A low-density single crystal(LDS) alloy with the composition of high Mo content was designed.The extra 1.5 wt% Mo was added in the Alloy A with the composition of Ni-6.5 Al-8.0 Mo-2.4 Cr-6.2 Ta-4.9 Co-1.5 Re-(0.01-0.0...A low-density single crystal(LDS) alloy with the composition of high Mo content was designed.The extra 1.5 wt% Mo was added in the Alloy A with the composition of Ni-6.5 Al-8.0 Mo-2.4 Cr-6.2 Ta-4.9 Co-1.5 Re-(0.01-0.05) Y(wt%) to study the influence of Mo on the lattice parameter and partitioning behavior.Scanning electron microscope(SEM) with energy-dispersive spectrometer(EDS),transmission electron microscopy(TEM)and high-temperature X-ray diffraction(HT-XRD) were used to observe the microstructure,analyze the elemental content and measure the lattice parameter of the alloys.The natural lattice misfit was calculated by lattice constants which were measured by HT-XRD at the temperature from 25 to 1150℃,and the results showed that the lattice misfit would be more and more negative with temperature increasing.It was found that 1.5 wt% addition of Mo will increase the absolute value of the lattice misfit of γ/γ’phases and the volume fraction of γ’,and at the same time,influence the elemental distribution in γ and γ’ phases,especially Re and Cr.Re has a higher partitioning ratio(k) after the addition of Mo.展开更多
A novel organic-inorganic composite, sorbic acid intercalated zinc aluminum layered double hydroxides (SA-ZnAl-LDHs) has been successfully assembled by a sim- ple direct coprecipitation method. A holistic approach in-...A novel organic-inorganic composite, sorbic acid intercalated zinc aluminum layered double hydroxides (SA-ZnAl-LDHs) has been successfully assembled by a sim- ple direct coprecipitation method. A holistic approach in- cluding normal XRD, FT-IR, and UV-Vis measurements and simultaneous TG/DTA/MS and in situ HT-XRD techniques was employed to explore the supramolecular intercalation structure and the thermal decomposition properties of as-synthesized SA-ZnAl-LDHs material.展开更多
基金National Natural Science Foundation of China(51202280)Shanghai Technical Platform for Testing and Characterization on Inorganic Materials(14DZ2292900)
基金financially supported by the National Natural Science Foundation of China(Nos.U1435207,51371007 and 51671015)the National Defense Basic Scientific Research Program of China(No.A2120132006)。
文摘A low-density single crystal(LDS) alloy with the composition of high Mo content was designed.The extra 1.5 wt% Mo was added in the Alloy A with the composition of Ni-6.5 Al-8.0 Mo-2.4 Cr-6.2 Ta-4.9 Co-1.5 Re-(0.01-0.05) Y(wt%) to study the influence of Mo on the lattice parameter and partitioning behavior.Scanning electron microscope(SEM) with energy-dispersive spectrometer(EDS),transmission electron microscopy(TEM)and high-temperature X-ray diffraction(HT-XRD) were used to observe the microstructure,analyze the elemental content and measure the lattice parameter of the alloys.The natural lattice misfit was calculated by lattice constants which were measured by HT-XRD at the temperature from 25 to 1150℃,and the results showed that the lattice misfit would be more and more negative with temperature increasing.It was found that 1.5 wt% addition of Mo will increase the absolute value of the lattice misfit of γ/γ’phases and the volume fraction of γ’,and at the same time,influence the elemental distribution in γ and γ’ phases,especially Re and Cr.Re has a higher partitioning ratio(k) after the addition of Mo.
基金This work was supported by the Key Project of the National Natural Science Foundation of China(Grant No．2O1060021)the Ivlinistry of Education Science and Technology Research Project of China IGrant No．Key 104239)．
文摘A novel organic-inorganic composite, sorbic acid intercalated zinc aluminum layered double hydroxides (SA-ZnAl-LDHs) has been successfully assembled by a sim- ple direct coprecipitation method. A holistic approach in- cluding normal XRD, FT-IR, and UV-Vis measurements and simultaneous TG/DTA/MS and in situ HT-XRD techniques was employed to explore the supramolecular intercalation structure and the thermal decomposition properties of as-synthesized SA-ZnAl-LDHs material.