Phenolic-resin composites reinforced with carbon fiber（CF） and basalt fiber（BF） interlayer hybrid fibers plain fabric were fabricated.The tensile strength,compressive strength and interlaminar shear strength of th...Phenolic-resin composites reinforced with carbon fiber（CF） and basalt fiber（BF） interlayer hybrid fibers plain fabric were fabricated.The tensile strength,compressive strength and interlaminar shear strength of the prepared composites were studied.The results indicated that hybrid fibers reinforced composites possessed the advantages of both CF and BF.When resin content was 35% by volume fraction,the comprehensive mechanical performance of BF/CF reinforced phenolic resin composites reached the optimal values with the warp and weft direction tensile strength,compressive strength and interlayer shear strength being 252 MPa and 487 MPa,105 MPa and 129 MPa,21 MPa and 20 MPa,respectively.The scanning electron microscope（SEM） observations showed that the BF/CF hybrid fibers reinforced composites had better interfacial adhesion.展开更多
A novel super-hybrid composite (NSHC) is prepared with three-dimension reticulated SiC ceramic (3DRC), high performance carbon fibers and modified phenolic resin (BPR) in this paper. Ablation performance of super-hybr...A novel super-hybrid composite (NSHC) is prepared with three-dimension reticulated SiC ceramic (3DRC), high performance carbon fibers and modified phenolic resin (BPR) in this paper. Ablation performance of super-hybrid composite is studied. The results show that the NSHC has less linear ablation rate compared with pure BPR and CF/BPR composite, for example, its linear ablation rate is 50% of CF/BPR at the same fiber content. Mass ablation rate of the NSHC is slightly lower than that of pure BPR and CF/BPR composite because of their difference in the density. Scanning electron microscopic analysis indicates that 3DRC can increase anti-erosion capacity of materials because its special reticulated structure can control the deformation of materials and strengthen the stability of integral structure.展开更多
The role of nanofillers in reducing the microleakage of dental composite resins has not been previously investigated. So this study was designed to evaluate microleakage of nanofilled composite resin in comparison to ...The role of nanofillers in reducing the microleakage of dental composite resins has not been previously investigated. So this study was designed to evaluate microleakage of nanofilled composite resin in comparison to the conventional hybrid composite. Twenty extracted sound molars were selected. Class II cavities were prepared. All cavities were etched (enamel and dentin) with 37% phosphoric acid. Dentin bonding agents were applied to etched tooth surfaces and restored with nanofilled and hybrid composite restorative materials. The restored teeth were thermocycled. Specimens were immersed in 2% methylene blue dye, sectioned along the mesio-distal direction;dye penetration of occlusal and gingival margins of each section was evaluated using a stereo-microscope. No significant difference was found between the microleakage of nanofilled and hybrid composite restorations at occlusal / enamel and at gingival / dentin margins. Also, there were no significant differences for nanofilled composite restorations at occlusal / enamel margins and gingival / dentin margins. On the other hand, there were a significant differences for hybrid composite restorations at occlusal / enamel margins and gingival / dentin margins.展开更多
New liquid free radical-cationic hybrid photopolymer, consisting of acrylate-based photocurable resin and epoxy-based photosensitive resin for stereolithography by UV laser was developed. The experiment results indica...New liquid free radical-cationic hybrid photopolymer, consisting of acrylate-based photocurable resin and epoxy-based photosensitive resin for stereolithography by UV laser was developed. The experiment results indicated that the hybrid photopolymer exhibits advantages of both the acrylate-based photosensitive resin and the epoxy-based photosensitive polymer contained in the hybrid system with relatively high photospeed and low linear shrinkage. Stereolithography parts without obvious distortion were built on the stereolithography apparatus HRPLA- I from this hybrid resin successfully and efficiently.展开更多
文摘Phenolic-resin composites reinforced with carbon fiber（CF） and basalt fiber（BF） interlayer hybrid fibers plain fabric were fabricated.The tensile strength,compressive strength and interlaminar shear strength of the prepared composites were studied.The results indicated that hybrid fibers reinforced composites possessed the advantages of both CF and BF.When resin content was 35% by volume fraction,the comprehensive mechanical performance of BF/CF reinforced phenolic resin composites reached the optimal values with the warp and weft direction tensile strength,compressive strength and interlayer shear strength being 252 MPa and 487 MPa,105 MPa and 129 MPa,21 MPa and 20 MPa,respectively.The scanning electron microscope（SEM） observations showed that the BF/CF hybrid fibers reinforced composites had better interfacial adhesion.
文摘A novel super-hybrid composite (NSHC) is prepared with three-dimension reticulated SiC ceramic (3DRC), high performance carbon fibers and modified phenolic resin (BPR) in this paper. Ablation performance of super-hybrid composite is studied. The results show that the NSHC has less linear ablation rate compared with pure BPR and CF/BPR composite, for example, its linear ablation rate is 50% of CF/BPR at the same fiber content. Mass ablation rate of the NSHC is slightly lower than that of pure BPR and CF/BPR composite because of their difference in the density. Scanning electron microscopic analysis indicates that 3DRC can increase anti-erosion capacity of materials because its special reticulated structure can control the deformation of materials and strengthen the stability of integral structure.
文摘碳纤维混杂增强复合材料由于具有重量轻、可设计性强等诸多优点,广泛用于汽车、海洋、航空航天等行业.根据固化剂与环氧树脂的配比化学原理,计算出石墨烯-碳纤维混杂增强树脂基(GO-CF/EP)复合材料的最佳配比为1∶5,并采用真空浸渗热压成型工艺(VIHPS)制备1∶2~1∶7共六个配比的试样,结合形状记忆性能测试及微观形貌的观察,得到固化剂与环氧树脂实际最佳配比.实验结果表明,GO-CF/EP复合材料性能主要取决于体系中交联度的大小,交联度越大,复合材料的形状记忆性能越好,微观组织形貌也较理想.当基体配比为1∶5时,GO-CF/EP复合材料体系中交联度最大,微观形貌呈现均匀致密的状态,形状固定率最大,为95.90%;形状回复率最大,为95.40%;形状回复时间最短,为80.30 s;形状回复力最大,为9.48 N.当基体配比为1∶2或1∶7时,固化剂过量或不足,交联度较小,微观组织形貌中有大量的基体聚集区,其形状记忆性能下降,形状固定率及回复率也相应减小,分别为82.99%,81.66%,81.91%,78.75%;形状回复力分别只有5.20 N和5.50 N.
文摘The role of nanofillers in reducing the microleakage of dental composite resins has not been previously investigated. So this study was designed to evaluate microleakage of nanofilled composite resin in comparison to the conventional hybrid composite. Twenty extracted sound molars were selected. Class II cavities were prepared. All cavities were etched (enamel and dentin) with 37% phosphoric acid. Dentin bonding agents were applied to etched tooth surfaces and restored with nanofilled and hybrid composite restorative materials. The restored teeth were thermocycled. Specimens were immersed in 2% methylene blue dye, sectioned along the mesio-distal direction;dye penetration of occlusal and gingival margins of each section was evaluated using a stereo-microscope. No significant difference was found between the microleakage of nanofilled and hybrid composite restorations at occlusal / enamel and at gingival / dentin margins. Also, there were no significant differences for nanofilled composite restorations at occlusal / enamel margins and gingival / dentin margins. On the other hand, there were a significant differences for hybrid composite restorations at occlusal / enamel margins and gingival / dentin margins.
文摘New liquid free radical-cationic hybrid photopolymer, consisting of acrylate-based photocurable resin and epoxy-based photosensitive resin for stereolithography by UV laser was developed. The experiment results indicated that the hybrid photopolymer exhibits advantages of both the acrylate-based photosensitive resin and the epoxy-based photosensitive polymer contained in the hybrid system with relatively high photospeed and low linear shrinkage. Stereolithography parts without obvious distortion were built on the stereolithography apparatus HRPLA- I from this hybrid resin successfully and efficiently.