Effect of Fluoride on the Ion-association of Calcium Phosphate and Crystallization of Hydroxyapatite

Using a titration setup to accurately control the reaction conditions and in situ monitor the reaction,we showed that fluoride exhibited negligible effects on the ion association process of calcium and phosphate and the formation of ACP nanospheres in a buffer solution with constant ionic strength.However,the stability of ACP increased with increasing fluoride concentration,which was ascribed to the inhibitory effect of fluoride on the aggregation of ACP nanospheres and the nucleation of nanocrystals on the surface of ACP nanospheres.Furthermore,fluoride could inhibit the lateral growth of HAP nanosheets and promote the formation of rod-like crystals.These results further improve our understanding of the crystallization pathway of HAP crystals and the regulatory effects of fluoride.

Characterization of Hydroxyapatite Extracted from Crab Shell Using the Hydrothermal Method with Varying Holding Times

Hydroxyapatite(HA)is a bio ceramic commonly utilized in bone tissue engineering due to its bioactive and osteoconductive properties.Crab shells are usually disregarded as waste material despite their significant CaCO_(3) content,and have not been widely utilized in the synthesis of HA.This study aims to synthesize and analyze HA derived from crab shells using the hydrothermal method with different durations of holding time.This study utilized precipitated calcium carbonate(PCC)derived from crab shells.With a hydrothermal reactor set at 160°C and varying holding times of 14(HA_14),16(HA_16),and 18(HA_18)h,a PCC and(NH4)2HPO4 mixture was used to synthesize HA.The synthesis results were analyzed using scanning electron microscopy(SEM),fourier transform infrared spectroscopy(FTIR),and X-ray diffraction(XRD)tests.This study has accomplished the synthesis of HA from crab shells.Nonetheless,the final product of synthesis still contained CaCO_(3) as an impurity.The prolonged hydrothermal holding time of 14 to 18 h resulted in a reduction of impurities while increasing the percentage of crystal weight and crystallite size of HA.Specimen CH_18 is the best-quality product generated in this study.This specimen produced HA with the highest percentage of crystal weight and crystallite size compared to the other specimens.Furthermore,specimen CH_18 exhibited the lowest concentration of impurities.The Ca/P ratio in this specimen was also the closest to 1.67.The Ca/P ratio,crystallite size,and crystal weight percentage of this specimen are 1.54,19.06 nm,and 99.1%,respectively.

Bio-inspired Hydroxyapatite/Gelatin Transparent Nanocomposites

Hydroxyapatite(HA)nanoparticles impart outstanding mechanical properties to organicinorganic nanocomposites in bone.Inspired by the composite structure of HA nanoparticles and collagen in bone,a high performance HA/gelatin nanocomposite was first developed.The nanocomposites have much better mechanical properties(elongation at break 29.9%,tensile strength 90.7 MPa,Young’s modulus 5.24 GPa)than pure gelatin films(elongation at break 9.3%,tensile strength 90.8 MPa,Young’s modulus 2.5 GPa).In addition,the composite films keep a high transmittance in visible wavelength range from 0%to 60%of the HA solid content.These differences in properties are attributed to the homogeneous distribution of HA nanoparticles in the gelatin polymer matrix and the strong interaction between the particle surfaces and the gelatin molecules.This protocol should be promising for HA-based nanocomposites with enhanced mechanical properties for biomedical applications.

Ionic liquid-assisted preparation of hydroxyapatite and its catalytic performance for decarboxylation of itaconic acid

The synthesis of methacrylic acid from biomass-derived itaconic acid is a green route,for it can get rid of the dependence on fossil resource.In order to solve the problems on this route such as use of a preciousmetal catalyst and a corrosive homogeneous alkali,we prepared a series of hydroxyapatite catalysts by an ionic liquid-assisted hydrothermal method and evaluated their catalytic performance.The results showed that the ionic liquid[Bmim]BF_(4) can affect the crystal growth of hydroxyapatite,provide fluoride ion for fluorination of hydroxyapatite,and adjust the surface acidity and basicity,morphology,textural properties,crystallinity,and composition of hydroxyapatite.The[Bmim]BF4 dosage and hydrothermal temperature can affect the fluoride ion concentration in the hydrothermal system,thus changing the degree of fluoridation of hydroxyapatite.High fluoride-ion concentration can lead to the formation of CaF_(2) and thus significantly decrease the catalytic performance of hydroxyapatite.The hydrothermal time mainly affects the growth of hydroxyapatite crystals on the c axis,leading to different catalytic performance.The suitable conditions for the preparation of this fluoridized hydroxyapatite are as follows:a mass ratio of[Bmim]BF4 to calcium salt=0.2:1,a hydrothermal time of 12 h,and a hydrothermal temperature of 130℃.A maximal methacrylic acid yield of 54.7%was obtained using the fluoridized hydroxyapatite under relatively mild reaction conditions(250℃ and 2 MPa of N_(2))in the absence of a precious-metal catalyst and a corrosive homogeneous alkali.

Influence of Ca/P ratio on the catalytic performance of hydroxyapatite for decarboxylation of itaconic acid to methacrylic acid

Methacrylic acid,an important organic chemical,is commercially manufactured starting from fossil feedstock.The decarboxylation of itaconic acid derived for biomass is a green route to the synthesis of methacrylic acid.In view of the problems existing in the researches on this route such as use of noble metal catalyst,harsh reaction conditions and low desired-product yield,we prepared a series of hydroxyapatite catalysts with different Ca/P molar ratios and evaluated their catalytic performance.The results showed that the hydroxyapatite catalyst with a Ca/P molar ratio of 1.58 had the best catalytic activity.The highest yield of MAA up to 61.2%was achieved with basically complete conversion of itaconic acid under the suitable reaction conditions of 1 equivalent of NaOH,2 MPa of N_(2),250℃,and 2 h.On this basis,a reaction network for the decarboxylation of itaconic acid to methacrylic acid catalyzed by hydroxyapatite was established.With the aid of catalyst characterization using X-ray powder diffraction,NH3/CO2 temperature-programmed desorption,N_(2)physisorption,inductively coupled plasma optical emission spectrometry,and scanning electron microscopy,we found that the distribution of surface acid sites and basic sites,crystal growth orientation,texture properties and morphology of hydroxyapatite varied with the Ca/P molar ratio.Furthermore,the change of the crystal growth orientation and its influence on the surface acidity and alkalinity were clarified.

Hydroxyapatite-containing PEO-coating design for biodegradable Mg-0.8Ca alloy: Formation and corrosion behaviour

In this study, the biocompatible protective coating was formed using plasma electrolytic oxidation(PEO) on bioresorbable Mg-0.8Ca alloy. The composition of the formed coating was studied using XRD, SEM-EDX analysis, and micro-Raman spectroscopy. The uniform distribution of hydroxyapatite over the thickness of protective PEO-layer was established. Using traditional(EIS, PDP, OCP) and local scanning electrochemical methods(SVET, SIET with H^(+)-selective microelectrode), the level of protective properties of PEO-layer in a biological environment(mammalian cell culture medium, MEM) was determined. It was established that modification of Mg-0.8Ca alloy surface by PEO contributes to a significant increase in the corrosion resistance of the surface layer, making it possible to control the process of material‘s biodegradation. The maximum local electrochemical activity was recorded after 72 h of testing, while for the uncoated sample,intense corrosion degradation was recorded in the first 12 min of exposure to the cell culture medium. Formation of the PEO-coating results in a twofold decrease in the corrosion current density(2.8·10^(-6)A cm^(-2)) and an increase in the impedance modulus measured at a low frequency(1.7·10^(4)Ω cm^(2)) in comparison with the uncoated material(9.5·10^(-6)A cm^(-2);8.1·10^(3)Ω cm^(2)). The mechanism of material bioresorption was established and a model for biodegradation process of Mg-0.8Ca alloy with hydroxyapatite-containing PEO-coating in MEM was proposed. Analysis of these results and comparing with others obtained by various scientific groups indicate the prospects for application of biocompatible PEO-coating on Mg-Ca alloy in implant surgery.

Corrosion behavior of composite coatings containing hydroxyapatite particles on Mg alloys by plasma electrolytic oxidation: A review

Mg and its alloys have been introduced as promising biodegradable materials for biomedical implant applications due to their excellent biocompatibility, mechanical behavior, and biodegradability. However, their susceptibility to rapid corrosion within the body poses a significant challenge and restricts their applications. To overcome this issue, various surface modification techniques have been developed to enhance the corrosion resistance and bioactivity of Mg-based implants. PEO is a potent technique for producing an oxide film on a surface that significantly minimizes the tendency to corrode. However, the inevitable defects due to discharges and poor biological activity during the coating process remain a concern. Therefore, adding suitable particles during the coating process is a suitable solution. Hydroxyapatite(HAp)has attracted much attention in the development of biomedical applications in the scientific community. HAp shows excellent biocompatibility due to its similarity in chemical composition to the mineral portion of bone. Therefore, its combination with Mg-based implants through PEO has shown significant improvements in their corrosion resistance and bioactivity. This review paper provides a comprehensive overview of the recent advances in the preparation, characterization, corrosion behavior and bioactivity applications of HAp particles on Mg-based implants by PEO.

Synthesis of Crystalline Hydroxyapatite from CaCO_3 and CaHPO_4·2H_2O by Mechanochemical Method

The mixture of CaHPO 4·2H 2O and CaCO 3 was ground in an aqueous system under appropriate conditions to investigate the mechanochemical reaction for the synthesis of crystalline hydroxyapatite (HA) powder. Hydroxyapatite of high crystallinity powder including trace Ca 10 (PO 4) 6CO 3(OH) and Ca 9HPO 4(PO 4) 6OH can be synthesized by mechanical activation without further thermal treatment at a high temperature. The synthesis reaction during the grinding process was almost completed within 1h. The as-ground powder exhibits a particle distribution of 20-100nm in size with a spherical or rodlike morphology. The composition and degree of crystallinity of the mechanochemical synthesized hydroxyapatite powders were coincident with the cement-type hydroxyapatite.

Synthesis and characterization of arginine-modified and europium-doped hydroxyapatite nanoparticle and its cell viability

The arginine-modified and europium-doped hydroxyapatite nanoparticles（HAP-Eu） were synthesized by hydrothermal synthesis.The prepared nanoparticles were characterized by transmission electron microscopy（TEM）,X-ray diffractometry（XRD）,Fourier transform infrared（FTIR） and zeta potential analyzer.The cell viability of HAP-Eu was tested by image flow cytometry.The results indicated that HAP-Eu is short column shapes and its size is approximately 100 nm,its zeta potential is about 30.10 mV at pH of 7.5,and shows no cytotoxicity in human epithelial cells and endothelial cells.

2022-2023年山东省A(H1N1)pdm09流感病毒HA、NA基因变异特征分析

目的 了解山东省2022-2023流感监测年度分离的A(H1N1)pdm09亚型流感病毒血凝素(hemagglutinin,HA)和神经氨酸酶(neuraminidase,NA)基因的变异特征,为流感的防控提供科学依据。方法 从流感监测网络实验室分离的流感毒株中按地市随机选取14株A(H1N1)pdm09亚型流感毒株,以WHO推荐的当季疫苗株为参考进行全基因组测序,并采用荧光法开展神经氨酸酶抑制(neuraminidase inhibition,NI)实验以评估药物敏感性。结果 山东省2022-2023年度分离的A(H1N1)pdm09流感病毒属于6B.1A分支中的5a.2a进化簇,核苷酸序列比对分析显示,HA和NA基因与2021-2023年度北半球疫苗株A/Victoria/2570/2019的亲缘关系较为接近,同源性分别为98.5%~98.7%和98.8%~99.1%。氨基酸序列分析显示,HA蛋白有20个位点发生了氨基酸序列变异,并发现1株病毒可能发生抗原漂移,有3株病毒发生了HA蛋白糖基化位点的缺失。NA酶相关重要位点未发生变异。NI实验显示,所测流感毒株均对抗流感病毒药物敏感。结论 所监测毒株与疫苗株整体同源性很高,但氨基酸存在一定程度变异,今后有必要持续开展流感病毒基因变异特征监测以了解流感流行的风险,以及评价基因变异对流感疫苗和治疗药物效果的影响。

电化学沉积时间对碱预处理钛合金表面HA涂层的影响

采用碱预处理钛合金表面再电化学沉积的方法,研究了电化学沉积时间对羟基磷灰石(HA)涂层物相、形貌、生物活性及其与钛合金基体间结合强度的影响。结果表明,碱预处理钛合金表面制备的电化学沉积涂层主要由片状HA相组成,电化学沉积时间对涂层物相组成没有影响,但会影响涂层厚度;沉积时间60 min时得到的HA涂层较致密,与基体的结合强度达17.85 MPa。各沉积时间下得到的HA涂层均具有较好的生物活性,在模拟体液(SBF)中,CO_(3)^(2-)置换HA中的PO_(4)^(3-)进入磷灰石中形成类骨磷灰石CHA,呈馒头状,直径7~8μm,且在SBF中浸泡3 d,CHA可铺满HA表面。

基于SPARTA框架的HAS4决赛攻击路径分析

太空网络面临的安全威胁越来越多,美国自2020年起,连续四年举办黑掉卫星(Hack-A-Sat,HAS)挑战赛,并发射真实卫星“月光者”用于HAS比赛。太空攻击研究与战术分析框架SPARTA是针对太空网络安全的对抗战术和技术知识库。借助SPARTA框架,详细分析了第四届HAS决赛中攻击使用的战术技术,对于深入理解SPARTA框架、太空网络安全具有一定借鉴意义。

Cytotoxinic Mechanism of Hydroxyapatite Nanoparticles on Human Hepatoma Cell Lines

Stable and single dispersed HAP nanoparticles were synthesized with chemical method assisted by ultrasonic treatment.HAP nanoparticles were surveyed by AFM and Zataplus.The effect on the Bel-7402 human hepatoma cell lines treated with HAP nanoparticles was investigated by the MTT methods and observation of morphology,and the mechanism was studied in changes of cell cycle and ultrastructure.The result shows that inhibition of HAP nanoparticles on the Bel 7402 human hepatoma cell lines is obviously in vitro.HAP nanoparticles the entered cancer cytoplasm,and cell proliferation is stopped at G 1 phase of cell cycle,thus,cancer cells die directly.

Hot pressing of hydroxyapatite(HA)-Ti material and stability of HA

Hot pressing of hydroxyapatite(HA) Ti system material and the stability of HA component were investigated to supply the foundation of optimizing sintering procedure of HA Ti functionally graded material(FGM). The results show that the HA powders used have excellent thermal stability and no decomposition is observed at 1 300 ℃. The existence of Ti can promote the dehydration and decomposition of HA. However, no new compounds form between HA and Ti. By selecting sintering parameters properly, ideal HA Ti material can be acquired. The relative densities of the mixtures of HA and Ti are always lower than those of pure HA or Ti, which may be caused by the decomposition of HA in the mixtures.

H5N1亚型禽流感病毒HA蛋白在水稻胚乳中的表达及其纯化

为制备H5N1亚型禽流感病毒HA蛋白并评估其免疫原性,利用水稻表达系统表达H5N1亚型禽流感病毒重组HA蛋白。首先构建了重组植物表达载体pCAMBIA1300-HA,该载体具有GT13特有启动子、信号肽SP和终止子,有利于外源基因在水稻中表达。之后将重组质粒pCAMBIA1300-HA通过电转化法导入根癌农杆菌EHA105中,筛选出阳性菌落并侵染水稻愈伤组织。经过暗培养、潮霉素筛选、分化、生根、成苗,采用CTAB法提取水稻叶片DNA,PCR鉴定结果显示,HA基因已插入到水稻基因组中,重组HA基因大小为4660 bp。将阳性植株移植到大田中,4个月后收获水稻种子,提取水稻胚乳蛋白,Western blot鉴定结果表明,HA蛋白在水稻胚乳中成功表达。重组HA蛋白通过Q阴离子层析、疏水层析和凝胶过滤层析三步分离纯化,其纯度达到90%以上。最后将纯化后的重组HA蛋白与ISA 50V佐剂混合并乳化制成疫苗,免疫小鼠,小鼠血清具有较高的特异性抗体水平,表明重组HA蛋白免疫原性较好。综上,成功构建了H5N1亚型禽流感病毒HA重组蛋白的水稻表达系统,并分离纯化获得了高纯度和免疫原性良好的重组HA蛋白。

Preparation, Characterization and Antibacterial Property of Cerium Substituted Hydroxyapatite Nanoparticles

Nanoparticles of hydroxyapatite （HAP） and cerium substituted hydroxyapatite （CeHAP） with the atomic ratio of Ce/[ Ca ＋ Ce] （xco） from 0 to 0.2 were prepared by sol-gel-supercritical fluid drying （SCFD） method. The nanoparticles were characterized by TEM, XRD, and FT-IR, and the effects of cerium on crystal structure, crystallinity, and particle shape were discussed. With the tests of bacterial inhibition zone and antibacterial ratio, the antibacterial property of HAP and CeHAP nanoparticles on Escherichia coli, Staphylococcus aureus, Lactobacillus were researched. Results showed that the nanoparticles of HAP and CeHAP could be made by sol-gel-SCFD, cerium could partially substitute for calcium and enter the structure of HAP. After substitution, the crystallinity, the IR wavenumbers of bonds in CeHAP decreased gradually with increase of cerium substitution, and the morphology of the nanoparticles changed from the short rod-shaped HAP to the needle-shaped CeHAP. The nanoparticles of HAP and CeHAP with Xco below 0.08 had antibacterial property only forcibly contacting with the test bacteria at the test concentration of 0.1 g · mi^-1, however, the Ce- HAP nanoparticles had antibacterial ability at that concentration no matter statically or dynamically contacting with the test bacteria when Xco was above 0.08, and the antibacterial ability gets better with the increase Of Xce, indicating that the antibacterial property was improved after calcium was partially substituted by cerium. The improved antibacterial effects of CeHAP nanoparticle on Lactobacillus showed its potential ability to anticaries.

Morphology and Phase Compositions of Hydroxyapatite Powder Particles Plasma-sprayed into Water

Hydroxyapatite powder particles were plasma sprayed into water, their inner structures and phase compositions were studied by using scanning electron microscope(SEM) and X-ray diffractometer. The results show that the molten HA particles have a central hollow morphology and high crystallinity. The hollow morphology was caused by sublimated P2O5 and H2O, which will have an effect on surface morphology, cohesive and adhesive strength as well as dissolution and degradation of coating. The high crystallinity is attributed to lower cooling speed in water.

HA/H_(2)O_(2)体系对磺胺噻唑降解的机理与效能

以盐酸羟胺/过氧化氢(HA/H_(2)O_(2))作为研究体系,考察其对于磺胺噻唑(STZ)的降解效能。文章考察了HA初始浓度、H_(2)O_(2)初始浓度、STZ初始浓度、pH、天然有机物(NOM)、阴离子(SO_(4)^(2-)、Cl-和NO_(3)^(-))对STZ降解的影响。结果表明:在pH值=3.0的条件下,HA/H_(2)O_(2)体系对STZ具有高效的降解效果,当HA的物质的量浓度由2 mmol/L增加到10 mmol/L时,对STZ的去除率从56.06%增加到85.26%;当H_(2)O_(2)的物质的量浓度从2 mmol/L增加到10 mmol/L时,对STZ的去除率从58.96%增加到85.26%,当STZ的物质的量浓度从2μmol/L增加到10μmol/L时,对STZ的去除率从98.72%降低到71.86%。随着pH的增大,STZ的去除率逐渐降低,在pH值>7的条件下对STZ的去除率可以忽略不计。向反应体系中分别投加5 mmol/L的SO_(4)^(2-)和5 mmol/L的NO_(3)^(-)都可以有效促进STZ的降解,而5 mmol/L的Cl^(-)则会抑制STZ的降解。当向体系中投加小于5 mg/L的NOM则对STZ的降解的影响可以忽略不计。测定了体系中共有17种降解产物,并推测STZ通过取代反应、羟基化反应等方式逐步被降解。通过明亮发光杆菌发光值变化分析降解过程中溶液毒性的变化,测定发现STZ降解过程中急性毒性不高。实际水体试验结果表明,HA/H_(2)O_(2)系统对二级出水中的荧光类物质具有较好的降解效果。

Synthesis,Characterization and Antibacterial Property of Strontium Half and Totally Substituted Hydroxyapatite Nanoparticles

Nanoparticles of hydroxyapatite（HAP）, strontium half substituted hydroxyapatite （SrCaHAP） and strontium totally substituted hydroxyapatite （SrHAP） were prepared by sol-gel-supercritical fluid drying （SCFD） method. The nanoparticles were characterized by element content analysis, FT-IR, XRD and TEM, and the effects of strontium substitution on crystal structure, crystallinity, particle shape and antibacterial properties of the nanoparticles on Escherichia coli, Staphylococcus aureus, Lactobacillus were researched. Results show that strontium can half and totally substitute for calcium and enter the structure of apatite according to the initial atomic ratios of Sr/[Sr＋Ca] as 0.5, 1. The substitution decreases the IR wavenumbers of SrCaHAP and SrHAP, and changes the morphology of the nanoparticles from short rod shaped HAP to needle shaped SrCaHAP, and back to short rod shaped SrHAP. The crystallinity of HAP is higher than that of SrCaHAP, but is lower than that of SrHAP. Moreover, the antibacterial property of SrCaHAP and SrHAP are improved after the calcium is half and totally substituted by strontium.

Synthesis and Characterization of Core-shell Hydroxyapatite/chitosan Biocomposite Nanospheres

Novel core-shell hydroxyapatite/chitosan biocomposite nanospheres were synthesized in a multiple emulsion. The multiple emulsion was a w/o/w emulsion, made of diammonium phosphate solution as an inner aqueous phase, cyclohexane as an oil phase, and calcium nitrate solution and chitosan solution as an outer aqueous. The forming mechanism of core-shell spheres and the influence of temperature on the morphology of the nanospheres were investigated. The diameter of the resulting core-shell nanospheres was 100-200 nm and the thickness of the chitosan shell was about 10 nm. And it concluded that at different reaction temperature the morphologies of the products would be changed. The core-shell nanospheres have potential applications for the development of new biomedical materials.