A substrate hot holes injection method is used to quantitatively examine the roles of electrons and holes separately in thin gate oxides breakdown.The shift of threshold voltage under different stress is discussed.It ...A substrate hot holes injection method is used to quantitatively examine the roles of electrons and holes separately in thin gate oxides breakdown.The shift of threshold voltage under different stress is discussed.It is indicated that positive charges are trapped in SiO 2 while hot electrons are necessary for SiO 2 breakdown.The anode holes injection model and the electron traps generation model is linked into a consistent model,describing the oxide wearout as an electron correlated holes trap creation process.The results show that the limiting factor in thin gate oxides breakdown depends on the balance between the amount of injected hot electrons and holes.The gate oxides breakdown is a two step process.The first step is hot electron's breaking Si-O bonds and producing some dangling bonds to be holes traps.Then the holes are trapped and a conducted path is produced in the oxides.The joint effect of hot electrons and holes makes the thin gate oxides breakdown complete.展开更多
Although hot carriers induced degradation of NMOSFETs has been studied for decades, the role of hot electron in this process is still debated. In this paper, the additional substrate hot electrons have been intentiona...Although hot carriers induced degradation of NMOSFETs has been studied for decades, the role of hot electron in this process is still debated. In this paper, the additional substrate hot electrons have been intentionally injected into the oxide layer to analyze tile role of hot electron in hot carrier degradation. The enhanced degradation and the decreased time exponent appear with the injected hot electrons increasing, the degradation increases from 21.80% to 62.00% and the time exponent decreases from 0.59 to 0.27 with Vb decreasing from 0 V to -4 V, at the same time, the recovery also becomes remarkable and which strongly depends on the post stress gate bias Vg. Based on the experimental results, more unrecovered interface traps are created by the additional injected hot electron from the breaking Si-H bond, but the oxide trapped negative charges do not increase after a rapid recovery.展开更多
文摘A substrate hot holes injection method is used to quantitatively examine the roles of electrons and holes separately in thin gate oxides breakdown.The shift of threshold voltage under different stress is discussed.It is indicated that positive charges are trapped in SiO 2 while hot electrons are necessary for SiO 2 breakdown.The anode holes injection model and the electron traps generation model is linked into a consistent model,describing the oxide wearout as an electron correlated holes trap creation process.The results show that the limiting factor in thin gate oxides breakdown depends on the balance between the amount of injected hot electrons and holes.The gate oxides breakdown is a two step process.The first step is hot electron's breaking Si-O bonds and producing some dangling bonds to be holes traps.Then the holes are trapped and a conducted path is produced in the oxides.The joint effect of hot electrons and holes makes the thin gate oxides breakdown complete.
基金supported by the National Natural Science Foundation of China(Grant No.61376109)the Opening Project of National Key Laboratory of Science and Technology on Reliability Physics and Application Technology of Electrical Component,China(Grant No.ZHD201202)
文摘Although hot carriers induced degradation of NMOSFETs has been studied for decades, the role of hot electron in this process is still debated. In this paper, the additional substrate hot electrons have been intentionally injected into the oxide layer to analyze tile role of hot electron in hot carrier degradation. The enhanced degradation and the decreased time exponent appear with the injected hot electrons increasing, the degradation increases from 21.80% to 62.00% and the time exponent decreases from 0.59 to 0.27 with Vb decreasing from 0 V to -4 V, at the same time, the recovery also becomes remarkable and which strongly depends on the post stress gate bias Vg. Based on the experimental results, more unrecovered interface traps are created by the additional injected hot electron from the breaking Si-H bond, but the oxide trapped negative charges do not increase after a rapid recovery.