5vol%-15vol%,which can provide enough retained austenite and plastic stability for austenite with high carbon content.展开更多
The mechanical properties and microstructure of the 3D-printed high Co–Ni secondary hardening steel fabricated by the laser melting deposition technique was investigated using a material testing machine and electron ...The mechanical properties and microstructure of the 3D-printed high Co–Ni secondary hardening steel fabricated by the laser melting deposition technique was investigated using a material testing machine and electron microscopy. A microstructure investigation revealed that the samples consist of martensite laths, fine dispersed precipitates, and reverted austenite films at the martensite lath boundaries. The precipitates are enriched with Co and Mo. Because the sample tempered at 486°C has smaller precipitates and a higher number of precipitates per unit area, it exhibits better mechanical properties than the sample tempered at 498°C. Although the 3D-printed samples have the same phase constituents as Aer Met 100 steel, the mechanical properties are slightly worse than those of the commercial wrought Aer Met 100 steel because of the presence of voids.展开更多
A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and then reheated to 450°C(process B) to simula...A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and then reheated to 450°C(process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel(DP600) was investigated using optical microscopy, scanning electron microscopy(SEM), transmission electron microscopy(TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength(YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient(n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength(UTS) and elongation(A80) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties(YS = 362 MPa, UTS = 638 MPa, A_(80) = 24.3%, n = 0.17) was obtained via process A.展开更多
AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding jo...AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a fine dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.展开更多
文摘Dissimilar material joining of 6008 aluminum alloy to H220 YD galvanized high strength steel was performed by resistance spot welding with especial electrodes that were a flat tip electrode against the steel surface and a domed tip electrode upon the aluminum alloy surface. An intermetallic compound layer composed of Fe2Al5 and FeAl3 was formed at the steel/ aluminum interface in the welded joint. The thickness of the intermetallic compound layer increased with increasing welding current and welding time, and the maximum thickness being 7. 0 μm was obtained at 25 kA and 300 ms. The weld nugget diameter and tensile shear load of the welded joint had increased tendencies first with increasing welding current ( 18 -22 kA) and welding time ( 50 - 300 ms), then changed little with further increasing welding current ( 22 - 25 kA) and welding time (300 -400 ms). The maximum tensile shear load reached 5.4 kN at 22 kA and 300 ms. The welded joint fractured through brittle intermetallic compound layer and aluminum alloy nugget.
文摘In the present work, N 2, N 2+H 2, Ar and Ar+H 2, were used as the sintering atmosphere of Metal Injection Molded 316L stainless steel respectively. The influences of the sintering atmospheres on C, O, N contents of the sintered specimens, sintered density, grain morphology and mechanical properties were investigated. The results show that C, O, N contents of the sintered specimens can be controlled in permitted low values. The ultimate tensile strength and elongation of the specimen sintered in N 2+H 2 atmosphere are 765 MPa and 32% respectively. Using Ar and Ar+H 2 as the sintering atmosphere, the density of the sintered specimens is 98% of the theoretical density; the pores are uniformly distributed as small spherical shape and the grain size is about 50 μm. The mechanical properties of the specimen, i.e. ultimate tensile strength 630 MPa, yield strength 280 MPa, elongation 52%, HRB 71, are much better than those of the American Metal Powder Industries Federation(MPIF) 35 Standard after being sintered in Ar+H 2.
基金Funded by the National Natural Science Foundation of China(Nos.51701206 and 51671187)the Shanxi Natural Science Foundation(No.2019JQ-833)+2 种基金the Anhui Natural Science Foundation(1808085QE166)the Special Scientific Research Project of Shanxi Education Committee(No.19JQ0974)the Doctoral Research Initiation Project of Yan’an University(No.YDBD2018-21)。
文摘The mechanical behavior and microstructural evolution of an Fe-30Mn-3Al-3Si twinninginduced plasticity(TWIP)steel processed using warm forging was investigated.It is found that steel processed via warm forging improves comprehensive mechanical properties compared to the TWIP steel processed via cold rolling,with a high tensile strength(R_(m))of 793 MPa,a yield strength(R_(P))of 682 MPa,an extremely large R_(P)/R_(m)ratio as high as 0.86 as well as an excellent elongation rate of 46.8%.The microstructure observation demonstrates that steel processed by warm forging consists of large and elongated grains together with fine,equiaxed grains.Complicated micro-defect configurations were also observed within the steel,including dense dislocation networks and a few coarse deformation twins.As the plastic deformation proceeds,the densities of dislocations and deformation twins significantly increase.Moreover,a great number of slip lines could be observed in the elongated grains.These findings reveal that a much more dramatic interaction between microstructural defect and dislocations glide takes place in the forging sample,wherein the fine and equiaxed grains propagated dislocations more rapidly,together with initial defect configurations,are responsible for enhanced strength properties.Meanwhile,larger,elongated grains with more prevalently activated deformation twins result in high plasticity.
基金supported by the National Natural Science Foundation of China(Grant No.52275370)the Key R&D Program of Hubei Province,China(Grant Nos.2022BAD100,2021BAA048)the Open Fund of Hubei Longzhong Laboratory(Grant No.2022ZZ-04).
文摘Three types of steels were designed on the basis of GX40CrNiSi25-12 austenitic heat resistant steel by adding different Mn contents(2wt.%,6wt.%,and 12wt.%).Thermodynamic calculation,microstructure characterization and mechanical property tests were conducted to investigate the effect of Mn addition on the microstructure and mechanical properties of the austenitic heat resistant steel.Results show that the matrix structure in all the three types of steels at room temperature is completely austenite.Carbides NbC and M_(23)C_(6)precipitate at grain boundaries of austenite matrix.With the increase of Mn content,the number of carbides increases and their distribution becomes more uniform.With the Mn content increases from 1.99%to 12.06%,the ultimate tensile strength,yield strength and elongation increase by 14.6%,8.0%and 46.3%,respectively.The improvement of the mechanical properties of austenitic steels can be explained by utilizing classic theories of alloy strengthening,including solid solution strengthening,precipitation strengthening,and grain refinement.The increase in alloy strength can be attributed to solid solution strengthening and precipitation strengthening caused by the addition of Mn.The improvement of the plasticity of austenitic steels can be explained from two aspects:grain refinement and homogenization of precipitated phases.
基金Supported by the Research Institute,Baoshan Iron&Steel Co.,Ltd
文摘The characteristics of microstructure, mechanical property and corrosion behavior of Cr26Mo3.5 super stainless steel joints by pulse tungsten inert gas(P-TIG)welding and laser welding were investigated. The results indicate that the widths of the center equiaxed grain zone(EGZ)and the columnar grain zone(CGZ)increase with the increase of heat input in both welding processes. The precipitates of Nb and Ti carbides and nitrides are formed in the weld metal(WM)and the heat affected zone(HAZ). The joints by laser welding show better tensile and corrosion resistance properties than those by P-TIG welding due to the heat concentration and lower heat input. The tensile strength and elongation increase with the decrease of heat input, and the fracture mode of the joints turns into ductile-brittle mixed fracture from ductile fracture when the welding method turns into P-TIG welding from laser welding. Moreover, the corrosion resistance of all joints declines slightly with the increase of heat input. Hence, laser welding is more suitable for welding Cr26Mo3.5 super stainless steel in engineering applications.
文摘Ar-N_(2)-O_(2)ternary shielding gas is employed in dissimilar welding between high nitrogen steel and low alloy steel.The effect of O_(2)and N_(2)is investigated based on the systematical analysis of the metal transfer,nitrogen escape phenomenon,weld appearance,nondestructive detection,nitrogen content distribution,microstructure and mechanical properties.There are two nitrogen sources of the nitrogen in the weld:high nitrogen base material and shielding gas.The effect of shielding gas is mainly reflected in these two aspects.The change of the droplet transfer mode affects the fusion ratio,N2in the shielding gas can increase nitrogen content and promote the nitrogen uniform distribution.The addition of 2%O_(2)to Ar matrix can change the metal transfer from globular transfer to spray transfer,high nitrogen base material is thereby dissolved more to the molten pool,making nitrogen content increase,ferrite decrease and the mechanical properties improve.When applying N2-containing shielding gas,arc stability becomes poor and short-circuiting transfer frequency increases due to the nitrogen escape from droplets and the molten pool.Performance of the joints is improved with N_(2)increasing,but internal gas pores are easier to appear because of the poor capacity of low alloy steel to dissolve nitrogen,The generation of pores will greatly reduce the impact resistance.4-8%N2content in shielding gas is recommended in this study considering the integrated properties of the dissimilar welded joint.
文摘The microstructure and mechanical properties of titanium(Ti)-bearing medium-carbon nonquenched and tempered steel with different nitrogen content before and after hot forging were investigated through smelting,forging,and laboratory tests.The results show that the grain size of nonquenched and tempered steel was gradually refined,and the ferrite content gradually increased with an increase in nitrogen content.The grain size of the material with low nitrogen content increased abnormally,and its impact properties significantly decreased after hot forging.The grain size of nonquenched and tempered steel with higher nitrogen content was slightly larger than that before forging,and the tensile and yield strength increased,but the impact toughness was not significantly reduced.The Ti-bearing nonquenched and tempered steel showed better strength and toughness after hot forging with the addition of 0.010%0.015%nitrogen.
基金funded by the National Natural Science Foundation of China(No.52071212).
文摘A new thermomechanical process consisting of heavy cold rolling(HCR)and short-time heat treatment(STH)is developed to fabricate fine-grained martensite microstructure in a low-cost plain low-carbon steel.To achieve the optimal mechanical properties after STH,three different ferrite-pearlite(F-P)dual-phase microstructures are prepared via hot rolling(HR),HR and austenitizing,and HR and HCR.The microstructure evolution and the comprehensive mechanical properties of the alloy during STH are then investigated.We find that the volume fractions of transformed martensite after STH increase with decreasing grain sizes of the pre-STH F-P dual phases.The rapid heating and short-time holding of STH promote grain nucleation and inhibit grain growth,resulting in microstructure refinement.The formation of martensites with different morphologies and different carbon concentrations in the HR and HCR+STH alloy is identified,owing to the inhomogeneous carbon distribution by STH.Tensile experiments demonstrate that STH greatly improves the comprehension mechanical properties of the alloy.Excellent mechanical properties,with a yield strength of 1224 MPa,a tensile strength of 1583 MPa,a uniform elongation of 4.0%and a total elongation of 7.3%are achieved in the HR and HCR+STH alloy.These excellent mechanical properties are principally attributed to the microstructure refinement and martensite formation induced by STH,with a yield strength improvement of 134%and a tensile strength improvement of 150%relative to the HR alloy.
基金Funded by of Liaoning Science and Technology Bureau(No.2007221007)
文摘The mechanical properties and microstructure evolution of cold-deformed CrMnN austenitic stainless steel annealed in a temperature ranging from 50 ℃ to 650 ℃ for 90 min and at 550 ℃ for different time were investigated by tensile test, micro hardness test, and Transmission Electron Microscope (TEM). The steel was strengthened when it got annealed at temperatures ranging from 100 ℃ to 550 ℃, while it was softened when it got annealed at temperatures ranging from 550 ℃ to 650 ℃. Annealing temperature had stronger effect on mechanical properties than annealing time. TEM observations showed that nano-sized precipitates formed when the steel was annealed at 150 ℃ for 90 min, but the size and density of precipitates had no noticeable change with annealing temperature and time. Recrystallization occurred when the steel was annealed at temperatures above 550 ℃ for 90 min, and its scale increased with annealing temperature. Nano-sized annealing twins were observed. The mechanisms that controlled the mechanical behaviors of the steel were discussed.
文摘The effects of the microalloying element niobium(Nb) on the microstructure and mechanical properties of the hot stamped steel 38 Mn B5 were investigated. The impact of Nb addition on the microstructure was studied through scanning electron microscopy(SEM), transmission electron microscopy(TEM), and X-ray diffraction(XRD). The experimental results indicated that the microstructures of the steel containing Nb were finer than those of the steel without Nb. Moreover, Nb mainly presented as a second-phase particle in 38MnB5 steel, and the particles included Nb carbonitrides. In addition, the tensile strength and elongation of the hot rolled and hot stamped steels were also measured, and they demonstrated that the appropriate addition of Nb was beneficial to the mechanical properties of 38 MnB5. Under the same conditions, the tensile strength of 38 MnB5 Nb was higher than that of 38 MnB5, which increased from 2011 to 2179 MPa. The yield strength also increased from 1316 to 1476 MPa, and the elongation increased from 5.92% to 6.64%. Overall, Nb had a positive effect on the performance of the hot stamped steel.
基金financially supported by the National Natural Science Foundation of China(No.50904006)the Fundamental Research Funds for the Central Universities of China(No.FRT-TP-10-001A)
文摘The microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels were studied by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and tensile test. The results show that Si can promote the transformation of austenite (γ) to ferrite (α), enlarge the (α+γ) region, and increase the aging stability of martensite by inhibiting carbide precipitation. Adding Cr leads to the formation of retained austenite and martensite/austenite (M/A) constituents, as well as the decomposi- tion of martensite during the overaging stage. Both of the steels show higher initial strain-hardening rates and two-stage strain-hardening characteristics. The C-Mn-Si-Nb steel shows the higher strain-hardening rate than the C-Mn-Cr-Nb steel in the first stage; however, there is no significant difference in the second stage. Although the tensile strength and elongation of the two steels both exceed 1000 MPa and 15%, respectively, the comprehensive mechanical properties of the C-Mn-Si-Nb steel are superior.
基金financially supported by the Research Fund for the Doctoral Program of Higher Education,China(No.20120006110017)
文摘Thermomechanical experiments were carried out to reproduce the hot stamping process and to investigate the effects of process parameters on the microstructure and mechanical properties of stamped parts. The process parameters, such as austenitizing temperature, soaking time, initial deformation temperature and cooling rate, are studied. The resulting microstructures of specimens were observed and analyzed. To evaluate the mechanical properties of specimens, tensile and hardness tests were also performed at room temperature. The op-timum parameters to achieve the highest tensile strength and the desired microstructure were acquired by comparing and analyzing the results. It is indicated that hot deformation changes the transformation characteristics of 22MnB5 steel. Austenite deformation promotes the austen-ite-to-ferrite transformation and elevates the critical cooling rate to induce a fully martensitic transformation.
基金financially supported by the Fundamental Research Funds for the Central Universities of China (No. FRF-TP-12-046A)the Beijing Higher Education Young Elite Teacher Project (No. YETP0355)
文摘Uniaxial tension tests and hole-expansion tests were carried out to determine the influence of silicon on the microstructures, mechanical properties, and stretch-flangeability of conventional dual-phase steels. Compared to 0.03wt% silicon, the addition of 1.08wt% silicon induced the formation of finer ferrite grains (6.8μm ) and a higher carbon content of martensite (Cm≈ 0.32wt%). AS the silicon level increased, the initial strain-hardening rate (n value) and the uniform elongation increased, whereas the yield strength, yield ratio, and stretch-flangeability decreased. The microstructures were observed after hole-expansion tests. The results showed that low carbon content martensite (Cm ≈ 0.19wt%) can easily deform in coordination with ferrite. The relationship between the mechanical properties and stretch-flangeability indicated that the steel with large post-uniform elongation has good stretch-flangeability due to a closer plastic incom- patibility of the ferrite and martensite phases, which can effectively delay the production and decohesion of microvoids.
基金supported by the National Natural Science Foundation of China (Nos.50974014 and 51174026)
文摘Nitrogen can increase the strength of steels without weakening the toughness and improve the corrosion resistance at the same time. Compared with conventional nitrogen-free die steels, a new type of nitrogen-containing die steel was developed with many superior properties, such as high strength, high hardness, and good toughness. This paper focused on the effects of heat treatment on the microstruc- tures and mechanical properties of the new type of nitrogen-containing die steel, which were investigated by the optimized deformation process and heat treatment. Isothermal spheroidal annealing and high-temperature quenching as well as high-temperature tempering were ap- plied in the experiment by means of an orthogonal method after the steel was multiply forged. The mechanical properties of nitro- gen-containing die steel forgings are better than the standard of NADCA #207-2003.
基金Project(6990-HT-XEX-03-(2008)-0137) supported by the Major Special Project of Science and Technology of China National Petroleum Corporation
文摘The tempering microstructure and mechanical properties of X80 steel used for heating-bent pipe were analyzed. The results show that the microstructure of X80 steel tempered at 550 ℃ and 600 ℃ is bainitic ferrite (BF)+granular bainite (GB), and partial ferrite laths in BF merge and broaden. The interior sub-lath boundary of some GB begins to disappear due to merging, the M/A constituent (a mixture of martensite plus retained austenite) in GB is orbicular. At the two tempering temperatures the tested X80 steel shows a certain degree of tempering stability. After being tempered at 650 ℃, the microstructure of X80 steel is GB+quasi-polygonal ferrite(QF), and the original BF laths have merged to form smaller GB crystal grains. The reason is that the steel shows better match of strength and toughness. After being tempered at 700 ℃ , the microstructure of X80 steel is composed mainly of QF, which can improve the plasticity but decline severely the yield strength of X80, and the M/A constituent assembles and grows up at the grain boundary of QF, resulting in excellent lower low-temperature toughness of X80.
文摘TiC based steel bonded carbides with the addition of nano TiN were prepared by vacuum sintering techniques.The microstructure was investigated using scanning electron microscopy(SEM) and transmission electron microscopy(TEM),and the mechanical properties,such as bending strength,impact toughness,hardness,and density,were measured.The results indicate that the grain size becomes small and there is uniformity in the steel bonded carbide with nano addition;several smaller carbide particles are also found to be inlaid in the rim of the larger carbide grains and prevent the coalescence of TiC grains.The smaller and larger carbide grains joint firmly,and then the reduction of the average size of the grains leads to the increase in the mechanical properties of the steel bonded carbides with nano addition.But the mechanical properties do not increase monotonously with an increase in nano addition.When the nano TiN addition accounts for 6-8 wt.% of the amount of steel bonded carbides,the mechanical properties reach the maximum values and then decrease with further increase in nano TiN addition.
文摘The mechanical properties of transformation induced plasticity (TRIP) steel are strongly affected by the conditions of iso-thermal bainitic processing. The multiphase microstructure of TRIP steel under different conditions of isothermal bainitic processing was investigated using OM,SEM,XRD and TEM. The volume fraction of retained austenite and the carbon content in austenite were determined quantitatively using X-ray diffraction patterns. The relationship between mechanical properties and isothermal bainitic processing parameters was investigated. The stability of retained austenite was analyzed by the volume fraction of retained austenite and the carbon content in retained austenite. The experimental results show that the multiphase microstructure consists of ferrite,bainite and metastable retained austenite.To obtain good mechanical properties,the optimal conditions of isothermal bainitic temperature and holding time are 410-430°C and 180-240 s,respectively. After isothermal bainitic processing under the optimal conditions,the corresponding volume fraction of retained austenite is 5vol%-15vol%,which can provide enough retained austenite and plastic stability for austenite with high carbon content.
文摘The mechanical properties and microstructure of the 3D-printed high Co–Ni secondary hardening steel fabricated by the laser melting deposition technique was investigated using a material testing machine and electron microscopy. A microstructure investigation revealed that the samples consist of martensite laths, fine dispersed precipitates, and reverted austenite films at the martensite lath boundaries. The precipitates are enriched with Co and Mo. Because the sample tempered at 486°C has smaller precipitates and a higher number of precipitates per unit area, it exhibits better mechanical properties than the sample tempered at 498°C. Although the 3D-printed samples have the same phase constituents as Aer Met 100 steel, the mechanical properties are slightly worse than those of the commercial wrought Aer Met 100 steel because of the presence of voids.
基金financially supported by the National Natural Science Foundation of China (Nos.U1360202,51472030,and 51502014)
文摘A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and then reheated to 450°C(process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel(DP600) was investigated using optical microscopy, scanning electron microscopy(SEM), transmission electron microscopy(TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength(YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient(n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength(UTS) and elongation(A80) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties(YS = 362 MPa, UTS = 638 MPa, A_(80) = 24.3%, n = 0.17) was obtained via process A.
基金Funded by the National Natural Science Foundation of China(Nos.51201087,51165038)the Project of Jiangxi Province of Education(No.GJJ13493)+1 种基金the State Key Laboratory of Solidification Processing in NWPU(No.SKLSP201306)the China Postdoctoral Science Foundation(No.2014M552485)
文摘AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a fine dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.