The causes of tiny spot defects on the surface of hot-dip galvanized automotive steel sheets were studied using scanning electron microscopy(SEM)and energy dispersive spectrometer(EDS),and effective control measures w...The causes of tiny spot defects on the surface of hot-dip galvanized automotive steel sheets were studied using scanning electron microscopy(SEM)and energy dispersive spectrometer(EDS),and effective control measures were introduced.The results show that rubbing against the top roller after galvanizing is easy due to the local thickness of tiny spot defect location coating;therefore,the surface morphology is different from the normal part.Three kinds of defects,namely zinc slag,small slivers,and pitting,are likely to cause local thickening of the coating after galvanizing,leading to the formation of tiny spots.Therefore,resolving the three types of defects can effectively control the generation of tiny spot defects.Among them,due to the hereditary nature of the small sliver defect,focusing on its control and supervision is necessary.展开更多
Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel prod...Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel products.Some milestones achieved by Baosteel automotive steel sheet were briefly reviewed.The current challenges in producing ultra-high strength steel(UHSS),especially hot-dip galvanized UHSS,were summarized.The most current advancements in UHSS and the corresponding hot-dip galvanizing processes were discussed.The galvanizability of Si-Mn-added QP steel and DP steel, Mn-added TWIP steel, and Al-added low-density steel has been improved by different techniques in Baosteel.展开更多
文摘The causes of tiny spot defects on the surface of hot-dip galvanized automotive steel sheets were studied using scanning electron microscopy(SEM)and energy dispersive spectrometer(EDS),and effective control measures were introduced.The results show that rubbing against the top roller after galvanizing is easy due to the local thickness of tiny spot defect location coating;therefore,the surface morphology is different from the normal part.Three kinds of defects,namely zinc slag,small slivers,and pitting,are likely to cause local thickening of the coating after galvanizing,leading to the formation of tiny spots.Therefore,resolving the three types of defects can effectively control the generation of tiny spot defects.Among them,due to the hereditary nature of the small sliver defect,focusing on its control and supervision is necessary.
文摘Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel products.Some milestones achieved by Baosteel automotive steel sheet were briefly reviewed.The current challenges in producing ultra-high strength steel(UHSS),especially hot-dip galvanized UHSS,were summarized.The most current advancements in UHSS and the corresponding hot-dip galvanizing processes were discussed.The galvanizability of Si-Mn-added QP steel and DP steel, Mn-added TWIP steel, and Al-added low-density steel has been improved by different techniques in Baosteel.