Interface characteristics and wear resistance of Ni-B_(4)C plated ZTA reinforced high chromium cast iron composite

A chemical composite plating of Ni-B_(4)C was used to prepare the surface-modified zirconia toughened alumina(ZTA)ceramic particles.The ceramic preforms were prepared by the plated ZTA and sodium silicate solution binder,followed by casting infiltration to prepare the ZTA particles reinforced high chromium cast iron(HCCI)composites.The result reveals that a distinct interface layer forms at the ZTA/HCCI interface,which consists of phases of ZrB_(2),FeB,Fe_(2)B,and NaSiO_(4).The interfacial wettability between ZTA and HCCI is improved by the diffusion and reaction of Ni and B_(4)C.The wear test reveals that the Ni-B_(4)C plated ZTA particles can effectively improve the wear resistance of the ZTA/HCCI composite,and the wear rate of the composite is decreased to 11.6%of HCCI.

Analysis of High-Cr Cast Iron/Low Carbon Steel Wear-resistant Laminated Composite Plate Prepared by Hot-rolled Symmetrical Billet

This study developed a new technology for preparing high-chromium cast iron(HCCI)/low-carbon steel(LCS)wear-resistant composite plates by hot rolling at a 1050°C and a rolling speed of 0.2 m/s.The effects of different rolling reductions(30%,45%,and 60%)on the microstructure(interface and HCCI layer)and mechanical properties(bonding strength,hardness,and wear resistance)of the composite plate were studied.SEM images showed that when the reduction was increased,no impurities and interlayers were found between the microscopic interfaces after hot rolling,and the bonding interface exhibited a wave-like shape.EDS analysis showed that the Cr element diffusion between two metals after hot rolling was promoted when the reduction was increased,thereby improving the bonding quality under the same rolling temperature and rolling speed.Experiments showed that due to the stress release effect of the LCS of the cladded layer,the macro-slab shape after hot rolling performed well,and the brittle HCCI layer underwent thermoplastic deformation without cracking.Moreover,the increase of rolling reduction improved the bonding quality.As the rolling reduction was increased,the volume fraction of Cr-carbides in the HCCI layer also increased,resulting in an increase of hardness and wear-resistance.

Effect of Cryogenic Treatment on Property of 14Cr2Mn2V High Chromium Cast Iron Subjected to Subcritical Treatment

Effect of cryogenic treatment on the microstructure, hardening behavior and abrasion resistance of 14Cr2Mn2V high chromium cast iron （HCCI） subjected to subcritical treatment was investigated. The results show that cryogenic treatment after subcritical treatment can obviously improve the hardness and abrasion resistance of HCCI because abundant retained austenite is transformed into martensite and fine secondary carbides E（Fe, Cr）23 C6 ] precipitate. The amount of martensite and precipitated secondary carbide in HCCI experiencing subcritical treatment followed by cryogenic treatment was more than that experiencing the subcritical treatment followed by air cooling. When the abrasion resistance of HCCI reaches the maximum, its microstructure contains about 15 % retained austenite. Cryogenic treatment can further reduce the austenite content but the retained austenite cannot be transformed in to martensite completely.

Effects of Rare Earths and Al on Structure and Performance of High Chromium Cast Iron Containing Wolfram

Effects of RE and Al on the structure, impact toughness, hardness, and wear resistance of high chromium cast iron containing wolfram were investigated. The results show that without modification the volume fraction of austenite is high and the carbide appears to be thick lath and the grain size is relatively large; proper modification using RE combined with Al can reduce volume fraction of residual austenite in the as-cast structure obviously, refine grain size of primary austenite notably, and make the morphology of carbide changing from thick lath to thin lath, rosette, and feather-like modification can also increase hardness, wear resistance and impact toughness of cast iron.

Effect of Ti-V-Nb-Mo addition on microstructure of high chromium cast iron

The effects of trace additions of multi-alloying elements （Ti, Nb, V, Mo） on carbides precipitation and ascast microstructure of eutectic high chromium cast iron containing 2.85wt.%C and 31.0wt.%Cr were investigated from thermodynamic and kinetic considerations. The thermodynamic calculations show that Ti and Nb exist in the multi-alloying system in the forms of TiC and NbC. The formation of VC during the solidification is not feasible from the thermodynamic consideration. XRD analysis shows that the V exists in alloy compounds （VCr2C2, VCrFes）. The first precipitated high melting point particles （TIC, NbC） can act as the heterogeneous substrate of M7C3 carbides, which results in significant refinement of the M7C3 carbides. After the addition of alloying elements, C atom diffusion is hindered due to the strong affinities of the strong carbide forming elements for carbon, which decreases the growth rate of carbides. The combined roles of the increase of nucleation rate and the decrease of carbides growth rate lead to the finer microstructure.

Microstructure and wear resistance of highchromium cast iron containing niobium

In the paper, the effect of niobium addition on the microstructure, mechanical properties and wear resistance of high chromium cast iron has been studied. The results show that the microstructure of the heattreated alloys is composed of M7C3 and M23C6 types primary carbide, eutectic carbide, secondary carbide and a matrix of martensite and retained austenite. NbC particles appear both inside and on the edge of the primary carbides. The hardness of the studied alloys maintains around 66 HRC, not significantly affected by the Nb content within the selected range of 0.48%-0.74%. The impact toughness of the alloys increases with increasing niobium content. The wear resistance of the specimens presents little variation in spite of the increase of Nb content under a light load of 40 N. However, when heavier loads of 70 and 100 N are applied, the wear resistance increases with increasing Nb content.

Effect of vibration frequency on microstructure and performance of high chromium cast iron prepared by lost foam casting

In the present research, high chromium cast irons(HCCIs) were prepared using the lost foam casting(LFC) process. To improve the wear resistance of the high chromium cast irons(HCCIs), mechanical vibration was employed during the solidification of the HCCIs. The effects of vibration frequency on the microstructure and performance of the HCCIs under as-cast, as-quenched and as-tempered conditions were investigated. The results indicated that the microstructures of the LFC-produced HCCIs were refined due to the introduction of mechanical vibration, and the hardness was improved compared to that of the alloy without vibration. However, only a slight improvement in hardness was found in spite of the increase of vibration frequency. In contrast, the impact toughness of the as-tempered HCCIs increased with an increase in the vibration frequency. In addition, the wear resistance of the HCCIs was improved as a result of the introduction of vibration and increased with an increase in the vibration frequency.

Use of electron microscopy on microstructure characterization of high chromium cast irons

The physical metallurgy underlying the development of cast microstructures in abrasion resistant high chromium cast irons, and their structural modification by thermal treatments is relatively complex. Structural characterisation via electron microscopy therefore has a key role to play in furthering our understanding of the phase transformations that control the microstructures and hence the service performances of these irons as wear parts. This paper shows how both scanning and especially transmission electron microscopy can provide valuable information on the nature of eutectic and secondary carbides and on the matrix structures in these irons. Particular attention is given to current characterisation research on conventionally cast 30%Cr irons that are used for applications involving corrosive wear e.g. slurry pumps and on a semi-solid cast 27%Cr iron that has a potential for applications in industry.

SPHERICAL MICROSTRUCTURE FORMATION OF THE SEMI-SOLID HIGH CHROMIUM CAST IRON Cr20Mo2

The nondendritic semi-solid slurry preparation of high chromium cast iron Cr20Mo2 has been studied in this paper. The experiments show that the proeutectic austenitic particles are more spherical under a larger stirring power condition, even if the stirring time is shorter, while the proeutectic austenitic particles are not very much spherical under a smaller stirring power condition and some proeutectic austenitic dendrites also exist, even if the stirring time is very long. The experiments also show that when stirred for 5-6 minutes under the test condition, the semi-solid slurry with 40vol.%-50vol.% solid fraction and spherical proeutectic austenite in the size of 50-80μm can be obtained.

Effect of surface Cr/C infiltration on microstructure,mechanical properties and wear resistance of high chromium cast iron

A new type of high chromium cast iron(HCCI)was prepared,and its microstructure,mechanical properties,and abrasion resistance were investigated systematically.Results showed that after surface carburizing and chromizing,the microstructure of HCCI mainly consists of martensite,boride(M_(2)B),and carbide(M_(7)C_(3)),accompanied with a large amount of secondary precipitations M_(23)C_(6).Moreover,the morphology and hardness of the carbide and boride in HCCI change little,while the volume fraction of carbide and boride increases from 16.23%to 23.16%.This effectively increases the surface hardness of HCCI from 64.53±0.50 HRC to 66.58±0.50 HRC,with the result that the surface of HCCI possesses a better abrasion resistance compared to the center position.Furthermore,the wear mechanism of HCCI changes from micro-plowing to micro-cutting with the increase of surface hardness.

STUDY ON THE STRUCTURE AND PROPERTIES OF HIGH CHROMIUM WHITE CAST IRON AND ITS TEMPERING STANDARD

The structure and properties of high chromium white cast iron in different treatment states were studied. Using X ray diffraction method, observing their metallograph and measuring their microhardness, the phases involved in the iron were determined. The notch toughness, macrohardness and the fractograph of the samples are compared and their performance was determined, which mainly depends on the matrix structure. Relatively good comprehensive properties can be obtained in the tempering state. Improvements have been made on the commonly used tempering standard. Tempering for a short period at low temperature can improve the materials′ service performance obviously.

Effect of Manganese on As-Cast Microstructure and Hardening Behavior of High Chromium White Cast Iron

The effect of manganese on the as-cast structure and hardening behavior of high chromium white cast iron subjected to sub-critical treatment was studied.The results indicate that the fraction of retained austenite and the manganese distribution in as-cast alloys are controlled by manganese content.The manganese distribution in as-cast alloys is not homogeneous.The manganese content in carbide is higher than that in matrix.Whether the secondary hardening occurs or not and the peak hardness of secondary hardening is controlled by manganese content in retained austenite in as-cast structure.Higher manganese content can cause more retained austenite.The secondary hardening occurs in sub-critical treating process if the fraction of retained austenite is high.

Effects of RE,V,Ti and B composite modification on the microstructure and properties of high chromium cast iron containing 3% molybdenum

The effects of RE, V, Ti and B on the microstructure and properties of high chromium cast iron containing 3% molybdenum under as-cast and heat treatment conditions were investigated with the method of comparing experiments. The results show that with the increase of RE content, the primary austenite of high chromium cast iron is obviously refined. The morphology of carbide is changed from netlike and lath to small multiangular isolated blocks or massive blocks, the isolated degree of carbide is improved obviously, and the size is significantly refined. The addition of V and B into high chromium cast iron can refine the microstmcture, reduce coarse columnar crystals and make the carbide smaller and uniform. Through composite modification with RE, V, Ti and B, the hardness, wear resistance and impact toughness of high chromium cast iron are increased conspicuously. After heat treatment, the hardness of high chromium iron is increased significantly, but the toughness and wear resistance do not show great improvement.

Effect of RE Complex Inoculation on the Fatigue Wear Behaviours of High Chromium Cast Iron

Inoculation of high chromium cast iron is made by RE complex inoculant. Influence of inoculating on rolling fatigue wear characteristics of high chromium cast iron is investigated. The experimental resutls indicate that high chromium cast iron inoculated by RE complex inoculation is improved in structure and properties, i. e. fatigue wear sevice life is prolonged and relative wear resistance is increased greatly.

Influences of copper on solidification structure and hardening behavior of high chromium cast irons

The influences of copper on microstructure and the hardening behavior of high chromium cast irons subjected to sub-critical treatment were investigated. The results show that the microstructure of the as-cast high chromium cast irons consists of retained austenite, martensite and M1C3 type eutectic carbide. When copper is added into high chromium cast irons, austenite and carbide contents are increased. The increased addition of copper content from 0% to 1.84% leads to the increase of austenite and carbide from 15.9% and 20. 0% to 61.0% and 35.5% , respectively. In the process of sub-critical treatment, the retained austenite in the matrix can be precipitated into secondary carbides and then transforms into martensite in cooling process, which causes the secondary hardening of the alloy under sub-critical treatment. High chromium cast irons containing copper in sub-critical treatment appear the second hardening curve peak due to the precipitation of copper from supersaturated matrix.

RESEARCH AND APPLICATION OF AS-CAST WEAR RESISTANCE HIGH CHROMIUM CAST IRON

The influence of alloy elements, such as boron and silicon, on the microstructure and properties of as cast high chromium cast iron is studied. The results show that boron and silicon have a great effect on the mechanical properties and the wear resistance. Through proper addition of boron and silicon, the properties of as cast high chromium cast iron can be improved effectively. Through analyzing the distribution of elements by scanning electron microscope, it has been shown that the addition of boron and silicon lowers the mass fraction of chromium saturated in as cast austenite, and makes it unstable and liable to be transformed into martensite. The as cast high chromium cast iron with proper content of boron and silicon is suitable for the manufacture of lining for asphalt concrete mixer and its wear resistance is 14 times that of lining made of low alloy white cast iron.

OXIDATION BEHAVIOUR OF HIGH Cr CAST IRON

The oxidation behaviour of high Cr Cast iron was investigated at 950 and 800℃ in terms of Cr content in matrix and the amount of carbide.The morphology and types of oxide films and the microstructure of subsurface were also examined.The main conclusions are:1)The original chromium content in the matrix determines the type of oxide film and it is an important factor for the oxidation resistance of high chromium cast iron;2) The oxidation resistance improves with increasing carbide content at 950℃ because of the decomposition of the carbide,while the decompsition of the carbide do not take place at 800℃ so the oxidation resisteance do not improve with increasing carbide volume.

Effects of Heat Treatment on Hardness and Dry Wear Properties of a Semi-Solid Processed Fe-27 wt pct Cr-2.9 wt pct C Cast Iron

EfFects of heat treatments on hardness and dry wear properties of a semi-solid processed Fe-26.96 wt pct Cr- 2.91 wt pct C cast iron were studied. Heat treatments included tempering at 500℃, destabilisation at 1075℃ and destabilisation at 1075℃ plus tempering at 500℃, all followed by air cooling. Electron microscopy revealed that, in the as-cast condition, the primary proeutectic austenite was round in shape while the eutectic M7C3 carbide was found as radiating clusters mixed with directional clusters. Tempering did not change the microstructure significantly when observed by scanning or transmission electron microscopy. Destabilisation followed by air cooling led to a precipitation of secondary M23C6 carbide and a transformation of the primary austenite to martensite. Precipitation behaviour is comparable to that observed in the conventionally cast iron. Tempering after destabilisation resulted in a higher amount of secondary carbide precipitation within the tempered martensite in the eutectic structure. Vickers macrohardness and microhardness in the proeutectic zones were measured. Dry wear properties were tested by using a pin-on-disc method. The maximum hardness and the lowest dry wear rate were obtained from the destabilisation-plus-tempering heat treatment due to the precipitation of secondary carbides within the martensite matrix and a possible reduction in the retained austenite.

Electron theory study on the effect of Mn on as-cast structure of Fe-C-Cr-Mn cast irons

The valence electron structure of alloying austenite of 3C-15Cr high chromium white cast iron with different Mn contents from 1% to 6% is analyzed by BLD method and EET. Results show that the addition of Mn has major influence on the valence electron structure of the alloying austenite, especially on that of Fe-C, Fe-C-Cr and Fe-C-Cr-Mn unit cells of it. The effect becomes weak when Mn content is over 4%. Based on the effect of n~, F~~, the weighting of each unit cell and the degree of undercooling on phase transition of the aus- tenite, we can calculate the retained austenite content of as-cast structure of the high chromium white cast iron. The calculation results coincide well with those of the experiment. The phase transition characters of the austenite in high chromium white cast iron can be forecasted through valence electron structure analysis of alloying austenite by BLD method and EET on the basis of Fe-C-Cr equilibrium phase diagram.

镍含量对高铬铸铁组织结构及耐热性能的影响

利用X射线衍射仪(XRD)、光学显微镜(OM)、扫描电镜(SEM)、高温抗氧化试验以及高温热疲劳试验等研究了3种镍含量不同(0.65%、1.5%和3.05%)的高铬铸铁组织结构以及耐热性能。结果表明:3种高铬铸铁的物相均为奥氏体、马氏体和(Cr,Fe)_(7)C_(3)碳化物,镍含量的增加使得奥氏体含量增加,马氏体含量减少。高铬铸铁组织结构均由先共晶树枝晶以及枝晶间的共晶组织构成,镍含量的增加使得树枝晶粗化,共晶组织得到了细化。在高温抗氧化试验中,随着镍含量的增加,高铬铸铁的氧化增重减少,氧化层厚度减薄。3种高铬铸铁的氧化层都有内外两层,含0.65%和1.5%镍的高铬铸铁的外层主要元素是O和Fe,内层主要元素是O和Cr;含3.05%镍的高铬铸铁的外层主要元素是O和Cr,内层主要元素是O和Fe。高温热疲劳试验中,3种高铬铸铁的主裂纹均沿着V型缺口延展而出,随着镍含量的增加,主裂纹的长度减少。含3.05%镍的高铬铸铁的抗热疲劳性能比含0.65%镍的高铬铸铁提高了36%。