The analysis of the crack on the HRB400 screw-thread steel surface has been carried out by means of metallographic microscope, scanning electron microscope and EDAX. It is shown that the type of inclusions in the crac...The analysis of the crack on the HRB400 screw-thread steel surface has been carried out by means of metallographic microscope, scanning electron microscope and EDAX. It is shown that the type of inclusions in the crack steel samples is mainly class B oxide, C silicate, and the inclusion size of the majority below 10 μm, and a small number of large inclusions are observed. The content of oxygen in the steel is high, and the carbon segregation is the main reason of the crack formation of HRB400 screw-thread steel. The measures to improve the crack formation of HRB400 screw-thread steel are put forward, which provides a powerful basis for the practical production.展开更多
The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing wit...The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing with HRB335 steel bars, i.e. coordination of strength and ductility, strain-aging sensibility, low temperature impact toughness, weld ability and high strain low cycle fatigue. The ductile-brittle transit temperatures of hot-rolled and strain-aged steel bars were evaluated as –17 °C and ?8 °C respectively, and the low temperature impact toughness of HRB400 steel bars remains to be improved. Transmission electron microscopy (TEM) and electron diffraction showed little vanadium existed in ferrite as VN, most of which existed in pearlite as alloy cementite which resulted in the declination of impact toughness. Methods were suggested to improve the anti- seismic properties of steel bars.展开更多
文摘The analysis of the crack on the HRB400 screw-thread steel surface has been carried out by means of metallographic microscope, scanning electron microscope and EDAX. It is shown that the type of inclusions in the crack steel samples is mainly class B oxide, C silicate, and the inclusion size of the majority below 10 μm, and a small number of large inclusions are observed. The content of oxygen in the steel is high, and the carbon segregation is the main reason of the crack formation of HRB400 screw-thread steel. The measures to improve the crack formation of HRB400 screw-thread steel are put forward, which provides a powerful basis for the practical production.
文摘The properties of anti-seismic HRB400 steel bars with 25 mm diameter were systematically investigated. The results showed that the properties of the HRB400 reinforced steel bars had been greatly enhanced comparing with HRB335 steel bars, i.e. coordination of strength and ductility, strain-aging sensibility, low temperature impact toughness, weld ability and high strain low cycle fatigue. The ductile-brittle transit temperatures of hot-rolled and strain-aged steel bars were evaluated as –17 °C and ?8 °C respectively, and the low temperature impact toughness of HRB400 steel bars remains to be improved. Transmission electron microscopy (TEM) and electron diffraction showed little vanadium existed in ferrite as VN, most of which existed in pearlite as alloy cementite which resulted in the declination of impact toughness. Methods were suggested to improve the anti- seismic properties of steel bars.