Characteristics and formation mechanisms of defect bands in vacuum-assisted high-pressure die casting AE44 alloy

The microstructure in vacuum-assisted high-pressure die casting(HPDC) Mg-4Al-4RE(AE44) alloy was studied. Special attention was paid to the characteristics of defect bands and their formation mechanisms. Since double defect bands are commonly observed, the cross section of die cast samples is divided into five parts with different grain morphologies and size distributions. The inner defect band is much wider than the outer one. Both the defect bands are solute segregation bands, resulting in a higher area fraction of Al;RE;phase than that in the adjacent regions. No obvious aggregation of porosities is observed in the defect bands of AE44 alloy. This may be due to a narrow solidification temperature range of AE44 alloy and a large amount of latent heat released during the precipitation of intermetallic phases. The formation of the defect bands is related to the shear stress acting upon the partially solidified alloy, which can lead to collapse of the grain network. However, the generation mechanisms of shear stress in the outer and inner defect bands are quite different.

Finite element analysis for die casting parameters in high-pressure die casting process

The gating system and the overflow system were designed according to the casting structure during high pressure die casting(HPDC) process. The simulation was carried out by ProCAST software to visualize the injection chamber pre-crystallization and the flow of molten metal. The main work is to research four die casting process parameters, i.e. injection temperature, low-pressure velocity, high-and low-pressure velocity’s switching position, and high-pressure velocity. Experimental results show that the higher injection temperature and lowpressure velocity can mitigate the pre-crystallization of the injection chamber. However, when the low-pressure velocity exceeds 0.2 m·s-1, the air entrapment in the chamber occurs. Besides, when the high-pressure velocity is greater than 2.5 m·s-1, the overflow channel at the final filling position is covered by the liquid metal too early. Finally, the injection temperature of 650 °C, the low-pressure velocity of 0.2 m·s-1, the high-and low-pressure velocity’s switching position of 320 mm and the high-pressure velocity of 2 m·s-1 are obtained as the optimal parameters by the software simulation, which has been verified by actual production.

Feasibility of semi-solid die casting of ADC12 aluminum alloy

The feasibility of semi-solid die casting of ADC12 aluminum alloy was studied. The effects of plunger speed, gate thickness, and solid fraction of the slurry on the defects were determined. The defects investigated are gas and shrinkage porosity. In the experiments, semi-solid slurry was prepared by the gas-induced semi-solid （GISS） technique. Then, the slurry was transferred to the shot sleeve and injected into the die. The die and shot sleeve temperatures were kept at 180 ℃ and 250 ℃, respectively. The results show that the samples produced by the GISS die casting give little porosity, no blister and uniform microstructure. From all the results, it can be concluded that the GISS process is feasible to apply in the ADC12 aluminum die casting process. In addition, the GISS process can give improved properties such as decreased porosity and increased microstructure uniformity.

Strengthening technology and mechanism for semi-solid die casting of aluminum alloy

Combined with theoretical evaluation, an optimized strengthening process for the semi-solid die castings of A356 aluminum alloy was obtained by studying the mechanical properties of castings solution treated and aged under different conditions in detail, then, the semi-solid die castings and liquid die castings were heat treated with the optimized process. The results show that the mechanical properties of semi-solid die castings of aluminum alloy are superior to those of the liquid die castings, especially the strengthening degree of heat treated semi-solid die castings is much greater than that of liquid die castings with the tensile strength more than 330 MPa and the elongation more than 10%, and this is mainly contributed to the non-dendritic and more compact microstructure of semi-solid die castings. The strengthening mechanism of heat treatment for the semi-solid die castings of A356 aluminum alloy is due to the dispersive precipitation of the second phase（Mg2Si） and formation of GP Zone.

Mould filling ability and microstructure of aluminum alloy under electromagnetic die casting

In order to solve the mould filling problem of large thin walled aluminum alloy castings effectively, a new casting technology called electromagnetic die casting has been developed. Emphasis has laid on studying the mould filling ability and microstructure under the mentioned method. The results show that the mould filling ability of A357 is increasing continually with the increasing of the input voltage, that is, the magnetic induction intensity. The pressure head of the molten metal increases from the lowest one at the input of the mould to the highest one at the end of the mould while in a conventional mould the pressure head depends invariably on the sprue height. Under electromagnetic die casting, the grains of A357 alloy are refined, and the pattern of eutectic silicon of alloy changes from rough plate to smooth strip.

Semi-solid near-net shape rheocasting of heat treatable wrought aluminum alloys

Flexibility of the CSIR-RCS, induction stirring with simultaneous air cooling process, in combination with high pressure die casting is successfully demonstrated by semi-solid rheocasting of plates performed on commercial 2024, 6082 and 7075 wrought aluminum alloys. Tensile properties were measured for the above mentioned rheocast wrought aluminum alloys in the T6 condition. The results showed that tensile properties were close to or even in some cases exceeded the minimum specifications. The yield strength and elongation of rheocast 2024-T6 exceeded the minimum requirements of the wrought alloy in the T6 condition but the ultimate tensile strength achieved only 90% of the specification because the Mg content of the starting alloy was below the commercial alloy specification. The strengths of rheocast 6082-T6 exceeded all of the wrought alloy T6 strength targets but the elongation only managed 36% of the required minimum due to porosity, caused by incipient melting during solution heat treatment, and the presence of fine intermetallie needles in the eutectic. The yield strength of rheocast 7075 exceeded the required one and the ultimate tensile strength also managed 97% of the specification; while the elongation only reached 46% of the minimum requirement also due to incipient melting porosity caused during the solution heat treatment process.

Die Casting Mold Design of the Thin-walled Aluminum Case by Computational Solidification Simulation

Recently, demand for the lightweight alloy in electric/electronic housings has been greatly increased. However, among the lightweight alloys, aluminum alloy thin-walled die casting is problematic because it is quite difficult to achieve sufficient fluidity and feedability to fill the thin cavity as the wall thickness becomes less than 1mm. Therefore, in this study, thin-walled die casting of aluminum （Al-Si-Cu alloy： ALDC 12） in size of notebook computer housing and thickness of 0.8 mm was investigated by solidification simulation （MAGMA soft） and actual casting experiment （Buhler Evolution B 53D）. Three different types of gating design, finger, tangential and split type with 6 vertical runners, were simulated and the results showed that sound thin-walled die casting was possible with tangential and split type gating design because those gates allowed aluminum melt to flow into the thin cavity uniformly and split type gating system was preferable gating design comparing to tangential type gating system at the point of view of soundness of casting and distortion generated after solidification. Also, the solidification simulation agreed well with the actual die-casting and the casting showed no casting defects and distortion.

Characterization on the formation of porosity and tensile properties prediction in die casting Mg alloys

The 3D visualization of the porosity in high-pressure die casting(HPDC)Mg alloys AZ91D and Mg4Ce2Al0.5Mn(EA42)was investigated by X-ray computed tomography.It was demonstrated that the volumetric porosity at the near-gate location for alloy EA42 was significantly higher than that far from the gate location.This difference resulted from the low valid time during intensified casting pressure conditions.Specimens of alloy EA42 exhibited a narrow pore distribution in the side view(~0.5 mm)compared to the wide distribution(~1.8 mm)of alloy AZ91D,which was mainly attributed to the formation mechanism of the defect band.The formation of microporosity in the defect band of alloy EA42 was inhibited because of the significant latent heat released by a large amount of the Al11Ce3phase segregated in the defect band during solidification.Additionally,an effective estimator(Z-Propagation)was introduced,which is proposed to predict the projected area fraction of the porosity(f)involved during tensile failure with better effectiveness compared with traditional methods based on the actual fractured surface.By coupling the Z-Propagation method with the critical local strain model,the logarithmic fracture strain and true fracture stress of the specimens were predicted within 3.03%and 1.65%of the absolute value of the average relative error(AARE),respectively.

High thermal conductivity and high strength magnesium alloy for high pressure die casting ultrathin-walled components

With the rapid development of 3C industries,the demand for high-thermal-conductivity magnesium alloys with high mechanical performance is increasing quickly.However,the thermal conductivities of most common Mg foundry alloys(such as Mg-9wt%-1wt%Zn)are still relatively low.In this study,we developed a high-thermal-conductivity Mg-4Al-4Zn-4RE-1Ca(wt%,AZEX4441)alloy with good mechanical properties for ultrathin-walled cellphone components via high-pressure die casting(HPDC).The HPDC AZEX4441 alloy exhibited a fine homogeneous microstructure(average grain size of 2.8μm)with granular Al_(11)RE_(3),fibrous Al_(2)REZn_(2),and networked Ca_(6)Mg_(2)Zn_(3) phases distributed at the grain boundaries.The room-temperature thermal conductivity of the HPDC AZEX4441 alloy was 94.4 W·m^(-1)·K^(-1),which was much higher than 53.7 W·m^(-1)·K^(-1) of the HPDC AZ91D alloy.Al and Zn in the AZEX4441 alloy were largely consumed by the formation of Al_(11)RE_(3),Al_(2)REZn_(2),and Ca_(2)Mg_(6)Zn_(3) phases because of the addition of RE and Ca.Therefore,the lattice distortion induced by solute atoms of the AZEX4441 alloy(0.171%)was much lower than that of the AZ91D alloy(0.441%),which was responsible for the high thermal conductivity of the AZEX4441 alloy.The AZEX4441 alloy exhibited a high yield strength of~185 MPa,an ultimate tensile strength of~233 MPa,and an elongation of~4.2%.This result indicated that the tensile properties were comparable with those of the AZ91D alloy.Therefore,this study contributed to the development of high-performance Mg alloys with a combination of high thermal conductivity,high strength,and good castability.

Mechanism of die soldering during aluminum die casting

Soldering is a unique casting defect associated with die casting or metal mold casting of aluminum al oys. It occurs when molten aluminum sticks or solders the surface of the die steel and remains there after the ejection of the casting, causing a surface defect and dimensional inaccuracy of the castings and increased machine downtime. Soldering occurs easily when a bare die steel mold is used for die casting of aluminum al oys. When molten aluminum comes in contact with the die steel at a temperature higher than a critical temperature, the iron and aluminum atoms diffuse into each other, forming a series of intermetallic phases and a liquid aluminum-rich fcc phase. This liquid phase exists between intermetal ic phases. On cooling, the liquid fcc phase solidiifes on the intermetal ic phases and grows into the casting, resulting in soldering. The critical temperature is the eutectic temperature near the aluminum corner of the phase diagram. If the die is protected using a nonreactive ceramic coating, soldering starts at locations where local coating failure occurs. Molten aluminum comes into contact with die steel through the coating failure locations and eats into the steel matrix, forming smal pits. As these smal pits grow, the coating is gradual y removed and soldering becomes more severe. Details of die soldering step on a bare steel die and on a coated die material are discussed.

Influence of samarium content on microstructure and mechanical properties of recycled die-cast YL112 aluminum alloys

The influence of Sm （Samarium） content on microstructure and mechanical properties of recycled die-cast YLl12 aluminum alloys was investigated. The results show that many small Sm-rich particles form in the recycled die-cast YLl12 alloys with Sm addition. At the same time, the secondary dendrite arm spacing in the YLl12 alloys modified with Sm is smaller than that of the unmodified alloy. The eutectic Si of recycled die- cast YL112-xSm alloys transforms from coarse acicular morphology to fine fibres. Mechanical properties of the investigated recycled die-cast YLl12 aluminum alloys are enhanced with Sm addition, and a maximal ultimate tensile strength value （276 MPa） and elongation （3.76%） are achieved at a Sm content of 0.6wt.%. Due to the modification of eutectic Si by Sm, numerous tearing ridges and tiny dimples on the fractures of tensile samples are observed.

Machining studies of die cast aluminum alloy-silicon carbide composites

Metal matrix composites （MMCs） with high specific stiffness, high strength, improved wear resistance, and thermal properties are being increasingly used in advanced structural, aerospace, automotive, electronics, and wear applications. Aluminum alloy-silicon carbide composites were developed using a new combination of the vortex method and the pressure die-casting technique in the present work. Machining studies were conducted on the aluminum alloy-silicon carbide （SiC） composite work pieces using high speed steel （HSS） end-mill tools in a milling machine at different speeds and feeds. The quantitative studies on the machined work piece show that the surface finish is better for higher speeds and lower feeds. The surface roughness of the plain aluminum alloy is better than that of the aluminum alloy-silicon carbide composites. The studies on tool wear show that flank wear increases with speed and feed. The end-mill tool wear is higher on machining the aluminum alloy-silicon carbide composites than on machining the plain aluminum alloy.

Comparative Analysis of the Effects of Pressure on the Mechanical Properties and Microstructure of Die Cast Aluminum Alloys

A study of the effects of pressure on the microstructure and mechanical properties of two aluminum alloys (A1350 and A380) was carried out and subsequent analysis made. Pressure was regulated at various levels in the die cast machine. Samples of both alloys were cast under varying regulated applied pressure. The mechanical properties of both alloy casts were tested and microstructure analysis done and the results compared for both alloys. The results obtained show that hardness, tensile strength, yield strength and impact strengths for both alloy cast samples followed similar pattern in the casting process. The hardness values increased with applied pressure but not too significantly in both alloy casts as pressure rose in the casting process. The yield strength of both alloy casts also increased with applied pressure. The impact strength and elongations also increased with applied pressure in both alloy casts. Also the microstructure analysis carried out on both alloy casts showed similar pattern of structural changes in the morphologies of both alloy casts as grains became fine as pressure rose from 350 to 1400 kg/cm2. Models were developed for the results and for all the models developed, a close relationship with the experimental results were underlying in view of the small errors generated by them and can be used to predict the experimental values.

基于ProCAST的一模多腔YL112铝合金压铸件数值模拟及工艺优化

针对YL112压铸铝合金一模多铸产品的组织性能均一性需求,采用ProCAST软件对典型一模多铸工艺进行模拟,比较了两种不同充型顺序的压铸方案。结果表明:基于顺序凝固一模多腔压铸件由于充型与凝固过程的温度场分布不均,导致近浇口端铸件出现明显缩松缩孔缺陷,造成铸件性能均一性差。后续采用等流程浇注系统,实现一模多腔铸件同时充型凝固过程,改善了铸件温度场分布,减少了工艺缺陷。经过实际生产验证,获得了组织性能均一性好的压铸件。

Design of Mg-Zn-Si-Ca casting magnesium alloy with high thermal conductivity

Magnesium alloys are commonly used to produce lightweight parts.While most magnesium alloys exhibit low thermal conductivities,high thermal conductivities are needed for electronic devices.In this study,we attempted to develop new magnesium casting alloys with high thermal conductivities.The Mg-Zn-Si-Ca alloy compositions were chosen using CALPHAD(CALculation of PHAse Diagrams)calculations,and alloy samples were prepared.The fluidity and hot-tearing resistance were measured.The results indicated that these properties were similar to those of AZ91 alloy.Tensile tests showed that high-pressure die casting could produce Mg-Zn-Si-Ca alloys possessing mechanical properties 1.5-3 times higher than those produced via sand casting.The alloy thermal conductivity was 126 W/mK at room temperature.The corrosion rates of the as-cast samples in NaCl/water solutions were two times higher than that of AZ91.

Low-cycle fatigue behavior of permanent mold cast and die-cast Al-Si-Cu-Mg alloys

Fatigue failure is one of the main failure forms of Al-Si-Cu-Mg aluminum alloys. To feature their mechanical aspect of fatigue behavior, the low-cycle fatigue behavior of permanent mold cast and die-cast AI-Si- Cu-Mg alloys at room temperature was investigated. The experimental results show that both permanent mold cast and die-cast AI-Si-Cu-Mg alloys mainly exhibit cyclic strain hardening. At the same total strain amplitude, the diecast AI-Si-Cu-Mg alloy shows higher cyclic deformation resistance and longer fatigue life than does the permanent mold cast AI-Si-Cu-Mg alloy. The relationship between both elastic and plastic strain amplitudes with reversals to failure shows a monotonic linear behavior, and can be described by the Basquin and Coffin-Manson equations, respectively.

Application of Photon-Counting X-ray Computed Tomography to Aluminum-Casting Inspection

One of the issues in the aluminum-alloy die casting industry is the space occurring inside the casting, and the improvement of the verification technology is expected. The purpose of this research is to seal holes inside the aluminum metal by resin and verify them by photon-counting X-ray computed tomography (CT) using an energy-discrimination 64-channel cadmium-telluride (CdTe) line detector. Moreover, it is important to estimate the image of the effective atomic number and the electronic density by the energy mapping of the attenuation coefficient utilizing photon-counting X-ray CTto distinguish both the aluminum metal and the resin filler in the aluminum hole. As a result, the energy discrimination of the resin filler in the space of aluminum casting has been attained. We could observe the atomic number image utilizing dual-energyX-ray CTmethod with the 64-channel CdTe photon-counting detector.

Strength and ductility optimization of HPDC AlSi8MgCuZn2 alloys by modifying pre-aging treatment

Considering the components produced by high pressure die casting(HPDC)process usually with ultra-large sizes and complex morphologies,high temperature solid solution treatment is not a suitable method to further improve their mechanical properties.In this study,two-stage aging treatment with different pre-aging times was designed and employed to further improve the mechanical properties of HPDC Al8SiMgCuZn alloy.The characteristics of precipitates were evaluated by a transmission electron microscope(TEM),and the precipitation strengthening mechanism was discussed.The results reveal that the strengthening is mainly contributed by the precipitation ofβ″phase after two-stage aging,and the number density and size of the precipitates are significantly depended on the pre-aging time.The number density of precipitates is increased with the pre-aging time prolonged from 0 h to 4 h,and then decreases with the further increase of pre-aging time from 4 h to 6 h.The precipitates with the highest density and smallest size are observed after pre-aging for 4 h.After pre-aged at 100℃for 4 h and then artificial aged at 200℃for 30 min,the yield strength of 207 MPa,ultimate tensile strength of 325 MPa and elongation of 7.6%are achieved.

Advanced casting technologies for lightweight automotive applications

This paper provides an overview of alloy and process developments in aluminum and magnesium castings for lightweight automotive applications. Wear-resistant aluminum alloys, creep-resistant and high strength/ductility magnesium alloys have been developed for automotive applications. On the process front, vacuumassisted die casting and high vacuum die casting technologies have been developed for high-integrity body and chassis applications. Thin-wall and hollow casting components are being produced by low-pressure die casting processes for structural applications. Overcasting technology is gaining traction and has enabled mixed material designs for automotive sub-systems such as engine cradles and instrument panel beams. Simulation tools developed to predict the interfacial interactions of the dissimilar components and the structural integrity of the overcast systems are being validated in the casting trials.

Microstructures and mechanical properties of a newly developed high-pressure die casting Mg-Zn-RE alloy

A newly developed Mg-4Zn-2La-3Y alloy with high strength was fabricated by high-pressure die casting method,and its microstructures were thoroughly studied using transmission electron microscopy.The results demonstrate that it owns fine grains and approximately highly interconnected intermetallic phase skeletons,and exhibits ultra-high strength at both room and high temperatures.Interestingly,the eutectic intermetallic skeleton of this alloys is consisted of numerous fine particles,which are mainly consisted of two intermetallic phases,namely W and Mg12RE.Multiple{101}twins and SFs were found in the Mg12RE phase while a few of SFs in the W phase.Additionally,minor long-period stacking ordered phase was observed in the eutectoid phase,and it probably nucleated on the Mg12RE phase following a certain OR as(0002)14H//(110)Mg12REand[1120]14H//[111]Mg12RE,or(0002)14H//(211)Mg12REand[1120]14H//[111]Mg12RE.This special intermetallic skeleton with many interfaces and planar faults can efficiently transfer dislocations across grain boundaries,and this is the key factor for the outstanding mechanical properties of the studied alloy.